Project : Combined Materials Testing Results (Simple)

Unisono Iv, 94

Creation Baumann

Temporary

2020-04-09

MMA

Oddy test (method: 20190226_OT_1)

Color: white; fine woven, 100% cotton fabric; washed with detergent by manufacturer before testing; 150 cm width, 240 g/m^2; Purchased Jan 2020

White

fabric, linen), natural (eg.: cotton

Unisono Iv, 401

Creation Baumann

Temporary

2020-03-26

MMA

Oddy test (method: 20190226_OT_1)

Color: yellow, mustard; fine woven, 100% cotton fabric; washed with detergent by manufacturer before testing; 150 cm width, 240 g/m^2; batch 40_45607, Purchased December 2019

Yellow

fabric, linen), natural (eg.: cotton

Unisono Iv, 413

Creation Baumann

Temporary

2020-03-26

MMA

Oddy test (method: 20190226_OT_1)

Color: green; fine woven, 100% cotton fabric; washed with detergent by manufacturer before testing; 150 cm width, 240 g/m^2; Batch 40_58717, Purchased Jan 2020

Green

fabric, linen), natural (eg.: cotton

Angelsuede (blue Stone)

Fishman's Fabrics

Suitable

Consistent with Control

2019-07-19

FMNH

Oddy test

Blue, dark; Polyester woven fabric 58""W

Blue, Dark

exhibition/woven, fabric

Angelsuede (bone)

Fishman's Fabrics

Temporary

Consistent with Control

2019-01-04

FMNH

Oddy test

White, Off-white or cream; Polyester woven fabric

Off-White

exhibition/woven, fabric

Angelsuede (burgundy)

Fishman's Fabrics

Unsuitable

Consistent with Control

2018-01-12

FMNH

Oddy test

Red, dark; Polyester woven fabric 56"W

Dark, Red

exhibition/woven, fabric

Angelsuede (cappuccino)

Fishman's Fabrics

Suitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Beige; Polyester woven fabric 58"W

Beige

exhibition/woven, fabric

Angelsuede (cedar)

Fishman's Fabrics

Suitable

Consistent with Control

2017-09-18

FMNH

Oddy test

Beige; Polyester woven fabric

Beige

exhibition/woven, fabric

Angelsuede (chamois)

Fishman's Fabrics

Temporary

Consistent with Control

2019-01-04

FMNH

Oddy test

Polyester woven fabric 58"W

Polyester

exhibition/woven, fabric

Angelsuede (charcoal)

Fishman's Fabrics

Unsuitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Grey, dark; Polyester woven fabric 58"W

Dark, Gray

exhibition/woven, fabric

Angelsuede (chocolate)

Fishman's Fabrics

Suitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Brown; Polyester woven fabric 58"W

Brown

exhibition/woven, fabric

Autex

Autex Interior Acoustics

Suitable

Consistent with Control

2017-02-17

AWMM

Oddy test

In vitrine or case

grey; flatiron

Gray

exhibition/woven, fabric

Angelsuede (dark Brown)

Fishman's Fabrics

Unsuitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Brown; Polyester woven fabric 58"W

Brown

exhibition/woven, fabric

Angelsuede (grey)

Fishman's Fabrics

Unsuitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Grey; Polyester woven fabric 58"W

Gray

exhibition/woven, fabric

Angelsuede (kiwi)

Fishman's Fabrics

Unsuitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Polyester woven fabric 58"W

Polyester

exhibition/woven, fabric

Angelsuede (ocean)

Fishman's Fabrics

Suitable

Consistent with Control

2017-10-24

FMNH

Oddy test

Blue; Polyester woven fabric

Blue

exhibition/woven, fabric

Angelsuede (periwinkle)

Fishman's Fabrics

Suitable

Consistent with Control

2019-11-01

FMNH

Oddy test

Blue, light; Polyester, nappy surface

Blue, Light

exhibition/woven, fabric

Angelsuede (pewter)

Fishman's Fabrics

Suitable

Consistent with Control

2017-09-18

FMNH

Oddy test

Grey; Polyester woven fabric

Gray

exhibition/woven, fabric

Angelsuede (sand)

Fishman's Fabrics

Suitable

Consistent with Control

2017-09-18

FMNH

Oddy test

Beige; Polyester woven fabric

Beige

exhibition/woven, fabric

Angelsuede (silver)

Fishman's Fabrics

Suitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Grey; Polyester woven fabric 58"W

Gray

exhibition/woven, fabric

Angelsuede (snow)

Fishman's Fabrics

Suitable

Consistent with Control

2017-09-18

FMNH

Oddy test

White; Polyester woven fabric

White

exhibition/woven, fabric

Angelsuede (terracotta)

Fishman's Fabrics

Suitable

Consistent with Control

2017-10-24

FMNH

Oddy test

Red/brown; Polyester woven fabric

Brown, Red

exhibition/woven, fabric

Angelsuede (thunder)

Fishman's Fabrics

Suitable

Consistent with Control

2017-09-18

FMNH

Oddy test

Brown/Grey; Polyester woven fabric

Brown, Gray

exhibition/woven, fabric

Buffalo Batt

Buffalo Batt And Felt, University Products

Suitable

Consistent with Control

2015-09-30

FMNH

Oddy test

Polyester fiber fill

Polyester

batting & padding, fabric

Dye-namix 8mm Habotai Unprinted Silk Fabric

Dye-namix

Suitable

Consistent with Control

2016-09-13

FMNH

Oddy test

8mm Habotai unprinted silk fabric

exhibition/woven, fabric

Dye-namix Silk 8mm Inkjet Printed

Dye-namix

Suitable

Consistent with Control

2016-09-13

FMNH

Oddy test

Blue; Silk fabric, direct dye, InkJet Printed, Habotai base fabric

Blue

exhibition/woven, fabric

Felt With Acrylic Adhesive (black), 35-111bk

Benchmark Catalog

Suitable

Consistent with Control

2018-01-12

FMNH

Oddy test

Black; Polyester felt with acrylic adhesive

Black

batting & padding, fabric

Felt With Acrylic Adhesive (cool Grey), 31-111cg

Benchmark Catalog

Suitable

Consistent with Control

2017-10-24

FMNH

Oddy test

Grey, dark; Polyester felt with acrylic adhesive

Dark, Gray

batting & padding, fabric

Felt With Acrylic Adhesive (ivory), 31-111iv

Benchmark Catalog

Temporary

Consistent with Control

2018-03-30

FMNH

Oddy test

White, Off-white or cream; Polyester felt with acrylic adhesive

Off-White

batting & padding, fabric

Felt With Acrylic Adhesive (moss), 31-111mo

Benchmark Catalog

Suitable

Consistent with Control

2018-03-30

FMNH

Oddy test

Green; Polyester felt with acrylic adhesive

Green

batting & padding, fabric

Felt With Acrylic Adhesive (oat), 31-111ot

Benchmark Catalog

Suitable

Consistent with Control

2018-03-30

FMNH

Oddy test

Beige; Polyester felt with acrylic adhesive

Beige

batting & padding, fabric

Felt With Acrylic Adhesive (smoke), 31-111sm

Benchmark Catalog

Suitable

Consistent with Control

2017-10-24

FMNH

Oddy test

Grey; Polyester felt with acrylic adhesive

Gray

batting & padding, fabric

Felt With Acrylic Adhesive (tan), 31-111tn

Benchmark Catalog

Suitable

Consistent with Control

2018-01-12

FMNH

Oddy test

Beige; Polyester felt with acrylic adhesive

Beige

batting & padding, fabric

Felt With Acrylic Adhesive (terracotta), 31-111tc

Benchmark Catalog

Suitable

Consistent with Control

2018-01-12

FMNH

Oddy test

Red/brown; Polyester felt with acrylic adhesive

Brown, Red

batting & padding, fabric

Velling Iii Upholstery Fabric (batch 86)

Creation Baumann

Unsuitable

Consistent with Control

2019-09-26

AMNH

Oddy test

AMNH test #233

grey; Fabric swatc - 100% cotton velour

Gray

exhibition/woven, fabric

Flame-retardant Heavy Weight Muslin, Mush0007

Rosebrand East

Suitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Grey; Heavy extra-wide 100% cotton with flame retardant

Gray

exhibition/woven, fabric

Movie-weight Flame-retardant Muslin, Mush 0005

Rosebrand East

Suitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Grey, light; Extra-wide 100% cotton muslin with flame retardant

Gray, Light

exhibition/woven, fabric

Poly-felt Punched Fleece 1/8", Virgin Polyester

University Products

Suitable

Consistent with Control

2017-10-24

FMNH

Oddy test

White; Virgin polyester

White

exhibition/woven, fabric

Poly-fil

Fairfield Processing

Suitable

Consistent with Control

2015-09-30

FMNH

Oddy test

White; Low-loft polyester batting

White

batting & padding, fabric

Polyester Batting, Virgin, 979-1000

University Products

Suitable

Consistent with Control

2018-03-30

FMNH

Oddy test

White; Polyester batting, .75" loft

White

batting & padding, fabric

Polyester Felt 1/4" Thick, Virgin, 50078

Gaylord Archival

Suitable

Consistent with Control

2018-01-12

FMNH

Oddy test

White; 1/4" polyester, 100% virgin polyester, needle- punched

White

batting & padding, fabric

Pongee Plus (black), M-luc1217mmq-nwa

Vogue Fabrics

Suitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Black; Polyester

Black

exhibition/woven, fabric

Pongee Plus (cashmere), M-luc417mmq-nwa

Vogue Fabrics

Suitable

Consistent with Control

2018-10-16

FMNH

Oddy test

Beige; Polyester

Beige

exhibition/woven, fabric

Pongee Plus (charcoal)

Vogue Fabrics

Suitable

Consistent with Control

2018-10-16

FMNH

Oddy test

Grey, dark; Polyester

Dark, Gray

exhibition/woven, fabric

Pongee Plus (mauve) M-luc105mmq-nwa

Vogue Fabrics

Suitable

Consistent with Control

2019-01-04

FMNH

Oddy test

Pink, dark; Mauve (pinkish grey), polyester

Dark, Pink

exhibition/woven, fabric

Pongee Plus (off-white), M-luc816mmq-nwa

Vogue Fabrics

Suitable

Consistent with Control

2018-10-16

FMNH

Oddy test

White, Off-white or cream; Polyester

Off-White

exhibition/woven, fabric

Unisono Iii Decoration Fabric (color 303)

Creation Baumann

Temporary

Consistent with Control

2020-01-03

AMNH

Oddy test

AMNH test #273

tan; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Brown, Light

exhibition/woven, fabric

Silk Habotai 8mm, 609/1413007

Test Fabrics

Suitable

Consistent with Control

2016-09-13

FMNH

Oddy test

White; Silk fabric, 8mm

White

exhibition/woven, fabric

Sueded Polyethylene (warm Black) 35-111wb

Benchmark Catalog

Unsuitable

Consistent with Control

2018-01-16

FMNH

Oddy test

Black, warm; Acrylic adhesive-backed sueded-polyethylene, 9x12" sheet

Black

exhibition/woven, fabric

Sueded Polyethylene With Acrylic Adhesive (warm Black), 35-111wb

Benchmark Catalog

Unsuitable

Consistent with Control

2017-10-24

FMNH

Oddy test

Black; Acrylic adhesive-backed sueded-polyethylene

Black

batting & padding, fabric

Sueded Polyethylene With Acrylic Adhesive (white), 35-111wh

Benchmark Catalog

Unsuitable

Consistent with Control

2017-10-24

FMNH

Oddy test

White; Acrylic adhesive-backed sueded-polyethylene

White

batting & padding, fabric

Unisono Iv-0150, 304

Creation Baumann

Benchmark Catalog

Temporary

2018-06-22

MMA

Oddy test

Grey; Finely Woven Grey Fabric Bolt of Cloth Cotton May 2018

Gray

exhibition/woven, fabric

Sueded Polyethylene With Adhesive Backing (brown), 35-111br

Benchmark Catalog

Temporary

Consistent with Control

White/Orange haze

2018-01-16

FMNH

Oddy test

Brown; Acrylic adhesive-backed sueded-polyethylene, 9x12" sheet

Brown

batting & padding, fabric

Unisono Iii Decoration Fabric (color 350)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test

AMNH test #275

brown; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Brown

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Extreme darkening on coupon B, thin orange compacted corrosion, blue tarnish

Sueded Polyethylene With Adhesive Backing (steel Grey), 35-111sg

Benchmark Catalog

Unsuitable

Consistent with Control

Heavy White haze

2017-10-24

FMNH

Oddy test

Grey; Acrylic adhesive-backed sueded-polyethylene

Gray

batting & padding, fabric

Sueded Polyethylene With Adhesive Backing (camel Hair), 35-111cm

Benchmark Catalog

Unsuitable

Slight red discoloration

Consistent with Control

White crystal growth

2018-01-12

FMNH

Oddy test

Brown, Light; Acrylic adhesive-backed sueded-polyethylene, 9x12" sheet

Brown, Light

batting & padding, fabric

Ultrasuede St (aztec Leather), 2223-3636

Toray Industries

Vogue Fabrics

Suitable

Consistent with Control

2019-04-22

FMNH

Oddy test

Brown; 65% polyester ultra-microfiber non-woven with 35% non-fibrous polyurethane binder

Brown

exhibition/woven, fabric

Ultrasuede St (black Onyx), 2223-5813

Toray Industries

Vogue Fabrics

Suitable

Consistent with Control

2019-04-22

FMNH

Oddy test

Black; 65% polyester ultra-microfiber non-woven with 35% non-fibrous polyurethane binder

Black

exhibition/woven, fabric

Plc

Toray Industries

John Ranger Textiles

Suitable

Consistent with Control

2016-05-02

AWMM

Oddy test

In vitrine or case

"drill"; 65% Polyseter, 35% Cotton

65% Polyseter, 35% Cotton

exhibition/woven, fabric

Ultrasuede St (coffee Cream), 2223-0328

Toray Industries

Vogue Fabrics

Suitable

Consistent with Control

2019-04-22

FMNH

Oddy test

Beige; 65% polyester ultra-microfiber non-woven with 35% non-fibrous polyurethane binder

Beige

exhibition/woven, fabric

Ultrasuede St (country Cream), 2223-0357

Toray Industries

Vogue Fabrics

Suitable

Consistent with Control

2019-04-22

FMNH

Oddy test

Beige; 65% polyester ultra-microfiber non-woven with 35% non-fibrous polyurethane binder

Beige

exhibition/woven, fabric

Ultrasuede St (executive Grey), 2223-5609

Toray Industries

Vogue Fabrics

Suitable

Consistent with Control

2019-04-22

FMNH

Oddy test

Grey; 65% polyester ultra-microfiber non-woven with 35% non-fibrous polyurethane binder

Gray

exhibition/woven, fabric

Ultrasuede St (silver Pearl), 2223-0068

Toray Industries

Vogue Fabrics

Suitable

Consistent with Control

Consistent with control

2019-04-22

FMNH

Oddy test

Grey; 65% polyester ultra-microfiber non-woven with 35% non-fibrous polyurethane binder

Gray

exhibition/woven, fabric

Style: 2300-5663 D.B.

Testfabrics

Suitable

2014-03-01

Autry

Oddy test

Unwashed; don't use in contact with object

Black; 98% Bamboo, 2% Spandex Jersey

Black

exhibition/woven, fabric

none

Benchmark Sueded Polyethylene

Benchmark Catalog

Suitable

2017-06-23

BKM

Oddy test

Acrylic-adhesive backed sueded polyethylene;

batting & padding, fabric

Ag: no corrosion,Cu: red- same as control,Pb: no corrosion

Jet Black Cotton Commercial Fabric

Suitable

no change, same as control

green tinge on inside, possibly because in contact with water vial.

2012-02-28

BKM

Oddy test

Black; mid weight twill weave fabric. 100% cotton.

Black

exhibition/woven, fabric

Pongee Plus (off-white), M-luc816mmq-nwa

Vogue Fabrics

Suitable

Consistent with Control

2018-10-16

FMNH

Oddy test

one anomaly Pb coupon that corroded very heavily, likely an issue with test conditions

White, Off-white or cream; Polyester

Off-White

exhibition/woven, fabric

Northern Lights Fleece Solids "light Blue"

Northern Lights

Suitable

2007-03-10

BKM

Oddy test

Blue, light; 100% polyester

Blue, Light

exhibition/woven, fabric

Synthetic Sinew

Jas Townsend & Son

Temporary

2007-02-14

BKM

Oddy test

No tarnish, but roll in bag - color has worn off. TEMP USE ONLY.

waxed nylon strands

fiber or thread

Synthetic Sinew

Jas Townsend & Son

Temporary

2007-02-14

BKM

Oddy test

No tarnish, but roll in bag - color has worn off. TEMP USE ONLY.

waxed nylon strands

fiber or thread

Tribeca Vat-dyed "champagne" Cotton Twill

Test Fabrics

Suitable

great- no tarnish

2007-02-14

BKM

Oddy test

exhibition/woven, fabric

Ag: great- no tarnish,Cu: great- no tarnish,Pb: great- no tarnish

Wonderflex Fosshape (black) Heated With Steam From Iron

Wonderflex World

Suitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days. One sample's lid popped off and moisture escaped

Black; non woven thermoplastic polyester fabric

Black

batting & padding, fabric

Ag: no corrosion,Cu: no corrosion,Pb: no corrosion

Wonderflex Fosshape (black) Unheated

Wonderflex World

Suitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days

Black; non woven thermoplastic polyester fabric

Black

batting & padding, fabric

Ag: no corrosion,Cu: no corrosion,Pb: no corrosion

Pique Ducal 290 Blanco Natural

Textil Batavia

Suitable

no visible corrosion on metal coupons in Oddy test or control

2020-04-29

CRP

Oddy test

Natural/White; 100% Cotton, 290 g/m ^2

Natural, White

exhibition/woven, fabric

no visible corrosion on metal coupons in Oddy test or control

Duero Canvas 200 Blanco Natural

Textil Batavia

Suitable

no visible corrosion on metal coupons in Oddy test or control

2020-04-29

CRP

Oddy test

Natural/White; 100% Polyester, 200 g/m ^2

Natural, White

exhibition/woven, fabric

no visible corrosion on metal coupons in Oddy test or control

100% Wool Flannel, Style 527

Unknown

Testfabrics

Unsuitable

2020-01-02

MMA

Purchased: February 2019

White, off; Natural, 100% wool carbonized flannel fabric, 142 cm width, 268 g/m^2

Off-White

exhibition/woven, fabric

Ultra V 404 Fabric

Creation Baumann

Temporary

2020-01-02

MMA

Oddy test (method: 20190226_OT_1)

Purchased October 2019

Grey; Grey 100% cotton woven fabric, prewashed in detergent, 150 cm width, 240 g/m2

Gray

exhibition/woven, fabric

Peluche 29 Velvet Fabric

Baumann Dekor

Temporary

2020-01-02

MMA

Oddy test (method: 20190226_OT_1)

Black; Black, 100% cotton velvet fabric, ~2mm thick, not prewashed in detergent

Black

exhibition/woven, fabric

100% Wool Flannel, Style 527

Unknown

Testfabrics

Unsuitable

2019-12-12

MMA

Oddy test (method: 20190226_OT_1)

Purchased February 2019

Natural; 100% wool carbonized flannel fabric, 142 cm width, 268 g/m^2

Natural

exhibition/woven, fabric

Revive 1, 224 Fabric

Kvadrat

Temporary

2019-12-12

MMA

Oddy test (method: 20190226_OT_1)

Purchased October 2019

Grey and white; 100% recycled polyester (PET) fire retardant woven fabric, 420 g/lin.m, 140 cm width

Gray, White

exhibition/woven, fabric

Parkland 111 Fabric

Kvadrat

Unsuitable

2019-12-12

MMA

Oddy test (method: 20190226_OT_1)

Purchased October 2019

Grey and white; 100% trevira fire retardant woven fabric, 600 g/lin.m, 140 cm width

Gray, White

exhibition/woven, fabric

Patio 110 Fabric

Kvadrat

Temporary

2019-12-12

MMA

Oddy test (method: 20190226_OT_1)

Purchased October 2019

Grey and white; 100% trevira cs, water repellent fire retardant woven fabric, 560 g/lin.m, 140 cm width,

Gray, White

exhibition/woven, fabric

7 Oz Unbleached, Desized Cotton Duck 464u Cloth

Unknown

Testfabrics

Temporary

2019-11-27

MMA

Oddy test (method: 201900226_OT_1)

Natural; 7 oz unbleached, desized cotton duck, not washed: Purchased September 2019

Natural

exhibition/woven, fabric

Ultra V Decoration Fabric (batch 55554)

Creation Baumann

Temporary

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #223

light blue; Fabric swatch - 100% cotton - Washed and cut to weight

Blue, Light

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Thin orange compacted corrosion, Light white compacted corrosion

Ultra V Decoration Fabric (batch 56815)

Creation Baumann

Temporary

2019-10-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #224

dark blue; Fabric swatch - 100% cotton - Washed and cut to weight

Blue, Dark

exhibition/woven, fabric

Copper: Very slight red tarnish on coupon B - Silver: OK - Lead:Light white compacted corrosion on coupon A, slight darkening on coupon B, Thin Yellow/green compacted corrosion

Ultra V Decoration Fabric (batch 55081)

Creation Baumann

Temporary

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #225

blue/green; Fabric swatch - 100% cotton - Washed and cut to weight

Blue/Green

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead:Slight darkening, Thin Yellow/green compacted corrosion

Ultra V Decoration Fabric (batch 48606)

Creation Baumann

Temporary

OK

Slight darkening, Thin Yellow/green compacted corrosion

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #226

green; Fabric swatch - 100% cotton - Washed and cut to weight

Green

exhibition/woven, fabric

Velos Ii Upholstery Fabric (batch 92316)

Creation Baumann

Unsuitable

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #227

dark blue; Fabric swatch - 100% flame retardant polyester (Trevira CS - comonomer, organophosphorous compound)

Blue, Dark

exhibition/woven, fabric

matte short napped velours

Velos Ii Upholstery Fabric (batch 85276)

Creation Baumann

Temporary

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #228

jade; Fabric swatch - 100% flame retardant polyester (Trevira CS - comonomer, organophosphorous compound)

100% flame retardant polyester (Trevira CS - comonomer, organophosphorous compound)

Green

exhibition/woven, fabric

matte short napped velours

Velos Ii Upholstery Fabric (batch 88104)

Creation Baumann

Temporary

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #229

blue; Fabric swatch - 100% flame retardant polyester (Trevira CS - comonomer, organophosphorous compound)

Blue

exhibition/woven, fabric

matte short napped velours

Velling Iii Upholstery Fabric (batch 43)

Creation Baumann

Unsuitable

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #230; 395 g/m2

gray/green; 100% cotton velour

100% cotton velour

Gray, Green

exhibition/woven, fabric

Velling Iii Upholstery Fabric (batch 81)

Creation Baumann

Unsuitable

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #231; 395 g/m2 - Washed and cut to weight

dark blue; Fabric swatc - 100% cotton velour

Fabric swatch - 100% cotton velour

Blue, Dark

exhibition/woven, fabric

Velling Iii Upholstery Fabric (batch 61)

Creation Baumann

Temporary

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #232; 395 g/m2 - Washed and cut to weight

green; Fabric swatc - 100% cotton velour

Fabric swatch - 100% cotton velour

Green

exhibition/woven, fabric

Velling Iii Upholstery Fabric (batch 86)

Creation Baumann

Unsuitable

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #233; 395 g/m2 - Washed and cut to weight

grey; Fabric swatc - 100% cotton velour

Fabric swatch - 100% cotton velour

Gray

exhibition/woven, fabric

Fosshape Fs 600

Wonderflex World

Test Fabrics

Temporary

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH test #243

white; Heat activated proprietary non-woven synthetic fabric

White

exhibition/woven, fabric

grades 300, 400, 600.

Fosshape Fs 300

Wonderflex World

Test Fabrics

Temporary

OK

Very slight darkening, very slight blue tarnish on the edges

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH test #244

white; Swatch - Heat activated proprietary non-woven synthetic fabric - Cut to weight

White

exhibition/woven, fabric

Wonderflex Wf

Wonderflex World

Test Fabrics

Temporary

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH test #245

white; Swatch - Heat activated composite material

White

exhibition/woven, fabric

contains its own proprietary adhesive - Cut to weight

Ultra V Decoration Fabric (color 0501)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #271

tan; Fabric swatch - 100% cotton, 240 g/m2 - Washed and cut to weight

Brown, Light

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Very slight darkening

Ultra Iv Decoration Fabric (color 414)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #272

brown; Fabric swatch - 100% cotton, 240 g/m2 - Washed and cut to weight

Brown

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Very slight darkening

Unisono Iii Decoration Fabric (color 303)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #273

tan; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Brown, Light

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Very slight darkening

Unisono Iii Decoration Fabric (color 307)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #274

beige; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Beige

exhibition/woven, fabric

Copper: Slight red tarnish - Silver: Light purple tarnish on coupon B on fold - Lead: Very slight darkening

Unisono Iii Decoration Fabric (color 350)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #275

brown; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Brown

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Extreme darkening on coupon B, thin orange compacted corrosion, blue tarnish

Unisono Iii Decoration Fabric (color 351)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #276

brown/ burgundy; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Brown, Red

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Very slight darkening, very thin Yellow/green compacted corrosion

Unisono Iv Decoration Fabric (color 0409)

Creation Baumann

Temporary

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH test #277

blue; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Blue

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Slight darkening, very slight thin Yellow/green compacted corrosion

Unisono Iv Decoration Fabric (color 0412)

Creation Baumann

Temporary

2020-01-07

AMNH

Oddy test (method: 20190130_OT)

AMNH test #280

teal/green; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Green

exhibition/woven, fabric

Copper: Slight red tarnish - Silver: OK - Lead: Darkening, Thin Yellow/green compacted corrosion

Unisono Iv Decoration Fabric (color 0411)

Creation Baumann

Temporary

2020-01-07

AMNH

Oddy test (method: 20190130_OT)

AMNH test #281

dark blue; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Blue, Dark

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Darkening, very thin Yellow/green compacted corrosion

Unisono Iv Decoration Fabric (color 0409)

Creation Baumann

Temporary

2020-01-13

AMNH

Oddy test (method: 20190130_OT)

AMNH test #283

medium blue; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Blue, Medium

exhibition/woven, fabric

Copper: Slight red tarnish - Silver: OK - Lead: Darkening, Thin Yellow/green compacted corrosion

Unisono Iv Decoration Fabric (color 0410)

Creation Baumann

Temporary

2020-01-13

AMNH

Oddy test (method: 20190130_OT)

AMNH test #284

light blue; Fabric swatch - 100% cotton, 211g/m2 - Washed and cut to weight

Blue, Light

exhibition/woven, fabric

Copper: Slight red tarnish - Silver: OK - Lead: Slight darkening, Thin Yellow/green compacted corrosion

Light Weight Cotton Fabric (light Gray)

Joann Fabrics

Temporary

2020-01-13

AMNH

Oddy test (method: 20190130_OT)

AMNH test #285

light gray ; Fabric swatch - 100% cotton - Washed and cut to weight

Blue, Light

exhibition/woven, fabric

Copper: Very slight red tarnish - Silver: OK - Lead: Darkening, Thin Yellow/green compacted corrosion

Faux Suede Fabric (dark Grey)

Joann Fabrics

Temporary

OK

Darkening, Thin Yellow/green compacted corrosion

2020-01-13

AMNH

Oddy test (method: 20190130_OT)

AMNH test #286

dark grey; Fabric swatch - 90% polyester 10% spandex - Washed and cut to weight

Dark, Gray

exhibition/woven, fabric

100% Wool Flannel, Style 527

Testfabrics

Test Fabrics

Unsuitable

2019-11-06

MMA

Oddy test (method: 20190226_OT_1)

Natural; 100% Carbonized wool flannel fabric, 142cm width, 268g/m^2, purchased February 2019

Natural

exhibition/woven, fabric

Haze 104, Woven Fire Retardant Fabric

Kvadrat

Temporary

2019-11-06

MMA

Oddy test (method: 20190226_OT_1)

White; 60% Polyester fire retardant woven fabric, 40% polyester, not washed before testing, model number: 104, 650 g/lin.m, purchased September 2019

White

exhibition/woven, fabric

Haze 164, Woven Fire Retardant Fabric

Kvadrat

Unsuitable

2019-11-06

MMA

Oddy test (method: 20190226_OT_1)

Grey; 60% Polyester fire retardant woven fabric, 40% polyester, not washed before testing, model number: 164, 680 g/lin.m, purchased September 2019

Gray

exhibition/woven, fabric

Haze 134, Woven Fire Retardant Fabric

Kvadrat

Temporary

2019-11-06

MMA

Oddy test (method: 20190226_OT_1)

Grey; 60% Polyester fire retardant woven fabric, 40% polyester, not washed before testing, model number: 134, 680 g/lin.m, purchased September 2019

Gray

exhibition/woven, fabric

Unisono Iii, 316

Creation Baumann

Temporary

2019-11-06

MMA

Oddy test (method: 20190226_OT_1)

Grey; 100% Cotton woven fabric, prewashed with detergent, custom order as the color was discontinued from the line, 150 cm width, 211 g/m^2, purchased September 2019

Gray

exhibition/woven, fabric

Bemberg Rayon, 56995 Woven Fabric

Asahi Kasei

Logantex

Unsuitable

2019-10-24

MMA

Oddy test (method: 20190226_OT_1)

Black; Woven rayon fabric, Bemberg is the brand name for cupro, which is regenerated cellulose fiber made from cotton, refined and dissolved linter transformed into pure regenerated fiber, purchased January 2019

Black

exhibition/woven, fabric

100% Wool Flannel, Style 527

Testfabrics

Unsuitable

2019-10-10

MMA

Oddy test (method: 20190226_OT_1)

Natural; 100% Carbonized wool flannel fabric, 142cm width, 268g/m^2, purchased February 2019

Natural

exhibition/woven, fabric

Bleached Cotton Flannel With Optical Brightener, Style 425

Testfabrics

Unsuitable

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

White; Bleached cotton flannel with optical brightener, napped on both sides, 114cm width, 152g/m^2, Model/Cataolg Number: 1403017, unwashed

White

exhibition/woven, fabric

Unbleached Cotton Flannel, Style 425u

Testfabrics

Unsuitable

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

Cream; Unbleached Cotton Flannel, 114cm width, 125g/m^2, Model/Catalog Number: 1403018

Cream, White

exhibition/woven, fabric

Lorenzo 101 Grey

Baumann Dekor

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT)

Grey, 101 grey; 100% Cotton fabric, not washed before testing, purchased September 2018

Gray

exhibition/woven, fabric

Unisono Iii 311

Creation Baumann

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT)

Taupe; 100% Cotton fabric, Pre-washed in detergent, 150 cm width, 211 g/m^2, purchased August 2018

Brown, Light

exhibition/woven, fabric

Messenger 458640–058 Snow

Maharam

Kvadrat

Temporary

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #10

White; Fabric swatch, 78% Post-Industrial Recycled Polyester, 15% Polyester, 7% Nylon - Cut to weight

White

exhibition/woven, fabric

Copper: very slight red tarnish - Silver: ok - Lead: darkening with blue tarnish around the edges

Ultra V Col 401

Creation Baumann

Temporary

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #12

Grey; Fabric swatch, 100% Cotton - Cut to weight

Gray

exhibition/woven, fabric

Copper: red tarnish, rainbow tarnish, light haze - Silver: ok - Lead: darkening, blue compacted corrosion, white crystal on A contamination from other sample

Lorenzo 009, Cotton Fabric

Baumann Dekor

Temporary

2019-05-23

MMA

Oddy test (method: 20190226_OT), SPME GCMS

Black; Black 100% cotton fabric, Likely not pre-washed with detergent, Purchased: October 2018.

Black

exhibition/woven, fabric

Polyester Felt & Anti-squeak Felt (pe-6.5-60)

Sutherland Felt Company

Unsuitable

2019-05-23

MMA

Oddy test (method: 20190226_OT)

Black; Polyester Felt & Anti-Squeak Felt. Product#: PE-6.5-60, black, Thickness: 1mm, Weight (Oz. Per Sq. Yd.): 6 Oz, GSM (grams per sq mtr): 200, Roll Width:60". Month/Year Purchased: November 2018. This felt tape is used to cushion the painting from the rabbet of the frame.

Black

batting & padding, fabric

Falstaff 6 Point Sharkstooth, Cotton Fabric

Gerriets

Gerriets International

Temporary

2019-05-23

MMA

Oddy test (method: 20190226_OT)

White

exhibition/woven, fabric

Pacific Silvercloth®, Pc3815-3

Unknown

Gaylord Archival

Temporary

2019-03-26

MMA

Oddy test (method: 20190226_OT), SPME GCMS

Black; Silvercloth, black, Catalog Number: PC3815-3, Purchased: December 2018

Black

exhibition/woven, fabric

Evolon Cr Cushion Cover Material, 2219140

Unknown

Deffner And Johann

Temporary

2019-02-27

MMA

Oddy test (method: 20180821_OT), SPME GCMS

White; Cushion covers, outer pillow fabric, Model/Catalog Number: Item no.: 2219140, Details: polyester/ polyamide microfilament fabric, purchased 10/18

White

exhibition/woven, fabric

Fosshape 600, Polyester

Wonderflex World

Temporary

2019-02-13

MMA

Oddy test (method: 20180821_OT)

White; Fosshape, Details: thermoplastic nonwoven polyester, Chemical Components: polyester/co-polyester, purchased december 2018

White

batting & padding, fabric

0.5 Mm Polyester Felt With 3f Br Back, White (acrylic Adhesive)

Sutherland Felt Company

Unsuitable

2017-12-14

MMA

Oddy test (method: 20171116_OT)

white; 0.5 mm thick white polyester felt with acrylic adhesive backing, purchased 10/2017

White

batting & padding, fabric

1.5 Mm Polyester Felt With 3f Br Back, White (acrylic Adhesive)

Sutherland Felt Company

Unsuitable

2017-12-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

white; 1.5 mm thick white polyester felt with acrylic adhesive backing, purchased 10/2017

White

batting & padding, fabric

2.0 Mm Polyester Felt With 3f Br Back, White (acrylic Adhesive)

Sutherland Felt Company

Unsuitable

2017-12-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

white; 2 mm thick white polyester felt with acrylic adhesive backing, purchased 10/2017

White

batting & padding, fabric

Umbria Iii 0155

Creation Baumann

Temporary

2017-12-28

MMA

Oddy test (method: 20171116_OT), SPME GCMS

taupe; 100% flame retardant polyester, purchased April 2017

Brown, Light

exhibition/woven, fabric

Linaria Crash Ii 0229

Creation Baumann

Unsuitable

2017-12-28

MMA

Oddy test (method: 20171116_OT), SPME GCMS

gray purple; 91% Linen 9% polyamide

Gray, Purple

exhibition/woven, fabric

Hollywood Lin, F2832003

Pierre Frey

Temporary

2017-12-28

MMA

Oddy test (method: 20171116_OT), SPME GCMS

blue; pale blue,100% flame retardant polyester, purchased May 2017

Blue

exhibition/woven, fabric

Brooklyn Pensee 14, F2833014

Pierre Frey

Temporary

2017-12-28

MMA

Oddy test (method: 20171116_OT), SPME GCMS

purple; metallic plum,100% flame retardant polyester, purchased May 2017

Purple

exhibition/woven, fabric

0202-3562-1 Off-white Cotton Fabric

Baumann Dekor

Temporary

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

purchased summer 2017

off-white; 100% cotton fabric

Off-White

exhibition/woven, fabric

0402-3817-1 White Cotton/linen Blend Fabric

Baumann Dekor

Temporary

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

purchased summer 2017

white; 100% cotton fabric

White

exhibition/woven, fabric

Unisono Iii 0234 (gray)

Creation Baumann

Temporary

2018-03-26

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Prewashed with detergent

gray; 100% cotton fabric

Gray

exhibition/woven, fabric

Cotton Duck 1060-nat

Unknown

Unsuitable

2018-05-23

Oddy test (method: 20171116_OT)

natural; Cotton duck fabric, 10 oz/sq. yard weight, tightly woven flat weave duck canvas, 100% cotton, shrinkage: approx. 12-15%, purchased 4/2018

Natural

exhibition/woven, fabric

No

Velos Ii 0050

Creation Baumann

Unsuitable

2018-06-28

MMA

Oddy test (method: 20180525_OT), SPME GCMS

grey; Velvet fabric, From a bolt, flame retardant polyester (Trevira), not washed with detergent as the company doesn't have that capability for this fabric line, May 2018,

Gray

exhibition/woven, fabric

Velos Ii, 0011

Creation Baumann

Unsuitable

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

grey; Grey flame retardant polyester fabric, 100% PLF, 100% Flame retardant polyester (Trevira CS), Chemical Components: polyester, trevira, purchased may 2018.

Gray

exhibition/woven, fabric

325 Unisono Iv-150

Creation Baumann

Unsuitable

2018-07-17

MMA

Oddy test (method: 20171106_OT), SPME GCMS

dark grey; 100% cotton, washed with detergent by CB

Dark, Gray

exhibition/woven, fabric

Long Lasting Insecticidal Net

Duranet

Temporary

2018-08-03

MMA

Oddy test (method: 20180706_B_OT), SPME GCMS

white; Insecticidal netting, Details: removed from bolt that was stored in a sealed plastic bag, Chemical Components: 100% polyethylene fabric infused with alphacypermethrin, 261mg/sq. meter +/- 25%, purchased 5/2016

White

exhibition/woven, fabric

Long Lasting Insecticidal Net

Pramex

Temporary

2018-08-03

MMA

Oddy test (method: 20180706_B_OT), SPME GCMS

white; Insecticidal netting, Details: removed from bolt that was stored in a sealed plastic bag., Chemical Components: made with Olyset technology, Active ingredients: Permethrin* 2% , other ingredients 98%, Purchased: 1/2018, *cis/trans isomer ratio: Max 55% /-cis and min 45%/-trans.

White

exhibition/woven, fabric

Royal Sentry Llin Fabric

Royal Sentry

Temporary

2018-08-03

MMA

Oddy test (method: 20180706_B_OT), SPME GCMS

white; Insecticidal netting, Details: removed from open air roll, Chemical Components: 100% polyethylene fabric infused with alphacypermethrin, 261mg/sq. meter +/- 25%, Purchased: 4/2018

White

exhibition/woven, fabric

P191 Flax-0024 Belgian Linen

Libeco

Temporary

2018-08-03

MMA

Oddy test (method: 20180704_OT), SPME GCMS

natural; Linen fabric, Details: beige preshrunk mill washed Belgian linen, Chemical Components: Linen, Purchased: 2/2018

Natural

exhibition/woven, fabric

Velling 378

Creation Baumann

Temporary

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

green, sea foam green; Cotton velvet fabric, 100% cotton, Fabrics NOT washed or pre-washed by CB, Purchased:July 2018

Green

exhibition/woven, fabric

Velling 361

Creation Baumann

Unsuitable

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

cream; Cotton velvet fabric, 100% cotton, NOT washed/pre-washed, Purchased:July 2018

Cream, White

exhibition/woven, fabric

Velling Iii 366

Creation Baumann

Temporary

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

green, light grey/green; Cotton velvet fabric, 100% cotton, NOT washed/pre-washed, Purchased: July 2018

Green, Light

exhibition/woven, fabric

Velling Iii 379cp

Creation Baumann

Temporary

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

blue, grey/blue; Cotton velvet fabric, 100% cotton, NOT washed/pre-washed, Purchased: July 2018

Blue, Gray

exhibition/woven, fabric

Velling 380

Creation Baumann

Temporary

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

purple, lavender; Cotton velvet fabric, 100% cotton, NOT washed/pre-washed, Purchased: July 2018

Purple

exhibition/woven, fabric

Encore 64 In Ifr 22 Oz Black, Vl220001

Unknown

Unsuitable

2018-09-11

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

purchased July 2018

black; 100% cotton fabric with flame retardant

Black

exhibition/woven, fabric

Rashmi 0036815.0002, Color 0002

Creation Baumann

Unsuitable

2018-09-11

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

beige, 0002; Dense curtain fabric,Dense curtain fabric, 100% Silk, Fabric width:140 cm/55 inch/1.53 yard, Weight:70 g/m²

100% Silk

Beige

exhibition/woven, fabric

Celtic Cloth

Dazian Fabrics

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

purchased july 2018

grey; Grey 100% polyester fabric, IFR, NOT washed with detergent

Gray

exhibition/woven, fabric

Lorenzo 101 Grey

Baumann Dekor

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

WASHED with detergent, purchased august 2018

grey; 100% cotton fabric

Gray

exhibition/woven, fabric

Poly Silk White

Dazian Fabrics

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

purchased: august 2018

black; 100% polyester fabric

Black

exhibition/woven, fabric

Velling Iii Black

Creation Baumann

Unsuitable

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

purchased august 2018

white; 100% cotton fabric

White

exhibition/woven, fabric

1/4" Stiff-felt W/ 8950 Psa, Pe-f-59230-48

Sutherland Felt Company

Temporary

2018-10-25

MMA

Oddy test (method: 20180821_OT), SPME GCMS

grey / black; Stiff felt with adhesive backing, PE-F-59230-48, 1/4" thick, purchased september 2018

Black, Gray

exhibition/woven, fabric

Ultra V 439

Creation Baumann

Temporary

2018-11-28

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Purchased: September 2018,

blue ; 100% cotton fabric, Details: Prewashed in detergent,,Details: Prewashed in detergent,

Blue

exhibition/woven, fabric

1/4" Stiff-felt, Pe-f-59230-48

Sutherland Felt Company

Temporary

2019-12-19

MMA

Oddy test (method: 20180821_OT), SPME GCMS

grey / black; Stiff felt (no adhesive), PE-F-59230-48, 1/4" thick, purchased september 2018

Black, Gray

exhibition/woven, fabric

Unisono Iv-150-350

Creation Baumann

Temporary

2019-12-19

MMA

Oddy test (method: 20180821_OT), SPME GCMS

purchased March 2018

brown/taupe; Cotton fabric, Model/Catalog Number: 00040000.0350, Material Class:100% Cotton, Details: Lot# 40-49965

Brown

exhibition/woven, fabric

1111 Ifr Polyester Sheer Muslin Cs/theatrical Gauze, White

Gerriets International

Unsuitable

2016-08-29

MMA

Oddy test (method: 20160630_OT), SPME GCMS

purchased July 2016

white; Inherently Flame Retardent polyester sheer muslin

White

exhibition/woven, fabric

1112 Ifr Polyester Muslin Cs, White

Gerriets International

Unsuitable

2016-08-29

MMA

Oddy test (method: 20160630_OT), SPME GCMS

purchased July 2016

white; Inherently Flame Retardent polyester muslin

White

exhibition/woven, fabric

24 Opsy Pet Needle Punched Plain Batting

Superior Felt And Filtration

Temporary

2016-08-19

MMA

Oddy test (method: 20160722_OT)

Purchased June 2016

white; needle punched polyester plain batting, 24 oz/sq. yd.

White

exhibition/woven, fabric

Q305 Natural 23 Sanfor Airo

Libeco

Temporary

2016-08-04

MMA

Oddy test (method: 20160705_OT)

purchased October 2015

natural; 100% linen

Natural

exhibition/woven, fabric

L493 Natural-0023

Libeco

Unsuitable

2016-08-04

MMA

Oddy test (method: 20160705_OT), SPME GCMS

Purchased January 2016

natural; 100% linen PFP

Natural

exhibition/woven, fabric

W-n-02-1000 Black Nylon Webbing

Jontay

Temporary

2016-08-04

MMA

Oddy test (method: 20160705_OT)

purchased January 2016

black; black nylon webbing

Black

exhibition/woven, fabric

T9534bc

The Ribbon Factory

Temporary

2016-08-04

MMA

Oddy test (method: 20160705_OT), SPME GCMS

purchased January 2016

black; Pat 95 3/4" black cotton 100 yd roll

Black

exhibition/woven, fabric

Ultra Iv 0401 Gray

Creation Baumann

Temporary

2016-08-04

MMA

Oddy test (method: 20160705_OT), SPME GCMS

purchased January 2016

gray; prewashed 100% cotton

Gray

exhibition/woven, fabric

112-b8760

Libeco

Temporary

2016-08-02

MMA

Oddy test (method: 20160705_OT)

purchased January 2016

natural

Natural

exhibition/woven, fabric

Ultra V, 401 Prewashed

Creation Baumann

Temporary

2016-08-02

MMA

Oddy test (method: 20160705_OT), SPME GCMS

Purchased December 2015

gray; 100% cotton, weight 240 g/m^2

Gray

exhibition/woven, fabric

Unisono Iii 0234 Prewashed

Creation Baumann

Temporary

2016-07-28

MMA

Oddy test (method: 20160630_OT), SPME GCMS

purchased June 2016

gray; 100% cotton, prewashed

Gray

exhibition/woven, fabric

Unisono Iii 350 Gray

Creation Baumann

Suitable

2016-07-27

MMA

Oddy test (method: 20160629_OT), SPME GCMS

purchased June 2016

gray; 100% cotton fabric

Gray

exhibition/woven, fabric

Evolon Paper

Talas

Temporary

2016-07-27

MMA

Oddy test (method: 20160629_OT), SPME GCMS

purchased January 2016

white; woven polyester/nylon split microfiber paper

White

exhibition/woven, fabric

Ultra Spez Ultra Fab Dye #9527

Creation Baumann

Temporary

2016-06-22

MMA

Oddy test (method: 20160512_OT)

purchased February 2016

green gray; pre-washed by Creation Baumann

Gray, Green

exhibition/woven, fabric

Unisono Iii 234

Creation Baumann

Temporary

2016-06-22

MMA

Oddy test (method: 20160512_OT), SPME GCMS

Purchased May 2016

grey; 100% cotton, unwashed

Gray

exhibition/woven, fabric

Ultra V, Color 113

Creation Baumann

Temporary

2016-06-22

MMA

Oddy test (method: 20160512_OT), SPME GCMS

Purchased May 2016

grey, dark grey ; 100% cotton, unwashed

Dark, Gray

exhibition/woven, fabric

314 Unisono Iv-150

Creation Baumann

Temporary

2018-07-17

MMA

Oddy test (method: 20171106_OT), SPME GCMS

Purchased May 2018

Grey; 100% Cotton Fabric Washed with Detergent

Gray

exhibition/woven, fabric

Velos Ii 0013

Creation Baumann

Temporary

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Purchased May 2018

Black; Details: 100% PLF 100% Flame Retardant Polyester (Trevira CS) Chemical Components: Polyester, Trevira

Black

exhibition/woven, fabric

Velos Ii, 0041

Creation Baumann

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Purchased May 2018.

Dark Grey; Grey Flame Retardant Polyester Fabric: 100% PLF 100% Flame Retardant Polyester (Trevira CS) Chemical Components: Polyester, Trevira

Dark, Gray

exhibition/woven, fabric

Velling 0395

Creation Baumann

Temporary

2018-06-28

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Grey; Velvet Fabric From a Bolt Cotton Not Washed with Detergent (Company doesn't have capability for this fabric line) May 2018

Gray

exhibition/woven, fabric

Velling 0396

Creation Baumann

Temporary

2018-06-28

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Purple; Velvet Fabric From a Bolt Cotton Not Washed with Detergent (Company doesn't have capability for this fabric line) May 2018

Purple

exhibition/woven, fabric

Velling 0402

Creation Baumann

Temporary

2018-06-28

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Blue; Velvet Fabric From a Bolt Cotton Not Washed with Detergent (Company doesn't have capability for this fabric line) May 2018

Blue

exhibition/woven, fabric

Unisono Iii 0234

Creation Baumann

Temporary

2018-06-28

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Grey; Finely Woven Fabric Bolt of Cloth, Cotton, Washing Status Not Reported, Acquired 2018, Repeat of Oddy test 2121

Gray

exhibition/woven, fabric

Unisono Iii 0347

Creation Baumann

Temporary

2018-06-28

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Purple; Finely Woven Purple Fabric Bolt of Cloth Cotton May 2018

Purple

exhibition/woven, fabric

Unisono Iv 0350

Creation Baumann

Temporary

2018-06-22

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Grey; Finely Woven Grey Fabric Bolt of Cloth, Cotton Cotton May 2018

Gray

exhibition/woven, fabric

Unisono Iv-0150, 304

Creation Baumann

Temporary

2018-06-22

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Grey; Finely Woven Grey Fabric Bolt of Cloth Cotton May 2018

Gray

exhibition/woven, fabric

F3168016 Loft

Pierre Frey

Temporary

2017-11-08

MMA

Oddy test (method: 20171030_OT), SPME GCMS

Purchased September 2017

Grey, Graminees; Cotton Twill FABRIC

Gray

exhibition/woven, fabric

Ultrav-506

Creation Baumann

Temporary

2017-11-08

MMA

Oddy test (method: 20171030_OT), SPME GCMS

Grey, 100% Cotton; Washed with Detergent

Gray

exhibition/woven, fabric

8941-3593-1 White

Baumann Dekor

Suitable

2017-10-11

MMA

Oddy test (method: 20170913_OT), SPME GCMS

White, White Cotton Fabric; Purchased Summer 2017

White

exhibition/woven, fabric

0202-1233-1 Off-white

Baumann Dekor

Temporary

2017-10-11

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Off-White, Off-White Cotton Fabric; Purchased Summer 2017

Off-White

exhibition/woven, fabric

Coton De Vie, 17221-08 In Anthracite (dark Grey)

Dominique Kieffer

Temporary

2017-10-11

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Dark Grey, Anthracite; Dark Grey 100% Cotton Fabric

Dark, Gray

exhibition/woven, fabric

Sup0000alm

Philips-Boyne

Temporary

2017-10-11

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Purchased: August 2017

Brown, Superba Almond; 100% Cotton Fabric, Broadcloth Superba Almond Fabric

Brown

exhibition/woven, fabric

35-111wh

Benchmark Catalog

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

White; White Sueded Polyethylene Padding with No Adhesive Backing ("dry"), .015

White

exhibition/woven, fabric

35-111wb

Benchmark Catalog

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Black; Warm Black Sueded Polyethylene Padding with No Adhesive Backing ("dry"), .015

Black

exhibition/woven, fabric

35-111br

Benchmark Catalog

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Brown; Brown Sueded Polyethylene Padding with No Adhesive Backing ("dry"), .015

Brown

exhibition/woven, fabric

35-111cm

Benchmark Catalog

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Tan, Camel Hair; Camel Hair Sueded Polyethylene Padding with No Adhesive Backing ("dry"), .015

Brown, Light

exhibition/woven, fabric

35-111cr

Benchmark Catalog

Suitable

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Crème; Creme Sueded Polyethylene Padding with No Adhesive Backing ("dry"), .015

Cream, White

exhibition/woven, fabric

35-111sg

Benchmark Catalog

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Grey, Steel Grey ; Steel Grey Sueded Polyethylene Padding with No Adhesive Backing ("dry"), .015

Gray

exhibition/woven, fabric

31-111tn

Benchmark Catalog

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Tan, Camel Hair; 100% Polyester Felt Padding with No Adhesive Backing ("dry"), .25

Brown, Light

exhibition/woven, fabric

Imperial 2750-19

Sahco

Donghia

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Off-White/Beige; Beige/Off-White 100% Cotton Fabric

Off-White

exhibition/woven, fabric

Satin De Coton 17161-03 Perle

Dominique Kieffer

Suitable

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Crème, Palest Grey/Cream ; White 100% Cotton Fabric

Cream, White

exhibition/woven, fabric

Pampelonne Lc164/746

Aka Castel

Temporary

2017-09-13

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Purchased 7/2017

Tan, Linen; 100% Cotton Tan Fabric

Brown, Light

exhibition/woven, fabric

Canvas Weave 600-28

Perennials

Temporary

2017-09-13

Oddy test (method: 20170913_OT), SPME GCMS

off-White, Blanca; Off-White 100% Solution Dyed Acrylic

Off-White

exhibition/woven, fabric

No

Control coupon · [[media:|GCMS]]

Collection Boussac, Noir (color), Fire Retardant Polyester

Pierre Frey

Vision

Temporary

2018-01-16

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Black, Noir; Black Fire Retardant Polyester Fabric

Black

exhibition/woven, fabric

Sprint Polyester Fabric In Plum (color #18)

Unknown

Clarence House (nyc), Decortex Firenze (italy)

Temporary

2018-01-16

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Purple, Plum; Sprint DF2003 Polyester Fabric in Plum (Color #18)

Purple

exhibition/woven, fabric

Sprint Polyester Fabric In Sepia (color #39)

Unknown

Clarence House (nyc), Decortex Firenze (italy)

Temporary

2018-01-16

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Brown, Sepia, Firenze; Sprint DF2003 Polyester Fabric in Sepia (Color #39)

Brown, Sepia

exhibition/woven, fabric

Sprint Polyester Fabric In Walnut (color #40)

Unknown

Clarence House (nyc), Decortex Firenze (italy)

Temporary

2018-01-16

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Brown, Walnut, Firenze; Sprint DF2003 Polyester Fabric in Walnut (Color #40)

Brown

exhibition/woven, fabric

Brushed Flannel, 3797-804 In Black

Designtex

Temporary

2018-01-10

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Designed by West Elm

Black; Synthetic Flannel

Black

exhibition/woven, fabric

Ultrasuede Hp Pink Ribbon

Toray Industries

Temporary

2017-02-08

MMA

Oddy test (method: 20170111_OT), SPME GCMS

Pink, Pink Ribbon; Style 5522/Color 6661, Width: 55”/1,420mm, Put-Up: 33 yard/30meter R.O.T., Weight: approx. 11.1 oz. per sq. yard/375g per sq. meter, Thickness: 1mm, Fiber Fineness: 0.21dtex, Composition: 80% polyester with 20% polyurethane

Pink

exhibition/woven, fabric

Ultrasuede Hp Sunset

Toray Industries

Temporary

2017-02-08

MMA

Oddy test (method: 20170111_OT), SPME GCMS

Orange, Sunset; Style 5522/Color 6661, Width: 55”/1,420mm, Put-Up: 33 yard/30meters R.O.T., Weight: approx. 11.1 oz. per sq. yard/375g per sq. meter, Thickness: 1mm, Fiber Fineness: 0.21dtex, Composition: 80% polyester with 20% polyurethane

Orange

exhibition/woven, fabric

Unisono Iii 0010 (green)

Creation Baumann

Suitable

2016-05-18

MMA

Oddy test (method: 20160629_OT), SPME GCMS

Green; 100% cotton

Green

exhibition/woven, fabric

Unisono Iii 0324 (blue)

Creation Baumann

Suitable

2016-05-18

MMA

Oddy test (method: 20160629_OT), SPME GCMS

Blue; 100% cotton

Blue

exhibition/woven, fabric

2.0 Mm Polyester Felt

Sutherland Felt Company

Temporary

2017-12-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Polyester Felt

exhibition/woven, fabric

1.5 Mm Polyester Felt

Sutherland Felt Company

Temporary

2017-12-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Polyester Felt

exhibition/woven, fabric

0.5 Mm Polyester Felt

Sutherland Felt Company

Temporary

2017-12-14

MMA

Oddy test (method: 20171116_OT)

Polyester Felt

exhibition/woven, fabric

Sueded Polyethylene With Acrylic Adhesive Backing, 35-111cr

Benchmark Catalog

Temporary

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Purchased 6/2017

Crème; Sueded Polyethylene with acrylic adhesive Backing

Cream, White

exhibition/woven, fabric

Black Polyester Felt, 11 Oz

Testfabrics

Temporary

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Purchased 11/2017

Black; Black Polyester Felt

Black

exhibition/woven, fabric

Ultra V 0405 (beige)

Creation Baumann

Temporary

2017-02-17

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Purchased January 2018

Beige; cotton Fabric

Beige

exhibition/woven, fabric

Fosshape 300/600

Wonderflex World

Trinity Treasures

Suitable

2016-08-18

AWMM

Oddy test

In vitrine or Case

White; Non-Activated, Non-Woven Polyester Fibre

White

exhibition/woven, fabric

Stretch Velvet

Candy Textiles

Suitable

1999-12-12

AWMM

Oddy test

In Vitrine or Case

not provided; 100% Polyester

100% Polyester

exhibition/woven, fabric

Brushed Fabric

Nz Fabrics

Suitable

1999-12-12

AWMM

Oddy test

In Vitrine or Case

Black

exhibition/woven, fabric

Sky Blue Fabric

Suitable

2003-01-12

AWMM

Oddy test

In Vitrine or Case

Blue, Light; 50% linen, 50% cotton

Blue, Light

exhibition/woven, fabric

Quality Euro 125g Display

Macflex International

Spyder Displays

Temporary

2008-05-28

AWMM

Oddy test

In Vitrine or Case

Black; Brushed Nylon

Black

exhibition/woven, fabric

Quality Mac 9 Pinboard Felt

Macflex International

Spyder Displays

Temporary

2008-05-28

AWMM

Oddy test

In vitrine or case

silver; 100% Polyester Non Wove

Silver

exhibition/woven, fabric

Suitable for temporary use. Can be used for the display period of 6 month as cover for mounting boards. Not suitable for objects containing lead.

Wonderflex Fosshape (black) Heated With Steam From Iron

Macflex International

Wonderflex World

Suitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days. One sample's lid popped off and moisture escaped

Black; non woven thermoplastic polyester fabric

Black

batting & padding, fabric

Ag: no corrosion,Cu: no corrosion,Pb: no corrosion

Quality Mac 9 Pinboard Felt

Macflex International

Spyder Displays

Suitable

2008-05-28

AWMM

Oddy test

In vitrine or case

red, cherry; 100% Polyester Non Woven

Red

exhibition/woven, fabric

Quality Mac Foam Backed Loop Nylon

Macflex International

Spyder Displays

Temporary

2008-05-28

AWMM

Oddy test

In vitrine or case

black fabric, grey foam; Heat Bonded Fabric/ Polyethylene Foam

Black

exhibition/woven, fabric

Fabric (unprinted Area), Peter Hayward

Temporary

2016-03-24

AWMM

Oddy test

In vitrine or case

not provided;

exhibition/woven, fabric

Fabric was not washed, may test better if it was washed. The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Printed Fabric, Peter Hayward

Temporary

2016-03-24

AWMM

Oddy test

In vitrine or case

not provided;

exhibition/woven, fabric

Fabric was not washed, may test better if it was washed. The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Unspecified Fabric From Centrepoint

Centrepoint Fabrics

Suitable

2016-03-24

AWMM

Oddy test

In vitrine or case

blue; unwashed

Blue

exhibition/woven, fabric

Fabric was not washed, may test better if it was washed. The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Brushed Nylon

Spyder Displays

Temporary

2016-04-04

AWMM

Oddy test

In vitrine or case

silver-grey; 100% nylon

Silver

exhibition/woven, fabric

Fabric was not washed, may test better if it was washed. The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Calico

John Ranger Textiles

Temporary

2016-04-04

AWMM

Oddy test

In vitrine or case

white, off; 100% unbleached cotton

Off-White

exhibition/woven, fabric

Fabric was not washed, may test better if it was washed. The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Linen

Centrepoint Fabrics

Suitable

2016-04-04

AWMM

Oddy test

In vitrine or case

blue dyed; washed

Blue

exhibition/woven, fabric

Fabric was not washed, may test better if it was washed. The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Calico

Unsuitable

2016-05-02

AWMM

Oddy test

white, off; 100% unbleached cotton

Off-White

exhibition/woven, fabric

Brushed Nylon

Suitable

2016-05-02

AWMM

Oddy test

In vitrine or case

100% nylon

exhibition/woven, fabric

Serge

John Ranger Textiles

Suitable

notably darker purple/red than the control

2016-05-02

AWMM

Oddy test

In vitrine or case

grey, charcoal; 65% Polyseter, 35% Rayon/ Viscose

Gray

exhibition/woven, fabric

The copper foil was notably darker purple/red than the control, so avoid direct contact with the object.

Linen Blard

John Ranger Textiles

Temporary

worse than control

2016-05-02

AWMM

Oddy test

In vitrine or case

brown, tea; 40% cotton, 60% Line

Brown

exhibition/woven, fabric

The lead and copper foils were worse than control, but only just, so this only just fails for permenent use. Re-testing may result in a pass.

Plc

John Ranger Textiles

Suitable

2016-05-02

AWMM

Oddy test

In vitrine or case

"drill"; 65% Polyseter, 35% Cotton

65% Polyseter, 35% Cotton

exhibition/woven, fabric

Canvas

John Ranger Textiles

Suitable

2016-05-02

AWMM

Oddy test

In vitrine or case

brown, light, fawn; 100% cotton

Brown, Light

exhibition/woven, fabric

No

Cotton

John Ranger Textiles

Suitable

notably darker purple/red than the control

2016-05-02

AWMM

Oddy test

In vitrine or case

"drill"; 100% cotton

100% cotton

exhibition/woven, fabric

The copper foil was notably darker purple/red than the control, so avoid direct contact with the object.

Autex

Temporary

slight white fuzziness at the edges

2016-05-09

AWMM

Oddy test

In vitrine or case

Brown/Red, Composition, Clay; polyester fibre (PET)

Brown, Red

exhibition/woven, fabric

The lead coupon had slight white fuzziness at the edges, so there is slight organic acids ebing offgassed. These will not affect trhe objects being proposed for display with the materials, but could affect objects highly sensitive to organic acids.

Autex

Suitable

2016-06-07

AWMM

Oddy test

In vitrine or case

Grey, Symphony, Charcoal; polyester fibre (PET)

Gray

exhibition/woven, fabric

Autex

Suitable

2016-06-07

AWMM

Oddy test

In vitrine or case

Grey, Composition, Charcoal; polyester fibre (PET)

Gray

exhibition/woven, fabric

Autex

Suitable

2016-06-07

AWMM

Oddy test

In vitrine or case

Black, Composition, Noir; polyester fibre (PET)

Black

exhibition/woven, fabric

Autex

Suitable

2016-08-18

AWMM

Oddy test

In vitrine or case

grey; polyester fibre (PET), "Cube", Flatiron, 12mm non-woven polyester fibre board

Gray

exhibition/woven, fabric

Brushed Nylon

Spyder Displays

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

snow

exhibition/woven, fabric

Brushed Nylon

Spyder Displays

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

silver

Silver

exhibition/woven, fabric

Brushed Nylon

Spyder Displays

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

sahara

Brown

exhibition/woven, fabric

Taffeta

Testfabrics

Suitable

2016-07-01

CAM

Oddy test

In vitrine or case

not provided; 100% Silk

100% Silk

exhibition/woven, fabric

Description: Ag - no change, Cu - Slight darkening, Pb - no change

Autex

Autex Interior Acoustics

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

grey; flatiron

Gray

exhibition/woven, fabric

Autex

Autex Interior Acoustics

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

white; pavillion

White

exhibition/woven, fabric

Autex

Autex Interior Acoustics

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

black; petronas

Black

exhibition/woven, fabric

Velos Ii 0013

Creation Baumann

Temporary

2018-07-05

MMA

Oddy test

Purchased May 2018

Black; Details: 100% PLF 100% Flame Retardant Polyester (Trevira CS) Chemical Components: Polyester, Trevira

Black

exhibition/woven, fabric

Linen

The Fabric Store

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

medium grey;

Gray, Medium

exhibition/woven, fabric

Fosshape 300/600

Wonderflex World

Trinity Treasures

Suitable

2016-08-18

AWMM

Oddy test

In vitrine or case

white; activated, non-woven polyester fibre, hardened

White

exhibition/woven, fabric

Cotton Tape

Wt Distributors

Suitable

more whitish colour than the controls

2015-01-27

AWMM

Oddy test

In vitrine or case

natural; cotton

Natural

exhibition/woven, fabric

The lead coupon had more whitish colour than the controls, so there is a small amount of organic acids, as expected from plant materials. Ensure a barrier is used between the object and the cotton tape.

Cotton Tape

Wt Distributors

Suitable

more whitish colour than the controls

2015-01-27

AWMM

Oddy test

In vitrine or case

beige; cotton

Beige

exhibition/woven, fabric

The lead coupon had more whitish colour than the controls, so there is a small amount of organic acids, as expected from plant materials. Ensure a barrier is used between the object and the cotton tape.

Cotton Tape

Wt Distributors

Suitable

more whitish colour than the controls

2015-01-27

AWMM

Oddy test

In vitrine or case

sage green; cotton

Green

exhibition/woven, fabric

The lead coupon had more whitish colour than the controls, so there is a small amount of organic acids, as expected from plant materials. Ensure a barrier is used between the object and the cotton tape.

Cotton Tape

Wt Distributors

Suitable

The lead coupon has slightly more whitish colour than the controls but is not significant.

2015-01-27

AWMM

Oddy test

In vitrine or case

dark green; cotton

cotton

Dark, Green

exhibition/woven, fabric

In vitrine or case

The lead coupon has slightly more whitish colour than the controls, but is not significant.

Cotton Tape

The Canvas

Suitable

more whitish colour than the controls

2015-01-27

AWMM

Oddy test

In vitrine or case

natural; cotton

Natural

exhibition/woven, fabric

The lead coupon had more whitish colour than the controls, so there is a small amount of organic acids, as expected from plant materials. Ensure a barrier is used between the object and the cotton tape.

Cotton

Testfabrics

Suitable

2016-07-01

CAM

Oddy test

In vitrine or case

not provided; 100% cotton

100% cotton

exhibition/woven, fabric

Description: Ag - No change, Cu - Slight tarnish, Pb - Grey spots

Nylex Suede Self Adhesive

Suitable

2024-12-21

AWMM

Oddy test

In vitrine or case

black

Black

exhibition/woven, fabric

Tyvek 1443r, Flm06

Conservation Supplies

Suitable

2014-02-26

AWMM

Oddy test

In vitrine or case

white; tyvek

White

exhibition/woven, fabric

Benchmark Felt With Adhesive Backing 31-111cg

Benchmark Catalog

Temporary

1999-09-14

AWMM

Oddy test

Outside vitrine or case

black

Black

batting & padding, fabric

Velos Ii Upholstery Fabric (batch 92316)

Creation Baumann

Unsuitable

2019-09-26

AMNH

Oddy test

AMNH test #227

dark blue; Fabric swatch - 100% flame retardant polyester (Trevira CS - comonomer, organophosphorous compound)

Blue, Dark

exhibition/woven, fabric

matte short napped velours

Verona Bark

Artmark

Unsuitable

2005-12-23

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - moderate yellow discoloration, Cu - uneven discoloration, Pb - white haze across one side. Otherwise, dark grey

Unisono 83

Creation Baumann

Testfabrics

Unsuitable

2004-10-30

CAM

Oddy test

Reinstallation sf 6216+6217, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - bright orange corrosion, Cu - silver corrosion irregular, Pb - light gray corrosion

Unisono 83

Creation Baumann

Testfabrics

Temporary

2004-10-30

CAM

Oddy test

Reinstallation sf 6216+6217, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - almost slight yellow tarnished, Cu - almost slight orange tarnished, Pb - almost tarnished

14225 Chocolate

Duralee

Temporary

2005-12-27

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 72% Polyester, 28% Cotton

exhibition/woven, fabric

Description: Ag - minor yellow discoloration, one corner dark brown, Cu - Uneven , moderate discoloration, Pb - even, black overall

Avanti Cocoa

Fabricut

Unsuitable

2005-12-27

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; Pile: 50% polyester, 50% cotton. Back: 65% polyester,35% cotton

exhibition/woven, fabric

Description: Ag - slight yellowing around edges, Cu - Even darkening overall, bluish discoloration in center of one side, Pb - white corrosion across one side, otherwise dark grey

Rembrandt Chocolate

Fabricut

Temporary

2005-12-27

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 82% polyester, 18% cotton

exhibition/woven, fabric

Description: Ag - slight yellow cast, Cu - moderate darkening, purple discoloration on one side, Pb - dark grey with whitish cloudiness around edges of one side

Jb Martin 8550 Juliet, 1000 Black

Jb Martin

Suitable

2007-06-11

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - great, Cu - slight tarnish, Pb - slight darkening

Jb Martin 8550 Juliet, 5786 Chicory

Jb Martin

Suitable

2007-06-11

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - great, Cu - slight tarnish, Pb - slight darkening

Jb Martin 8500 Juliet 5791 Charcoal

Jb Martin

Unsuitable

2006-07-10

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

no recorded results

Corona Black

Philips-Boyne

Temporary

2005-12-23

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - slight haziness, Cu - Severe uneven discoloration, multiple colors, Pb - black

Corona Navy

Philips-Boyne

Temporary

2005-12-23

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - slight yellowing, Cu - uneven discoloration, some spots of blue, Pb - uneven dark grey with cloudiness along edges of one side

Tan

Philips-Boyne

Suitable

2004-12-08

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; 100% cotton

exhibition/woven, fabric

Description: Ag - No tarnish, Cu - No tarnish, Pb - No tarnish

Pembroke Glacier

Robert Allen

Temporary

2005-12-27

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; Pile: 100% cotton. Back: 77% cotton, 23% polyester.

exhibition/woven, fabric

Description: Ag - slight yellow cast, Cu - moderate, multicolored discoloration, Pb - black with blue cast

Pembroke Mink

Robert Allen

Suitable

2005-12-27

CAM

Oddy test

for use lining exhibit cases, test run at 60 ˚C for 4 weeks

not provided; Pile: 100% cotton. Back: 77% cotton, 23% polyester.

exhibition/woven, fabric

Description: Ag - Moderate tarnish around edges, Cu - dark corrosion on one side, multi colored on other, Pb - black with some whitish cloudiness around edges

Cotton

Testfabrics

Suitable

2016-07-01

CAM

Oddy test

not provided; 100% cotton

100% cotton

exhibition/woven, fabric

Description: Ag - No change, Cu - Slight tarnish, Pb - Grey spots

Muslin

Testfabrics

Suitable

2016-07-01

CAM

Oddy test

not provided; 100% cotton

100% cotton

exhibition/woven, fabric

Description: Ag - no change, Cu - No change, Pb - Uneven whitening

Satin

Testfabrics

Suitable

2016-07-01

CAM

Oddy test

not provided; 100% Silk

100% Silk

exhibition/woven, fabric

Description: Ag - no change, Cu - Darkening, black at the edge, Pb - no change

Taffeta

Testfabrics

Suitable

2016-07-01

CAM

Oddy test

not provided; 100% Silk

100% Silk

exhibition/woven, fabric

Description: Ag - no change, Cu - Slight darkening, Pb - no change

Style: 2300-5663 D.B.

Testfabrics

Suitable

2014-03-01

Autry

Oddy test

Unwashed; don't use in contact with object

Black; 98% Bamboo, 2% Spandex Jersey

Black

exhibition/woven, fabric

none

Stretch Satin

A1 Fabrics

Temporary

2009-11-04

BM

Oddy test

sample prep: N/A, test #6652

CREAM; SILK BLEND

Cream, White

exhibition/woven, fabric

none

Sensuede Cordovan 9

American Silk Mills

Unsuitable

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Brown; 88% Recycled Polyester, 12% Polyurethane

Brown

exhibition/woven, fabric

Sensuede Rain 2004

American Silk Mills

Temporary

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Grey; 88% Recycled Polyester, 12% Polyurethane

Gray

exhibition/woven, fabric

Sensuede Pebble 2013

American Silk Mills

Unsuitable

2012-05-15

CMA

Oddy test

none

tan; Nylon fiber matrix

Brown, Light

exhibition/woven, fabric

none

Sensuede Moss 2014

American Silk Mills

Unsuitable

2012-01-07

CMA

Oddy test

none

green; Nylon fiber matrix

Green

exhibition/woven, fabric

none

Sensuede Verde 2046

American Silk Mills

Suitable

2012-05-15

CMA

Oddy test

none

green; Nylon fiber matrix

Green

exhibition/woven, fabric

none

Sensuede Ebony 2050

American Silk Mills

Unsuitable

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Black; 88% Recycled Polyester, 12% Polyurethane

Black

exhibition/woven, fabric

Sensuede Cocoa 2064

American Silk Mills

Temporary

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Brown; 88% Recycled Polyester, 12% Polyurethane

Brown

exhibition/woven, fabric

Sensuede Sistine Grey 2081

American Silk Mills

Unsuitable

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Grey, light; 88% Recycled Polyester, 12% Polyurethane

Gray, Light

exhibition/woven, fabric

Sensuede Loam 2141

American Silk Mills

Unsuitable

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Brown, medium; 88% Recycled Polyester, 12% Polyurethane

Brown, Medium

exhibition/woven, fabric

Sensuede Tan 2305

American Silk Mills

Temporary

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Brown, light; 88% Recycled Polyester, 12% Polyurethane

Brown, Light

exhibition/woven, fabric

Sensuede Chocolate 2456

American Silk Mills

Suitable

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Brown, dark; 88% Recycled Polyester, 12% Polyurethane

Brown, Dark

exhibition/woven, fabric

Sensuede Cloud 2507

American Silk Mills

Unsuitable

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Grey; 88% Recycled Polyester, 12% Polyurethane

Gray

exhibition/woven, fabric

Sensuede Black 2531

American Silk Mills

Unsuitable

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Black; 88% Recycled Polyester, 12% Polyurethane

Black

exhibition/woven, fabric

Sensuede Incense 2629

American Silk Mills

Unsuitable

2014-12-05

CMA

Oddy test, Sodium Azide test

fabric washed

brown, dark; Polyester

Brown, Dark

exhibition/woven, fabric

Sensuede Mink 2637

American Silk Mills

Temporary

2014-12-05

CMA

Oddy test, Sodium Azide test

none

Brown, dark; 88% Recycled Polyester, 12% Polyurethane

Brown, Dark

exhibition/woven, fabric

Felt 31-220 Black

Benchmark Catalog

Temporary

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed; don't use in contact with object

Black; Polyester, acrylic or poly-acrylic blend adhesive backed

Black

batting & padding, fabric

Felt 31-220 Cool Gray

Benchmark Catalog

Suitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

Gray; Polyester, acrylic or poly-acrylic blend adhesive backed

Gray

batting & padding, fabric

Felt 31-220 Dark Brown

Benchmark Catalog

Temporary

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed; don't use in contact with object

Brown, Dark; Polyester, acrylic or poly-acrylic blend adhesive backed

Brown, Dark

batting & padding, fabric

Felt 31-220 Ivory

Benchmark Catalog

Temporary

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed; don't use in contact with object

White, off-; Polyester, acrylic or poly-acrylic blend adhesive backed

Off-White

batting & padding, fabric

Felt 31-220 Moss

Benchmark Catalog

Temporary

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed; don't use in contact with object

Green; Polyester, acrylic or poly-acrylic blend adhesive backed

Green

batting & padding, fabric

Felt 31-220 Tan

Benchmark Catalog

Suitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

Tan; Polyester, acrylic or poly-acrylic blend adhesive backed

Brown, Light

batting & padding, fabric

Felt 31-220 Terracotta

Benchmark Catalog

Unsuitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

Red/Brown; Polyester, acrylic or poly-acrylic blend adhesive backed

Brown, Red

batting & padding, fabric

Felt 31-220 Warm Gray

Benchmark Catalog

Unsuitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

Gray; Polyester, acrylic or poly-acrylic blend adhesive backed

Gray

batting & padding, fabric

Felt 31-220 White

Benchmark Catalog

Suitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

white; Polyester, acrylic or poly-acrylic blend adhesive backed

White

batting & padding, fabric

Sueded Polyethylene, Moleskin 35-220 Beige

Benchmark Catalog

Suitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

Tan; Non-woven polyethylene, acrylic adhesive backed

Brown, Light

batting & padding, fabric

Sueded Polyethylene, Moleskin 35-220 Brown

Benchmark Catalog

Unsuitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

Brown; Non-woven polyethylene, acrylic adhesive backed

Brown

batting & padding, fabric

Sueded Polyethylene, Moleskin 35-220 Camel Hair

Benchmark Catalog

Unsuitable

2014-09-15

CMA

Oddy test, Sodium Azide test

not washed

Tan; Non-woven polyethylene, acrylic adhesive backed

Brown, Light

batting & padding, fabric

Sueded Polyethylene, Moleskin 35-220 Crème

Benchmark Catalog

Unsuitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

White, off-; Non-woven polyethylene, acrylic adhesive backed

Off-White

batting & padding, fabric

Sueded Polyethylene, Moleskin 35-220 Steel Grey

Benchmark Catalog

Temporary

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed; don't use in contact with object

Gray; Non-woven polyethylene, acrylic adhesive backed

Gray

batting & padding, fabric

Sueded Polyethylene, Moleskin 35-220 Warm Black

Benchmark Catalog

Temporary

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed; don't use in contact with object

Black; Non-woven polyethylene, acrylic adhesive backed

Black

batting & padding, fabric

Sueded Polyethylene, Moleskin 35-220 White

Benchmark Catalog

Suitable

2014-08-27

CMA

Oddy test, Sodium Azide test

not washed

white; Non-woven polyethylene, acrylic adhesive backed

White

batting & padding, fabric

Eco Linen 263

Calvin Fabrics

Temporary

2014-04-22

CMA

Oddy test

fabric washed; don't use in contact with object

Beige, natural; 100% cotton

exhibition/woven, fabric

n/a

Celtic Linen 581, #25

Calvin Fabrics

Unsuitable

2011-02-14

CMA

Oddy test

fabric washed

White, Pearl; 100% linen/ (Belgium) 57"width

White

exhibition/woven, fabric

none

Ecolinen 0263, #582

Calvin Fabrics

Suitable

2012-02-01

CMA

Oddy test

fabric washed

Natural; 100% linen/ (Belgium) 72"width

Natural

exhibition/woven, fabric

none

Ecolinen 0266x, #537

Calvin Fabrics

Unsuitable

2011-02-10

CMA

Oddy test

fabric washed

White; 100% linen/ (Belgium) 54"width

White

exhibition/woven, fabric

none

Ecolinen 0681, #710

Calvin Fabrics

Suitable

2011-02-14

CMA

Oddy test

fabric washed

Natural; 100% linen/ (Belgium) 54"width

Natural

exhibition/woven, fabric

none

Ecolinen 1260, #675

Calvin Fabrics

Unsuitable

2011-02-14

CMA

Oddy test

fabric washed

Natural; 100% linen/ (Belgium) 54"width

Natural

exhibition/woven, fabric

none

Ecolinen 1376, #207

Calvin Fabrics

Suitable

2011-02-14

CMA

Oddy test

fabric washed

White; 100% linen/ (Belgium) 72"width

White

exhibition/woven, fabric

none

Ecolinen 2383, #287

Calvin Fabrics

Suitable

2011-02-10

CMA

Oddy test

fabric washed

White; 100% linen/ (Belgium) 59"width

White

exhibition/woven, fabric

none

Parsilk

Charles Parsons

Suitable

2020-12-20

NAA

PAT

washed

Brown; 100% Polyester

Brown

exhibition/woven, fabric

n/a

Parsilk

Charles Parsons

Suitable

2020-12-20

NAA

PAT

washed

White; 100% Polyester

White

exhibition/woven, fabric

n/a

Basic Plus 513

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8119

BLUE; 100% PLF CS

Blue

exhibition/woven, fabric

none

Basic Plus Iii Un 527

Creation Baumann

Temporary

2009-06-23

BM

Oddy test

sample prep: N/A, test #6513

BLUE-GREEN; PLF

Blue/Green

exhibition/woven, fabric

none

Dimmer Ii 212 Turquiose

Creation Baumann

Temporary

2009-08-04

BM

Oddy test

sample prep: N/A, test #6568

TURQUOISE; PLF

Blue, Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0073 Cinnamon

Creation Baumann

Unsuitable

2009-02-12

BM

Oddy test

sample prep: N/A, test #6207

BROWN, LIGHT; 100% SILK

Brown, Light

exhibition/woven, fabric

none

Indiana Ii 96

Creation Baumann

Suitable

2010-01-17

CMA

Oddy test

Washed @ Coit Rd Services in Industrial Washer, warm H2O 1 rinse

brown, red; 100% cotton, medium weight plain weave

Brown, Red

exhibition/woven, fabric

none

Tyvek

Creation Baumann

Suitable

2014-04-04

BM

Oddy test

sample prep: N/A, test #8177

BLACK; POLYPROPYLENE

Black

fabric, non-woven

none

Indiana Ii 96

Creation Baumann

Suitable

2012-02-01

CMA

Oddy test

Washed @ Coit Rd Services in Industrial Washer, warm H2O 1 rinse

brown, red; 100% cotton, medium weight plain weave

Brown, Red

exhibition/woven, fabric

none

Indiana Ii 96

Creation Baumann

Suitable

2012-02-01

CMA

Oddy test

Washed @ Coit Rd Services in Industrial Washer, warm H2O, 2 rinses

brown, red; 100% cotton, medium weight plain weave

Brown, Red

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0165 Lilac

Creation Baumann

Temporary

2010-12-13

BM

Oddy test

sample prep: N/A, test #7079

GREY; 100% SILK

Gray

exhibition/woven, fabric

none

Piuma 413

Creation Baumann

Unsuitable

2009-01-20

BM

Oddy test

test 6190

Yellow; 85% silk 15% PL

Yellow

exhibition/woven, fabric

exhibition/woven

n/a

Benchmark Sueded Polyethylene

Creation Baumann

Suitable

2017-06-23

BKM

Oddy test

sample prep: N/A, test #7886

Acrylic-adhesive backed sueded polyethylene;

batting & padding, fabric

Ag: no corrosion,Cu: red- same as control,Pb: no corrosion

Novasuede Cypress T3phw

Creation Baumann

Unsuitable

2012-05-15

CMA

Oddy test

none

green; Nylon fiber matrix

Green

exhibition/woven, fabric

none

Rashmi 10

Creation Baumann

Unsuitable

2010-07-15

BM

Oddy test

sample prep: N/A, test #6887

GREY; SILK

Gray

exhibition/woven, fabric

none

Rashmi 12

Creation Baumann

Unsuitable

2010-07-15

BM

Oddy test

sample prep: N/A, test #6882

BLUE; SILK

Blue

exhibition/woven, fabric

none

Rashmi 13

Creation Baumann

Unsuitable

2010-07-15

BM

Oddy test

sample prep: N/A, test #6884

BROWN; SILK

Brown

exhibition/woven, fabric

none

Rashmi 17

Creation Baumann

Unsuitable

2010-07-15

BM

Oddy test

sample prep: N/A, test #6883

GREEN; SILK

Green

exhibition/woven, fabric

none

Rashmi 2

Creation Baumann

Unsuitable

2010-07-15

BM

Oddy test

sample prep: N/A, test #6888

BEIGE; SILK

Beige

exhibition/woven, fabric

none

Velos 15

Creation Baumann

Suitable

2008-01-01

CMA

Oddy test

none

cotton

exhibition/woven, fabric

none

Slate Blue Gray 1622 /08

Creation Baumann

Suitable

2010-01-21

CMA

Oddy test

none

blue, gray; 100% cotton, fine plain weave

Blue, Gray

exhibition/woven, fabric

none

Novasuede Moss

Creation Baumann

Unsuitable

2012-01-07

CMA

Oddy test

none

green; Nylon fiber matrix

Green

exhibition/woven, fabric

none

Collection Boussac, Noir (color), Fire Retardant Polyester

Pierre Frey

Creation Baumann

Temporary

2018-01-16

MMA

Oddy test (method: 20171116_OT), SPME GCMS

sample prep: N/A, test #6541

Black, Noir; Black Fire Retardant Polyester Fabric

Black

exhibition/woven, fabric

Samar Un 230

Creation Baumann

Suitable

2009-06-29

BM

Oddy test

sample prep: N/A, test #6542

GREY, LIGHT; PLF

Gray, Light

exhibition/woven, fabric

none

Samar Un 233

Creation Baumann

Suitable

2009-06-29

BM

Oddy test

sample prep: N/A, test #6543

GREY, DARK; PLF

Dark, Gray

exhibition/woven, fabric

none

Cotton, T 3340

Creation Baumann

Suitable

2017-02-16

HCC

Oddy test

none

PURPLE; cotton

Purple

exhibition/woven, fabric

Unisono Ii 87

Creation Baumann

Suitable

2008-01-01

CMA

Oddy test

none

gray, blue; 100% cotton

Blue, Gray

exhibition/woven, fabric

none

Buckram

Creation Baumann

Suitable

2009-02-13

BM

Oddy test

sample prep: MACHINE WASHED, test #6339

BEIGE; LINEN

Beige

exhibition/woven, fabric

none

Sendal Un 118

Creation Baumann

Unsuitable

2013-05-30

BM

Oddy test

sample prep: N/A, test #7861

BROWN; 100% PLF CS

Brown

exhibition/woven, fabric

none

Ultra Iv 401

Creation Baumann

Suitable

2013-03-08

CMA

Oddy test

fabric washed, no detergent

Grey; plain weave 100% cotton

Gray

exhibition/woven, fabric

Northern Lights Fleece Solids "light Blue"

Creation Baumann

Suitable

2007-03-10

BKM

Oddy test

sample prep: N/A, test #7729

Blue, light; 100% polyester

Blue, Light

exhibition/woven, fabric

Unisono 302

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8124

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Sendal Un 159

Creation Baumann

Unsuitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7721

GREEN; FLAME RETARDANT POLYESTER (PLF) TREVIRA CS

Green

exhibition/woven, fabric

none

Sendal Un 160

Creation Baumann

Temporary

2013-02-25

BM

Oddy test

sample prep: N/A, test #7728

GREEN; FLAME RETARDANT POLYESTER (PLF) TREVIRA CS

Green

exhibition/woven, fabric

none

Indian-indian Douppion 845/0020 Aubergine

Creation Baumann

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7845

RED, DARK; 100% SILK

Dark, Red

exhibition/woven, fabric

none

Sendal Un 166

Creation Baumann

Suitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7730

BLUE, LIGHT; FLAME RETARDANT POLYESTER (PLF) TREVIRA CS

Blue, Light

exhibition/woven, fabric

none

Sendal Un 169

Creation Baumann

Unsuitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7727

PURPLE; FLAME RETARDANT POLYESTER (PLF) TREVIRA CS

Purple

exhibition/woven, fabric

none

Prelle Cotton 13012 Bt307451 Bleu19

Creation Baumann

Unsuitable

2009-01-22

BM

Oddy test

test 6112

Blue; cotton

Blue

exhibition/woven, fabric

n/a

Telos 57

Creation Baumann

Suitable

2009-06-23

BM

Oddy test

sample prep: N/A, test #6512

BLUE-GREEN; LINEN

Blue/Green

exhibition/woven, fabric

none

Ultima 88

Creation Baumann

Unsuitable

2009-06-23

BM

Oddy test

sample prep: N/A, test #6515

BLUE-GREEN; 87% WV/13% PA

Blue/Green

exhibition/woven, fabric

none

Ultra 98 123

Creation Baumann

Unsuitable

2008-01-01

CMA

Oddy test

none

white, grey; unknown

Gray, White

exhibition/woven, fabric

none

Ultra 102

Creation Baumann

Suitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7717

BLUE; 100% COTTON

Blue

exhibition/woven, fabric

none

Ultra 108

Creation Baumann

Suitable

2009-11-23

BM

Oddy test

sample prep: N/A, test #6661

BLUE, LIGHT; 100% cotton

Blue, Light

exhibition/woven, fabric

none

Ultra 109

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7159

BLUE; 100% COTTON

Blue

exhibition/woven, fabric

none

Ultra 116

Creation Baumann

Suitable

2012-03-20

BM

Oddy test

sample prep: N/A, test #7418

GREY; 100% cotton BLUE AND GREEN FABRIC

Gray

exhibition/woven, fabric

none

Ultra 121

Creation Baumann

Suitable

2009-06-23

BM

Oddy test

sample prep: N/A, test #6506

WHITE; 100% cotton

White

exhibition/woven, fabric

none

Ultra 122

Creation Baumann

Suitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7714

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Ultra 122

Creation Baumann

Unsuitable

2012-09-21

CMA

Oddy test

fabric not washed

White; plain weave cotton (est.)

White

exhibition/woven, fabric

n/a

Ultra 123

Creation Baumann

Suitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7713

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Ultra Suede Light 5743 Asphault

Creation Baumann

Unsuitable

2009-06-05

BM

Oddy test

sample prep: N/A, test #6450

BLACK

Black

exhibition/woven, fabric

Indian Chinese-douppion, 845/0136 Hazel

Creation Baumann

Unsuitable

2009-01-20

BM

Oddy test

test 6187

Brown, Light; 100% silk

Brown, Light

exhibition/woven, fabric

n/a

Ultra 225

Creation Baumann

Suitable

2012-11-19

BM

Oddy test

sample prep: N/A, test #7652

GREEN, LIGHT; 100% cotton

Green, Light

exhibition/woven, fabric

none

Ultra 236

Creation Baumann

Suitable

2011-10-25

BM

Oddy test

sample prep: N/A, test #7338

PINK; 100% cotton

Pink

exhibition/woven, fabric

none

Unisono 321

Creation Baumann

Suitable

2012-04-20

BM

Oddy test

sample prep: N/A, test #7485

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Ultra 336

Creation Baumann

Temporary

2012-03-20

BM

Oddy test

sample prep: N/A, test #7417

BLUE, LIGHT; 100% cotton

Blue, Light

exhibition/woven, fabric

none

Crepe Backed Satin Stretch 931d/0062 Celadon

Creation Baumann

Temporary

2011-10-25

BM

Oddy test

sample prep: N/A, test #7332

GREEN, LIGHT; 92% SILK, 8% LYCRA

Green, Light

exhibition/woven, fabric

none

Ultra 403

Creation Baumann

Temporary

2011-10-25

BM

Oddy test

sample prep: N/A, test #7337

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Lightweight Crepe Back Satin Stretch 831d-0004 Ivory

Creation Baumann

Temporary

2011-10-25

BM

Oddy test

sample prep: N/A, test #7333

CREAM; 92% SILK, 8% LYCRA

Cream, White

exhibition/woven, fabric

none

Brushed Nylon

Creation Baumann

Suitable

2020-12-20

NAA

PAT

washed

Black; Nylon

Black

exhibition/woven, fabric

n/a

Ultra 413

Creation Baumann

Suitable

2012-11-19

BM

Oddy test

sample prep: N/A, test #7657

YELLOW, DARK; 100% cotton

Dark, Yellow

exhibition/woven, fabric

exhibition/woven

none

Ultra 414

Creation Baumann

Suitable

2012-09-08

BM

Oddy test

sample prep: N/A, test #7605

BROWN; 100% cotton

Brown

exhibition/woven, fabric

none

Army Carded Cotton Sateen, 428u

Creation Baumann

Unsuitable

2013-06-07

CMA

Oddy test

batch? 55196, fabric washed, no detergent

white, natural; cotton, unbleached, desized

Natural, White

exhibition/woven, fabric

n/a

Ultra 416

Creation Baumann

Suitable

2009-11-23

BM

Oddy test

sample prep: N/A, test #6660

BROWN; 100% cotton

Brown

exhibition/woven, fabric

none

Ultra 417

Creation Baumann

Suitable

2013-04-05

BM

Oddy test

sample prep: N/A, test #7752

PURPLE, DARK; 100% cotton

Dark, Purple

exhibition/woven, fabric

none

Ultra 418

Creation Baumann

Suitable

2012-12-06

BM

Oddy test

sample prep: N/A, test #7663

PURPLE; 100% cotton

Purple

exhibition/woven, fabric

none

Ultra 419

Creation Baumann

Suitable

2011-09-14

BM

Oddy test

sample prep: N/A, test #7325

PINK, DARK; 100% cotton

Dark, Pink

exhibition/woven, fabric

none

Dark Gray F9t 1a

Creation Baumann

Suitable

2012-01-02

CMA

Oddy test

none

gray, dark; 100% cotton, fine plain weave

Dark, Gray

exhibition/woven, fabric

none

Ultra 423

Creation Baumann

Suitable

2013-04-05

BM

Oddy test

sample prep: N/A, test #7753

RED; 100% cotton

Red

exhibition/woven, fabric

none

Ultra 426

Creation Baumann

Suitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7718

YELLOW; 100% cotton

Yellow

exhibition/woven, fabric

exhibition/woven

none

Ultra 430

Creation Baumann

Suitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7719

ORANGE; 100% cotton

Orange

exhibition/woven, fabric

none

Ultra 431

Creation Baumann

Suitable

2012-09-08

BM

Oddy test

sample prep: N/A, test #7604

ORANGE; 100% cotton

Orange

exhibition/woven, fabric

none

Ultra 435

Creation Baumann

Suitable

2013-04-05

BM

Oddy test

sample prep: N/A, test #7754

BLUE, LIGHT; 100% cotton

Blue, Light

exhibition/woven, fabric

none

Ultra 436

Creation Baumann

Suitable

2012-10-19

BM

Oddy test

sample prep: N/A, test #7643

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Ultra 438

Creation Baumann

Suitable

2012-11-19

BM

Oddy test

sample prep: N/A, test #7653

GREEN, LIGHT; 100% cotton

Green, Light

exhibition/woven, fabric

none

Ultra 440

Creation Baumann

Suitable

2013-02-25

BM

Oddy test

sample prep: N/A, test #7716

BLUE, DARK; 100% cotton

Blue, Dark

exhibition/woven, fabric

none

Ultra 441

Creation Baumann

Suitable

2012-11-19

BM

Oddy test

sample prep: N/A, test #7654

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Ultra 446

Creation Baumann

Suitable

2012-09-08

BM

Oddy test

sample prep: N/A, test #7606

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Ultra 447

Creation Baumann

Suitable

2012-12-06

BM

Oddy test

sample prep: N/A, test #7662

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Ultra 448

Creation Baumann

Suitable

2010-12-07

BM

Oddy test

sample prep: N/A, test #7053

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Ultra 450

Creation Baumann

Suitable

2013-04-11

BM

Oddy test

sample prep: N/A, test #7755

GREEN, DARK; 100% cotton

Dark, Green

exhibition/woven, fabric

none

Ultra Iv 116

Creation Baumann

Suitable

2013-05-10

CMA

Oddy test

fabric washed, no detergent

Blue, light; plain weave 100% cotton

Blue, Light

exhibition/woven, fabric

Ultra Iv 116

Creation Baumann

Unsuitable

2013-09-19

CMA

Oddy test

fabric washed, no detergent

Blue, light; plain weave 100% cotton

Blue, Light

exhibition/woven, fabric

Ultra Iv 121

Creation Baumann

Unsuitable

2012-09-21

CMA

Oddy test

fabric not washed

White; plain weave cotton (est.)

White

exhibition/woven, fabric

n/a

Ultra Iv 121

Creation Baumann

Unsuitable

2013-05-10

CMA

Oddy test

fabric washed, no detergent

White; plain weave 100% cotton

White

exhibition/woven, fabric

Ultra Iv 122

Creation Baumann

Suitable

2013-03-08

CMA

Oddy test

none

tan; 100% cotton

Brown, Light

exhibition/woven, fabric

Pongee Plus (mauve) M-luc105mmq-nwa

Creation Baumann

Suitable

Consistent with Control

2019-01-04

FMNH

Oddy test

none

Pink, dark; Mauve (pinkish grey), polyester

Dark, Pink

exhibition/woven, fabric

Ultra Iv 124

Creation Baumann

Suitable

2013-02-04

CMA

Oddy test

none

brown, grey; 100% cotton

Brown, Gray

exhibition/woven, fabric

none

Ultra Iv 336

Creation Baumann

Suitable

2013-03-08

CMA

Oddy test

none

grey; 100% cotton

Gray

exhibition/woven, fabric

Ultra Iv 401

Creation Baumann

Suitable

2013-03-08

CMA

Oddy test

fabric washed, no detergent

Grey; plain weave 100% cotton

Gray

exhibition/woven, fabric

Ultra Iv 404

Creation Baumann

Suitable

2013-03-08

CMA

Oddy test

fabric washed, no detergent

Grey; plain weave 100% cotton

Gray

exhibition/woven, fabric

Ultra Iv 404

Creation Baumann

Suitable

2009-05-15

CMA

Oddy test

none

grey; 100% cotton, plain weave

Gray

exhibition/woven, fabric

none

Velling 364

Creation Baumann

Unsuitable

2012-09-11

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Ultra Iv 405

Creation Baumann

Suitable

2013-02-04

CMA

Oddy test

none

Tan; 100% cotton

Brown, Light

exhibition/woven, fabric

none

Ultra Iv 406

Creation Baumann

Unsuitable

2013-03-08

CMA

Oddy test

fabric not washed

White; plain weave cotton (est.)

White

exhibition/woven, fabric

Ultra Iv 407

Creation Baumann

Unsuitable

2013-03-08

CMA

Oddy test

none

Tan; 100% cotton

Brown, Light

exhibition/woven, fabric

Ultra Iv 415

Creation Baumann

Unsuitable

2013-03-08

CMA

Oddy test

none

Brown; 100% Cotton

Brown

exhibition/woven, fabric

Ultra Iv 416

Creation Baumann

Unsuitable

2013-03-08

CMA

Oddy test

none

Brown; 100% cotton

Brown

exhibition/woven, fabric

Ultra Iv 416

Creation Baumann

Suitable

2009-12-09

CMA

Oddy test

Washed in hot and cold H2O

brown; 100% cotton

Brown

exhibition/woven, fabric

none

Ultra Iv 421

Creation Baumann

Unsuitable

2013-03-08

CMA

Oddy test

none

Pink; 100% cotton

Pink

exhibition/woven, fabric

Ultra Iv 431

Creation Baumann

Unsuitable

2013-03-08

CMA

Oddy test

none

orange/brown; 100% cotton

Orange/Brown

exhibition/woven, fabric

Ultra Iv 436

Creation Baumann

Suitable

2013-03-08

CMA

Oddy test

none

blue/green; 100% cotton

Blue/Green

exhibition/woven, fabric

Ultra Iv 439

Creation Baumann

Unsuitable

2012-09-11

CMA

Oddy test

none

blue; 100% cotton

Blue

exhibition/woven, fabric

none

Pisano 1-6313-355

Creation Baumann

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7873

BLUE; SILK

Blue

exhibition/woven, fabric

none

Umbria

Creation Baumann

Suitable

2006-08-10

GCI

Oddy test

no notes

unknown; 100% polyester

exhibition/woven, fabric

n/a

Unisono 13

Creation Baumann

Suitable

2009-09-25

BM

Oddy test

sample prep: N/A, test #6616

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Synthetic Sinew

Creation Baumann

Temporary

2007-02-14

BKM

Oddy test

No tarnish, but roll in bag - color has worn off. TEMP USE ONLY.

waxed nylon strands

fiber or thread

Unisono 14

Creation Baumann

Unsuitable

2012-01-02

CMA

Oddy test

Supplied in 1996 by Carnegie

green/blue; 100% cotton

Green/Blue

exhibition/woven, fabric

none

Unisono 14

Creation Baumann

Suitable

2012-01-02

CMA

Oddy test

Retested after washed

green/blue; 100% cotton

Green/Blue

exhibition/woven, fabric

none

Unisono 27

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8111

YELLOW, LIGHT; 100% cotton

Light, Yellow

exhibition/woven, fabric

exhibition/woven

none

Unisono 29

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8110

YELLOW; 100% cotton

Yellow

exhibition/woven, fabric

exhibition/woven

none

Unisono 50

Creation Baumann

Suitable

2009-06-23

BM

Oddy test

sample prep: N/A, test #6511

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Unisono 51

Creation Baumann

Suitable

2009-01-20

BM

Oddy test

test 6161, pH 6

Blue; 100% cotton

Blue

exhibition/woven, fabric

n/a

Unisono 60

Creation Baumann

Suitable

2009-01-20

BM

Oddy test

test 6162, pH 6.5

Red; 100% cotton

Red

exhibition/woven, fabric

n/a

Ultra 448

Creation Baumann

Suitable

2010-12-07

BM

Oddy test

sample prep: N/A, test #7053

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Unisono 81

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8116

BEIGE; 100% COTTON

Beige

exhibition/woven, fabric

none

Unisono 81

Creation Baumann

Suitable

2008-01-01

CMA

Oddy test

none

gray, light; 100% cotton

Gray, Light

exhibition/woven, fabric

none

Unisono 87

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8114

GREY, LIGHT; 100% cotton

Gray, Light

exhibition/woven, fabric

none

Regal Taffeta P403/0162 Leaf

Creation Baumann

Unsuitable

2009-01-22

BM

Oddy test

sample prep: N/A, test #6129

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Unisono 91

Creation Baumann

Suitable

2011-09-12

BM

Oddy test

sample prep: N/A, test #7319

CREAM; 100%cotton

Cream, White

exhibition/woven, fabric

none

Unisono 96

Creation Baumann

Suitable

2012-04-20

BM

Oddy test

sample prep: N/A, test #7481

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Unisono 207

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7143

YELLOW; 100% cotton

Yellow

exhibition/woven, fabric

exhibition/woven

none

Unisono 211

Creation Baumann

Suitable

2009-06-23

BM

Oddy test

sample prep: N/A, test #6509

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Unisono 213

Creation Baumann

Suitable

2009-09-25

BM

Oddy test

sample prep: N/A, test #6617

BLUE, LIGHT; 100% cotton

Blue, Light

exhibition/woven, fabric

none

Unisono 215

Creation Baumann

Suitable

2009-06-23

BM

Oddy test

sample prep: N/A, test #6508

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Unisono 220

Creation Baumann

Suitable

2009-09-25

BM

Oddy test

sample prep: N/A, test #6615

PINK, DARK; 100% cotton

Dark, Pink

exhibition/woven, fabric

none

Unisono 232

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8115

YELLOW, LIGHT; 100% cotton

Light, Yellow

exhibition/woven, fabric

exhibition/woven

none

Unisono 0233

Creation Baumann

Unsuitable

2012-01-02

CMA

Oddy test

washed w/o detergent

green/brown, olive; 100% cotton

Brown, Green

exhibition/woven, fabric

none

Unisono 0233

Creation Baumann

Suitable

2011-03-03

CMA

Oddy test

Fabric has been through washing machine w/o detergent

green/brown, olive; 100% cotton

Brown, Green

exhibition/woven, fabric

none

Unisono 234

Creation Baumann

Suitable

2012-04-20

BM

Oddy test

sample prep: N/A, test #7482

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Unisono 301

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8118

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 302

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8124

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 304

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7144

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Unisono 305

Creation Baumann

Suitable

2013-08-02

BM

Oddy test

sample prep: N/A, test #7904

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 306

Creation Baumann

Suitable

2012-04-20

BM

Oddy test

sample prep: N/A, test #7483

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 310

Creation Baumann

Suitable

2014-04-04

BM

Oddy test

sample prep: N/A, test #8172

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 311

Creation Baumann

Suitable

2014-04-04

BM

Oddy test

sample prep: N/A, test #8173

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 312

Creation Baumann

Suitable

2014-04-04

BM

Oddy test

sample prep: N/A, test #8174

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 313

Creation Baumann

Suitable

2014-04-04

BM

Oddy test

sample prep: N/A, test #8175

BEIGE; 100% cotton

Beige

exhibition/woven, fabric

none

Unisono 314

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7145

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Unisono 315

Creation Baumann

Suitable

2012-03-20

BM

Oddy test

sample prep: N/A, test #7428

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Unisono 316

Creation Baumann

Suitable

2012-04-20

BM

Oddy test

sample prep: N/A, test #7484

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Unisono 318

Creation Baumann

Suitable

2014-04-04

BM

Oddy test

sample prep: N/A, test #8176

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Unisono 319

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7146

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Unisono 320

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7147

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Unisono 321

Creation Baumann

Suitable

2012-04-20

BM

Oddy test

sample prep: N/A, test #7485

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Unisono 324

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7148

BLUE; 100% cotton

Blue

exhibition/woven, fabric

none

Unisono 325

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7149

GREY; 100% cotton

Gray

exhibition/woven, fabric

none

Unisono 329

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7150

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Unisono 330

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7151

GREEN; 100% cotton

Green

exhibition/woven, fabric

none

Unisono 337

Creation Baumann

Suitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8112

YELLOW, LIGHT; 100% cotton

Light, Yellow

exhibition/woven, fabric

exhibition/woven

none

Indian-chinese Douppion 745/0003 White

Creation Baumann

Unsuitable

2012-08-14

BM

Oddy test

sample prep: N/A, test #7595

WHITE; 100% SILK

White

exhibition/woven, fabric

none

Unisono 344

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7153

RED; 100% cotton

Red

exhibition/woven, fabric

none

Unisono 347

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7154

RED; 100% cotton

Red

exhibition/woven, fabric

none

Unisono 348

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7155

PURPLE; 100% cotton

Purple

exhibition/woven, fabric

none

Unisono 349

Creation Baumann

Suitable

2011-02-17

BM

Oddy test

sample prep: N/A, test #7156

PURPLE; 100% cotton

Purple

exhibition/woven, fabric

none

Haze 104, Woven Fire Retardant Fabric

Kvadrat

Creation Baumann

Temporary

2019-11-06

MMA

Oddy test (method: 20190226_OT_1)

sample prep: N/A, test #7157

White; 60% Polyester fire retardant woven fabric, 40% polyester, not washed before testing, model number: 104, 650 g/lin.m, purchased September 2019

White

exhibition/woven, fabric

Setefano Vol 2 1-6731-351

Creation Baumann

Temporary

2013-06-26

BM

Oddy test

sample prep: N/A, test #7870

BLUE; SILK

Blue

exhibition/woven, fabric

none

Unisono 352

Creation Baumann

Suitable

2012-03-20

BM

Oddy test

sample prep: N/A, test #7427

BROWN; 100% cotton

Brown

exhibition/woven, fabric

none

Unisono 9169

Creation Baumann

Unsuitable

2012-01-02

CMA

Oddy test

washed w/o detergent

tan; 100% cotton

Brown, Light

exhibition/woven, fabric

none

Unisono 9200

Creation Baumann

Suitable

2012-01-02

CMA

Oddy test

washed w/o detergent

brown, dark; 100% cotton

Brown, Dark

exhibition/woven, fabric

none

Unisono Ii 87

Creation Baumann

Suitable

2008-01-01

CMA

Oddy test

none

gray, blue; 100% cotton

Blue, Gray

exhibition/woven, fabric

none

Unisono Ii 233

Creation Baumann

Unsuitable

2008-01-01

CMA

Oddy test

none

gray/green, light; 100% cotton

Gray, Green

exhibition/woven, fabric

none

Unisono Ii 14

Creation Baumann

Unsuitable

2009-04-15

CMA

Oddy test

none

blue, light; 56% linen, 44% cotton, coarse plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Ii 14

Creation Baumann

Unsuitable

2009-05-15

CMA

Oddy test

none

blue, light; 56% linen, 44% cotton, coarse plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Ii 15

Creation Baumann

Unsuitable

2009-04-15

CMA

Oddy test

none

blue, light; 56% linen, 44% cotton, coarse plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Ii 15

Creation Baumann

Unsuitable

2009-05-15

CMA

Oddy test

none

blue, light; 56% linen, 44% cotton, coarse plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Ii 90

Creation Baumann

Unsuitable

2009-04-15

CMA

Oddy test

none

white, off/ cream; 100% cotton, fine plain weave

Off-White

exhibition/woven, fabric

none

Unisono Ii 90

Creation Baumann

Unsuitable

2009-05-15

CMA

Oddy test

none

white, off/ cream; 100% cotton, fine plain weave

Off-White

exhibition/woven, fabric

none

Unisono Ii 91

Creation Baumann

Unsuitable

2009-04-15

CMA

Oddy test

none

white, off; 100% cotton, fine plain weave

Off-White

exhibition/woven, fabric

none

Unisono Ii 91

Creation Baumann

Suitable

2009-05-15

CMA

Oddy test

none

white, off; 100% cotton, fine plain weave

Off-White

exhibition/woven, fabric

none

Unisono Ii 92

Creation Baumann

Unsuitable

2009-04-15

CMA

Oddy test

none

white, off; 100% cotton, fine plain weave

Off-White

exhibition/woven, fabric

none

Unisono Ii 92

Creation Baumann

Suitable

2009-05-15

CMA

Oddy test

none

white, off; 100% cotton, fine plain weave

Off-White

exhibition/woven, fabric

none

Unisono Ii 115

Creation Baumann

Unsuitable

2009-04-15

CMA

Oddy test

none

blue, light; 100% cotton, medium plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Ii 115

Creation Baumann

Unsuitable

2009-05-15

CMA

Oddy test

none

blue, light; 100% cotton, medium plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Ii 1661

Creation Baumann

Unsuitable

2009-04-15

CMA

Oddy test

none

blue, light; 100% cotton, medium plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Ii 1661

Creation Baumann

Unsuitable

2009-05-15

CMA

Oddy test

none

blue, light; 100% cotton, medium plain weave

Blue, Light

exhibition/woven, fabric

none

Unisono Iii-150 91

Creation Baumann

Unsuitable

2013-09-19

CMA

Oddy test

washed, no detergent

Off-white; 100% cotton

Off-White

exhibition/woven, fabric

Unisono Regular 90

Creation Baumann

Unsuitable

2008-01-01

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Unisono Regular 91

Creation Baumann

Unsuitable

2008-01-01

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Universal Iii 209

Creation Baumann

Unsuitable

2009-09-14

CMA

Oddy test

none

red, brown medium; 100% PLF CS, fine plain weave

Brown, Red

exhibition/woven, fabric

none

Velling 339

Creation Baumann

Unsuitable

2009-12-09

CMA

Oddy test

washed in hot and cold H2O

red, brown; 100% cotton, velvet/cut pile

Brown, Red

exhibition/woven, fabric

none

Velling 362

Creation Baumann

Suitable

2012-05-23

CMA

Oddy test

none

tan; 100% cotton

Brown, Light

exhibition/woven, fabric

none

Velling 364

Creation Baumann

Unsuitable

2012-05-15

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Velling 364

Creation Baumann

Unsuitable

2012-09-11

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Velling 365

Creation Baumann

Suitable

2012-05-15

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Velling 365

Creation Baumann

Suitable

2012-09-11

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Velling 366

Creation Baumann

Suitable

2008-01-01

CMA

Oddy test

none

blue, light; 100% cotton/velvet

Blue, Light

exhibition/woven, fabric

none

Velling 368

Creation Baumann

Unsuitable

2008-01-01

CMA

Oddy test

none

blue, dark; 100% cotton/velvet

Blue, Dark

exhibition/woven, fabric

none

Velling 368

Creation Baumann

Suitable

2009-12-23

CMA

Oddy test

Machine washed in H20 - 1 wash, 2 Rinses

blue; 100% cotton/ velvet

Blue

exhibition/woven, fabric

none

Velling 368

Creation Baumann

Unsuitable

2012-09-11

CMA

Oddy test

none

blue; 100% cotton

Blue

exhibition/woven, fabric

none

Velling 369

Creation Baumann

Suitable

2012-03-15

CMA

Oddy test

Allowed to hang dry

brown; 100% cotton

Brown

exhibition/woven, fabric

none

Velling 370

Creation Baumann

Unsuitable

2012-01-07

CMA

Oddy test

none

purple; 100% cotton/ velvet

Purple

exhibition/woven, fabric

none

Velling 379

Creation Baumann

Suitable

2012-01-10

CMA

Oddy test

don't use in contact with object

blue, light; cotton

Blue, Light

exhibition/woven, fabric

none

Velling 381

Creation Baumann

Suitable

2012-05-15

CMA

Oddy test

none

blue; 100% cotton

Blue

exhibition/woven, fabric

none

Velling 381

Creation Baumann

Unsuitable

2012-09-11

CMA

Oddy test

none

Blue; 100% cotton

Blue

exhibition/woven, fabric

none

Velling 382

Creation Baumann

Suitable

2012-09-11

CMA

Oddy test

none

Blue; 100% cotton

Blue

exhibition/woven, fabric

none

Velling 393

Creation Baumann

Suitable

2012-05-23

CMA

Oddy test

none

white; 100% cotton

White

exhibition/woven, fabric

none

Velling 394

Creation Baumann

Unsuitable

2012-01-02

CMA

Oddy test

washed and pressed by "Carmen's Custom Window treatment"

grey; 100% cotton

Gray

exhibition/woven, fabric

none

Velling 395

Creation Baumann

Suitable

2012-09-11

CMA

Oddy test

none

Brown; 100% cotton

Brown

exhibition/woven, fabric

none

Velling 395

Creation Baumann

Suitable

2008-01-01

CMA

Oddy test

none

gray; 100% cotton/velvet

Gray

exhibition/woven, fabric

none

Velling 396

Creation Baumann

Unsuitable

2009-12-23

CMA

Oddy test

Machine washed in H20- 1 wash, 2 Rinses

purple, dark; 100% cotton/ velvet

Dark, Purple

exhibition/woven, fabric

none

Velling 397

Creation Baumann

Unsuitable

2009-12-23

CMA

Oddy test

Machine washed in H20- 1 wash, 2 Rinses

purple; 100% cotton

Purple

exhibition/woven, fabric

none

Velling 397

Creation Baumann

Unsuitable

2012-09-11

CMA

Oddy test

Fabric dye transferred when ironed after washing

red, dark; 100% cotton

Dark, Red

exhibition/woven, fabric

none

Velling 398

Creation Baumann

Unsuitable

2012-05-15

CMA

Oddy test

none

brown, dark/ velvet; 100% cotton

Brown, Dark

exhibition/woven, fabric

none

Velling 399

Creation Baumann

Unsuitable

2009-12-23

CMA

Oddy test

Machine washed in H20- 1 wash, 2 Rinses

purple; 100% cotton

Purple

exhibition/woven, fabric

none

Velling 399

Creation Baumann

Unsuitable

2011-01-27

CMA

Oddy test

none

brown, red; 100% cotton, velvet, cut pile

Brown, Red

exhibition/woven, fabric

none

Velling 399

Creation Baumann

Suitable

2012-09-11

CMA

Oddy test

Fabric dye transferred when ironed after washing

red; 100% cotton

Red

exhibition/woven, fabric

none

Velling 401

Creation Baumann

Suitable

2012-03-15

CMA

Oddy test

Fabric dye transferred when ironed after washing

Green; 100% cotton

Green

exhibition/woven, fabric

none

Velling 402

Creation Baumann

Suitable

2012-01-07

CMA

Oddy test

don't use in contact with object

blue; 100% cotton/ velvet

Blue

exhibition/woven, fabric

none

Velos 2

Creation Baumann

Unsuitable

2008-01-01

CMA

Oddy test

none

blue, light; cotton

Blue, Light

exhibition/woven, fabric

none

Velos 15

Creation Baumann

Suitable

2008-01-01

CMA

Oddy test

none

cotton

exhibition/woven, fabric

none

Nomex Needle Felt

Dale Intertec

Unsuitable

2009-03-20

BM

Oddy test

sample prep: N/A, test #6322

BEIGE; FELT

Beige

batting & padding, fabric

none

100% Nylon Net, 20 Denier Monofilament Scoured And Heat Set Natural N8000

Dukeries Textiles And Fancy Goods.

Suitable

2011-03-10

BM

Oddy test

sample prep: NOT PREWASHED, test #7195

WHITE; NYLON

White

fiber or thread

none

100% Pure Silk Tulle White 7518f

Dukeries Textiles And Fancy Goods.

Suitable

2011-03-10

BM

Oddy test

sample prep: NOT PREWASHED, test #7194

WHITE; SILK

White

exhibition/woven, fabric

none

Ultra Suede Light 5553 Nior

Fifield Fabrics

Suitable

2009-06-05

BM

Oddy test

sample prep: N/A, test #6451

BLACK

Black

exhibition/woven, fabric

Ultra Suede Light 5743 Asphault

Fifield Fabrics

Unsuitable

2009-06-05

BM

Oddy test

sample prep: N/A, test #6450

BLACK

Black

exhibition/woven, fabric

Daguerre Coated Canvas 400

Hahnemuhle Fine Art

Suitable

2014-01-16

BM

Oddy test

sample prep: N/A, test #8133

WHITE; POLY cotton + COATING

White

exhibition/woven, fabric

none

Goya Coated Canvas 340

Hahnemuhle Fine Art

Temporary

2014-01-16

BM

Oddy test

sample prep: N/A, test #8135

WHITE; POLY cotton+ COATING

White

exhibition/woven, fabric

none

Monet Coated Canvas 410

Hahnemuhle Fine Art

Suitable

2014-01-16

BM

Oddy test

sample prep: N/A, test #8136

WHITE; 100% cotton + COATING

White

exhibition/woven, fabric

none

Binding Cloth 541

Hakko Soteisha .

Temporary

2011-01-18

BM

Oddy test

sample prep: N/A, test #7117

GREY

Gray

book cloth, fabric

Binding Cloth 544

Hakko Soteisha .

Unsuitable

2011-01-18

BM

Oddy test

sample prep: N/A, test #7118

BLACK

Black

book cloth, fabric

Binding Cloth E2101

Hakko Soteisha .

Unsuitable

2011-01-18

BM

Oddy test

sample prep: N/A, test #7120

BLACK

Black

book cloth, fabric

Binding Cloth Eu79

Hakko Soteisha .

Temporary

2011-01-18

BM

Oddy test

sample prep: N/A, test #7121

BLACK

Black

book cloth, fabric

Binding Cloth Sa-13

Hakko Soteisha .

Unsuitable

2011-01-18

BM

Oddy test

sample prep: N/A, test #7119

BLACK

Black

book cloth, fabric

Tyvek

Hanotex

Suitable

2014-04-04

BM

Oddy test

sample prep: N/A, test #8177

BLACK; POLYPROPYLENE

Black

fabric, non-woven

none

"st Margaret" Brocade

Hayes Finch

Unsuitable

2009-09-16

BM

Oddy test

sample prep: N/A, test #6606

RED

Red

exhibition/woven, fabric

Testfabrics Cotton Sateen 479-58"

Iris Color Studio

Unsuitable

2013-06-07

CMA

Oddy test

Unwashed/undyed

natural; cotton; (fabric Source: Testfabrics Cotton Sateen 479-58")

Natural

exhibition/woven, fabric

Testfabrics Cotton Sateen 479-58"

Iris Color Studio

Unsuitable

2013-06-07

CMA

Oddy test

Washed/undyed

natural; cotton; (fabric Source: Testfabrics Cotton Sateen 479-58")

Natural

exhibition/woven, fabric

Dark Gray F9t 1a

Iris Color Studio

Suitable

2012-01-02

CMA

Oddy test

none

gray, dark; 100% cotton, fine plain weave

Dark, Gray

exhibition/woven, fabric

none

Slate Blue Gray 1622 /08

Iris Color Studio

Suitable

2010-01-21

CMA

Oddy test

none

blue, gray; 100% cotton, fine plain weave

Blue, Gray

exhibition/woven, fabric

none

Ecru Gray 1544.125

Iris Color Studio

Suitable

2012-02-01

CMA

Oddy test

none

gray; 100% cotton, fine plain weave

Gray

exhibition/woven, fabric

none

Gray Ecru 1543

Iris Color Studio

Suitable

2013-06-07

CMA

Oddy test

washed by dyer

gray; cotton; (fabric Source: Testfabrics Cotton Sateen 479-58")

Gray

exhibition/woven, fabric

Lighter Dark Gray

Iris Color Studio

Suitable

2013-06-07

CMA

Oddy test

washed by dyer

gray; cotton; (fabric Source: Whaleys Arian Cotton Sateen)

Gray

exhibition/woven, fabric

Dark Brown Cotton Velvet

Iris Studio

Suitable

2010-08-10

CMA

Oddy test

washed by manufacturer

brown, dark; cotton, velvet

Brown, Dark

exhibition/woven, fabric

none

Raisin Brown Cotton Velvet

Iris Studio

Suitable

2012-02-01

CMA

Oddy test

washed by manufacturer

brown; cotton, velvet

Brown

exhibition/woven, fabric

none

Dark Indigo Heavy Cotton Satin

Iris Studio

Suitable

2011-02-14

CMA

Oddy test

washed by manufacturer

blue, dark; cotton, heavy satin

Blue, Dark

exhibition/woven, fabric

none

Dark Cobalt Heavy Cotton Satin

Iris Studio

Suitable

2012-02-01

CMA

Oddy test

washed by manufacturer

blue, dark; cotton, heavy satin

Blue, Dark

exhibition/woven, fabric

none

Wheat 100% Linen

Iris Studio

Suitable

2011-02-14

CMA

Oddy test

washed by manufacturer

tan; 100% linen, plain weave

Brown, Light

exhibition/woven, fabric

none

Ancient Chinese Grey 100% Linen

Iris Studio

Unsuitable

2012-02-01

CMA

Oddy test

washed by manufacturer

gray; 100% linen, plain weave

Gray

exhibition/woven, fabric

none

Peru Cotton Satin Cinnabar (indian Red)

Iris Studio

Unsuitable

2012-02-01

CMA

Oddy test

none

red; cotton, satin

Red

exhibition/woven, fabric

none

Peru Cotton Satin (light Green)

Iris Color Studio

Unsuitable

2012-02-01

CMA

Oddy test

none

green, light; cotton, satin

Green, Light

exhibition/woven, fabric

none

Peru Cotton Satin (dark Green)

Iris Color Studio

Unsuitable

2012-02-01

CMA

Oddy test

none

green, dark; cotton, satin

Dark, Green

exhibition/woven, fabric

none

Pisano 1-6313-171

Jab International Furnishings

Temporary

2013-06-26

BM

Oddy test

sample prep: N/A, test #7875

GOLD; SILK

Gold

exhibition/woven, fabric

none

Pisano 1-6313-272

Jab International Furnishings

Temporary

2013-05-03

BM

Oddy test

sample prep: N/A, test #7841

CREAM; SILK

Cream, White

exhibition/woven, fabric

none

Pisano 1-6313-298

Jab International Furnishings

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7838

RED, DARK; SILK

Dark, Red

exhibition/woven, fabric

none

Pisano 1-6313-314

Jab International Furnishings

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7837

RED, DARK; SILK

Dark, Red

exhibition/woven, fabric

none

Pisano 1-6313-355

Jab International Furnishings

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7873

BLUE; SILK

Blue

exhibition/woven, fabric

none

Pisano 1-6313-413

Jab International Furnishings

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7839

SILVER; SILK

Silver

exhibition/woven, fabric

none

Pisano 1-6313-454

Jab International Furnishings

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7871

BLUE, DARK; SILK

Blue, Dark

exhibition/woven, fabric

none

Pisano 1-6313-512

Jab International Furnishings

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7842

RED; SILK

Red

exhibition/woven, fabric

none

Pisano 1-6313-579

Jab International Furnishings

Temporary

2013-05-03

BM

Oddy test

sample prep: N/A, test #7836

GOLD; SILK

Gold

exhibition/woven, fabric

none

Pisano 1-6313-595

Jab International Furnishings

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7876

GREY; SILK BLUE WARP, GREEN WEFT THREAD

Gray

exhibition/woven, fabric

none

Pisano 1-6313-652

Jab International Furnishings

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7872

BLUE; SILK

Blue

exhibition/woven, fabric

none

Pisano 1-6313-694

Jab International Furnishings

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7877

BLACK; SILK

Black

exhibition/woven, fabric

none

Pisano 1-6313-777

Jab International Furnishings

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7840

GOLD; SILK

Gold

exhibition/woven, fabric

none

Pisano 1-6314-122

Jab International Furnishings

Temporary

2013-06-26

BM

Oddy test

sample prep: N/A, test #7874

GOLD; SILK

Gold

exhibition/woven, fabric

none

Saba Vol 2, 1-6206-583

Jab Fabric

Suitable

2009-01-22

BM

Oddy test

test 6124, pH 6.7

Green; Polyester

Green

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6206-278

Jab Fabric

Temporary

2009-01-22

BM

Oddy test

test 6117, pH 6.5

Cream; Polyester

Cream, White

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6243-933

Jab Fabric

Temporary

2009-01-22

BM

Oddy test

test 6119, pH 6.6

Gold; Polyester

Gold

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6206-559

Jab Fabric

Temporary

2009-01-22

BM

Oddy test

test 6121, pH 6.7

Blue; Polyester

Blue

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6243-255

Jab Fabric

Temporary

2009-01-22

BM

Oddy test

test 6122, pH 6.6

Blue; Polyester

Blue

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6206-658

Jab Fabric

Temporary

2009-01-22

BM

Oddy test

test 6123, pH 6.5

Blue; Polyester

Blue

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6206-138

Jab Fabric

Temporary

2009-01-22

BM

Oddy test

test 6126, pH 6.7

Green; Polyester

Green

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6243-339

Jab Fabric

Unsuitable

2009-01-22

BM

Oddy test

test 6125, pH 6.7

Green; Polyester

Green

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6243-735

Jab Fabric

Unsuitable

2009-01-22

BM

Oddy test

test 6118, pH 6.6

Gold; Polyester

Gold

exhibition/woven, fabric

n/a

Saba Vol 2, 1-6206-299

Jab Fabric

Unsuitable

2009-01-22

BM

Oddy test

test 6120, pH 6.6

Green; Polyester

Green

exhibition/woven, fabric

n/a

Setefano Vol 2 1-6731-011

Jab International Furnishings

Suitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7867

RED; SILK

Red

exhibition/woven, fabric

none

Setefano Vol 2 1-6731-012

Jab International Furnishings

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7868

RED; SILK

Red

exhibition/woven, fabric

none

Setefano Vol 2 1-6731-310

Jab International Furnishings

Unsuitable

2013-06-26

BM

Oddy test

sample prep: N/A, test #7869

RED, DARK; SILK

Dark, Red

exhibition/woven, fabric

none

Setefano Vol 2 1-6731-351

Jab International Furnishings

Temporary

2013-06-26

BM

Oddy test

sample prep: N/A, test #7870

BLUE; SILK

Blue

exhibition/woven, fabric

none

Patong Silk 3045/02

Jim Thompson

Temporary

2010-12-22

BM

Oddy test

sample prep: RINSED IN DISTILLED WATER, test #7098

BROWN; SILK

Brown

exhibition/woven, fabric

none

Silk Fabric 137255

Jim Thompson

Unsuitable

2010-07-12

BM

Oddy test

sample prep: N/A, test #6867

BROWN; SILK

Brown

exhibition/woven, fabric

none

Silk Fabric 180451

Jim Thompson

Unsuitable

2010-07-12

BM

Oddy test

sample prep: N/A, test #6868

ORANGE; SILK

Orange

exhibition/woven, fabric

none

Silk Fabric 3013/15

Jim Thompson

Unsuitable

2010-07-12

BM

Oddy test

sample prep: N/A, test #6866

BLUE; SILK

Blue

exhibition/woven, fabric

none

Domette Interlining 137cm Wide

John Lewis

Suitable

2012-03-30

BM

Oddy test

sample prep: N/A, test #7471

WHITE; cotton

White

exhibition/woven, fabric

none

Calico, Natural

Lincraft

Suitable

2020-12-20

NAA

PAT

washed

Brown, light; 100% cotton

Brown, Light

exhibition/woven, fabric

n/a

Novasuede Bordeaux T3j5w

Majilite

Temporary

2013-07-19

CMA

Oddy test

fabric washed, no detergent

Red, dark; Nylon fiber matrix

Dark, Red

exhibition/woven, fabric

Novasuede Cypress T3phw

Majilite

Unsuitable

2012-05-15

CMA

Oddy test

none

green; Nylon fiber matrix

Green

exhibition/woven, fabric

none

Novasuede Madison Grey

Majilite

Unsuitable

2012-10-19

CMA

Oddy test

none

gray; nylon fiber matrix

Gray

exhibition/woven, fabric

none

Novasuede Mauve T3r1w

Majilite

Unsuitable

2013-07-19

CMA

Oddy test

fabric washed, no detergent

Purple/Pink; Nylon fiber matrix

Purple/Pink

exhibition/woven, fabric

Novasuede Moss

Majilite

Unsuitable

2012-01-07

CMA

Oddy test

none

green; Nylon fiber matrix

Green

exhibition/woven, fabric

none

Novasuede Jade T3pew

Majilite

Unsuitable

2013-07-19

CMA

Oddy test

fabric washed, no detergent

Green; Nylon fiber matrix

Green

exhibition/woven, fabric

Novasuede Sable T3i8w

Majilite

Unsuitable

2013-07-19

CMA

Oddy test

fabric washed, no detergent

Brown; Nylon fiber matrix

Brown

exhibition/woven, fabric

Novasuede Teal T3n1w

Majilite

Temporary

2013-07-19

CMA

Oddy test

fabric washed, no detergent

Blue; Nylon fiber matrix

Blue

exhibition/woven, fabric

Kamla Garnet #07

Malabar

Suitable

2013-05-10

CMA

Oddy test

fabric washed, no detergent

Red/Brown; 100% cotton

Brown, Red

exhibition/woven, fabric

Kamla Rajah #12

Malabar

Unsuitable

2013-05-10

CMA

Oddy test

fabric washed, no detergent

Red, dark; 100% cotton

Dark, Red

exhibition/woven, fabric

Kamla Pewter #35

Malabar

Unsuitable

2013-05-10

CMA

Oddy test

fabric washed, no detergent

Grey; 100% cotton

Gray

exhibition/woven, fabric

Kamla Tamarind #41

Malabar

Suitable

2013-05-10

CMA

Oddy test

none

Brown, dark; 100% cotton

Brown, Dark

exhibition/woven, fabric

Kamla Taupe #209

Malabar

Suitable

2013-05-10

CMA

Oddy test

none

Brown, grey; 100% cotton

Brown, Gray

exhibition/woven, fabric

Kamla Ash #211

Malabar

Suitable

2013-05-10

CMA

Oddy test

none

Brown, light; 100% cotton

Brown, Light

exhibition/woven, fabric

Kamla Pecan #213

Malabar

Suitable

2014-04-22

CMA

Oddy test

fabric washed, no detergent

Brown, light; 100% cotton

Brown, Light

exhibition/woven, fabric

n/a

Kamla Arabica #215

Malabar

Suitable

2013-05-10

CMA

Oddy test

none

brown/red, dark; 100% cotton

Brown, Red

exhibition/woven, fabric

Kamla Mocha #216

Malabar

Suitable

2013-05-10

CMA

Oddy test

none

brown; 100% cotton

Brown

exhibition/woven, fabric

Kamla Larch #246

Malabar

Temporary

2014-04-22

CMA

Oddy test

fabric washed, no detergent; don't use in contact with object

Brown, light; 100% cotton

Brown, Light

exhibition/woven, fabric

n/a

Kamla Indigo #252

Malabar

Unsuitable

2014-04-22

CMA

Oddy test

fabric washed, no detergent

Blue; 100% cotton

Blue

exhibition/woven, fabric

n/a

Tyvek 14m

Material Concepts

Suitable

2009-06-09

BM

Oddy test

sample prep: N/A, test #6482

WHITE; POLYETHELYNE

White

fabric, non-woven

none

Japara, Natural

Material World

Suitable

2020-12-20

NAA

PAT

washed

Brown, Light; cotton

Brown, Light

exhibition/woven, fabric

n/a

Royal Felt

Maish Felts

Unsuitable

2010-01-06

BM

Oddy test

sample prep: N/A, test #6757

GREEN; 100% Viscose

Green

exhibition/woven, fabric

none

Crepe Backed Satin Stretch 931d/0062 Celadon

Pongees

Temporary

2011-10-25

BM

Oddy test

sample prep: N/A, test #7332

GREEN, LIGHT; 92% SILK, 8% LYCRA

Green, Light

exhibition/woven, fabric

none

Crepe Backed Satin Stretch 931d-0129 Golden

Pongees

Temporary

2011-10-25

BM

Oddy test

sample prep: N/A, test #7334

GOLD; 92% SILK, 8% LYCRA

Gold

exhibition/woven, fabric

none

Crepe Backed Satin Stretch 931d-0208 Pale Pink

Pongees

Temporary

2011-10-25

BM

Oddy test

sample prep: N/A, test #7335

PINK, LIGHT; 92% SILK, 8% LYCRA

Light, Pink

exhibition/woven, fabric

none

Honan Pongee 822w-0001 Bleached

Pongees

Unsuitable

2009-01-22

BM

Oddy test

sample prep: N/A, test #6131

CREAM; 100% SILK

Cream, White

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0002 Black

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7243

BLACK; 100% SILK

Black

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0003 White

Pongees

Unsuitable

2012-08-14

BM

Oddy test

sample prep: N/A, test #7595

WHITE; 100% SILK

White

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0005 Porcelain

Pongees

Unsuitable

2012-08-14

BM

Oddy test

sample prep: N/A, test #7594

WHITE; 100% SILK

White

exhibition/woven, fabric

none

Indian Chinese-douppion, 745/0009 Almond

Pongees

Unsuitable

2009-01-20

BM

Oddy test

test 6185

Gold; 100% silk

Gold

exhibition/woven, fabric

n/a

Indian-chinese Douppion 745/0010 Amethyst

Pongees

Unsuitable

2009-02-12

BM

Oddy test

sample prep: N/A, test #6206

PURPLE; 100% SILK

Purple

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0018 Aster

Pongees

Unsuitable

2013-01-18

BM

Oddy test

sample prep: N/A, test #7683

BLUE; 100% SILK

Blue

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0019 Atlantic

Pongees

Temporary

2013-12-30

BM

Oddy test

sample prep: N/A, test #8122

TURQUOISE; 100% SILK

Blue, Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0047 Burgundy

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7242

RED; 100% SILK

Red

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0060 Cascade

Pongees

Unsuitable

2012-08-14

BM

Oddy test

sample prep: N/A, test #7593

BLUE, LIGHT; 100% SILK

Blue, Light

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0064 Celestial

Pongees

Unsuitable

2013-01-18

BM

Oddy test

sample prep: N/A, test #7682

PURPLE; 100% SILK

Purple

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0072 Chocolate

Pongees

Temporary

2009-02-12

BM

Oddy test

sample prep: N/A, test #6204

BROWN; 100% SILK

Brown

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0073 Cinnamon

Pongees

Unsuitable

2009-02-12

BM

Oddy test

sample prep: N/A, test #6207

BROWN, LIGHT; 100% SILK

Brown, Light

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0075 Claret

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7248

RED; 100% SILK

Red

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0085 Cornflower

Pongees

Temporary

2010-07-12

BM

Oddy test

sample prep: N/A, test #6864

BLUE, LIGHT; 100% SILK

Blue, Light

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0106 Eggshell

Pongees

Unsuitable

2012-08-14

BM

Oddy test

sample prep: N/A, test #7599

PINK; 100% SILK

Pink

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0110 Ether

Pongees

Temporary

2013-12-30

BM

Oddy test

sample prep: N/A, test #8131

BLUE, LIGHT; 100% SILK

Blue, Light

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0111 Evergreen

Pongees

Unsuitable

2009-11-04

BM

Oddy test

sample prep: N/A, test #6641

GREEN, DARK; 100% SILK

Dark, Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0116 Flame

Pongees

Temporary

2010-12-13

BM

Oddy test

sample prep: N/A, test #7077

ORANGE; 100% SILK

Orange

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0118 Lincoln

Pongees

Unsuitable

2009-11-04

BM

Oddy test

sample prep: N/A, test #6642

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian Chinese-douppion, 745/0129 Golden

Pongees

Unsuitable

2009-01-20

BM

Oddy test

test 6186

Gold; 100% silk

Gold

exhibition/woven, fabric

n/a

Indian-chinese Douppion 745/0136 Hazel

Pongees

Temporary

2013-12-30

BM

Oddy test

sample prep: N/A, test #8130

GOLD; 100% SILK

Gold

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0138 Hemlock

Pongees

Unsuitable

2012-08-14

BM

Oddy test

sample prep: N/A, test #7598

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0139 Herb

Pongees

Temporary

2011-03-29

BM

Oddy test

sample prep: N/A, test #7246

BROWN; 100% SILK

Brown

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0140 Honey

Pongees

Temporary

2012-08-14

BM

Oddy test

sample prep: N/A, test #7596

YELLOW; 100% SILK

Yellow

exhibition/woven, fabric

exhibition/woven

none

Indian-chinese Douppion 745/0147 Ink

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7247

BLACK; 100% SILK

Black

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0151 Jade

Pongees

Unsuitable

2013-12-30

BM

Oddy test

sample prep: N/A, test #8121

GREEN, LIGHT; 100% SILK

Green, Light

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0159 Lagoon

Pongees

Temporary

2013-08-02

BM

Oddy test

sample prep: N/A, test #7905

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0165 Lilac

Pongees

Temporary

2010-12-13

BM

Oddy test

sample prep: N/A, test #7079

GREY; 100% SILK

Gray

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0167 Lime

Pongees

Suitable

2009-04-28

BM

Oddy test

sample prep: N/A, test #6433

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0180 Military

Pongees

Temporary

2010-07-12

BM

Oddy test

sample prep: N/A, test #6873

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0186 Moonlight

Pongees

Unsuitable

2010-12-13

BM

Oddy test

sample prep: N/A, test #7076

GREY; 100% SILK

Gray

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0192 Navy

Pongees

Unsuitable

2010-07-12

BM

Oddy test

sample prep: N/A, test #6863

BLUE, DARK; 100% SILK

Blue, Dark

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0196 Oasis

Pongees

Temporary

2013-12-30

BM

Oddy test

sample prep: N/A, test #8120

BLUE; 100% SILK

Blue

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0200 Old Gold

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7244

YELLOW; 100% SILK

Yellow

exhibition/woven, fabric

exhibition/woven

none

Indian-chinese Douppion 745/0202 Olive

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7241

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0209 Paprika

Pongees

Temporary

2010-12-13

BM

Oddy test

sample prep: , test #7081

ORANGE; 100% SILK

Orange

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0212 Peacock

Pongees

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7847

MULTI; 100% SILK

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0215 Pebble

Pongees

Unsuitable

2012-08-14

BM

Oddy test

sample prep: N/A, test #7597

BEIGE; 100% SILK

Beige

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0229 Pumpkin

Pongees

Suitable

2010-12-13

BM

Oddy test

sample prep: N/A, test #7082

ORANGE; 100% SILK

Orange

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0254 Sangria

Pongees

Unsuitable

2009-11-04

BM

Oddy test

sample prep: N/A, test #6644

RED, DARK; 100% SILK

Dark, Red

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0267 Silver

Pongees

Temporary

2010-12-13

BM

Oddy test

sample prep: , test #7080

GREY; 100% SILK PURPLE WARP, GREEN WEFT THREAD

Gray

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0274 Star

Pongees

Temporary

2010-12-13

BM

Oddy test

sample prep: , test #7078

GREY; 100% SILK

Gray

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0290 Thyme

Pongees

Unsuitable

2009-04-28

BM

Oddy test

sample prep: N/A, test #6432

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0291 Turquiose

Pongees

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7848

TURQUOISE; 100% SILK

Blue, Green

exhibition/woven, fabric

none

Indian-chinese Douppion 745/0300 Wine

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7245

RED; 100% SILK

Red

exhibition/woven, fabric

none

Indian-indian Douppion 845/0002 Black

Pongees

Temporary

2011-03-29

BM

Oddy test

sample prep: N/A, test #7249

BLACK; 100% SILK

Black

exhibition/woven, fabric

none

Indian-indian Douppion 845/0003 White

Pongees

Unsuitable

2009-10-26

BM

Oddy test

sample prep: N/A, test #6630

WHITE; 100% SILK

White

exhibition/woven, fabric

none

Indian-indian Douppion 845/0004 Ivory

Pongees

Unsuitable

2009-10-26

BM

Oddy test

sample prep: N/A, test #6631

CREAM; 100% SILK

Cream, White

exhibition/woven, fabric

none

Indian-indian Douppion 845/0005 Porcelain

Pongees

Unsuitable

2009-10-26

BM

Oddy test

sample prep: N/A, test #6629

WHITE; 100% SILK

White

exhibition/woven, fabric

none

Indian Chinese-douppion, 845/0009 Almond

Pongees

Temporary

2009-01-20

BM

Oddy test

test 6188

Beige; 100% silk

Beige

exhibition/woven, fabric

n/a

Indian-indian Douppion 845/0020 Aubergine

Pongees

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7845

RED, DARK; 100% SILK

Dark, Red

exhibition/woven, fabric

none

Indian-indian Douppion 845/0075 Claret

Pongees

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7846

RED, DARK; 100% SILK

Dark, Red

exhibition/woven, fabric

none

Indian-indian Douppion 845-0075 Claret

Pongees

Temporary

2009-02-12

BM

Oddy test

sample prep: N/A, test #6213

RED; 100% SILK

Red

exhibition/woven, fabric

none

Indian-indian Douppion 845/0110 Ether

Pongees

Unsuitable

2010-07-12

BM

Oddy test

sample prep: N/A, test #6869

GREEN, LIGHT; 100% SILK

Green, Light

exhibition/woven, fabric

none

Indian Chinese-douppion, 845/0136 Hazel

Pongees

Unsuitable

2009-01-20

BM

Oddy test

test 6187

Brown, Light; 100% silk

Brown, Light

exhibition/woven, fabric

n/a

Indian-indian Douppion 845/0147 Ink

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7251

BLACK; 100% SILK BLUE WARP, PURPLE WEFT THREAD

Black

exhibition/woven, fabric

none

Indian-indian Douppion 845/0155 Khaki

Pongees

Unsuitable

2010-07-12

BM

Oddy test

sample prep: N/A, test #6870

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-indian Douppion 845/0159 Lagoon

Pongees

Unsuitable

2010-07-12

BM

Oddy test

sample prep: N/A, test #6871

BLUE, LIGHT; 100% SILK

Blue, Light

exhibition/woven, fabric

none

Indian Chinese-douppion, 845/0164 Light Bronze

Pongees

Suitable

2009-01-20

BM

Oddy test

test 6189

Brown, Light; 100% silk

Brown, Light

exhibition/woven, fabric

n/a

Indian-indian Douppion 845/0192 Navy

Pongees

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7844

BLUE, DARK; 100% SILK

Blue, Dark

exhibition/woven, fabric

none

Indian-indian Douppion 845-0196 Oasis

Pongees

Suitable

2009-02-12

BM

Oddy test

sample prep: N/A, test #6212

BLUE, LIGHT; 100% SILK

Blue, Light

exhibition/woven, fabric

none

Indian-indian Douppion 845/0212 Peacock

Pongees

Temporary

2010-07-12

BM

Oddy test

sample prep: N/A, test #6872

BLUE, LIGHT; 100% SILK

Blue, Light

exhibition/woven, fabric

none

Indian-indian Douppion 845/0215 Pebble

Pongees

Temporary

2011-03-29

BM

Oddy test

sample prep: N/A, test #7252

BEIGE; 100% SILK

Beige

exhibition/woven, fabric

none

Indian-indian Douppion 845-0254 Sangria

Pongees

Unsuitable

2009-02-12

BM

Oddy test

sample prep: N/A, test #6211

RED; 100% SILK

Red

exhibition/woven, fabric

none

Indian-indian Douppion 845/0267 Silver

Pongees

Temporary

2009-10-26

BM

Oddy test

sample prep: N/A, test #6628

SILVER; 100% SILK

Silver

exhibition/woven, fabric

none

Indian-indian Douppion 845/0282 Tabasco

Pongees

Unsuitable

2013-05-03

BM

Oddy test

sample prep: N/A, test #7843

RED; 100% SILK

Red

exhibition/woven, fabric

none

Indian-indian Douppion 845/0290 Thyme

Pongees

Temporary

2011-03-29

BM

Oddy test

sample prep: N/A, test #7256

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Indian-indian Douppion 845/0300 Wine

Pongees

Unsuitable

2011-03-29

BM

Oddy test

sample prep: N/A, test #7254

RED; 100% SILK

Red

exhibition/woven, fabric

none

Lightweight Crepe Back Satin Stretch 831d-0004 Ivory

Pongees

Temporary

2011-10-25

BM

Oddy test

sample prep: N/A, test #7333

CREAM; 92% SILK, 8% LYCRA

Cream, White

exhibition/woven, fabric

none

Regal Taffeta P403/0012 Antique Gold

Pongees

Unsuitable

2009-01-22

BM

Oddy test

sample prep: N/A, test #6127

GOLD; 100% SILK

Gold

exhibition/woven, fabric

none

Regal Taffeta P403/0118 Forest

Pongees

Unsuitable

2009-01-22

BM

Oddy test

sample prep: N/A, test #6128

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Regal Taffeta P403/0122 French

Pongees

Unsuitable

2009-01-22

BM

Oddy test

sample prep: N/A, test #6130

BLUE; 100% SILK

Blue

exhibition/woven, fabric

none

Regal Taffeta P403/0162 Leaf

Pongees

Unsuitable

2009-01-22

BM

Oddy test

sample prep: N/A, test #6129

GREEN; 100% SILK

Green

exhibition/woven, fabric

none

Prelle Cotton 13012 Bt307451 Bleu19

Prelle

Unsuitable

2009-01-22

BM

Oddy test

test 6112

Blue; cotton

Blue

exhibition/woven, fabric

n/a

Prelle Cotton 5212 Bleu 199/ff30745

Prelle

Suitable

2009-01-22

BM

Oddy test

test 6113

Blue; cotton

Blue

exhibition/woven, fabric

n/a

Brushed Nylon

Spyder Displays

Suitable

2020-12-20

NAA

PAT

washed

Black; Nylon

Black

exhibition/woven, fabric

n/a

Brushed Nylon

Spyder Displays

Suitable

2020-12-20

NAA

PAT

unwashed

Black; Nylon

Black

exhibition/woven, fabric

n/a

Rosebrand Pinehurst Archival Flame Retardant Lightweight Linen

Rosebrand

Suitable

2010-12-07

BM

Oddy test

sample prep: WASHED WITH ORVUS AND RINSED IN DISTILLED WATER, test #7072

BEIGE; LINEN

Beige

exhibition/woven, fabric

none

Rosebrand Pinehurst Archival Flame Retardant Linen

Rosebrand

Suitable

2010-12-07

BM

Oddy test

sample prep: WASHED WITH ORVUS AND RINSED IN DISTILLED WATER, test #7069

GREY; LINEN

Gray

exhibition/woven, fabric

none

Army Carded Cotton Sateen, 428u

Testfabrics

Unsuitable

2013-06-07

CMA

Oddy test

batch? 55196, fabric washed, no detergent

white, natural; cotton, unbleached, desized

Natural, White

exhibition/woven, fabric

n/a

Cotton Duck, 464u

Testfabrics

Unsuitable

2013-06-07

CMA

Oddy test

batch? 6165, fabric washed, no detergent

white, natural; cotton, unbleached, desized

Natural, White

exhibition/woven, fabric

n/a

Unbleached Cotton Flannel (unwashed)

Testfabrics

Unsuitable

2013-05-10

CMA

Oddy test

none

natural; cotton

Natural

exhibition/woven, fabric

Unbleached Cotton Flannel (washed)

Testfabrics

Unsuitable

2013-05-10

CMA

Oddy test

none

natural; cotton

Natural

exhibition/woven, fabric

Country Cream Ultrasuede Soft

Toray Industries

Suitable

2012-09-21

CMA

Oddy test

fabric not washed; don't use in contact with object

white; 65% polyester ultra-microfiber non-woven with 35% non-fibrous polyurethane binder

White

exhibition/woven, fabric

n/a

Topiary 4545

Toray Industries

Carmen's

Suitable

2013-01-04

CMA

Oddy test

don't use in contact with object

Green; Polyester and polyurethane

Green

exhibition/woven, fabric

none

Trevira Cs 206

Trevira

Temporary

2012-12-04

BM

Oddy test

sample prep: N/A, test #7661

GREY; FLAME RETARDANT POLYESTER (PLF) TREVIRA

Gray

exhibition/woven, fabric

none

Ultrasuede Macrosuede Port +

Warwick

Unsuitable

2013-03-22

BM

Oddy test

sample prep: N/A, test #7740

RED

Red

exhibition/woven, fabric

Buckram

Whaleys Bradford

Suitable

2009-02-13

BM

Oddy test

sample prep: MACHINE WASHED, test #6339

BEIGE; LINEN

Beige

exhibition/woven, fabric

none

Cotton Domette Natural Cm15956

Whaleys Bradford

Unsuitable

2012-03-30

BM

Oddy test

sample prep: N/A, test #7470

WHITE; cotton

White

exhibition/woven, fabric

none

Cotton Jersey Fabric Cd26

Whaleys Bradford

Temporary

2012-03-30

BM

Oddy test

sample prep: N/A, test #7465

CREAM; cotton

Cream, White

exhibition/woven, fabric

none

Cotton Jersey Fabric Cm15956

Whaleys Bradford

Temporary

2012-03-30

BM

Oddy test

sample prep: N/A, test #7466

WHITE; cotton

White

exhibition/woven, fabric

none

Linen Scrim

Whaleys Bradford

Temporary

2009-02-13

BM

Oddy test

sample prep: MACHINE WASHED, test #6337

BEIGE; LINEN

Beige

exhibition/woven, fabric

none

Acrylic Prefelt Forest

World Of Fabric

Unsuitable

2010-01-06

BM

Oddy test

sample prep: N/A, test #6756

GREEN, DARK; ACRYLIC

Dark, Green

exhibition/woven, fabric

none

Cotton Jersey

Teoh Huat Textile, Singapore

Suitable

2017-02-16

HCC

Oddy test

none

OFF WHITE; cotton JERSEY

Off-White

exhibition/woven, fabric

Cotton, T 3340

Khoon Heng, Singapore

Suitable

2017-02-16

HCC

Oddy test

none

PURPLE; cotton

Purple

exhibition/woven, fabric

Cotton, Tc 36

Khoon Heng, Singapore

Unsuitable

2017-02-16

HCC

Oddy test

none

BLACK; cotton

Black

exhibition/woven, fabric

Cotton, T 3712

Khoon Heng, Singapore

Temporary

2017-02-16

HCC

Oddy test

none

GREY; cotton

Gray

exhibition/woven, fabric

Cotton, P 33

Khoon Heng, Singapore

Unsuitable

2017-02-16

HCC

Oddy test

none

NAVY BLUE; cotton

Blue

exhibition/woven, fabric

Cotton, T 3888

Khoon Heng, Singapore

Suitable

2017-02-16

HCC

Oddy test

none

BLUE; cotton

Blue

exhibition/woven, fabric

Cotton, Hj 3300

Khoon Heng, Singapore

Unsuitable

2017-02-16

HCC

Oddy test

none

BURGUNDY; cotton

Red

exhibition/woven, fabric

Cotton, Tr 268

Khoon Heng, Singapore

Suitable

2017-02-16

HCC

Oddy test

none

GREY; cotton

Gray

exhibition/woven, fabric

Cotton, Rm Ultra 439

Creation Baumann

Suitable

2017-02-16

HCC

Oddy test

none

NAVY BLUE; cotton

Blue

exhibition/woven, fabric

Cotton, Rm Unisono 81

Creation Baumann

Suitable

2017-02-16

HCC

Oddy test

none

BEIGE; cotton

Beige

exhibition/woven, fabric

Show Case Fabric T3741 (21)

Khoon Heng, Singapore

Unsuitable

2017-08-16

HCC

Oddy test

none

GREEN; 65 % Polyester, 35 % Viscose

Green

exhibition/woven, fabric

Show Case Fabric T3867 (1)

Khoon Heng, Singapore

Suitable

2017-08-16

HCC

Oddy test

none

BLUE; 65 % Polyester, 35 % Viscose

Blue

exhibition/woven, fabric

Show Case Fabric T3724

Khoon Heng, Singapore

Suitable

2017-08-16

HCC

Oddy test

none

YELLOW; 65 % Polyester, 35 % Viscose

Yellow

exhibition/woven, fabric

exhibition/woven

Show Case Fabric Umbria Iii Col 115

Creation Baumann

Suitable

2019-02-14

HCC

Oddy test

none

Umbria

exhibition/woven, fabric

Cotton Tape

Tunity

Thye Wah Heng

Suitable

2019-02-14

HCC

Oddy test

none

NATURAL, RAW OFF; Cotton

Natural

fiber or thread

Cotton Tape - Twill 3/8"

Talas

Suitable

2019-02-14

HCC

Oddy test

none

Natural; Cotton

Cotton

Natural

fiber or thread

Unisono Iv Col 4ll

Creation Baumann

Suitable

2019-02-14

HCC

Oddy test

none

BLUEISH-GREY; ---

Blue/Gray

exhibition/woven, fabric

Carbon Beach Carpet

Temporary

2016-01-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Sand Colored; Polypropylene/polystyrene backing with nylon fiber

Brown

exhibition/woven, fabric

Kings Road Carpet

Suitable

2016-01-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Navy; Polyethylene terephthalate backing with nylon fiber

Blue

exhibition/woven, fabric

Ultrasuede Fabric (unwashed)

Temporary

2016-01-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Red/Orange; Polyethylene terephthalate

Orange, Red

exhibition/woven, fabric

Ultrasuede Fabric (washed)

Temporary

2016-01-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Red/Orange; Polyethylene terephthalate

Orange, Red

exhibition/woven, fabric

Tan Carpet

Unsuitable

2016-01-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Tan; Polyethylene terephthalate

Brown, Light

exhibition/woven, fabric

Upholstery Fabric (unwashed)

Unsuitable

2016-01-01

IMA

Oddy test

none

Black; Polyethylene terephthalate

Black

exhibition/woven, fabric

Upholstery Fabric (washed)

Temporary

2016-01-01

IMA

Oddy test

none

Black; Polyethylene terephthalate

Black

exhibition/woven, fabric

Mushroom Packaging

Paradise Packaging Company

Unsuitable

2021-01-12

MMA

Oddy test (method: 20190226_OT_1)

Replacement for Styrofoam made from hemp hurd and mycelium; 100% compostable; 1 inch thick form; Purchased November 2020

hemp hurd and mycelium

cotton), foam replacement, natural (eg: wood

Usuyo, Japanese "thin Paper"

Unknown

Yoshida Shoten

Temporary

2021-01-12

MMA

Oddy test (method: 20190226_OT_1)

Machine made, mass produced, Japanese, extremely thin, highly calendared paper; used for interleaving; imported from Kyoto, Japan; Purchased March 2012

paper-based, sheet

Dartek-cast Nylon Film, C-917na

Tc Transcontinental Packaging

Masterpak

Temporary

2021-01-12

MMA

Oddy test (method: 20191213_B_OT)

A cast film made from nylon 6,6 and modified with a heat stabilizing additive for use as a carrier, barrier and release film in extreme prolonged high temperature applications; absorbs up to 10% of its weight in moisture, no surface coatings or plasticizers; 3/4 mil thick; Purchased September 2020

nylon 6,6

membrane (< 1mm thick), polymer

Strong And Flexible Nylon 12, Pa12

Shapeways

Suitable

2020-11-04

MMA

Oddy test (method: 20190226_OT_1)

Strong and Flexible Nylon 12 Plastic, PA12, polyamide, PA2200; 3D printed nylon in custom shape; purchased September 2020

Nylon 12 Plastic

3d printed, block/bulk/pellet, polymer

Spaceloft Insulation

Aspen Aerogels

Unsuitable

2020-11-04

MMA

Oddy test (method: 20190226_OT_1)

Flexible, nanoporous aerogel blanket insulation; combines silica gel with reinforcing fiber. Comes in 0.2 inch and 0.4 inch thicknesses. Maximum temperature of 390°F. 0.15 g/cc density. R-value of 10.3 per inch. Received January 2020

silica gel and reinforcing fiber

building insulation, foam, polymer

Grey Silicone Spg W/ Silicone Psa

Netherland Rubber Company

Netherland Rubber

Temporary

2020-11-04

MMA

Oddy test (method: 20190226_OT_1)

Platinum cured silicone foam, reactive foaming process, 1/4" thick, gray silicone sponge w/ silicone PSA and clear release liner. Purchased 2017

Platinum cured silicone foam

gasket, polymer

Cafco Board Foil-faced

Isolatek International

Temporary

2020-11-04

MMA

Oddy test (method: 20190226_OT_1)

A rigid mineral wool board which combines fire protection, thermal insulation and acoustical control all in one product. R-value of 4.2 R/inch, 0.144 g/mL density. Contains mineral wool, phenolic resin, and urea. Received July 2020

mineral wool

building insulation, foam, polymer

Tpu F70d-035tr Uv, 3d Print Material

Keene Village Plastics

Suitable

2020-10-28

MMA

Oddy test (method: 20190226_OT_1)

Thermoplastic polyurethane 3D printing material. 6 grams of material was printed prior to printing an addition 6 grams for the Oddy test. Print bed has white glue stick on it for adhesion. This layer was NOT used for the Oddy test. 235°C print temp on 50°C bed with Kapton tape on bed surface on top of the white glue. Received November 2018, printed on 9/11/2020

Thermoplastic polyurethane

block/bulk/pellet, polymer

Petg, 3d Print Material

Keene Village Plastics

Suitable

2020-10-22

MMA

Oddy test (method: 20190226_OT_1)

Polyethylene Terephthalate Glycol Modified (PETG) filament 3D printing material. 6 grams of material was printed prior to printing an addition 6 grams for the Oddy test. Print bed has white glue stick on it for adhesion. This layer was NOT used for the Oddy test. 250°C print temp. 85°C bed temp. Received November 2018, printed on 9/11/2020.

Polyethylene Terephthalate Glycol Modified (PETG)

block/bulk/pellet, polymer

Vivak Thermoplastic Pteg, Glossy

Plaskolite

Laird Plastics

Temporary

2020-10-16

MMA

Oddy test (method: 20190226_OT_1)

Clear thermoplastic sheet, polyethylene terephthalate glycol (PETG); 2mm thick; sample received with protective plastic covering on either side, which was removed before testing; Purchased September 2020

Clear

board, plastic/polymeric/synthetic

Hm-43 Akaso Kozo

Tatsuyuki Kitaoka

Hiromi Paper

Unsuitable

2020-10-02

MMA

Oddy test (method: 20190226_OT_1)

100% Akaso Kozo paper from Tosa Kozo family, handmade in Japan, no coloration added, cooked with lime, board dried. 10.5 g/m^2. Purchased January 2020

100% Akaso Kozo

Natural

paper-based, sheet

Tyvek 1622e

Dow Chemical Company

Material Concepts

Temporary

2020-09-18

MMA

Oddy test (method: 20191213_B_OT)

Uncoated, 6.1 mil, 44gsm, 3" core, pin perforated with .025mm - .038mm holes throughout, highly air and moisture permeable, soft and fabric-like. Received June 2020

membrane (< 1mm thick), polymer

Cafco Board

Isolatek International

Temporary

2020-09-04

MMA

Oddy test (method: 20190226_OT_1)

A rigid mineral wool board which combines fire protection, thermal insulation and acoustical control all in one product. R-value of 4.2 R/inch, 0.144 g/mL density. Contains mineral wool, phenolic resin, and urea. Received July 2020

mineral wool, phenolic resin, and urea

board, composite

Migrations Bbt Diamond 10 Technology Coating, Z3543

Armstrong Flooring

Temporary

2020-09-04

MMA

Oddy test (method: 20190226_OT_1)

Biobased non-pvc floor tile, 1.8 inch thickness, 12 inch x 12 inch tiles, Diamond 10 Technology coating, scratch and stain resistant. Received December 2019

non-pvc floor tile

flooring, non-carpet

Migrations Bbt Diamond 10 Technology Coating, Z3503

Armstrong Flooring

Temporary

2020-09-04

MMA

Oddy test (method: 20190226_OT_1)

Biobased non-pvc floor tile, 1.8 inch thickness, 12 inch x 12 inch tiles, Diamond 10 Technology coating, scratch and stain resistant. Received December 2019

non-pvc floor tile

flooring, non-carpet

Silicone Parchment Release Paper, #2-23

Unknown

Masterpak

Temporary

2020-08-27

MMA

Oddy test (method: 20191213_B_OT)

Non-stick thin parchment release paper, vegetable parchment, silicone-treated on two sides; pH value of 5.5 to 6.5; 100 sheets of 24 inches x 36 inches, 2 mil thick

vegetable parchment, silicone-treated

paper-based, sheet

Formglas Gfrg, Glass Fiber Reinforced Gypsum

Formglas Products

Formglas(r) Products

Temporary

2020-08-27

MMA

Oddy test (method: 20190226_OT_1)

Glass fiber reinforced gypsum board, 'thin cast' alpha gypsum, 1675 kg/m^3; calcium sulfate hemihydrate, glass fiber, portland cement, crystalline silica; oxides of sulfur released when burned; Purchased January 2020

calcium sulfate hemihydrate, glass fiber, portland cement, crystalline silica

board, composite

Obomodulan 500

OBO-Werke

Mccausey Specialty Products

Suitable

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Stiff, foamed polyurethane board; density is 500 kg/m3; pink colored; Purchased: 12/2017

Pink

board, plastic/polymeric/synthetic

Komatex White Matte

Unknown

Harbor Sales

Temporary

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Rigid foam PVC sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; Prepared on 1/27/2020, cut into strips on table saw and broken/cut into large pieces; Purchased May 2019

polyvinyl chloride and minor components

board, plastic/polymeric/synthetic

Komacel White Gloss 4813Mck

Unknown

Harbor Sales

Suitable

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Rigid Foam PVC Sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; Prepared 1/27/2020, cut into strips on table saw and broken into large pieces; Purchased May 2019

polyvinyl chloride and minor components

board, plastic/polymeric/synthetic

Heritage Archival Corrugated Board, E-flute Tpb567017

Unknown

Talas

Temporary

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Acid-free corrugated cardboard; single ply construction; 100% bleached alpha cellulose, potato starch, alkaline reserve (buffer) > 3% calcium carbonate; 1/16" x 8" x 10" sheets; Prepared on 1/27/2020; cut with Exacto knives; Purchased May 2019

100% bleached alpha cellulose, potato starch, alkaline reserve (buffer) > 3% calcium carbonate

board, natural

Davey Board Red Label, #18

Unknown

Colophon Book Arts Supply

Unsuitable

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Single ply book board; acid neutral with a pH of 7-8; 20.625" x 30"; Prepared on 1/27/2020, cut with cleaned scissors; Purchased May 2019

board, natural

Neopor Gps Type Ii Insulation

Basf

Temporary

2020-03-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Gray

Graphite polystyrene (GPS) rigid foam insulation, comprised of many small pockets of air within a polymer matrix containing graphite. R-value of 5.0 @ 75°F and 5.2 @ 40°F. ~1 inch thick. Density of 21.6 kg/m3. 1 g of material in each jar. Sample received February 2020

Gray

building insulation, foam, polymer

Walltite Spray Foam

Basf

Unsuitable

2020-03-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Green

Two-component closed-cell spray polyurethane foam system, zero ozone-depleting blowing agent. Density of 2.0-2.3 pcf, maximum temperature of 180°F. Sample received February 2020. Only 1.5 g of material in each jar.

Green

building insulation, foam, polymer

Aero Rubber Closed Cell Eva Sponge

Aero Rubber Company

Spacesaver Corporation

Unsuitable

2020-03-26

MMA

Oddy test (method: 20190226_OT_1)

Color: Black

Black closed cell EVA foam; 1/4 inches thick, 4lb density; tested without adhesive; ethyl vinyl acetate cross-linked polyethylene; Purchased February 2020

Black

foam, non-building insulation, polymer

Polyvinyl Print Media, Prime 75ct - Clear

Bild

Varidirect

Unsuitable

2020-03-26

MMA

Oddy test (method: 20190226_OT_1)

Color: Green

Flexible PVC floor coating; ceramic(TM) textured surface with satin top coat finish, 100% polyvinyl wear layer, and reverse printing surface - sample with printed green grass; 8 oz/sq ft, 75mil thick; extruded PVC; Purchased January 2020

Green

anti-slip), coating, floor (eg.: anti-wear

Sequel Rubber Cork, Ebony Sq5013

Capri Collections

Unsuitable

2020-03-26

MMA

Oddy test (method: 20190226_OT_1)

Color: Ebony

Vulcanized rubber with homogeneous cork content, abrasion resistance; 3 mm thick tiles; Purchased January 2020

Ebony

anti-slip), coating, floor (eg.: anti-wear

Lens Tissue, J51-lens

Unknown

Legion Paper

Unsuitable

2020-03-19

MMA

Oddy test (method: 20190226_OT_1)

Color: White

100% rayon, machine made in Japan, neutral pH, no deckles, 12 gsm, sold as 24 inch x 36 inch sheets. Sample received February 2020

White

paper-based, sheet

Sekishu Mare Hp-07

So Kubota

Hiromi Paper

Temporary

2020-03-19

MMA

Oddy test (method: 20180821_B_OT)

Color: Natural

100% Japanese kozo paper, cooked with soda ash, dried on wooden boards, 21.4g/m^2, pH 7.0, unbuffered, no sizing, handmade, hand beaten, inner green and white layer of bark. Purchased January 2020.

Natural

paper-based, sheet

Tek Wipe

Unknown

Polistini

Temporary

2020-03-19

MMA

Oddy test (method: 20180821_B_OT)

Color: White

Non-woven fabric, a blend of 45% polyester and 55% cellulose hydrospun with high tensile strength and without the use of any binders, starches, or thermal binding techniques. Sample received February 2020.

White

membrane (< 1mm thick), polymer

Comforttherm Fiberglass Insulation R-30

Johns Manville

Unsuitable

2020-03-19

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Formaldehyde-free plastic wrapped fiberglass batt. Available in either vapor retarder or non-vapor retarder poly-encapsulated plastic casing. 10.25 inch thickness. 30 maximum r-value. Sample received January 2020.

White

building insulation

Softwrap Nomex

DuPont

Masterpak

Temporary

2020-03-19

MMA

Oddy test (method: 20180821_B_OT)

Color: White

Synthetic aromatic polyamide polymer wrap permeable to air and water, chemically inert, complete temperature stability, nondusting, flame resistant. 5 mil thickness, 2.0 oz/yd^2. Sample received February 2020.

White

membrane (< 1mm thick), polymer

Ceiling Mirror

Mirrorlite

Unsuitable

2020-03-05

MMA

Oddy test (method: 20190226_OT_1)

Silver mirror

Lightweight glassless mirror, reflective polyester film metalized with vacuum deposited aluminum stretched over internal foam and adhesive; Purchased January 2020

Silver mirror

board, composite

Thermax Xarmor Ci Insulation

Dow Chemical Company

Dow Chemical

Unsuitable

2020-03-04

MMA

Oddy test (method: 20190226_OT_1)

Color: Silver

Glass-fiber-reinforced polyisocyanurate foam core with aluminum facing. 4.0 mil embossed exterior foil facer. Maximum use temperature of 250°F, R-value of 6.5 per inch. 2-inch thick sample received January 2020

Silver

building insulation, polymer

Thermafiber Ultrabatt Ff Insulation

Owens Corning

Unsuitable

2020-03-04

MMA

Oddy test (method: 20190226_OT_1)

Color: Brown

Formaldehyde-free mineral wool insulation, non-combustible, moisture-resistant, non-corrosive, non-deteriorating, and mold resistant. 3.0 inch thick sample. Sample received January 2020

Brown

building insulation

Thermafiber Ultrabatt Insulation

Owens Corning

Temporary

2020-03-04

MMA

Oddy test (method: 20190226_OT_1)

Color: Yellow

Mineral wool insulation, non-combustible, moisture-resistant, non-corrosive, non-deteriorating, and mold resistant. 3.5 inch thick sample, R-15. Sample Received January 2020

Yellow

building insulation

Ap Foil Faced Foam Sheathing

Johns Manville

Unsuitable

2020-03-04

MMA

Oddy test (method: 20190226_OT_1)

Color: Silver

Uniform closed-cell polyisocyanurate foam core bonded on each side to a foil facer; one side has a reflective foil facer and the other side a white non-reflective foil facer. Produced with hydrocarbon blowing agent with zero ozone depletion potential and virtually no global warming potential. Free of CFC and HCFC. Service temperature of -100 to 250°F. R-value of 6.0 per inch. Sample received January 2020

Silver

building insulation, foam, polymer

Non-perforated Silverboard Type I

Amvic System

Unsuitable

2020-03-04

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Expanded polystyrene (EPS) covered with a layer of polypropylene reflective lamination on both sides. No off-gassing and does not contain HFCs, CFCs, or HCFCs. R-value of 4.1 @ 75°F and 5.2 @ 0°F. 158°F maximum use temperature. Density of 16 kg/m^3. Sampled received January 2020

White

building insulation, foam, polymer

Alusuise Composites

Suitable

very slightly tarnished, same as control and zinsser shieldz coated sample

no change, same as control

2011-03-04

BKM

Oddy test

moderately expanded closed-cell polyvinyl acetate (PVC)

polyvinyl acetate (PVC)

board, plastic/polymeric/synthetic

Ag: no change, same as control,Cu: very slightly tarnished, same as control and zinsser shieldz coated sample,Pb: no change, same as control

Sintra Coated With 3x Zinsser Shieldz

Alusuise Composites

Suitable

very slightly tarnished, same as control and non-coated sample

no change, same as control

2011-03-04

BKM

Oddy test

moderately expanded closed-cell polyvinyl acetate (PVC)

polyvinyl acetate (PVC)

board, plastic/polymeric/synthetic

Ag: no change, same as control,Cu: very slightly tarnished, same as control and non-coated sample,Pb: no change, same as control

Alusuise Composites

Suitable

very slightly tarnished, same as control and zinsser shieldz coated sample

no change, same as control

2011-03-04

BKM

Oddy test

moderately expanded closed-cell polyvinyl acetate (PVC)

polyvinyl acetate (PVC)

exhibition/woven, fabric

Ag: no change, same as control,Cu: very slightly tarnished, same as control and zinsser shieldz coated sample,Pb: no change, same as control

Sintra Coated With 3x Zinsser Shieldz

Alusuise Composites

Suitable

very slightly tarnished, same as control and non-coated sample

no change, same as control

2011-03-04

BKM

Oddy test

moderately expanded closed-cell polyvinyl acetate (PVC)

polyvinyl acetate (PVC)

exhibition/woven, fabric

Ag: no change, same as control,Cu: very slightly tarnished, same as control and non-coated sample,Pb: no change, same as control

Abatron, Wood Epoxy

Abatron

Temporary

slightly redder

marginally more corroded

2007-08-28

BKM

Oddy test

9/26/07 - 64F in chamber

epoxy wood replacement compound; permanent, high strength, parts A and B

filler/binder mixture (non-paint), paste

Ag:,Cu: slightly redder,Pb: marginally more corroded

Abatron, Wood Epoxy

Abatron

Temporary

tarnished

2008-05-08

BKM

Oddy test

9 month cure time ok; would recommend 2 week and cure before inside case; ok for outside of case

filler/binder mixture (non-paint), paste

Ag: na,Cu: tarnished,Pb: na

Benchmark Sueded Polyethylene

Benchmark Catalog

Suitable

2017-06-23

BKM

Oddy test

Acrylic-adhesive backed sueded polyethylene

batting & padding, fabric

Ag: no corrosion,Cu: red- same as control,Pb: no corrosion

Clean Seal Gasket Epdm 105

Clean Seal

Suitable

2017-06-23

BKM

Oddy test

.438 x .375 Ethylene propylene diene monomer (M-class) rubber, no adhesive

Ethylene propylene diene monomer (M-class) rubber

gasket, polymer

Ag: no corrosion,Cu: minor darkening, some silver patches of discoloration,Pb: Slight white spots of corrosion- same as control

Clean Seal Gasket Silicone 8490

Clean Seal

Suitable

2017-06-23

BKM

Oddy test

Only 1 out of 2 samples opened, inconclusive

.3125 x .1875 ""D"" plain silicone no adhesive

gasket, polymer

Ag: no corrosion,Cu: red, patches of silver discoloration,Pb: Slight white spots of corrosion

Cleanseal 1153b Epdm

Clean Seal

Unsuitable

Darkened compared to controls and Cleanseal 8598

black tarnish localized at bottom of coupon

some corrosion

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days

Gasketing

gasket, polymer

Ag: black tarnish localized at bottom of coupon,Cu: Darkened compared to controls and Cleanseal 8598 (see above),Pb: some corrosion

Cleanseal 8598p Silicone

Clean Seal

Suitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days

Gasketing

gasket, polymer

Ag: no corrosion,Cu: darkened slightly compared to control,Pb: no corrosion

Dibond Panel Assembly / Anodized Aluminum Facing

3A Composites

Suitable

slightly red, but okay

no corrosion

No corrosion

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Dibond panel

board, plastic/polymeric/synthetic

Ag: no corrosion,Cu: slightly red, but okay,Pb: No corrosion

Dow Corning 3145 Rtv Mil-a-46146 Transparent / Structural Sealant And Adhesive

Dow Corning

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Sealant and Adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: very minor darkening,Pb: No corrosion

Dow Corning 7091 Black / Structural Adhesive / Sealant

Dow Corning

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Sealant and Adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Dow Corning Rtv Sealant 737 Neutral Cure Sealant, 100% Silicone Rubber

Dow Corning

Unsuitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days

sealing casework (SmallCorp cases on the 2nd floor)

adhesive caulk, polymer

Ag: no corrosion,Cu: multicolored corrosion,Pb: significantly darker than controls

Dow Corning Rtv Sealant 737 Neutral Cure Sealant, 100% Silicone Rubber

Dow Corning

Suitable

2018-12-17

BKM

Oddy test

sealing casework (SmallCorp cases on the 2nd floor)

adhesive caulk, polymer

Ag: no corrosion,Cu: darkened slightly compared to control,Pb: no corrosion

Europolveri Ral 9005 / Powdercoat (textured) On Steel

Europolveri

Suitable

very minor darkening

no corrosion

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Powdercoated steel

Steel

coating, paint & primer

Ag: no corrosion,Cu: very minor darkening,Pb: No corrosion

Hyflex Foam Gloves By Ansell 911-800

Ansell

Suitable

2009-03-16

BKM

Oddy test

4/13/09: Gloves themselves discolored significantly on foam pads but metals not tarnished.

glove, polymer

Hyflex Foam Gloves By Ansell 911-800 Ce

Ansell

Suitable

2008-12-30

BKM

Oddy test

No change in coupons but color change in glove material, should retest with glove in contact with coupons

gloves washed

glove, polymer

Ilpea Magnetic Gasket Assembly

Industrie Ilpea

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Magnetic gasket for case doors

gasket, polymer

Ag: no corrosion,Cu: slightly red, but okay,Pb: No corrosion

Ilpea Magnetic Gasket Assembly + 3M Vhb / Acrylic Foam Tape

Industrie Ilpea, 3M

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

2 Materials: Gasket tested in combination w/ Adhesive

gasket, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Ilpea Magnetic Gasket Assembly + Dow Corning 3145 Rtv Mil-a-46146 Transparent / Structural Sealant And Adhesive

Industrie Ilpea, Dow Corning

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

2 Materials: Gasket tested in combination w/ Adhesive

gasket, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Kraftmark Pro-create Professional Sculptors Putty

Kraftmark

Suitable

corroded

2008-12-30

BKM

Oddy test

Ok to useif allowed to cure for two weeks. Better to use outside case.

2 part epoxy putty

filler/binder mixture (non-paint), paste

Kraftmark Pro-create Professional Sculptors Putty

Kraftmark

Suitable

2008-12-30

BKM

Oddy test

Pass if allowed to cure for 2+ weeks. Oddy tested 5/8/08, new Oddy test requested

2 part epoxy putty (white and grey), similar to pliacre, 60hr air time, 50/50 mix ratio

filler/binder mixture (non-paint), paste

Kraftmark Pro-create Terrain Putty

Kraftmark

Suitable

corroded

2008-12-30

BKM

Oddy test

Ok to use with at least two week cure time. Better to use outside case.

2 part epoxy putty

filler/binder mixture (non-paint), paste

Kraftmark Pro-create Terrain Putty

Kraftmark

Suitable

2008-12-30

BKM

Oddy test

PASS if allowed to cure for 2 weeks. Oddy tested 5/8/08- new Oddy test requested

2 part epoxy putty (white and beige), lightweight, 60 hr air time, 50/50 mix

filler/binder mixture (non-paint), paste

Magic Sculpt 2 Part Epoxy Putty

Wesco Enterprises

Suitable

oxidized

2009-03-27

BKM

Oddy test

considered for use in mountmaking

cured for two weeks

filler/binder mixture (non-paint), paste

Magic Sculpt White

Wesco Enterprises

Suitable

oxidized

2009-03-27

BKM

Oddy test

considered for use in mountmaking

2 part epoxy putty cured 2 weeks

filler/binder mixture (non-paint), paste

Medex

Roseburg Forest Products

Unsuitable

covered with white corrosion products

2009-03-27

BKM

Oddy test

board, plastic/polymeric/synthetic

Ag:,Cu:,Pb: 4/17/09: covered with white corrosion products

Neoprene Spring Rubber Sheet

Suitable

darkened slightly compared to control

no change, same as control

2018-12-17

BKM

Oddy test

one anomaly Pb coupon that corroded very heavily, likely an issue with test conditions

neoprene rubber sheet, 1/4"" thick, 70A, 200% elongation, plain backing

block/bulk/pellet, polymer

Ag: no corosion,Cu: darkened slightly compared to control,Pb: almost no corrosion

Oece 414-9001 / White Back Paint For Glass

Oece [organizzazione Economica Commercio Emiliano (emilia Commerce Economic Organization)]

Suitable

very minor darkening

good - no corrosion

No corrosion

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

White back paint for glass - case material for Goppion cases

White

coating, paint & primer

Ag: good - no corrosion,Cu: very minor darkening,Pb: No corrosion

Oece 414-9001 / White Back Paint For Glass + Dow Corning 7091 Black / Structural Adhesive / Sealant

Oece [organizzazione Economica Commercio Emiliano (emilia Commerce Economic Organization)] and Dow Corning

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

2 Materials: Glass tested in combination w/ Adhesive

composite, other

Ag: no corrosion,Cu: slightly red, but okay,Pb: No corrosion

Pro-create Terrain Putty (2 Part)

Kraftmark

Suitable

oxidized

2009-03-27

BKM

Oddy test

considered for use in mountmaking

2 part epoxy putty cured 2 weeks

filler/binder mixture (non-paint), paste

Promante Mc Bond 2k Transparent / Structural Adhesive

Promanté

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Structural adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Se2040 - 40 Durometer Silicone

Stockwell Elastomerics

Unsuitable

2018-12-17

BKM

Oddy test

Silicone

gasket, polymer

Ag: no corosion,Cu: darkened slightly compared to control,Pb: some white corrosion spots overall, discrete areas of brown corrosion

Technical Rubber / Viton Tubular Gasket

Technical Rubber s.r.l.

Suitable

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Gasket

gasket, polymer

Ag: very slightly yellowed,Cu: minor darkening,Pb: No corrosion

Technical Rubber / Viton Tubular Gasket + 3M Vhb / Acrylic Foam Tape

Technical Rubber S.R.L And 3M

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

2 Materials: Gasket tested in combination w/ Adhesive

gasket, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Technical Rubber / Viton Tubular Gasket + Dow Corning 7091 Black / Structural Adhesive / Sealant

Technical Rubber S.R.L And Dow Corning

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

2 Materials: Gasket tested in combination w/ Adhesive

gasket, polymer

Ag: no corrosion,Cu: slightly red, but okay,Pb: No corrosion

Tempur-pedic

Suitable

2007-02-14

BKM

Oddy test

Great - no tarnish, BUT needs more research for use

Pressure-relieving swedish mattresses and pillows; Phone: 888-225-7984; lab sample - G0403M

foam, non building insulation, polymer

Usa Sealing 3/16"" Neoprene Sponge Cord

Usa Sealing

Unsuitable

2019-01-25

BKM

Oddy test

Control lead FAIL

neoprene sponge cord, 3/16""

gasket, polymer

Ag: same as control,Cu: very dark (purple) compared to control,Pb: Control lead FAIL

White Photomount

Legion Paper

Suitable

same as control

2019-09-04

BKM

Oddy test

4-ply non-buffered 100% cotton rag board

100% cotton

paper-based, sheet

Wilsonart Laminate

Wilsonart

Suitable

no change

2008-12-30

BKM

Oddy test

decorative surface paper impregnated with melamine resins over Kraft paper core sheets impregnated with phenolic resin

Kraft paper core sheets impregnated with phenolic resin

board, natural

Ag: Date Unknown: no change,Cu: Date Unknown: no change,Pb: Date Unknown: no change

Wonderflex

Wonderflex World

Unsuitable

2019-01-31

BKM

Oddy test

inconclusive - re-test recommended before use

thermoplastic composite

batting & padding, fabric

Ag: same as control,Cu: darkened red/purple slightly more than control,Pb: yellowish corrosion

Wonderflex Fosshape (black) Heated With Steam From Iron

Wonderflex World

Suitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days. One sample's lid popped off and moisture escaped

non woven thermoplastic polyester fabric

batting & padding, fabric

Ag: no corrosion,Cu: no corrosion,Pb: no corrosion

Wonderflex Fosshape (black) Unheated

Wonderflex World

Suitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days

non woven thermoplastic polyester fabric

batting & padding, fabric

Ag: no corrosion,Cu: no corrosion,Pb: no corrosion

Wonderflex Pro

Wonderflex World

Unsuitable

2019-01-31

BKM

Oddy test

thermoplastic composite

batting & padding, fabric

Ag: same as control,Cu: darkened red/purple slightly more than control and more than Wonderflex above,Pb: yellowish corrosion - more than Wonderflex above

Plexiglas G

Altuglas International By Arkema Group

Suitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2019-08-06

FMNH

Oddy test

Five samples run

Cell-cast acrylic sheet: Polymethyl methacrylate copolymer

polymer, sheet (>1mm thick)

Abs (3d Printing Filament)

Imaterialise

Suitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2019-04-22

FMNH

Oddy test

ABS 3D printing material (opaque white) acrylonitrile butadiene styrene

ABS acrylonitrile butadiene styrene

White

block/bulk/pellet, polymer

Alumide (3d Printing Filament)

Imaterialise

Suitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2019-04-22

FMNH

Oddy test

Aluminum and polyamide 3D printing material (metallic gray)

Aluminum and polyamide

Gray, metallic

block/bulk/pellet, polymer

High-detail Resin (3d Printing Filament)

Imaterialise

Unsuitable

Consistent with Control

Heavy white crystal growth

2019-04-22

FMNH

Oddy test

Resin 3D printing material (transparent)

Clear

block/bulk/pellet, polymer

High-detail Resin (3d Printing Filament)

Imaterialise

Temporary

Consistent with Control

Yellow/gray haze

2019-04-22

FMNH

Oddy test

Resin 3D printing material (opaque white)

White

block/bulk/pellet, polymer

High-detail Resin (paintable 3d Printing Filament)

Imaterialise

Unsuitable

Consistent with Control

Heavy white crystal growth

2019-04-22

FMNH

Oddy test

Resin 3D printing material (paintable)

block/bulk/pellet, polymer

Multicolor (3d Printing Filament)

Imaterialise

Unsuitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Heavy white crystal formation, complete delamination of coupon

2019-04-22

FMNH

Oddy test

Resin 3D printing material (multicolor)

Multicolor

block/bulk/pellet, polymer

Polyamide Mjp (3d Printing Filament)

Imaterialise

Suitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2019-04-22

FMNH

Oddy test

Polyamide 3D printing material (gray)

Gray

block/bulk/pellet, polymer

Polyamide Sls (3d Printing Filament)

Imaterialise

Temporary

Consistent with Control

Yellow/gray haze

2019-04-22

FMNH

Oddy test

Polyamide 3D printing material

block/bulk/pellet, polymer

Prime Gray (3d Printing Filament)

Imaterialise

Unsuitable

Consistent with Control

Heavy white crystal growth

2019-04-22

FMNH

Oddy test

Resin 3D printing material (gray)

Gray

block/bulk/pellet, polymer

Standard Resin (3d Printing Filament)

Imaterialise

Unsuitable

Consistent with Control

White crystal growth and haze

2019-04-22

FMNH

Oddy test

Resin 3D printing material (translucent yellow)

Yellow

block/bulk/pellet, polymer

Versatile Plastic (neutral White 3d Printing Filament)

Shapeways

Temporary

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2019-04-22

FMNH

Oddy test

White nylon plastic for 3D printing applications

White

block/bulk/pellet, polymer

Gaylord Archival 10 Pt. Folder Stock Artifact Tags (100-pack)

Gaylord Archival

Suitable

2020-02-14

MMA

Oddy test (method: 20190226_OT_1)

Color: Cream

Folder stock artifact tags; acid-free, lignin-free, pH 8.0-8.5, buffered; Purchased 2018

Cream

alumina), filled (eg.: silica gel, paper-based, zeolites

Rigilene Polyester Sewing Boning, 4336920980

Item4ever

Amazon.com

Temporary

2020-02-14

MMA

Oddy test (method: 20190226_OT_1)

Color: White

See through, flat type polyester plastic boning; Polypropylene sewn/woven inside; Washable, can be dry cleaned; Purchased November 2019

White

other, polymer

B-flute Corrugated Board Sheets, Cb810

Gaylord Archival

Temporary

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Blue Tested hanging and in contact

Corrugated board made with two outer sheets and a fluted inner sheet; 1/8" thick with a larger flute profile for vertical compression strength and cushioning; Buffered, acid-free, lignin-free, pH 8.0-9.5; 1/8 in. thick; Purchased November 2019

Blue

paper-based, sheet

Unbuffered Acid-free Interleaving Tissue, 741-0810

Unknown

University Products

Temporary

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Color: White Tested hanging and in contact

Unbuffered, acid-free, thin, translucent 16 g/m^2 tissue; 8 inch x 10 inch sheets; Purchased November 2019

White

paper-based, sheet

Acid-free Buffered Tissue Paper, Tpb001008

Unknown

Talas

Suitable

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Color: White Tested hanging and in contact

Interleaving tissue; acid-free, lignin-free, pH 9-10, and buffered with approximately 3% calcium carbonate; 24 g/m^2; 10 inch x 20 inch sheets; Purchased November 2019

White

paper-based, sheet

Archivart® Unbuffered Phototex Tissue

Archivart

Nielsen Bainbridge Group

Temporary

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Color: White Tested hanging and in contact

PhotoTex tissue; 10.5 lb. 100% cotton rag, sulfur-free, acid-free, lignin-free, pH 6.8-7.2, unbuffered, naturally white, sold as 24" x 36" sheets; Purchased November 2019

White

paper-based, sheet

Abaca.Sa Paper Hinging Tape, 533-0754

Lineco, Holyoke

Lineco

Temporary

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Color: White Tested hanging and in contact

Self-hinging tape made of Abaca paper (manila hemp) with very strong, permanent, and non-yellowing, water-activated acrylic adhesive; Purchased November 2019

White

paper-based, sheet

Insulbloc® Spray Foam System, 11-017

Ncfi Polyurethanes

Temporary

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Spray foam insulation; Two component, self-adhering, seamless, closed cell, spray applied polyurethane foam system; Formulated with highly insulating HFC-245fa as the blowing agent; Maximum service temperature: 180°F; Foam sprayed onto wooden boards by manufacturer, tested without wood, test sample taken from area farthest from the boards; Acquired November 2019

White

building insulation, foam, polymer

Styrofoam™ Brand Plazamate™

Dow Chemical Company

Dow Chemical

Temporary

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Color: Blue

Rigid extruded polystyrene board, foam insulation, hydrochlorofluorocarbon (HCFC) free with zero ozone-depletion potential; Maximum use temperature: 165°F; 2 inches thick; Acquired November 2019; Only 1.5 g of sample in each jar

Blue

building insulation, foam, polymer

Ksil & Surasil Gp Series Silicone Elastomer

Silicone Engineering

Unsuitable

2020-01-02

MMA

Oddy test (method: 20190226_OT_1)

Color: Grey

Extruded silicone gasket, circular profile with an arm that branches off (♇); chemical components: Polydimethylsiloxane with vinyl groups plus fillers and pigments where required; Purchased November 2019

Gray

gasket, polymer

Plastazote Ld 15 Bk

Zotefoams

Temporary

2020-01-02

MMA

Oddy test (method: 20190226_OT_1)

Color: Black

Low density polyethylene foam; closed-cell, cross-linked polyethylene block foam; maximum recommended operating temperature: 85 degrees C

Black

foam, non-building insulation, polymer

Obomodulan 500

OBO-Werke

Mccausey Specialty Products

Suitable

2019-12-12

MMA

Oddy test (method: 20190226_OT_1)

Color: Pink

Foamed polyurethane; density is 500 kg/m3; pink colored; Purchased: December 2017

Pink

board, plastic/polymeric/synthetic

Roxul Safe Insulation

Rockwool

Temporary

2019-11-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Green

Fire resistant mineral wool insulation with resin binder; 3 inches thick; 72 kg/m³ density; Received October 2019

Green

building insulation, foam, polymer

Foamular 250 Se 2" Insulation

Owens Corning

Temporary

2019-11-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Pink

Extruded polystyrene; moisture-resistant rigid foam board; 2 inches thick; New polystyrene 65-75%, Recycled polystyrene <30%, Flame retardant <1%, Colorant <1%, Blowing Agent 5-15%, Additives <1%; Received October 2019

Pink

foam, non-building insulation, polymer

Commercial Safb Ff Formaldehyde Free Mineral Wool Insulation

Owens Corning

Unsuitable

2019-11-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Brown

Formaldehyde-free mineral wool sound attenuation fire blanket; semi-rigid, non-structural insulation; 3 in thick; Mineral Wool, dextrose binder: Mineral Wool 93-98%, Dextrose 1-10%, proprietary material <1%; Received October 2019

Brown

building insulation, foam, polymer

Commercial Safb Mineral Wool Insulation

Owens Corning

Temporary

2019-11-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Green

Semi-rigid non structural mineral wool insulation; sound attenuation and fire blanket; 3 in thick; Mineral wool/fiber glass, Formaldehyde urea binder: 67-70% slag, 6-9% feldspar, 20-23% trap rock, 1-4% formic resin, 1-3% urea, <1% proprietary material; Received October 2019

Green

building insulation, foam, polymer

Obomodulan 500

OBO-Werke

Mccausey Specialty Products

Suitable

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Pink

Foamed polyurethane; density is 500 kg/m3; pink colored; Purchased: December 2017

Pink

board, plastic/polymeric/synthetic

Corafoam U280

Duna

Temporary

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Peach/Salmon

High density polyurethane rigid foam; carbon dioxide blowing agent; density: 450 kg/m^3; Received August 2019

Peach/Salmon

board, plastic/polymeric/synthetic

Corafoam U310

Duna

Unsuitable

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Brown/Mauve

High density polyurethane rigid foam; HFCs/CFCs/HCFCs-free blowing agent; density: 490 kg/m^3; Received August 2019

Brown/Mauve

board, plastic/polymeric/synthetic

Plastazote Ld18we

Zotefoams

Temporary

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Closed cell, cross-linked polyethylene block foam; 18 kg/m3 density; 0.8 mm cell size; Only 1.6g of sample added to each jar; Purchased May 2019

White

foam, non-building insulation, polymer

Artifact Identification Tags

Unknown

Talas

Temporary

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Natural

10 pt. manilla acid free and lignin free stock with 6 in looped cotton string; string included in testing; SKU: TAS046002; 1.5 inches x 3 inches

Natural

alumina), filled (eg.: silica gel, paper-based, zeolites

Artifact Identification Tags, 613-1530

Unknown

University Products

Suitable

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Natural

Artifact ID tags; 1.5 inches x 3 inches; buffered 10 pt. off-white lignin-free and acid-free; 6 in cotton string; string included in testing

Natural

alumina), filled (eg.: silica gel, paper-based, zeolites

Silicone Sheet Ss-.020x36-64904

Acme Rubber

Aaa-acme Rubber

Suitable

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

Silicone sheet .020" thick x 36" wide roll, 40 + OR -5 durometer, clear; General purpose silicone sheet with operating temperature of -65 to 400°F

Clear

membrane (< 1mm thick), polymer

Kodak Professional Endura Premier Paper

Kodak Alaris

Coloredge

Temporary

OK

Thin Yellow/green compacted corrosion

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #62

Resin-coated multilayers paper for making color prints; white medium weight paper with one glossy side - White - Cut to weight

board, cellulosic

Lexjet Premium Archival Matte Paper

Lexjet

Coloredge

Suitable

OK

Very slight darkening

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #70

Matte white paper for inkjet printing, pH neutral, acid-free, 9.5 mil - White - Cut to weight

White

board, cellulosic

Epson Presentation Matte Paper

Epson

Coloredge

Suitable

OK

light blue tarnish on coupon B

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #71

White paper medium weight for inkjet printable media; 7.20 mil - White - Cut to weight

White

board, cellulosic

Crescent Select 4-ply (1607)

Crescent

Dick Blick

Suitable

OK

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #91

4-ply alpha-cellulose mat board; acid and lignin-free - Brite White - Cut to weight

board, cellulosic

Bainbridge Alphamat Artcare Matboard 4-ply

Nielsen Bainbridge

Dick Blick

Suitable

OK

Very slight darkening on coupon B

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #92

Conservation-quality mat board with alkaline pH - Matte White (8464CR) - Cut to weight

White

board, cellulosic

Entrada Rag Bright 300

Moab

Duggal

Temporary

OK

Slight darkening, Light white compacted corrosion

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #175

100% cotton, acid-free, pH 8, buffered with calcium carbonate, 22.5mil, 300gsm, matte - White - Cut to weight

100% cotton with calcium carbonate

White

board, cellulosic

Somerset Enhanced Velvet 225

Moab

Duggal

Suitable

OK

OK, (slight darkening on edges)

OK

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #176

100% cotton mould made, acid-free, pH neutral, buffered with calcium carbonate, 18mil, 225gsm, matte - White - Cut to weight

100% cotton with calcium carbonate

White

board, cellulosic

Dibond (6mm Thickness)

3A Composites

Temporary

very slight red tarnish

OK

thin yellow/green compacted corrosion

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #29

Aluminum composite panel: AlMg1 alloy with black polyethylene (LDPE type) core with modified polyester system lacquer - Silver/Black - Cut to weight using circular saw

board, composite

Copper: very slight red tarnish - Silver: OK - Lead: thin yellow/green compacted corrosion

Exhibitshield Uv Laminate (5 Mil); Kodak Ektacolor Ra Chemicals; Kodak Professional Endura Premier Paper; Ultimate Optical Mount Removable (4-0167); Scratch-resistant Acrylic Sheet (optix E-series)

Plaskolite, Ritrama Inc., Kodak, Quality Media And Laminating Solutions

Coloredge

Temporary

OK

darkening

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #89

Fully assembled "Digital C" sandwich (2019 copy label from AMNH exhibit) - Multicolor - Cut to weight

board, composite

Ethafoam (220 Or 2.2 Pcf)

Dow Chemical Company

From Conservation Lab

Temporary

Very slight red tarnish

OK

Slight blue tarnish, Very slight darkening

2020-03-13

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #290

Polyethylene foam, density: 2.2 lbs per cubic foot - White - Cut to weight

board, foam

Copper: Very slight red tarnish - Silver: OK - Lead: Slight blue tarnish, Very slight darkening

Polyethylene Foam (s-12854) (1.7 Pcf)

Alusuise Composites

Uline

Suitable

very slightly tarnished, same as control and non-coated sample

no change, same as control

2011-03-04

BKM

Oddy test

AMNH Test #291

moderately expanded closed-cell polyvinyl acetate (PVC)

polyvinyl acetate (PVC)

board, plastic/polymeric/synthetic

board, foam

No

Ag: no change, same as control,Cu: very slightly tarnished, same as control and non-coated sample,Pb: no change, same as control

Scratch-resistant Acrylic Sheet (optix E-series)

Plaskolite

Coloredge

Temporary

OK

Light blue tarnish on coupon B, Very slight darkening

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #63

Clear acrylic sheet; contains olymethyl methacrylate (PMMA) and coating (proprietary) - Clear - Cut to weight with circular saw

Clear

board, plastic/polymeric/synthetic

Acrystar 0001 Clear P95 Matte Acrylic Sheet P48 (0.125")

Acrystar

Eplastics

Suitable

OK

OK, very light blue tarnish on coupon B

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #64

Cast acrylic sheet; acrylic polymer based on methyl methacrylate - 0001 frosted - Cut to weight with circular saw

board, plastic/polymeric/synthetic

Optix 0001 Non-glare Acrylic Sheet (0.125")

Plaskolite

Eplastics

Temporary

OK

Very slight darkening, light blue tarnish on coupon A

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #65

Acrylic sheet based on polymethyl methacryalte (PMMA) (99.5%) and methyl methacrylate (MMA) (0.5%) - 0001 clear - Cut to weight with circular saw.

board, plastic/polymeric/synthetic

Acrylite Uv/ Non-glare Acrylic Sheet (1/10")

Acrylite

Framedestination

Temporary

OK

Very slight darkening, very light blue tarnish on coupon A

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #66

Extruded thermoplastic acrylic sheet (proprietary) with UV filtering (OP3) - Clear - Cut to weight with circular saw

board, plastic/polymeric/synthetic

Acrylite Standard Acrylic Sheet (1/10")

Acrylite

Framedestination

Temporary

OK

Very slight darkening, very light blue tarnish on coupon A

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #67

Extruded thermoplastic acrylic sheet (proprietary) - Clear - Cut to weight with circular saw

board, plastic/polymeric/synthetic

Acrylite P95 Frosted Acrylic Sheet (1/2")

Evonik Industries

LeNoble Lumber

Temporary

OK

Very slight darkening, very light blue tarnish on coupon A

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #68

Acrylic copolymer (proprietary) - Frosted - Cut to weight with circular saw

board, plastic/polymeric/synthetic

Hdpe (white, 1/2")

Goppion

Suitable

OK

Very slight darkening

2019-07-10

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #169

Hard dense material - White - Cut in small strips; cut to weight

White

board, plastic/polymeric/synthetic

Vivak (grade 0.220)

Plaskolite

Temporary

OK

Slight darkening, very light white compacted corrosion at bottom

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #262

PETG (polyethylene terephthalate glycol-modified) copolyester sheet - Transparent - Cut to weight with circular saw

PETG (polyethylene terephthalate glycol-modified) copolyester sheet

Transparent

board, plastic/polymeric/synthetic

Hdpe (black, 1/2")

Indat Plastics

Goppion

Temporary

OK

Slight darkening, Thin Yellow/green compacted corrosion

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #263

High density polyethylene - Black - Cut to weight with circular saw

High density polyethylene

Black

board, plastic/polymeric/synthetic

Vutek Inks On Hips Filament (1/4") ("lexan")

Sabic Innovative Plastics

Suitable

OK

OK coupon B: Very slight darkening (P/T)

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #69

HIPS (High Impact Polystyrene Dissolvable Filament) with Vutek Inks (GSLX and GSR series) for inkjet/UV direct process printing - Color inks on clear substrate - Cut to weight with circular saw

board, plastic/polymeric/synthetic (and inks)

Compound Fpm 75 (rubber Ring)

(italian Supplier)

Temporary

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #30

Fluorinated carbon-based polymers (also known as Viton O-Ring); contains hexafluoropropylene and vindylidenefluoride - Black - Cut to weight

gasket

Copper: - Silver: - Lead: slight darkening, thin yellow green compact corrosion

Magnetic Rubber Strip (ndfeb) With Adhesive Backing (3M 9448)

Magnet Over Bros

Temporary

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #31

Plasto-ferrite strip (nedodymium magnet made from an alloy of neodymium, iron and boron) with adhesive back 3M 9448 (acrylate); attraction force: 1349 g/cm2 - Grey - Cut to weight; liner removed; tested on Mylar

gasket

Copper: slight red tarnish on coupon B - Silver: OK - Lead: darkening, rainbow tarnish

Tpe Transparent Compound (sha 70)/ Plastoferrite

Industrie Ilpea

Temporary

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #32

Transparent TPE (thermoplastic elastomer) on plastoferrite magnetic strip - Clear/Black - Cut to weight

gasket

Copper: very slight red tarnish - Silver: OK - Lead: very slight darkening

Viton Fluoroelastomer (vtr-9193)

DuPont

Rainbow Rubber

Temporary

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #94

Dark grey rubber; contains polyvinyllidenefluoride/hexafluoropropene and barium sulfate - Black - Cut to weight

Dark, Gray

gasket

Copper: Very slight red tarnish - Silver: OK - Lead: Slight darkening

Flexible Hose A8g16

Atag

Goppion

Temporary

OK

Slight darkening (darker at center),blue tarnish on coupon B

2020-01-07

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #279

Ether based PU wall with crushproof PVC helix - Transparent and yellow ribs - Cut to weight

gasket

Exhibitshield Uv Laminate (5 Mil) ("lexan Lam")

Quality Media And Laminating Solutions (qmls)

Coloredge

Unsuitable

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #61

Textured and rigid co-polymer film (PET) lined with pressure sensitive acrylic - Non-glare finish - Liner removed; cut to weight; sample folded on itself

membrane (<1mm thick), mpolymer

Copper: Black corrosion spots - Silver: Light purple tarnish, very light blue/blue-green tarnish on coupon B - Lead: Fluffy white crystals

Exhibitshield Uv Laminate (5 Mil) ("lexan Lam")

Quality Media And Laminating Solutions (qmls)

Coloredge

Temporary

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #90

Textured and rigid co-polymer film (PET) lined with pressure sensitive acrylic - Non-glare finish - Liner removed; sample cut to weight and laminated onto itself with bone folder

membrane (<1mm thick), polymer

Copper: OK - Silver: Blue/blue-green tarnish, Heavy purple tarnish - Lead: Slight darkening, Light white compacted corrosion

Computer Grafix Matte Film For Inkjet

Grafix

Unsuitable

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #139

Polyester base film - Translucent - Cut to weight

Polyester base film

Clear

membrane (<1mm thick), polymer

Copper: Very slight red tarnish - Silver: OK - Lead: Fluffy white crystals

Dura-lar Film (.005, Matte, 2 Sides)

Grafix

Temporary

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #140

Bi-axially oriented polyester film (PET) - Translucent (matte 2 sides) - Cut to weight

Bi-axially oriented polyester film (PET)

Clear

membrane (<1mm thick), polymer

Copper: Red tarnish - Silver: OK - Lead: Slight darkening, Light white compacted corrosion

Dura Clear

Kodak Alaris

Temporary

2019-07-10

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #162

Polyethylene teraphtalate and misc. additives - Transparent - Cut to weight

Polyethylene teraphtalate and misc. additives

Clear

membrane (<1mm thick), polymer

Copper: tiny lighter spots - Silver: OK - Lead: Thin Yellow/green compacted corrosion

Photo Tex

Temporary

OK

Very slight darkening, very slight blue tinge on coupon A

2019-07-10

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #163

Inkjet printing media made of polyester textile (40-45%), cellulose pulp (40-45%), silicon dioxide (3-7%), polyacrylic acid ester (3-7%), additives (3-7%) - White - Cut to weight

polyester textile (40-45%), cellulose pulp (40-45%), silicon dioxide (3-7%), polyacrylic acid ester (3-7%), additives (3-7%)

White

membrane (<1mm thick), polymer

Fasson Rapid-roll 1079 Tyvek

DuPont

Temporary

OK

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #221

Spunbound polyethylene, 8.3 mils - White - Cut to weight

White

membrane (<1mm thick), polymer

Fasson Rapid-roll 1085d Tyvek

DuPont

Temporary

OK

Slight darkening, Thin Yellow/green compacted corrosion

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #222

Spunbound polyethylene, 10.3 mils - White - Cut to weight

White

membrane (<1mm thick), polymer

Viton Gasket, 11mm Diameter

Rainbow Rubber

Suitable

OK

Very slight darkening

2019-07-10

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #168

Viton, soft and flexible tube gasket - Grey - Cut to weight

Gray

gasket

Plastazote Ld 70 Black Polyethylene Foam

Ufp Technologies

Zotefoams

Temporary

2019-11-06

MMA

Oddy test (method: 20190226_OT_1)

Black

Low density closed cell, cross-linked polyethylene block foam; recommended maximum operating temperature 105 degrees C; water absorption less than 2%; received May 2019

Black

foam, non-building insulation, polymer

Acoustic Textile Felt, Cotton Board

Really

Kvadrat

Temporary

2019-10-24

MMA

Oddy test (method: 20190226_OT_1)

White

Sound absorbing acoustic felt board; 70% cotton, 30% thermoplastic binder; 10 mm thick, 100 kg/m^3, 305 x 118 cm boards; purchased August 2019

White

batting or padding, fabric

Abaca Tissue, Mm-52 Lens Tissue

Unknown

Hiromi Paper

Temporary

2019-10-23

MMA

Oddy test (method: 20190226_OT_1)

Natural

100% Abaca tissue, pH neutral, cooked with caustic soda and dried on stainless steel; 9g/m^2; purchased August 2019

Natural

paper-based, sheet

Obomodulan 500

OBO-Werke

Mccausey Specialty Products

Suitable

2019-10-17

MMA

Oddy test (method: 20190226_OT_1)

Color: Pink; Comment: lead coupons are better than controls.

Foamed polyurethane board; density is 500 kg/m^3; pink colored; purchased December 2017

Pink

board, plastic/polymeric/synthetic

Solid Textile Board

Really

Kvadrat

Temporary

2019-10-11

MMA

Oddy test (method: 20190226_OT_1)

Cotton White

Recycled cotton board, 70% textile 30% thermoplastic binder; 300 cm x 110 cm, 7.8mm thick; designed to replace wood board in furniture and architecture construction; purchased August 2019

White

board, composite

Flutecorr, Corrugated Polypropylene Board

Laminacorr

Temporary

2019-10-10

MMA

Oddy test (method: 20190226_OT_1)

Natural

Extruded polypropylene corrugated board 10mm 1800 g/m^2; batch #2-0090907, extruded 1/6/17, cut 8/22/19; purchased August 2019

Natural

board, plastic/polymeric/synthetic

Cast Polymethylmethacrylate (pmma), Pmma Gs

Indat Plastics

Unknown

Suitable

2019-10-10

MMA

Oddy test (method: 20190226_OT_1)

Colorless

About 1" thick cast PMMA for use as display case plexi glass; purchased June 2019

Colorless

polymer, sheet (> 1mm thick)

Obomodulan 500

OBO-Werke

Mccausey Specialty Products

Suitable

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

Color Pink; Comment: lead coupons are better than controls.

Foamed polyurethane board; density is 500 kg/m^3; pink colored; purchased December 2017

Pink

board, plastic/polymeric/synthetic

Komatex White Matte 4812mktw, Rigid Pvc Board

Unknown

Harbor Sales

Unsuitable

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

White

Rigid foam PVC sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; purchased May 2019

White

board, plastic/polymeric/synthetic

Komacel White Gloss 4813Mkc, Rigid Pvc Board

Unknown

Harbor Sales

Suitable

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

White

Rigid Foam PVC Sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; purchased May 2019;

White

board, plastic/polymeric/synthetic

Heritage Archival Corrugated Board, E-flute Tpb67017

Unknown

Talas

Temporary

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

Blue/gray, white

Acid-free corrugated cardboard; single ply construction; 100% bleached alpha cellulose, potato starch, alkaline reserve (buffer) > 3% calcium carbonate; 1/16" x 8" x 10" sheets; purchased May 2019

Blue/gray, white

paper-based, sheet

Davey Board Red Label, #18

Unknown

Colophon Book Arts Supply

Unsuitable

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

Brown

Single ply book board; acid neutral with a pH of 7-8; 20.625" x 30"; purchased May 2019

Brown

paper-based, sheet

Multi-use Bi-corr Cross Direction Corrugated Board 613-4001

Unknown

University Products

Temporary

2019-08-16

MMA

Oddy test (method: 20190226_OT_1)

Blue/grey

1/4" Thick laminated corrugated board running perpendicular to each other; buffered with 3% calcium carbonate; lignin-free, acid-free; received May 2019

Blue/grey

alumina), filled (eg.: silica gel, paper-based, zeolites

Moisture Resistant Corrugated Board 156-1114

Unknown

University Products

Temporary

2019-08-16

MMA

Oddy test (method: 20190226_OT_1)

Grey

200 lb. Test B-flute corrugated paper board, 1/8 in thick; Acrylic water-resistant coating; acid-free lignin-free; buffered with 3% calcium carbonate; received May 2019

Gray

alumina), filled (eg.: silica gel, paper-based, zeolites

Ss-.047x36-65019 Silicone Sheet

Acme Rubber

Aaa-acme Rubber

Temporary

2019-08-16

MMA

Oddy test (method: 20190226_OT_1)

Black

General purpose Silicone Sheet; 0.47" thick x 36" wide +/- 5 durometer black color; Operating temperature of -65 to 400°F. Excellent electrical insulator. Resistance to oxygen & ozone

Black

polymer, sheet (> 1mm thick)

P-565 Silicone Rubber Clear

Silicones

Anglers Artistry

Temporary

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

Colorless, transparent

Silicone cast into large ~10 cm diam petri dish, about 8 mm thick; P-565 is not designed as a mold-making rubber; rather, it is used as the article.; cured 7 days before testing; Details: two-component, addition reaction, platinum catalyzed silicone rubber. It is designed to remain water-clear even after extended exposure to the sun. Chemical components: silicone. Mixing Instructions: Mix 100 parts by weight of P-565 Base with 10 parts by weight of P-565 Activator thoroughly. After mixing, place the material in a vacuum chamber capable of 28 to 29 inches of mercury vacuum. The material will expand to approximately quadruple its original volume and then collapse. Maintain the vacuum for an additional 2 to 3 minutes and then remove; purchased May 2018

Colorless, transparent

block/bulk/pellet, polymer

Spiders Wet Strength Tarantula Tissue Sheet, Paswtt7651

Unknown

Conservation By Design

Temporary

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

Cream

Unbuffered, low-opacity, long-fiber tissue. Application: repair work, lining, wrapping, interleaving; Chemical Components: 100% Manilla fiber; purchased September 2018

Cream

paper-based, sheet

Archival Corrugated Multi-use Board, #2-130, 2-131, 2-133, 2-148

Unknown

Masterpak

Temporary

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

Grey/White

Masterpak E Flute 1/16 inch single wall. 100% bleached alpha cellulose. No recycled or wooden fibers. No optical brighteners. Kappa level: 1-2 = lignin-free (TAPPI T 23 om-99). pH cold extraction: 8.0-9.5 (TAPPI T 509 om-02). Alkaline reserve (buffered) >3% calcium carbonate. Adhesive: potato starch, pH 7.0, moisture proof.

Grey/White

alumina), filled (eg.: silica gel, paper-based, zeolites

Teflon Relic Wrap Packaging Film, Part #51001

Technetics

Gaylord Archival

Temporary

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

White

Teflon PTFE film, pliable, chemically inert, nontoxic, and non-adsorbent; 3 mil thick, 10 in wide, 100 ft roll; Lot number 3161603004

White

membrane (< 1mm thick), polymer

Corobuff Roll, Three-dimensional Paper, P0011301

Unknown

Pacon Creative Products

Suitable

2019-07-05

MMA

Oddy test (method: 20190226_OT)

White and black

Three dimensional paper with black corrugation on one side, smooth and white on the opposite, 1/4" thick, 8"x8" sample; Product Number: P0011301; Chemical Components: Paper and recyclable substrate, glue (the Pacon website is vague on these materials); purchased September 2018

White and black

polymer, sheet (> 1mm thick)

Viton™ Tubing 5mm Id 10mm Od

Rainbow Rubber

Temporary

2019-01-11

MMA

Oddy test (method: 20180821_OT)

Black

Round black Viton™ gasket; model #1571806; black tubing, 5mm ID, 10mm OD; certified Viton rubber; purchased November 2018

Black

gasket, polymer

Heyco-molded™ Liquid Tight Break-thru Plugs; C2062-p, Ltbp 625-250 Black

Heyco

Unknown

Temporary

2018-08-01

MMA

Oddy test (method: 20180704_OT)

Black

Model/Catalog Number: part #: C2062-P; LTBP 625-250 black; Details: mounting hole diameter: 15.9 mm; cable diameter range: 3.3-9.5 mm; part no. C2062; A head diameter: 26.2 mm; Chemical Components: Nylon 6/6 and TPE; purchased June 2018

Black

block/bulk/pellet, polymer

#5 Mt Awg Jacketed Electric Cable; 28171a Multi-conductor 600v Type Tc-er Cable

Belden

Unknown

Temporary

2018-06-08

MMA

Oddy test (method: 20171116_OT)

Jacketed Wire: 2/0 AWG multi-conductor stranded (19 x 11) bare copper conductors, 6 AWG bare copper ground wire, PVC/nylon insulation, PVC jacket; received 2018

Black

composite, other

#1 Mt Air Conduit Tube; A8g16

Atag

Unknown

Temporary

2018-06-08

MMA

Oddy test (method: 20171116_OT)

Clear with an ivory spiral

Flexible tubing: ether based PU wall, food grade, with crushproof PVC helix; 1.1" diameter; received 2018

Clear with an ivory spiral

membrane (< 1mm thick), polymer

D-seal Gasket, Elastosil R 401/70

Wacker Silicones

Temporary

OK

rainbow tarnish, darkening

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #1

D-profile gasket; peroxide-cured high consistency silicone rubber (HCR) - Grey - Cut to weight

peroxide-cured high consistency silicone rubber (HCR)

Gray

gasket, polymer

Bubble-seal Gasket, Elastosil R 401/60

Wacker Silicones

Temporary

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #2

gasket; peroxide-cured high consistency silicone rubber (HCR) - Grey - Cut to weight

peroxide-cured high consistency silicone rubber (HCR)

Gray

gasket, polymer

Copper: red tarnish - Silver: ok - Lead: rainbow tarnish, darkening

D-seal Gasket, Elastosil R 401/70

Wacker Silicones

Temporary

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #3

D-profile gasket; peroxide-cured high consistency silicone rubber (HCR) - Black - Cut to weight

gasket, polymer

Copper: very slight red tarnish (light streaks) - Silver: ok - Lead: rainbow, darkening

Bubble-seal Gasket, Elastosil R 401/60

Wacker Silicones

Temporary

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #4

gasket; peroxide-cured high consistency silicone rubber (HCR) - Black - Cut to weight

gasket, polymer

Copper: red tarnish - Silver: ok - Lead: rainbow tarnish, darkening

Silifoam Seal, Adhesive Backed Ht603a

Newmet Silicones

Unsuitable

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #5

Rectangular profile silicone gasket with pressure-sensitive adhesive; low density, low compression set, fire retardant silicone foam - White - Cut, release paper removed

gasket, polymer

Copper: ok - Silver: ok,localized white spot - Lead: thick white and yellow compact corrosion,with fluffy spots

Interpon 610, Ral 7012

Interpon Powder Coatings

Temporary

OK

slight darkening

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #15

polyester-based powder coating on steel panel - Grey - Cut into small blocks using bandsaw

polyester-based powder coating on steel panel

Gray

board, plastic/polymeric/synthetic

Arreis Mdf With Dacrylate Clear Acrylic Emulsion Varnish Applied

Roseburg Forest Products, Dacrylate Paints

Unsuitable

red tarnish

ok

Thick yellow/white compact corrosion

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #16

Medium density fiberboard panel coated in Dacrylate Clear Acrylic Emulsion varnish (2-butoxyethanol) - Brown, Transparent - Cut into small blocks using bandsaw - cut edges are uncoated.

Medium density fiberboard panel coated in Dacrylate Clear Acrylic Emulsion varnish (2-butoxyethanol)

Brown, Transparent

board, plastic/polymeric/synthetic

Copper: red tarnish - Silver: ok - Lead: Thick yellow/white compact corrosion

Obomodulan 500

OBO-Werke

Mccausey Lumber

Suitable

OK

(better than control)

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #19

Rigid fine-cell polyurethane foam panel - Pink - Cut into small blocks using bandsaw

Pink

board, plastic/polymeric/synthetic

Alucore

3A Composites

Suitable

OK

very slight darkening (looks like control)

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #14

Aluminum honeycomb composite panel; core of AlMn alloys, cover sheets of corrosion-resistant Peraluman alloys (AlMg1/5005A) - Grey - Cut into small blocks using bandsaw

Aluminum honeycomb composite panel; core of AlMn alloys, cover sheets of corrosion-resistant Peraluman alloys (AlMg1/5005A)

Gray

board, plastic/polymeric/synthetic

Cor-x Polypropylene 4 Mm Corrugated Board

Primex Plastics

Temporary

2019-05-29

MMA

Oddy test (method: 20190226_OT), SPME GCMS

White

Corrugated polypropylene board; May 2018; 4 mm thickness. Purchased in May 2018. Reference Oddy 2199.

White

board, plastic/polymeric/synthetic

Masterpak B-flute 1/8 Inch Single Wall. Model #2-130, 2-131, 2-133

Masterpak

Unknown

Temporary

2019-05-29

MMA

Oddy test (method: 20190226_OT), SPME GCMS

Grey, white

Single-wall B Flute (1/8" thick). 100% bleached alpha cellulose. No recycled or wooden fibers. No optical brighteners. Kappa level: 1 - 2 = lignin-free (TAPPI T 23 om-99). pH cold extraction: 8.0 - 9.5 (TAPPI T 509 om-02). Alkaline reserve (buffered) >3% calcium carbonate. Adhesive: Potato starch, pH 7.0, moisture proof.

Grey, white

board, natural

Backer Rod, #860-1020

Unknown

University Products

Temporary

2019-05-29

MMA

Oddy test (method: 20190226_OT), SPME GCMS

White

1-Inch trapezoid backer rods, closed cell polyethylene foam. Purchased in January 2019.

White

foam, non-building insulation, polymer

Silicone Cabinet Gasket

Unknown

Delta Designs

Temporary

2019-05-23

MMA

Oddy test (method: 20190226_OT), SPME GCMS

Black

Cabinet gasket. Delta Designs. Month/Year Purchased: 2019. Silicone. 1cm diameter.

Black

gasket, polymer

Insite ® Acid Free Foamcore #136

The Gillman Brothers Company

The Gilman Brothers Company

Temporary

2019-05-23

MMA

Oddy test (method: 20190226_OT), SPME GCMS

White

Extruded polystyerene foamboard; acid free 100% High Alpha Cellulose paper faces; pH 7.5-9.5 buffered with 3-5% Calcium Carbonate. Standard thickness is 3/16″ and sizes range from 24″x 36″ to 48″x 96″. Month/Year Purchased: Unknown.

White

board, plastic/polymeric/synthetic

Insite ® Reveal® Colors

The Gillman Brothers Company

The Gilman Brothers Company

Temporary

2019-05-23

MMA

Oddy test (method: 20190226_OT), SPME GCMS

White

Paper faced foamboard. Acquired in 2018. GAUGES: Min: 1/8” Max: 1/2” SIZES: Min: 24″x 36″ Max: 60” x 192”. .

White

board, plastic/polymeric/synthetic

Binders Board

Unknown

Hollanders

Unsuitable

2019-03-26

MMA

Oddy test (method: 20190226_OT)

Grey

Binders Board; Purchased: Feb 2016

Gray

paper-based, sheet

Unbuffered Glassine Sheets, Uig810

Unknown

Gaylord Archival

Temporary

2019-03-26

MMA

Oddy test (method: 20190226_OT), SPME GCMS

White

Interleaving paper; Catalog Number: UIG810; Purchased: December 2018

White

paper-based, sheet

Davey Board Red Label #18

Unknown

Colophon Book Arts Supply

Unsuitable

2019-03-26

MMA

Oddy test (method: 20190226_OT)

Brown

Brown, 0.082" thick paper board; Catalog Number: Davey Board Red Label #18; Purchased: 12/2018

Brown

paper-based, sheet

Black Proof Box, 114-104

Unknown

Archival Methods

Unsuitable

2019-03-26

MMA

Oddy test (method: 20190226_OT)

Black

1/16" thick black colored cardboard; Catalog Number: 114-104; Purchased: December 2018

Black

paper-based, sheet

File Folder With Antimicrobial Product Protection, 10338

Smead

Amazon.com

Unsuitable

2019-03-26

MMA

Oddy test (method: 20190226_OT), SPME GCMS

Beige

Smead File Folder with Antimicrobial Product Protection, 1/3-Cut Tab, Letter Size, Manila, 100 per Box; Catalog Number: 10338; Month/Year Purchased: November 2018

Beige

paper-based, sheet

Permalife 20 Lb. Bond Paper, 132-a4

Unknown

Archival Methods

Suitable

2019-03-26

MMA

Oddy test (method: 20190226_OT), SPME GCMS

White

Weight: 20 Lb. or 75 gm2• pH 7.5-8.0 Acid-Free

White

paper-based, sheet

Cerex Spunbond Nylon, 23150/23200

Cerex Advanced Fabrics

Temporary

2019-03-14

MMA

Oddy test (method: 20190214_OT_a), SPME GCMS

White

"Gas bonded" continuous filament nylon fabric; white; Model/Catalog Number: 23150/23200 (same composition; last three numbers refer to thickness); Chemical Components: nylon 6,6 and nylon 6; Purchased: 01/2019

White

membrane (< 1mm thick), polymer

Item #a-pp2b, Polypropylene Pellets

Unknown

Fairfield Processing

Suitable

2019-02-27

MMA

Oddy test (method: 20180821_OT)

Colorless

Polypropylene pellets for pillow filling; colorless; Model/Catalog Number: Item #A-PP2B; Purchased: 10/18

Colorless

block/bulk/pellet, polymer

1/32" Fda Clear Silicone Sheet, Colorless

Unknown

Canal Rubber

Temporary

tarnish on the copper is very slight red tarnish boarding on Permanent

2019-02-27

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Colorless; tarnish on the copper is very slight red tarnish boarding on Permanent

1/32" Thick food safe silicone sheet; colorless; Purchased: January 2019 from Canal; washed with distilled water and wiped dry

Colorless

membrane (< 1mm thick), polymer

Extruded Ilpea Thermoplastic Elastomer (tpe)

Ilpea

Suitable

Haze on copper is due to copper not the gasket material

2019-02-27

MMA

Oddy test (method: 20180821_OT)

Colorless; Oddy results note: Haze on copper is due to copper not the gasket material

Ilpea TPE gasket; colorless; Model/Catalog Number: TPE-S Transparent Compound ShA 70; Purchased: 1/2019; Details: 1mm x 14 mm x 285 mm strips of TPE were extruded, stapled to printer paper, and shipped from Italy for testing. Extrusion details unknown. Shore A 70 durometer; Chemical Components: Material is Teknor's Medalis(r) MD-53273.

Colorless

gasket, polymer

Hp-pbn7 Metalized Barrier Film

Unknown

Heritage Packaging

Temporary

2019-02-27

MMA

Oddy test (method: 20190130_OT ), SPME GCMS

Silver

Heat Sealable barrier film; Details: heat sealable barrier film silver on outside, grey inside. 48ga. PET/Ink/Adhesive/35ga./Foil/Adhesive/60ga. oriented nylon/Adhesive/5.0mil Sealant; Chemical Components: PET, unknown adhesive, metal foil, and nylon; Purchased: 4/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested.

Silver

membrane (< 1mm thick), polymer

S411757 Or Nfe-016 Metalized Barrier Film

Unknown

Heritage Packaging

Temporary

2019-02-27

MMA

Oddy test (method: 20190130_OT ), SPME GCMS

Heat Sealable Barrier film; Details: metallized barrier film, silver on outside: 15 um BON/16g LDPE Coextrusion/9 um Aluminum foil/16g LDPE coextrusion/76 um LLDPE; purchased 11/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested.

LDPE Coextrusion/9 um Aluminum foil/16g LDPE coextrusion/76 um LLDPE

Silver

membrane (< 1mm thick), polymer

Cad Pak N (cpn) Barier Film

Unknown

Protective Packaging

Temporary

2019-02-27

MMA

Oddy test (method: 20190130_OT ), SPME GCMS

Heat Sealable Barrier film; Details: metallized barrier film, silver on outside: Nylon/polyethylene/aluminum foil/polyethylene. adheres to MIL-PRF-131K Type I Class I; Chemical Components: nylon, polyethylene, aluminum; purchased 10/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested.

Nylon/polyethylene/aluminum foil/polyethylene

Silver

membrane (< 1mm thick), polymer

Marvelseal 470, Mfs470 Metalized Barrier Film

Unknown

Protective Packaging

Temporary

2019-02-27

MMA

Oddy test (method: 20190130_OT ), SPME GCMS

Heat Sealable Barrier film; Details: metalized barrier film, silver with red lettering on outside, grey on inside: Oriented Polypropylene (0.9 mil) / polyethylene (0.65 mil) / Aluminum foil (0.000285 mil) / linear low-density polyethylene (2.9 mil); Chemical Components: polyethylene, aluminum; purchased 10/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested.

Oriented Polypropylene (0.9 mil) / polyethylene (0.65 mil) / Aluminum foil (0.000285 mil) / linear low-density polyethylene (2.9 mil); Chemical Components: polyethylene, aluminum;

Silver, and Red

membrane (< 1mm thick), polymer

Peterboro Museum Board Traditional White, M902-4

Peterboro

Talas

Unsuitable

2019-02-13

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Off-white, traditional white

Museum board; off-white; thickness 4-ply; 100% cotton; Purchased: 09/2018

Off-white, traditional white

board, natural

Peterboro Museum Board Warm White, M901-4

Peterboro

Talas

Unsuitable

2019-02-13

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Off-white, warm white

Museum board; off-white; thickness: 4-ply; 100% cotton; Purchased: 09/2018

Off-white, warm white

board, natural

Peterboro Museum Board Black, M905-4

Peterboro

Talas

Temporary

2019-02-13

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Black

Museum Board; thickness: 4-ply; black; 100% cotton; Purchased: 09/2018

Black

board, natural

Polyurethane Flexible Foam Wedges

Soundassured

Butera Brands

Temporary

2019-02-13

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Black

Acoustic foam wedges; black flexible solid foam with cellular structure; 3" base; Chemical Components:polyether and polyester based urethane polymers; purchased 12/2018

Black

foam, non-building insulation, polymer

Marvelseal 360; Film Foil Mil Prf-131-k Cl1 Type I

Midsouth Packaging

Edcosupply.Com

Temporary

2018-12-31

MMA

Oddy test (method: 20180305_OT)

Silver

Barrier film; Details: heat sealable barrier film, silver with writing on outside and grey on inside: biaxially oriented nylon (0.6mil) / polyethylene (1.4mil) / aluminum foil (0.0003mil) / polyethylene (1.2mil) / linear LDPE(1.5mil); Chemical Components: nylon, polyethylene, and aluminum; Purchased: 4/2018. TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested.

Silver

membrane (< 1mm thick), polymer

Cadpak Hd100, Mil-prf-131k Class1 Barrier Film

Unknown

Heritage Packaging

Temporary

2018-12-31

MMA

Oddy test (method: 20180305_OT)

Silver

Barrier film; Details: heavy duty heat sealable barrier film. silver with writing on outside and green on inside: 60ga biax nylon / 15# LDPE / 30ga foil / 6 mil Polyethylene co-extruded with heavy-duty green Sealant; Chemical Components: nylon, metal foil, polythylene; Purchased: 4/2018. TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested.

Silver

membrane (< 1mm thick), polymer

Cadpak Hd200, Qpl Mil-prf-131k Barrier Film

Unknown

Heritage Packaging

Temporary

2018-12-31

MMA

Oddy test (method: 20180305_OT)

White

Barrier film; Details: super heavy duty heat sealable barrier film. silver with writing on outside and green on inside: Biax Nylon/PE/Cross-Lam PE/PE/Foil/Heavy Duty Coextrusion; Chemical Components: nylon, polyethylene, metal foil; purchase date unknown. TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested.

White

membrane (< 1mm thick), polymer

Food-grade High-temperature Silicone Rubber Sheet, Catalog # 5827t21

J. A. Bar

Mcmaster-Carr

Temporary

2018-12-19

MMA

Oddy test (method: 20180821_OT)

Colorless

Colorless silicone rubber sheet; 1/32" thickness; purchased 11/2018; Temperature Range: -80° to 400° F Tensile Strength: 1,000 psi; 50A durometer

Colorless

polymer, sheet (> 1mm thick)

Kobracast Art

Worbla

Cosplaysupplies.Com

Temporary

2019-01-31

Penn

A-D Strips, Oddy test

Open-weave polyester with a thermoplastic backing

Polyester with thermoplastic backing

polymer, sheet (>1mm thick)

Copper: slight reddening, yellowing, or rainbow-like color change,Formation of up to 20 black spots (Temporary) Silver: similar to control,slight yellowing, purpling, or darkening. (Temporary) Lead: darkening,spots of corrosion where in direct contact with sample material (Temporary)

Finest Art

Worbla

Cosplaysupplies.Com

Unsuitable

2019-01-31

Penn

A-D Strips, Oddy test

Thermoplastic resin and wood flour filler

polymer, sheet (>1mm thick)

Copper: slight reddening, yellowing, or rainbow-like color change (Temporary) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: significant darkening and purple, red, green discoloration,coupon eaten away where in direct contact with sample material. (Fail),white fluffy crystal formation

Mesh Art

Worbla

Cosplaysupplies.Com

Unsuitable

2019-01-31

Penn

A-D Strips, Oddy test

Thermoplastic resin and filler partially made from recycled rice husks

polymer, sheet (>1mm thick)

Copper: slight reddening, yellowing, or rainbow-like color change (Temporary) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: yellow/olive tarnish (Temporary),white fluffy crystal formation. (Fail)

Transpart

Worbla

Cosplaysupplies.Com

Suitable

2019-01-31

Penn

A-D Strips, Oddy test

Transparent polymer thermoplastic, ionomer resin

polymer, sheet (>1mm thick)

Coupons look similar to the controls. (Pass/Permanent)

Wonderflex

Wonderflex World

Cosplaysupplies.Com

Unsuitable

2019-01-31

Penn

A-D Strips, Oddy test

Thermoplastic film, with a layer of polyester open weave scrim

polymer, sheet (>1mm thick)

Copper: slight reddening, yellowing, or rainbow-like color change,Formation of up to 20 black spots (Temporary) Silver: Coupons look similar to the controls. (Pass/Permanent) Lead: heavy, overall white fluffy crystal formation,coupon eaten away where in contact with sample material (Fail)

Varaform

Cosplaysupplies.Com

Unsuitable

2019-01-31

Penn

A-D Strips, Oddy test

Natural cotton fabric impregnated by a thermoplastic polymer

Natural

polymer, sheet (>1mm thick)

Copper: Inconsistent,coupon eaten away where in contact with sample material (Fail),reddening, yellowing, or darkening (Fail) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: heavy, overall white fluffy crystal formation

Polly Plastics Moldable Plastic Pellets

Polly Plastics

Amazon.com

Unsuitable

2019-01-31

Penn

A-D Strips, Oddy test

polycaprolactone pellets

pellet, polymer

Copper: severe blackening (Fail) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: heavy, overall white fluffy crystal formation,coupon eaten away where in contact with sample material (Fail)

Instamorph

Amazon.com

Unsuitable

2019-03-30

Penn

A-D Strips, Oddy test

polycaprolactone pellets

pellet, polymer

Copper: severe blackening,coupon eaten away where in contact with sample material (Fail),more alteration where in contact with sample material (Fail) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: heavy, overall white fluffy crystal formation

Bon 100 Clear

Cadillac Products Packaging Company

Heritage Packaging

Unsuitable

2018-05-23

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Heat sealable thin flexible transparent film; Biaxially oriented nylon/PE/EVOH/coextrusion; barrier material; nylon, polyethylene, ethylene vinyl alcohol; Quasi -repeat of Oddy 2084, where only the interior component was oddy tested (coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material); FOR THIS TEST, the material in its totality was cut into pieces and placed in the Oddy jars; sample provided 8/20/2017 - barrier film

nylon, polyethylene, ethylene vinyl alcohol

Clear

membrane (< 1mm thick), polymer

48 Ga Alox Pet/adhesive/2.5 Mil Lldpe

Unknown

Heritage Packaging

Temporary

2018-05-23

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Heat sealable ~0.1 mm thick barrier film; transparent, flexible, heat-sealable film with medium water and oxygen transmission rates (0.13 g/100 in^2/day and 0.13 cc/100 in^2/day; quasi-repeat of Oddy 2087, where coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material; FOR THIS TES, the material was cut into pieces and placed into the oddy test jars; Supplier: Heritage Packaging, Victor NY; purchased 8/2017 - barrier film

Clear

membrane (< 1mm thick), polymer

Bon 100 Clear

Cadillac Products Packaging Company

Heritage Packaging

Unsuitable

2018-05-23

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Heat sealable thin flexible transparent film; Biaxially oriented nylon/PE/EVOH/coextrusion; barrier material; nylon, polyethylene, ethylene vinyl alcohol; Quasi -repeat of Oddy 2084, where only the interior component was oddy tested (coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material); FOR THIS TEST, the material in its totality was cut into pieces and placed in the Oddy jars; sample provided 8/20/2017 - barrier film

nylon, polyethylene, ethylene vinyl alcohol

Clear

membrane (< 1mm thick), polymer

48 Ga Alox Pet/adhesive/2.5 Mil Lldpe

Unknown

Heritage Packaging

Temporary

2018-05-23

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Heat sealable ~0.1 mm thick barrier film; transparent, flexible, heat-sealable film with medium water and oxygen transmission rates (0.13 g/100 in^2/day and 0.13 cc/100 in^2/day; quasi-repeat of Oddy 2087, where coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material; FOR THIS TES, the material was cut into pieces and placed into the oddy test jars; Supplier: Heritage Packaging, Victor NY; purchased 8/2017 - barrier film

Clear

membrane (< 1mm thick), polymer

All Purpose Joint Compound (spackle)

Usg, Sheetrock Brand

Unknown

Unsuitable

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Drywall joint compound: premixed with water, 4.5 gallons (17 L) purchased (green label on container), which finishes 450 ft2 (42m2)of drywall. Allow 1/16” thick film to dry 24 hours; Chemical Components: Limestone, water, (may contain talc), ethylene vinyl acetate polymer, polyvinyl acetate, and may contain perlite. Contains 1.7 g/L of VOC. Received Spring 2018.

Chemical Components: Limestone, water, (may contain talc), ethylene vinyl acetate polymer, polyvinyl acetate, and may contain perlite

inorganic filler, other

Self-adhesive Drywall Joint Mesh, Fiflexmesh Fm2300

Fiflexmesh

Jaydee Group

Unsuitable

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Self-adhesive drywall joint mesh: 1-7/8” x 300’ roll; Chemical Components: Fiberglass and unknown adhesive. no SDS or chemical info available; unknown purchase date.

Fiberglass and unknown adhesive

other, polymer

Paper Drywall Joint Tape, 2 1/16" Paper Joint Tape

Proform Finishing Products

Unknown

Temporary

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Paper drywall joint tape, purchased sometime between 1/2018-5/2018; Details: 2 1/6” wide by 500’; Chemical Components: Paper, no other details available. Unknown purchase date.

Paper, no other details available

paper-based, sheet

Invision Transit Carpet Tile (style 7029)

Unknown

J & J Flooring

Temporary

2018-07-17

MMA

Oddy test (method: 20171106_OT), SPME GCMS

Carpet tile; Details: Closed loop, solution dyed, Encore(r) SD Ultima Nylon fiber with Nexus(r) Modulus PVC backing. Fiber and Backing include 49% recycled material in unknown ratio. Fibers heat treated with ProTex(r) fluorochemical anti-soiling treatment. Heat used to bond the fluorochemical to the fiber; Chemical Components: Nylon, PVC, Fluorochemical; purchased 6/2018

Nylon fiber with PVC backing

carpet, synthetic/plastic/polymeric

Self Adhesive Natural Cork, 04f-c6421-06

Con-tact Brand

Kittrich Corporation

Unsuitable

2018-08-01

MMA

Oddy test (method: 20180704_OT), SPME GCMS

Cork roll with self-adhesive; natural lignocellulosic plant material, unknown adhesive; Purchased: 2017

natural lignocellulosic plant material, unknown adhesive

Natural

natural, other

Natural Cork Roll, Upc 034138103005

Quartet

Acco Brands

Unsuitable

2018-08-01

MMA

Oddy test (method: 20180704_OT), SPME GCMS

Natural cork roll (no adhesive); 2mm thickness x 2.23 cm wide; Material Class: natural lignocellulosic plant material; Purchased: February 2018

Natural

natural, other

Tyvek® Envelopes With 2" Gusset & 4" Flap (50-pack), #3970

DuPont

Gaylord Archival

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Tyvek envelopes; Part# 3970; Chemical Components: Polyethylene; Tyvek antistatic coating; Purchased: July 2018

Polyethylene; Tyvek antistatic coating

White

membrane (< 1mm thick), polymer

Overspray Protective Sheeting, 3M No. 06728

3M

Zoro.Com

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Overspray protective sheeting; Details: Paintable, high-density, tear-resistant, translucent film designed for use in automotive painting industry for edge masking; Chemical Components: High Density Polyethylene film; Purchased: 1/2018

High Density Polyethylene film

Clear

membrane (< 1mm thick), polymer

Pro-form Splint Material, 9615000

Keystone Industries

Temporary

2018-09-27

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Transparent Pro-form formed plastic; thickness: 0.020" (0.5 mm); co-polyester; purchased August 2018; formed one week prior to testing

co-polyester

Transparent

block/bulk/pellet, polymer

Pvc Crystal Clear Glossy Binding Covers

Oregon Laminations Company

Temporary

2018-09-27

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Formable polyvinylchloride plastic; purchased August 2018; formed 1 week before testing

Formable polyvinylchloride plastic

block/bulk/pellet, polymer

Soft Eva .040 (1mm), #9596980

Proform Finishing Products

Keystone Industries

Temporary

2018-09-27

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Pro-form formable plastic; Ethyl vinyl acetate; thickness: 0.040" (1mm); August 2018; formed 2 days before testing; there is some residual plaster from the mould on the plastic (test with plaster side down)

Ethyl vinyl acetate

block/bulk/pellet, polymer

Sorbothane 0212012-40-10

Sorbothane

Unknown

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Flexible polymeric sheet; 40 durometer sheet, 12" x 12" x 1/8"; purchased more than 2 years ago

polymer, sheet (> 1mm thick)

And/or Rubber Cork; Skylight Ad1007

Capri Collections

Temporary

2018-11-28

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Cork & rubber flooring; white rubber & natural cork flecks; Purchased: September 2018

rubber & natural cork flecks

White and Natural

polymer, sheet (> 1mm thick)

And/or Rubber Cork; Gold Ad2004

Capri Collections

Unsuitable

2018-11-28

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Cork & rubber flooring; yellow & natural cork flecks; Purchased: September 2018

Cork & rubber

Yellow and Natural

polymer, sheet (> 1mm thick)

Rubber Cork Hybrid; Zonkey

Siena Usa

Unsuitable

2018-11-28

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Grey rubber & cork flooring; purchased september 2018

Gray

polymer, sheet (> 1mm thick)

Norseal Sponge Silicone Rubber, R10470

Saint-gobain

Stockwell Elastomerics

Temporary

2018-12-19

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Silicone Sheet of textured black foamed silicone 0.032 or 1/32 inch thick; purchased ~2015

Silicone

Black

polymer, sheet (> 1mm thick)

Norseal Sponge Silicone Rubber, 0.032 R10470m Sil Sponge Plain

Saint-gobain

Stockwell Elastomerics

Temporary

2018-12-19

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Sheet of textured orange foamed silicone 1/32 inch thick; Chemical Components: silicone; purchased 10/2018

foamed silicone

Orange

polymer, sheet (> 1mm thick)

Norseal Sponge Silicone Rubber, 0.062 R10470m Sil Sponge Plain

Saint-gobain

Stockwell Elastomerics

Temporary

2018-12-19

MMA

Oddy test (method: 20180821_B_OT ), SPME GCMS

Sheet of textured orange foamed silicone 1/16 inch thick; Chemical Components: silicone; purchased 10/2018

foamed silicone

Orange

polymer, sheet (> 1mm thick)

File:2348 GA.jpg

Clear Acrylic Emulsion Varnish

Dacrylate

Temporary

2019-01-11

MMA

Oddy test (method: 20181031_OT), SPME GCMS

Emulsion varnish; cured 2 weeks before testing; batch # 6801210318; date of manufacture: March 16, 2018

Emulsion varnish

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Expanded Polyethylene Foam; 1.3 Lb/ft^3; Epe 1.3#

New England Foam

Unknown

Temporary

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Expanded polyethylene foam; produced as bun; Chemical Components: polyethylene. Others unknown; PURCHASED 11/2017

polyethylene

foam, non-building insulation, polymer

Plastazote Ld33

Ufp Technologies

Zotefoams

Temporary

2018-01-10

MMA

Oddy test (method: 20171116_OT), SPME GCMS

White closed cell crosslinked PE foam; purchased 3/2017

White

foam, non-building insulation, polymer

Azote Evazote 30

Ufp Technologies

Zotefoams

Temporary

2018-01-10

MMA

Oddy test (method: 20171116_OT), SPME GCMS

White foam; purchased 3/2017

White

foam, non-building insulation, polymer

Cabinet Gasket Material; Black

Unknown

Delta Designs

Suitable

2018-02-16

MMA

Oddy test (method: 20171116_OT), SPME GCMS

From Delta case manufacturers; Gasket manufactured by Delta; unknown material type

gasket, polymer

Silicone (vmq) Black Gasket

Bsp Silikon Profile

Unknown

Temporary

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Black silicone gasket; SIPRO; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Ω profile with a 7mm wide base and 5mm diameter circle

Black

gasket, polymer

Silicone (vmq) Geometrical Shaped White Gasket

Bsp Silikon Profile

Unknown

Unsuitable

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

White silicone gasket; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Ω profile with a 7mm wide base and 5mm diameter circle

White

gasket, polymer

Silicone Sipro Black Gasket

Bsp Silikon Profile

Unknown

Temporary

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Artificially aged black silicone gasket; baked at 80°C for 8 hours; 5mm diameter; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Received April 2018; Ω profile with a 7mm wide base and 5mm diameter circle

Cured compound of polysiliaxanes and pyrogenic silica

Black

gasket, polymer

Silicone (vmq) White Gasket

Bsp Silikon Profile

Unknown

Unsuitable

2018-05-31

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Artificially aged white silicone gasket; sample was baked at 80°C for 8 hours; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Received April 2018; Ω profile with a 7mm wide base and 5mm diameter circle

Cured compound of polysiliaxanes and pyrogenic silica

White

gasket, polymer

Expanded White Silicone Tubular Gasket, 411/plt

Technical Rubber s.r.l.

Technical Rubber Srl

Temporary

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

Foamed round gasket; expanded white silicone tubular gasket. 10 mm O.D., 3 mm I.D.; Purchased: 7/2018

silicone

White

gasket, polymer

Expanded Black Viton-like Tubular Gasket, Fkm17514/esp

Technical Rubber s.r.l.

Technical Rubber Srl

Temporary

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

Expanded black viton-like tubular gasket. 7 mm O.D., 2 mm I.D. Purchased: 7/2018

Black

gasket, polymer

Heatlok Xt Insulating Expanding Foam

Airseal Insulation Systems

Demilec

Unsuitable

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

3" thick expanded green urethane foam; sample taken from center of cured block; Month/Year Purchased: 7/2018; Sample sprayed onto cardboard July 19th 2018;Chemical Components: Polyurethane

Polyurethane

Green

building insulation, foam, polymer

Viton™ O-rings

Unknown

Ace Glass

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Viton™ o-rings; comprised of linear co-polymer of vinylidine fluoride and hexafluoropropylene, florine content is between 66 and 70%; Production reference: Z156485- Batch 3110; dimensions: OD: 0.58", ID: 0.38", width: 0.1"; Purchased: August 2018

linear co-polymer of vinylidine fluoride and hexafluoropropylene, florine content is between 66 and 70%

gasket, polymer

Extruded Polystyrene Blue Board

Dow Corning

LeNoble Lumber

Temporary

2018-10-25

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Extruded polystyrene; 1" thick board; blue; R value = 5; material to be used for crate and box insulation; possible direct contact with larger objects; purchased September 2018

Extruded polystyrene

Blue

building insulation, foam, polymer

White Celtec® Expanded Pvc

Vycom

Unsuitable

2018-12-19

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Expanded PVC board, white, thickness: 12 mm thick; this is a repeat of Oddy 2301; Month/Year Purchased: 6/2018, tested after sitting in open air for ~5 months before testing

Expanded PVC board

White

board, plastic/polymeric/synthetic

Sintra™ 6 Mm White Pvc Board

3A Composites

Temporary

2018-12-19

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Expanded PVC board; white; thickness 6 mm; purchased 11/2017

Expanded PVC

White

board, plastic/polymeric/synthetic

Museum Board Black

Legion Paper

Talas

Temporary

2019-01-11

MMA

Oddy test (method: 20181031_OT), SPME GCMS

100% cotton mat board; black; thickness 4-ply; purchased 9/2018; catalog #R45-405820

100% cotton

board, natural

Museum Board Antique

Legion Paper

Talas

Temporary

2019-01-11

MMA

Oddy test (method: 20181031_OT), SPME GCMS

100% cotton mat board; off-white; thickness 4-ply; purchased 9/2018; catalog #R45-405602

100% cotton

Off-White

board, natural

No

Control coupon · [[media:|GCMS]]

Museum Board Warm White

Legion Paper

Talas

Temporary

2019-01-11

MMA

Oddy test (method: 20181031_OT), SPME GCMS

100% cotton mat board; off-white; thickness 4-ply; purchased 9/2018; catalog #R45-402447

100% cotton

Off-White

board, natural

Photomount Mat Board

Legion Paper

Talas

Temporary

2019-01-11

MMA

Oddy test (method: 20181031_OT), SPME GCMS

100% cotton mat board; white; thickness 4-ply; purchased 9/2018; catalog #R45-RPHO4WH3240

100% cotton

White

board, natural

White Natural Versatile Plastic, Laser Sintered Nylon, Printed As Custom #3631036

Shapeways

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Test of Shapeways nylon (white natural versatile plastic) Total weight of nylon in bottom of jar + nylon coupon holders is 2g.

White

block/bulk/pellet, polymer

3d Printed Nylforce Glass Fiber

Unknown

Printed Solid

Temporary

2018-05-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Printed at 245°C; nylon and glass filled; required corrosion resistant print head; purchased 3/2018

nylon and glass

block/bulk/pellet, polymer

3d Printed Primalloy 99026 Or 55500

Verbatim (possibly)

Verbatim

Temporary

2018-05-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed plastic; printed at 215°C; polyester based thermoplastic elastomer; recommended for use with direct drive extruder models; use < 30 mm/sec. Turn retraction off; purchased 02/2018;

polyester based thermoplastic elastomer

block/bulk/pellet, polymer

3d Printed Pet

Verbatim

Temporary

2018-04-13

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed plastic; Printed at 215C; catalog #55751; polyethylene terephthalate; hygroscopic so drying filament could be useful to avoid water bubbles in the print; purchased 02/2018

polyethylene terephthalate

block/bulk/pellet, polymer

3d Printed Polypropylene; 0555951-812

Verbatim

Suitable

2018-04-13

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed plastic; verbatim polypropylene 0555951-812; Printed at 205C; polypropylene purchased 02/2018; "material by nature is non-polar; use packing tape with PP or double sided adhesive on print bed" - per Verbatim

verbatim polypropylene 0555951-812

block/bulk/pellet, polymer

3d Printed Colorfabb Ht Clear

Eastman Chemical

Printed Solid

Temporary

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed plastic; print T 250-280C; extruded at 250C; build plate temp 100-110C; Tg = 100C; clear; Chemical Components: Eastman Amphora 3D(TM) Co-polyester; purchased 11/2017

Eastman Amphora 3D(TM) Co-polyester

Clear

block/bulk/pellet, polymer

3d Printed Cpe+ Material, Transparent

Ultimaker

Printed Solid

Temporary

2018-03-26

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed plastic; printed filament same day as test; details: 2.85mm diameter; print temp 250 degrees C; plate temp 107 C; flow of 101; speed 45 mm/sec; fan at 5%; no brim or support; supplier: printedsolid.com; purchased 9/2017

block/bulk/pellet, polymer

3d Printed Nylon, Material 1785

Ultimaker

Printed Solid

Temporary

2017-09-25

MMA

Oddy test (method: 20170918_OT), SPME GCMS

3D printed plastic; polypropylene printed with glue for adhesion to plate 2 days before testing; Details: 2.85mm diameter, print temp: 220-240 degrees C; Month/Year Purchased: Sept. 2017

polypropylene printed with glue

block/bulk/pellet, polymer

3d Printed Transparent Nylon, Material 1647

Ultimaker

Printed Solid

Suitable

2017-09-13

MMA

Oddy test (method: 20170918_OT), SPME GCMS

Note: Caprolactam (an amide) was identified as a VOC for this material using SPME-GCMS at 60 degrees C, though it does not appear to adversly affect the metals in the Oddy test.

3D printed plastic; printed WITHOUT platform adhesive; printed 1 day before testing; 120% speed; 2.85mm diameter; 215° C print temp.; month/year purchased: sept. 2017

block/bulk/pellet, polymer

File:1845 Si.jpg

3d Printed Transparent Nylon, Material 1647

Ultimaker

Printed Solid

Suitable

2017-09-13

MMA

Oddy test (method: 20170918_OT), SPME GCMS

Note: Caprolactam (an amide) was identified as a VOC for this material using SPME-GCMS at 60 degrees C, though it does not appear to adversly affect the metals in the Oddy test.

3D printed plastic; printed WITH platform adhesive; printed 4 days before testing; Details: 2.85mm diameter, print temp: 240-260 degrees C; month/year purchased: sept. 2017

block/bulk/pellet, polymer

Volara 040a 0250wh

Sekisui Voltek

Unsuitable

2018-01-10

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Volara type A foam; white; 4 pcf density; 0.25" thick; cross-linked polyolefin foam; purchased 11/2017

cross-linked polyolefin foam

White

foam, non-building insulation, polymer

Ethafoam Cellu-cushion; Product 120

Sealed Air

Temporary

2018-01-10

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Roll-form polyethylene foam, non-cross-linked; white; purchased 11/2017

foam, non-building insulation, polymer

Ethafoam Synergy; Product 1000

Sealed Air

Temporary

2018-01-10

MMA

Oddy test (method: 20171116_OT), SPME GCMS

2" thickness foam block; polyethylene foam; white; purchased 11/2017

foam, non-building insulation, polymer

Biodegradable Packing Peanuts; Catalog # S-156;

Unknown

Uline

Temporary

2018-05-15

MMA

Oddy test (method: 20171116_OT), SPME GCMS

White cylindrical packing peanuts; foamed cylinder; ~0.5x2 inches; made of starch; decomposes in water; purchased 3/2018.

White

foam, non-building insulation, polymer

Cellulose Wadding; S-656

Unknown

Uline

Unsuitable

2018-05-15

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Dimpled paper wadding; Made of recycled materials; kraft pulp; purchased 3/2018.

alumina), filled (eg.: silica gel, paper-based, zeolites

Komatex® 2210

Kömmerling

Unsuitable

2018-08-03

MMA

Oddy test (method: 20180704_OT), SPME GCMS

White matte board, 10 mm thickness; Chemical Components: PVC, limestone, titanium dioxide, Paraffin waxes, and Hydrocarbon waxes; Month/Year Purchased: 6/2018.

White

board, plastic/polymeric/synthetic

Hdpe Sheet 12" X 12" X 1/8"; #8619k441

King Plastic

Mcmaster-Carr

Suitable

2018-08-27

MMA

Oddy test (method: 20180704_OT), SPME GCMS

1/8" thick HDPE plastic sheet; white; high density polyethylene; durometer 60D; density 0.034 lbs./cu. in.; purchased 5/2018

board, plastic/polymeric/synthetic

Round Backer Rod

Alcot Plastics

Weatherall Company

Temporary

2018-08-27

MMA

Oddy test (method: 20180614_OT), SPME GCMS

Grey foamed polyethylene round backer rod; diameter 5/8"; Chemical Components: closed cell polyethylene, residual blowing agent: isobutane; Purchased: 5/2018

Gray

foam, non-building insulation, polymer

Armaform® Pet Gr 150

Armacell Canada

Armacell

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Foamed PET board; density 150 kg/m^3; Chemical Components: 100% post-consumer polyethylene terephthalate; Purchased 7/2018

board, plastic/polymeric/synthetic

Alpharag Artcare Museum, M8634

Nielsen Bainbridge

Unknown

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

white alpharag board; Supplier: purchased April 2018; thickness: 1.5 mm; Chemical Components: 100% cotton, zeolites, buffering agents (calcium carbonate)

White

board, natural

Alpharag Artcare Museum, M8644

Nielsen Bainbridge

Unknown

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

black alpharag board; Purchased: April 2018; ; thickness: 1.5 mm; Chemical Components: 100% cotton, zeolites, buffering agents (calcium carbonate)

Black

board, natural

Alpharag Artcare Museum, M8667

Nielsen Bainbridge

Unknown

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Natural alpharag board; Month/Year Purchased: April 2018; Details: thickness: 1.5 mm; Chemical Components: 100% cotton, zeolites, buffering agents (calcium carbonate)

board, natural

27310810 Oa 3Mm (optium Acrylic®)

Tru Vue

Temporary

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Acrylic plexi glass with optical coating; Abrasion resistant, anti-static, anti-reflective, 3mm thick acrylic sheet, washed with 1% Micro 90 and rinsed with 18.2 MOhm water prior to testing; filters 98% UV Rays; Chemical Components: acrylic & optical coatings; purchased 5/2018; From manufacturer: For removal of all traces of P-tape residue: Mix a couple drops of dish detergent with distilled water. Use on micro-fiber cloth to clean surface of glazing. Sourced from https://tru-vue.com/solution/optium-acrylic

board, plastic/polymeric/synthetic

Celtec® Expanded Pvc

Vycom

Unsuitable

2018-09-27

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Expanded PVC board, white, thickness: 12 mm thick; Month/Year Purchased: 6/2018

board, plastic/polymeric/synthetic

Dibond® 483Mdbww

3A Composites

Harbor Sales

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Aluminum composite sheet; white paint over aluminum with polyethylene core; 2 mm thickness; purchased 8/2018

board, plastic/polymeric/synthetic

0.031" Black Silicone Rubber Sheeting

Acme Rubber

Suitable

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

thin silicone rubber sheet; durometer: 20; thickness: 0.031"; manufacturer can dye-cut this sheeting if they are supplied drawings. However, their extruded silicone is a different compound and should not be confused with their sheeting; purchased August 2018

membrane (< 1mm thick), polymer

0.020" Black Silicone Rubber Sheeting

Acme Rubber

Suitable

2018-09-18

MMA

Oddy test (method: 20180821_OT), SPME GCMS

thin silicone rubber sheet; durometer: 20; thickness: 0.020"; manufacturer can dye-cut this sheeting if they are supplied drawings. However, their extruded silicone is a different compound and should not be confused with the sheeting; purchased August 2018

membrane (< 1mm thick), polymer

Komacel

Kömmerling

Suitable

2018-08-03

MMA

Oddy test (method: 20180704_OT), SPME GCMS

white PVC sheet/board; Details: white glossy, 10 mm thickness; Chemical Components: PVC, limestone, titanium dioxide. Month/Year Purchased: June/2018

White

board, plastic/polymeric/synthetic

Perma/cor E-flute Corrugated Board; 612-0810e

Unknown

University Products

Suitable

2018-05-31

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Blue/gray corrugated board; Thickness: .0625; Acid-free, lignin-free, and buffered with 3% calcium carbonate; purchased April 2018

Blue/Gray

paper-based, sheet

3d Printed Pp; 0555951-812

Verbatim

Suitable

2018-04-13

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D Printed polypropylene; printed at 205C; used U-line brown S-118 packing tape with PP carrier on print bed for adhesion; 2.85 diameter filament, opaque; purchased 02/2018

block/bulk/pellet, polymer

Colorfabb Xt Clear

Eastman Chemical

Printed Solid

Suitable

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Eastman Amphora 3D amorphous copolyester; extruded at 250C; Details: print temperature 230-260C, 2.85mm diameter filament, transparent, Tg is 75C.; purchased 11/2017

block/bulk/pellet, polymer

Colorfabb Ngen Clear

Eastman Chemical

Printed Solid

Suitable

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed copolyester; transparent; unknown extrusion temperature; Details: print temperature 220-240C, advised heat bed temp 60-80C, 2.85mm diameter filament; Purchased 11/2017

block/bulk/pellet, polymer

3d Printed Nylon Filament, Bridge Nylon - Natural

Taulman Bridge

Printed Solid

Suitable

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed nylon; extruded at 245-250C; Details: print temperature 250-255C, 2.85mm diameter filament, transparent; nylon; purchased 02/2018

block/bulk/pellet, polymer

Expanded Polyethylene (epe) Foam; 1.9 Lb/ft^3; Epe 1.9#

Unknown

New England Foam

Suitable

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Expanded polyethylene foam (EPE); white; produced as bun; purchased 11/2017

foam, non-building insulation, polymer

3d Printed Copolyester Plus (cpe+), Ultimaker Material 9725

Ultimaker

Printed Solid

Suitable

2017-12-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed copolyester; printed 11/14/2017; Details: 2.85mm diameter, print temp: 250 degrees C; Purchased Sept. 2017

block/bulk/pellet, polymer

10344-2130 Drawing Paper

Strathmore Artagain

Dick Blick

Suitable

2017-10-16

MMA

Oddy test (method: 20170918_OT), SPME GCMS

Drawing paper; coal black; acid free; 30% post consumer material; catalog# 10344-2130; Coal Black, 19"x15”, 160gsm; Purchased: 08/2017

paper-based, sheet

Tpb052016 Endleaf Bugra Paper

Hahnemuhle

Talas

Suitable

2017-10-16

MMA

Oddy test (method: 20170918_OT), SPME GCMS

antique endleaf Bugra paper; #313 black; 33" x 41"; 130 gsm; 100% alpha cellulose; acid free and age resistant; purchased aug. 2017

paper-based, sheet

Tpb007014 Antique Endleaf Ppaer

Talas

Suitable

2017-10-16

MMA

Oddy test (method: 20170918_OT), SPME GCMS

Antique endleaf paper; black, acid free and lignin free with a minimum of 2% alkaline reserve; purchased: august 2017

paper-based, sheet

Mylar Film Rolls

Unknown

Talas

Suitable

2017-09-20

MMA

Oddy test (method: 20170913_OT), SPME GCMS

Archival Mylar polyester film; transparent; thickness: 0.5 mm; unknown purchase date

membrane (< 1mm thick), polymer

Thermoplastic Vinyl Traditional Wall Base/trim

Johnsonite

Suitable

2017-03-23

MMA

Oddy test (method: 20170223_OT), SPME GCMS

wall base/trim in snow white; dimensions: 3mm thick x ~100mm tall; chemical components: PVC, and other proprietary ingredients; purchased 2017

polymer, sheet (> 1mm thick)

Renshape 460 Foamed Medium-high Density Board

Huntsman International

Suitable

2016-11-28

MMA

Oddy test (method: 20161007_OT), SPME GCMS

medium-high density polyurethane board; density: 48 lb./ft^3; light brown color; Purchased 2016

board

2# Vizion Std Black

Palziv North America

Rubberlite Incorporated

Temporary

2018-08-03

MMA

Oddy test (method: 20180704_OT), SPME GCMS

Black polyethylene foam; Details: 2 lb/cubic foot density black cross-linked polyethylene foam, purchased as 3"x12"x12" block; Month/Year Purchased: 12/2017; Chemical Components: cross-linked polyethylene

Black

foam, non-building insulation, polymer

Obomodulan® Polyurethane Board, Obomodulan 500

OBO-Werke

Mccausey Specialty Products

Suitable

2018-08-01

MMA

Oddy test (method: 20180704_OT), SPME GCMS

Obomodulan board; Month/Year Purchased: 5/2018; Details: density is 500 kg/m3; pink colored; foamed polyurethane; Chemical Components: polyurethane

board, plastic/polymeric/synthetic

Plascore Aluminum Honeycomb Core Panel; Aa3.6-80

Plascore

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Aluminum honeycomb; Chemical Components: 0.020” aluminum, epoxy primer finish, aluminum honeycomb Core 3.6 pcf; Purchased: 3/27/2018;

board, plastic/polymeric/synthetic

Archival Coroplast

Coroplast

Talas

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Polypropylene corrugated board; Details: Extruded twin wall fluted plastic sheet; Chemical Components: Polypropylene copolymer; Purchased: 4/2018;

board, plastic/polymeric/synthetic

Non-archival Coroplast

Coroplast

Van Owners

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Polypropylene corrugated board; Non-archival. Extruded twin wall fluted plastic sheet. Chemical Components: Polypropylene copolymer; Purchased: 4/2018;

board, plastic/polymeric/synthetic

Neoprene Epdm Foam Tape, 4311n

Jacobs And Thompson

Jacobs & Thompson

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Neoprene EPDM foam tape, black, closed cell foam with acrylic adhesive on one side; Chemical Components: EPDM foam, acrylic adhesive; www.foamparts.com; Purchased: 5/2017;

Black

gasket, polymer

Rising Museum Rag Matboard Antique; R405602

Unknown

Omega Moulings

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

100% cotton rag board, 4 ply, acid-free, neutral pH, buffered with calcium carbonate; received from the Walt Disney museum June 2018

board, natural

Microfoam Mf500 1/2

Pregis

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Polypropylene foam in roll; 1/2" thickness; multilayer sheet foam; purchased april 2018

foam, non-building insulation, polymer

King Starboard Marine Grade Hdpe Polymer Sheet, Ksbblakmm.75006.0006.00

King Plastic

Mcmaster-Carr

Suitable

2018-07-17

MMA

Oddy test (method: 20171106_OT), SPME GCMS

Black HDPE board; Purchased May 2018; Chemical Components: black polyethylene

Black

board, plastic/polymeric/synthetic

Mf-s1 Compression Seal

Manfred Frank

Temporary

2018-07-17

MMA

Oddy test (method: 20171106_OT), SPME GCMS

Silicone S-shaped compression Seal used for butt joints; purchased june 2017

gasket, polymer

Better Backer Polyethylene Foam

Robert Holmes Construction

Weatherall Company

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

White trapezoidal foamed polyethylene backer rod; thickness bottom: 1 3/4", top: 7/8"; purchased May 2018

White

foam, non-building insulation, polymer

Grip Strip Foam Backing Material Polyethylene Foam

Timeless Wood Care Products

Weatherall Company

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

White trapezoidal backer rod foam, Top: 1.5"; bottom: 1 7/8"; Chemical Components: (see percentages in SDS) polyethylene foam, dichlorodifluoromethane, dichlorotetrafluoroethane; chlorodifluoroethane; stearyl stearamide; color concentrate in polyethylene; purchased May 2018

White

foam, non-building insulation, polymer

Optium Museum Acrylic

Tru Vue

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Anti-reflective, abrasion resistant, and anti-static, 3mm acrylic sheet. Washed with tap water and 1% Micro 90 solution; rinsed with tap water then rinsed with 18.2 Mohm water. 99% UV protective; Chemical Components: acrylic, optical coating; acquired 5/2018;

board, plastic/polymeric/synthetic

10 Mm Polypropylene Flutecorr, "natural" Color

Laminacorr

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Extruded polypropylene corrugated board, 10mm thick; polypropylene; acquired 5/2018

board, plastic/polymeric/synthetic

Astro-foam (r); Af-500 1/2";

Pregis

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

White polyethylene foam sheet, 1/2" thick, non-abrasive; polyethylene; purchased March 2018

White

foam, non-building insulation, polymer

Cor-x Polypropylene 4 Mm Corrugated Board

Primex Plastics

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Corrugated polypropylene board; 4 mm thickness; Purchased May 2018

board, plastic/polymeric/synthetic

Proflex Profiles 2" Solid Rounds Structural Foam (polyethylene Foam); 49486

Unknown

New England Foam

Temporary

2018-07-17

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Round foamed backer rod; Polyethylene CAS No. 9002-88-4; Isobutane CAS No.75-28-5; Details: 1.7-1.9 PCF Extruded, white, 2" x 72"

foam, non-building insulation, polymer

Foam Core Board - 48 X 96" , Black, 3⁄16" Thick, S-12861

Unknown

Uline

Temporary

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Details: white; 3/16" thick clay coated foam board; https://www.uline.com/BL_870/Uline-Foam-Core-Board?keywords=Foam+Board; Chemical Components: clay coating, extruded polystyrene core; purchased May 2018.

White

board, plastic/polymeric/synthetic

Lj Acid-free, Laf40

Unknown

Larson Juhl

Temporary

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Details: white; 3/16" thick acid free foam board; purchased May 2018

White

board, plastic/polymeric/synthetic

Nylon Material 1647

Ultimaker

Temporary

2018-07-05

MMA

Oddy test (method: 20180525_OT), SPME GCMS

3D printed nylon: 3D printed at 250°C; Industrial-grade impact and abrasion resistance; Durable, High strength-to-weight ratio, Low friction coefficient, Good corrosion resistance to alkalis and organic chemicals; Reduced humidity absorption when compared to other Nylon filaments; purchased September 2017.

block/bulk/pellet, polymer

Poron Polyurethane 4701-40 Black

Rogers Corporation

Temporary

2017-11-27

MMA

Oddy test (method: 20171030_OT), SPME GCMS

Black polyurethane foam; purchased March 2017

Black

foam, non-building insulation, polymer

Supamag White Matt Magnetic Sheet

Anchor Magnets

Temporary

2017-11-21

MMA

Oddy test (method: 20171024_OT), SPME GCMS

Printable magnetic sheet with white matte thermoplastic binder on one side (often used for retail graphics); flexible in nature; thickness: 0.6 mm; purchased 9/2017;

White

membrane (< 1mm thick), polymer

Supamag White Glass Magnetic Sheet

Anchor Magnets

Suitable

2017-10-16

MMA

Oddy test (method: 20170918_OT), SPME GCMS

Printable magnetic sheet with white glossy thermoplastic binder surface on one side; thickness: 0.75 mm; uses: large format retail graphics; Purchased: 9/2017

White

polymer, sheet (> 1mm thick)

Platinum 2000 Silicone Tubing

Mcmaster-Carr

Temporary

2017-12-28

MMA

Oddy test (method: 20171116_OT), SPME GCMS

white silicone tubing; 0.040 ID x 0.085 OD; 60-411-44-10 ft; purchased april 2016

White

block/bulk/pellet, polymer

Pl Premium Polyurethane Construction Adhesive; "pl3x"

Unknown

Loctite

Suitable

2017-12-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

polyurethane construction adhesive; this sample was cured 19 days before testing; purchased october 2017

caulk or sealant, adhesive, polymer

Optix Extruded Acrylic Sheet

Plaskolite

Ain Plastics

Suitable

2018-05-17

MMA

Oddy test (method: 20171116_OT), SPME GCMS

extruded polymethyl methacrylate; Crystal clear, impact- and weather-resistant, OPTIX is a continuously processed acrylic sheet; contains UV stabilization; sourced from The Met's Plexi shop

polymer, sheet (> 1mm thick)

Astariglas Gp Cast Acrylic Sheet

Plaskolite

Ain Plastics

Suitable

2018-05-17

MMA

Oddy test (method: 20171116_OT), SPME GCMS

ASTARIGLAS® GP cast acrylic sheets are made from 100% virgin MMA (methyl methacrylate monomer); sourced from The Met's Plexi shop

polymer, sheet (> 1mm thick)

Clear Glass Joint Strips 180 Degree Joint

Cr Laurence

Temporary

2018-05-17

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Hard plastic I-beam for edge-joining sheets of glass; 1/2" tall 1/8" wide; copolyester plastic with unknown adhesive; Contains removable adhesive liner. Tested without red adhesive liner

gasket, polymer

Volara 040a 125wh Closed Cell Foam

Sekisui Voltek

Sekisui (US)

Temporary

2018-04-05

MMA

Oddy test (method: 20171116_OT), SPME GCMS

white polyethylene foam; 12"x12"x0.25"; density = 4 lb/ft^3; Grade A; Chemical Components: polyethylene; purchased 11/2017

White

foam, non-building insulation, polymer

Polystone G Polyethylene Board

Rochling

Ain Plastics

Suitable

2018-05-17

MMA

Oddy test (method: 20171116_OT)

white polyethylene board, HDPE, 3/16" thick

White

board, plastic/polymeric/synthetic

Komacel Plus, Striated Pvc Board

Kömmerling

Suitable

2016-12-19

MMA

Oddy test (method: 20162116_OT)

Striated; PVC board

board, plastic/polymeric/synthetic

Bpe-t50 / Polyethyene Tubing 0.023" Id X 0.038" Od

Soloman Scientific

Unknown

Suitable

2016-08-04

MMA

Oddy test (method: 20160705_OT), SPME GCMS

non-sterile polyethylene tubing

block/bulk/pellet, polymer

Tpb004003 (Tissue Paper)

Green's

Talas

Suitable

2018-05-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

unbuffered lens tissue; Month/Year Purchased: March/2018; Details: An unbuffered, neutral pH tissue made of a select blend of abaca fibers, softer than the acid-free tissues. Paper weight: 10 gsm, 60 microns thick;

paper-based, sheet

Crl Ez Glaze Sounstrip

Cr Laurence

Unknown

Temporary

2018-05-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Hollow core, square shaped; flexible; 1/4" x 1/4"; extruded silicone

gasket, polymer

Black Sil-b Silicone Foam With Acrylic 3M Brand Psa Backing Adhesive

Netherland Rubber Company

Netherland Rubber

Temporary

2018-01-10

MMA

Oddy test (method: 20171116_OT), SPME GCMS

black SIL-B silicone foam gasket with acrylic 3M Brand PSA backing adhesive

Black

gasket, polymer

Ethafoam® 900

Sealed Air

Hibco Plastics

Suitable

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

9.0 pounds per cubic ft. closed cell Polyethylene foam

foam, non-building insulation, polymer

Ethafoam® 220

Sealed Air

Hibco Plastics

Temporary

2018-01-04

MMA

Oddy test (method: 20171116_OT), SPME GCMS

2.2 pounds per cubic ft. closed cell Polyethylene foam

foam, non-building insulation, polymer

Alucobond

3A Composites

Unknown

Suitable

2017-12-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

unpainted silver with (seeming) black core

board, plastic/polymeric/synthetic

Translucent, Food Grade 1/32" Thick Silicone Rubber Sheet

Unknown

Canal Rubber Supply

Suitable

2017-11-27

MMA

Oddy test (method: 20171030_OT), SPME GCMS

(purchased off the shelf 8/2016)

polymer, sheet (> 1mm thick)

Shapeways Stainless Steel (infiltrated With Bronze) 60/40

Unknown

Shapeways

Temporary

2017-11-27

MMA

Oddy test (method: 20171030_OT), SPME GCMS

HIGH COPPER CONTENT; Chemical Components: Shapeways’ 3D printed steel is Stainless Steel Alloy 420 infiltrated with Bronze (90% Cu/10% Sn). It is a matrix material composed of 60% stainless steel and 40% bronze; Details: manufactured via additive manufacturing process; purchased 10/2017; NOTE: observe the sample material before and after test.

metal (eg.: mechanical fastener)

Raw Aluminum

Unknown

Shapeways

Suitable

2017-11-27

MMA

Oddy test (method: 20171030_OT), SPME GCMS

3D printed by Shapeways 10/2017; manufactured via selective laser melting. Aluminum is fused and melted using a laser from a bed of metallic powder. This process fully melts the powder rather than just sintering it, creating a solid, homogenous aluminum alloy; note: sample jars contained less than 2g of sample. jar A contained 1.845 g & Jar B contained 1.516 g sample

metal (eg.: mechanical fastener)

Food-grade Supercushioning Polyethylene Foam Sheets W/ Ultra-smooth Texture

Pres-on Corporation

Mcmaster-Carr

Unsuitable

2018-03-06

MMA

Oddy test (method: 20180206_OT), SPME GCMS

Polyethylene foam sheet, catalogue #8722K11; 3/8" thick

foam, non-building insulation, polymer

Transparent Extruded D-seal Rubber

Elastostar Rubber

Unsuitable

2018-03-06

MMA

Oddy test (method: 20180206_OT), SPME GCMS

transparent silicone D gasket; Clear 50-60 Durometer; FDA Silicone; 21-22mm Wide X 13-15mm high X 5mm wide X 2mm; FDA extruded silicone; purchased Januray 2018

gasket, polymer

Food-grade Supercushioning Polyethylene Foam Sheets W/ Ultra-smooth Texture

Pres-on Corporation

Mcmaster-Carr

Unsuitable

2018-03-06

MMA

Oddy test (method: 20180206_OT), SPME GCMS

3/8" thick black polyethylene foam sheet; catalogue #8722K11; purchased 10/2017

foam, non-building insulation, polymer

Bisco Bf 1000 White

Rogers Corporation

Elastomeric Material Solutions, Carol Stream, Il

Temporary

2018-02-26

MMA

Oddy test (method: 20171116_OT), SPME GCMS

White silicone foam with pressure sensitive adhesive on one side; purchased januray 2018

White

foam, non-building insulation, polymer

Bisco Bf-2000 Black

Rogers Corporation

Elastomeric Material Solutions, Carol Stream, Il

Temporary

2018-02-26

MMA

Oddy test (method: 20171116_OT), SPME GCMS

black silicone foam with pressure sensitive adhesive on one side; purchased January 2018;

Black

foam, non-building insulation, polymer

Renshape 440

Huntsman International

Freeman Manufacturing And Supply Co

Suitable

2018-02-26

MMA

Oddy test (method: 20171116_OT), SPME GCMS

foamed polyurethane board (dense)

board, plastic/polymeric/synthetic

Black Gasket

Bsp Silikon Profile

Temporary

2018-02-26

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Chemical Components: HTV-silicone, polysiliaxanes and pyrogenic silica; received January 2018

gasket, polymer

0.125" Clear Silicone Rubber Sheeting

Acme Rubber

Suitable

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Clear silicone rubber sheet; durometer: 40; manufacturer may dyeCut this sheeting if drawings are supplied. Their extruded silicone can be a different compound than the tested sheeting.

Clear

gasket, polymer

Intramedic Non-radiopaque Polyethylene Tubing, Model #427411

Clay Adams Brand

Beckton Dickenson

Suitable

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

non-sterile polyethylene tubing; 0.023" ID, 0.038" OD; purchased January 2018

block/bulk/pellet, polymer

Colorsil N In Color Ral 7022 (gray)

Kawo Karl Wolpers

Temporary

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Colored one component silicone sealant; cured 24 hours

caulk or sealant, adhesive, polymer

Pe60 Flesh - Model P60flxl8

Ultralon Foam Group

Ultralon

Unsuitable

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Polyethylene foam board; 34mm thick, 2ft x 3ft. Produced in Ho chi minh, Vietnam - only manufacture site for Ultralon. Batch made with pellets sourced from Germany. Ultralon chemically cross-linked polyethylene foam using azo carbamide foaming agent, claim high 90% cross-linking. Can laminate with heat or glue. available in 24-44mm thickness. purchased 12/2017

foam, non-building insulation, polymer

Pe30 White; Model #pe30whs3

Ultralon Foam Group

Ultralon

Temporary

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Polyethylene foam board; 41mm thick, 2ft x 3 ft. Produced in Ho chi minh, Vietnam - only manufacture site for Ultralon. Batch made with pellets sourced from Germany. Ultralon chemically cross-linked polyethylene foam using azo carbamide foaming agent, claim high 90% cross-linking. Can laminate with heat or glue. available in 24-44mm thickness. purchased: 12/2017

foam, non-building insulation, polymer

Ultralon Pe140 White; Model #pe140uvbwhxlhd

Ultralon Foam Group

Ultralon

Unsuitable

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Polyethylene foam board; Details: 39.5mm thick, 2ft x 3ft, Produced in Ho chi minh, Vietnam - only manufacture site for Ultralon. Batch made with pellets sourced from Germany. Ultralon chemically cross-linked polyethylene foam using azo carbamide foaming agent, claim high 90% cross-linking. Can laminate with heat or glue. available in 24-44mm thickness. purchased: 12/2017

foam, non-building insulation, polymer

Epu40

Carbon3d

Temporary

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

3D printed elastomeric polyurethane; Black, dog bone shaped samples printed on M2 Printer. ~4 inches long, 1 inch wide with 8mm width at narrow portion of 'bone'. Testing as possible customizable 'foam' or cushioning structure for shipping art. purchased december 2017

block/bulk/pellet, polymer

No

Control coupon · [[media:|GCMS]]

Viton® 60

Rainbow Rubber

Suitable

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

black Viton® 60 1/8" thick y 3/4" wide black gasketing; must be trademarked product

Black

gasket, polymer

Mdf + 3 Coats Resene Lumbersider White

Resene Paints

Unsuitable

2006-05-16

AWMM

Oddy test

Wood plus paint/varnish

board, composite

Mdf + 3 Coats Resene Polythane Moisture Cured Polyurethane, Clear Gloss

Resene Paints

Suitable

2006-05-16

AWMM

Oddy test

In vitrine or case

Wood plus paint/varnish

board, composite

Mdf

Unsuitable

2006-05-16

AWMM

Oddy test

Wood

board, composite

Medite Zf

Resene Paints

Unsuitable

2006-05-16

AWMM

Oddy test

Wood

board, composite

Medite Zf + 3 Coats Resene Lumbersider White

Resene Paints

Unsuitable

2006-05-16

AWMM

Oddy test

Wood plus paint/varnish

board, composite

Medite Zf + 3 Coats Resene Polythane Moisture Cured Polyurethane, Clear Gloss

Resene Paints

Unsuitable

2006-05-16

AWMM

Oddy test

Wood plus paint/varnish

board, composite

Hoop Pine + 3 Coats Resene Lumbersider White

Resene Paints

Unsuitable

2006-05-16

AWMM

Oddy test

Wood

board, composite

Hoop Pine + 3 Coats Resene Polythane Moisture Cured Polyurethane, Clear Gloss

Resene Paints

Unsuitable

2006-05-16

AWMM

Oddy test

Outside vitrine or case

Wood

board, composite

Cedar, Sample From Old Seasoned Shelving Plank

Suitable

Change in patina of copper coupon, (lightened) but no obvious corrosion.

1999-12-21

AWMM

Oddy test

Outside vitrine or case

Wood

board, natural

Change in patina of copper coupon, (lightened) but no obvious corrosion.

Pine

Temporary

Change in patina of copper coupon, (lightened) but no obvious corrosion.

Slight clouding of the lead coupon

1999-12-21

AWMM

Oddy test

Outside vitrine or case. Temporary use only.

Wood

board, natural

Slight clouding of the lead coupon, and change in patina of copper, as above.

Hoop Pine

Resene Paints

Unsuitable

2006-05-16

AWMM

Oddy test

Wood

board, natural

Pine Wood With Pink Surface (treated?)

Unknown

Unsuitable

2009-01-12

AWMM

Oddy test

Wood

board, natural

Colourfield Card, Ksa25a3pw-10

Gordon Harris

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paper, board

board, natural

Orfit Eco

Orfit Industries, Vosweld

Temporary

Few white spots on lead coupon.

2003-02-18

AWMM

Oddy test

Outside vitrine or case. Suitable for use in controlled situations.

Paper, board

paper-based, sheet

Few white spots on lead coupon.

Elastomer Products Ltd. Clear Gasket/bulb Seal

Elastomer Products

Temporary

slight discolouration of copper

small specks of white corrosion products on lead with uneven patina

1998-09-28

AWMM

Oddy test

Outside vitrine or case

Gasket materials

caulk or sealant, adhesive, polymer

Lead and copper coupons slightly changed: small specks of white corrosion products on lead with uneven patina, and slight discolouration of copper.

Compression Seal, Permanent Elastic Silicone, Clear

Frank Europe

Temporary

2007-11-29

AWMM

Oddy test

Outside vitrine or case

Gasket materials

caulk or sealant, adhesive, polymer

Foam Pvc

Unsuitable

2016-05-02

AWMM

Oddy test

foam, non building insulation, polymer

Woods Glass Gasket Materials

Temporary

Tarnishing on copper coupon in keeping with control copper coupon

Slight tarnish

moderate corrosion

2003-09-16

AWMM

Oddy test

Outside vitrine or case. Suitable for temporary use in display cases and storage units.

Gasket materials

gasket, polymer

Slight tarnish on silver coupon, moderate corrosion on lead coupon. Tarnishing on copper coupon in keeping with control copper coupon.

Manfred Frank Gasket Materials

Suitable

2003-09-16

AWMM

Oddy test

Outside vitrine or case

Gasket materials

gasket, polymer

Netherfield Case Gasket

Resene Paints

Temporary

2006-05-16

AWMM

Oddy test

Outside vitrine or case

Gasket materials

gasket, polymer

Brush Seal, Panel Connection System, Permanent Elastic Silicone, Clear

Frank Europe

Unsuitable

2007-11-29

AWMM

Oddy test

Gasket materials

gasket, polymer

Compression Seal, Permanent Elastic Silicone, Clear

Frank Europe

Temporary

Slight overall darkening of lead coupon.

2008-02-28

AWMM

Oddy test

In vitrine or case

Gasket materials

gasket, polymer

Slight darkening of lead coupon. Suitable for permanent use to seal butt joints in showcases.

Brush Seal, Panel Connection System, Permanent Elastic Silicone, Clear

Frank Europe

Temporary

Slight overall darkening of lead coupon.

2008-02-28

AWMM

Oddy test

In vitrine or case. Suitable for permanent use to apply to leading edges of doors and opposing edges.

Gasket materials

gasket, polymer

Slight overall darkening of lead coupon.

Ptfe (polytetrafluoroethylene, Teflon), White

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

polymer, sheet (>1mm thick)

In vitrine or case

Somos 9210

Dsm Desotech

Unsuitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer, sheet (>1mm thick)

Somos Next

Dsm Desotech

Unsuitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer, sheet (>1mm thick)

Somos Watershed Xc11122

Dsm Desotech

Unsuitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer, sheet (>1mm thick)

Pa 3200 Gf

Electro Optical Systems

Suitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer, sheet (>1mm thick)

Pa 2200

Electro Optical Systems

Suitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer, sheet (>1mm thick)

Benchmark Sueded Polyethylene With Adhesive , Black

Benchmark Catalog

Suitable

1999-07-13

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

batting & padding and adhesive, fabric

Benchmark Sueded Polyethylene With Adhesive , Grey

Benchmark Catalog

Temporary

1999-07-13

AWMM

Outside vitrine or case

Plastics, films, foams, plastic sheeting

batting & padding and adhesive, fabric

Benchmark Sueded Polyethylene With Adhesive , Black

Benchmark Catalog

Temporary

1999-09-14

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

batting & padding and adhesive, fabric

Clear Electrical Heat Shrink Tubing 41 Series

Dick Smith Electronics

Suitable

2003-01-12

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

3M Window Film, Scotchfield, Polyester Film Plus Acrylate Adhesive Liner, S40 (previous Sh4clarl)

3M New Zealand

Unsuitable

2008-02-28

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Rubber Mat, Black

Unsuitable

2013-11-26

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Rubber Mat, Black

Unsuitable

2013-11-26

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Anoxic Chamber Film, Cepac ® Hd100 Super Heavy Duty Barrier, Mil-prf-131k, Class 1, Green/silver

Cadillac Products Packaging Company

Suitable

Same as control

2015-07-22

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Pretty much the same as the control.

Uhmwpe (ultra High Molecular Weight Polyethylene), Black

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Hmpe (high Molecular Weight Polyethylene?), White

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Polypropylene, White

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Tapco Chamber Tool, Firearms Safety Lock, Ztoolcst01, Yellow

Tapco

Temporary

2016-03-24

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate. Only slight reaction with lead, so could probably be used for permanent storage so long as not direct contact with metal, and well ventilated.

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

In vitrine or case

Abs, White

Makerbot Industries

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Abs, Dark Saguine Red

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Pla, Natural

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Pla, Pearly White

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Pla, Black, Up Fila C-12-02 Pla-black

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Sla Perform

Suitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Procell Foam Non Cross Linked, Closed Cell, Ldp

Dunlop Foams

Suitable

1999-08-15

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Dark patina on lead coupon acceptable,other coupons unchanged. Suitable for permanent use.

Ethafoam 220, Dow Chemicals

Dunlop Foams

Suitable

2002-03-25

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Plastazote With Adhesive Backing Ld 45

Suitable

2002-03-25

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Evazote, Black Ev 50

Dunlop Foams

Suitable

2006-05-16

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Heat-bonded Polyethylene Foam, Black

A&E Karsten

Suitable

2006-05-16

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Cross-linked Expanded Pe Foam (black)

A&E Karsten

Suitable

2012-06-20

AWMM

Oddy test

In vitrine or case

Plastics, foams

foam, non building insulation, polymer

Clear Electrical Heat Shrink Tubing 41 Series

Dick Smith Electronics

Suitable

2003-01-12

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

3M Window Film, Scotchfield, Polyester Film Plus Acrylate Adhesive Liner, S40 (previous Sh4clarl)

3M New Zealand

Unsuitable

2008-02-28

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Rubber Mat, Black

Unsuitable

2013-11-26

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Rubber Mat, Black

Unsuitable

2013-11-26

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Anoxic Chamber Film, Cepac ® Hd100 Super Heavy Duty Barrier, Mil-prf-131k, Class 1, Green/silver

Cadillac Products Packaging Company

Suitable

Same as control

2015-07-22

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Pretty much the same as the control.

Uhmwpe (ultra High Molecular Weight Polyethylene), Black

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Hmpe (high Molecular Weight Polyethylene?), White

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Polyproylene, White

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Dwp 125, Es1000 Thin Wall Heat Shrink, Dwp 125 Unheated

Transnet

Suitable

Some change in the lead, but the yellow coating appeared on the control too, so I suspect it is contamination on the stoppers.

2014-06-06

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer -tubing

Some contaminaton of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distingished. Some change in the lead, but the yellow coating appeared on the control too, so I suspect it is contamination on the stoppers.

Dwp 125, Es1000 Thin Wall Heat Shrink, Dwp 125 Pre-shrunk

Transnet

Suitable

2014-06-06

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer -tubing

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Rnf100 General Purpose Low Voltage Heat Shrink, Rnf 100 Unheated

Tyco Electronics

Suitable

2014-06-06

AWMM

Oddy test

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Plastics, films, foams, plastic sheeting

polymer -tubing

In vitrine or case

No

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Rnf100 General Purpose Low Voltage Heat Shrink, Rnf 100 Pre-shrunk

Tyco Electronics

Suitable

2014-06-06

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer -tubing

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Ezishrink Ezhswh2/1, Hs Wh 2/1 Unheated

Transnet

Suitable

2014-06-06

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer -tubing

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Ezishrink Ezhswh2/1, Hs Wh 2/1pre-shrunk

Transnet

Suitable

2014-06-06

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer -tubing

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Ezishrink Ezhsbk3/1.5, Hs Bk 3/1.5 Unheated

Transnet

Suitable

2014-06-06

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer -tubing

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Ezishrink Ezhsbk3/1.5, Hs Bk 3/1.5 Pre-shrunk

Transnet

Suitable

2014-06-06

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

polymer -tubing

Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.

Medical Grade Silicone Lsr-4305 Platinum Liquid Silicone (set Solid)

Suitable

2017-03-23

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

other, silicone moulding compound

Mouldfast Fix-all Silicone, Neutral Cure

Suitable

2017-03-23

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

other, silicone moulding compound

Tygon Tube, S-50-hl Class Vi

Saint-gobain

Suitable

2009-01-12

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

other, tygon tubing

Tapco Chamber Tool, Firearms Safety Lock, Ztoolcst01, Yellow

Tapco

Temporary

2016-03-24

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate. Only slight reaction with lead, so could probably be used for permanent storage so long as not direct contact with metal, and well ventilated.

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

In vitrine or case

Abs, White

Makerbot Industries

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Abs, Dark Saguine Red

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Pla, Natural

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Pla, Pearly White

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Pla, Black, Up Fila C-12-02 Pla-black

Makerbot Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Sla Perform

Suitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

block/bulk/pellet, polymer

Procell Foam Non Cross Linked, Closed Cell, Ldp

Dunlop Foams

Suitable

1999-08-15

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Dark patina on lead coupon acceptable,other coupons unchanged. Suitable for permanent use.

Ethafoam 220, Dow Chemicals

Dunlop Foams

Suitable

2002-03-25

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Plastazote With Adhesive Backing Ld 45

Suitable

2002-03-25

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Evazote, Black Ev 50

Dunlop Foams

Suitable

2006-05-16

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Heat-bonded Polyethylene Foam, Black

A&E Karsten

Suitable

2006-05-16

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

foam, non building insulation, polymer

Cross-linked Expanded Pe Foam (black)

A&E Karsten

Suitable

2012-06-20

AWMM

Oddy test

In vitrine or case

Plastics, foams

foam, non building insulation, polymer

Clear Electrical Heat Shrink Tubing 41 Series

Dick Smith Electronics

Suitable

2003-01-12

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

3M Window Film, Scotchfield, Polyester Film Plus Acrylate Adhesive Liner, S40 (previous Sh4clarl)

3M New Zealand

Unsuitable

2008-02-28

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Rubber Mat, Black

Unsuitable

2013-11-26

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Rubber Mat, Black

Unsuitable

2013-11-26

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Anoxic Chamber Film, Cepac ® Hd100 Super Heavy Duty Barrier, Mil-prf-131k, Class 1, Green/silver

Cadillac Products Packaging Company

Suitable

Same as control

2015-07-22

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

Pretty much the same as the control.

Uhmwpe (ultra High Molecular Weight Polyethylene), Black

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Hmpe (high Molecular Weight Polyethylene?), White

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Polyproylene, White

Lep Engineering Plastics

Suitable

2016-04-04

AWMM

Oddy test

The tests all exploded (stopper blew off) during testing, so results may not be accurate.

Plastics, films, foams, plastic sheeting

membrane (<1mm thick), polymer

In vitrine or case

Neoprene Strip

Howard King And Assoc. Mt. Roskill

Temporary

changed color

unchanged

1998-05-07

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

neoprene strip

Pb and Ag unchanged, Cu coupon changed colour. Suitable for temporary use or permanent use with selected collections only.

6040 Sellotape Anti Skid Dots, Clear

Sellotape Products (nz)

Unsuitable

2008-03-04

AWMM

Oddy test

Plastics, films, foams, plastic sheeting

dots, other

Actifoam, Black/blue-grey

Beele Engineering Bv

Temporary

2014-03-06

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

fire barrier, other

Rise Multicable Transits:rapid Sealing System,

Beele Engineering Bv

Temporary

2014-03-06

AWMM

Oddy test

Outside vitrine or case; A building requirement, so it has to be used. Just ensure that objects are not located close to fire intrusions, and no fire intrusion are present in display cases against walls.

Plastics, films, foams, plastic sheeting

fire barrier, other

Outside vitrine or case

Nofirno Firestop, Sealant, Red

Beele Engineering Bv

Unsuitable

2014-03-06

AWMM

Oddy test

A building requirement, so it has to be used. Just ensure that objects are not located close to fire intrusions, and no fire intrusion are present in display cases against walls.

Plastics, films, foams, plastic sheeting

fire barrier, other

Rise/ultra Crusher, Black

Beele Engineering Bv

Temporary

2014-03-06

AWMM

Oddy test

Outside vitrine or case; A building requirement, so it has to be used. Just ensure that objects are not located close to fire intrusions, and no fire intrusion are present in display cases against walls.

Plastics, films, foams, plastic sheeting

fire barrier, other

Outside vitrine or case

3M Ultra Plastic Pipe Liner Material, Black

3M

Unsuitable

2014-03-06

AWMM

Oddy test

A building requirement, so it has to be used. Just ensure that objects are not located close to fire intrusions, and no fire intrusion are present in display cases against walls.

Plastics, films, foams, plastic sheeting

fire barrier, other

Avery Dennison Hp Dol 2080, Vinyl Laminate, Hp Dol 2080, Matte

3M New Zealand

Big Colour

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

board, plastic/polymeric/synthetic

3M Controltac, 180c-10, White

3M New Zealand

Big Colour

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

board, plastic/polymeric/synthetic

Clear Strip

Glass Relate, Kelston

Temporary

changed colour

Formation of corrosion beginning

1998-05-07

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

clear strip

Formation of corrosion on Pb beginning, Cu and Ag coupons have changed colour.

Parafilm M

Suitable

2017-03-23

AWMM

Oddy test

Outside vitrine or case

Plastics, films, foams, plastic sheeting

coating, grease, oil, wax

Tc-857 Part A, Polyurethane Resin

Bjb Enterprises

Suitable

2017-03-23

AWMM

Oddy test

In vitrine or case

Plastics, films, foams, plastic sheeting

coating, paint & primer

Kingspan Ks1100cs, Insulated Panel, Metal Surface Only

Kingspan

Kingspan (New Zealand)

Suitable

2016-06-20

AWMM

Oddy test

In vitrine or case

Misc.

board, composite

Kingspan Ks1100cs, Insulated Panel, Foam Core Only

Kingspan

Kingspan (New Zealand)

Suitable

2016-06-20

AWMM

Oddy test

In vitrine or case

Misc.

board, composite

Kingspan Ks1100cs, Insulated Panel

Kingspan

Kingspan (New Zealand)

Suitable

2016-06-20

AWMM

Oddy test

In vitrine or case

Misc.

board, composite

Alabaster-white With Grey

3form

Suitable

slight tarnish

slight yellowing around edges

dark gray

2008-12-19

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

White Alabaster with grey for exhibit cases

White

inorganic, stone

Chroma-ghost Applied

3form

Suitable

no change

2008-12-19

CAM

Oddy test

test run at 60 degrees C for 4 weeks

polymer resin substrate for exhibit cases- decks

board, plastic/polymeric/synthetic

Apoxie Sculpt

Aves Studio

Suitable

almost no change

no change

hazy gray appearance

2015-07-28

CAM

Oddy test

for use non-contact; test run at 65 degrees C for 4 weeks

epoxy paste for mounts and conservation treatment

block/bulk, polymer

Pure Bond

Columbia Forest Products

Nisbet Brower, Cincinnati

Suitable

slight darkening

good

slight traces of white

2007-01-31

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks; Result Ok with coating

plywood

board, natural composite

Purebond Birch Faced Plywood

Columbia Forest Products

Nisbet Brower, Cincinnati

Retest

slight darkening/ iridescence around edges

shiny, OK

thin layer white corrosion

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

plywood

board, natural composite

Purebond Birch Faced Plywood

Columbia Forest Products

Nisbet Brower, Cincinnati

Retest

shiny- OK

slightly dull at edges

white/yellow corrosion on both sides

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

plywood

board, natural composite

Plastic Tubing

Dunbar

Suitable

even darkening

slight haziness

2016-06-01

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

Clear Tubing, for mounts

Clear

polymer, sheet/tube (>1 mm thick)

Birch Plywood

Nisbet Brower, Cincinnati

Unsuitable

Red with slight black

no change

grey discoloration

2016-06-01

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

plywood

board, natural composite

Dow Mdf

Nisbet Brower, Cincinnati

Unsuitable

darkened overall

thick white corrosion

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

medium density fiberboard

board, natural composite

Dow Mdf

Nisbet Brower, Cincinnati

Unsuitable

darkened overall

thick white corrosion

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

medium density fiberboard

board, natural composite

Mdf

Uniboard Canada

Nisbet Brower, Cincinnati

Retest

slight darkening/ iridescence around edges

shiny, OK

white/yellow corrosion on both sides

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

medium density fiberboard

board, natural composite

Mdf

Uniboard Canada

Nisbet Brower, Cincinnati

Retest

slight darkening/ iridescence around edges

shiny, OK

white/yellow corrosion on both sides

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

medium density fiberboard

board, natural composite

Closed Cell Neoprene Sponge Snc-1 With Adhesive Backing

Netherland Rubber

Suitable

slight tarnish

great

slight darkening

2007-06-11

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

closed cell neoprene sponge SNC with adhesive backing

gasket, polymer

Gasket (thick)

Netherland Rubber

Temporary

spotted tarnish

no change

slight tarnish

2016-05-25

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

black gasket, thick

Black

gasket, polymer

Gasket (thin)

Netherland Rubber

Retest

uneven tarnish

slight yellow

no change

2016-06-01

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

black gasket, thin

Black

gasket, polymer

Gasket (thin)

Netherland Rubber

Unsuitable

uneven darkening

no change

uneven whitening

2016-07-01

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

black gasket, thin

Black

gasket, polymer

Poplar

Nisbet Brower, Cincinnati

Unsuitable

Mostly Black

Uneven corrosion

Uneven haziness

2016-06-01

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

wood

board, natural

Poplar Plywood

Nisbet Brower, Cincinnati

Suitable

purple

no change

slight lightening

2016-05-25

CAM

Oddy test

; test run at 60 degrees C for 4 weeks

plywood

board, natural composite

Volara

Sekisui Voltek

Retest

uneven tarnish

slight change

slight haziness

2016-06-01

CAM

Oddy test

for use non-contact; test run at 60 degrees C for 4 weeks

polyethylene closed cell foam sheet

foam, polymer

Extira

Jeld-wen

Unsuitable

slight darkening/ iridescence around edges

shiny, OK

dull white haze overall

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

alternative to MDF

board, composite

Extira

Jeld-wen

Unsuitable

slight darkening/ iridescence around edges

shiny, OK

dull white haze overall

2006-09-29

CAM

Oddy test

for use in contact; test run at 60 degrees C for 3 weeks

alternative to MDF

substrate with paint/coating

Fosshape-all Grades (dry Shaped)

Suitable

spotted tarnish

no change

even darkening

2009-11-04

CAM

Oddy test

test run at60 for 2 weeks

mounts for textiles

fabric, nonwoven synthetic

Fosshape-all Grades (raw)

Suitable

minor tarnish

no change

even darkening

2009-11-04

CAM

Oddy test

test run at60 for 2 weeks

mounts for textiles

fabric, nonwoven synthetic

Fosshape-all Grades (wet-heat Shaped)

Suitable

spotted tarnish

no change

even darkening

2009-11-04

CAM

Oddy test

test run at60 for 2 weeks

mounts for textiles

fabric, nonwoven synthetic

Polyethylene Foam

Suitable

slight darkening

no change

even darkening

2010-04-12

CAM

Oddy test

test run at 60 degrees C for 3 weeks

black polyethylene foam

Black

foam, non building insulation, polymer

Perma/dur Tan Unbuffered Barrier Board

Unknown

University Products

Temporary

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

Acid-free, lignin-free, non-buffered 40 pt. board

board

Perma/dur Tan Buffered Barrier Board

Unknown

University Products

Unsuitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

Acid-free, lignin-free, buffered (3% CaCO3) pH 8.5 40 and 60 pt. board

board

Bainbridge Alpharag Artcare Black Buffered

Nielsen Bainbridge

Unknown

Unsuitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

100% virgin alpha-cellulose fiber with zeolites, 3-5% buffer to pH 8.9

board

Rising Photomount Board White Unbuffered

Legion Paper

Unknown

Suitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

non-buffered 100% cotton board, acid and lignin free

board

Rising Museum Board Antique Buffered

Legion Paper

Unknown

Unsuitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

acid-free, neutral pH, buffered with calcium carbonate

board

Bainbridge Alpharag Artcare Colonial Cream

Nielsen Bainbridge

Unknown

Unsuitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

100% virgin alpha-cellulose fiber with zeolites, 3-5% buffer to pH 8.9

board

Black Volara

Sekisui Voltek

Unknown

Suitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

closed cell foam sheet

foam

White Volara

Sekisui Voltek

Unknown

Suitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

closed cell foam sheet

foam

White Volara, 10 Years Old

Sekisui Voltek

Unknown

Suitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

10 year old sample

closed cell foam sheet

foam

Mylar, 0.0005 Mm

Unknown

Suitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

clear polyester film

Clear

film, plastic

Expanded Pvc Foam Sheet 19 Mm Thick Celtec

Vycom

Ocip

Unsuitable

2015-06-01

Autry

Oddy test

none

PVC White

board

none

Expanded Pvc Foam Sheet 12 Mm Thick Celtec

Vycom

Ocip

Temporary

2015-06-01

Autry

Oddy test

Temp use, no contact with objects

PVC White

board

none

Celtec

Vycom

Ocip

Unsuitable

2014-12-01

Autry

Oddy test

Bought December 2013.

PVC White

board

none

Sintra Or Celtec

3A Composites or Vycom

Ocip

Unsuitable

2014-12-01

Autry

Oddy test

Bought April 2013.

PVC White

board

none

Freefoam Pvc 10 Mm Ordered In 2013

Jain Americas

Laird Plastics

Unsuitable

2014-12-01

Autry

Oddy test

Test 3 of 3

PVC , White, 48"x96"

board

none

Freefoam Pvc 10 Mm Ordered In 2013

Jain Americas

Laird Plastics

Unsuitable

2024-12-21

Autry

Oddy test

The pH of water in control: 5.5-6, in test material: 8.5. Test 2 of 3

PVC , White, 48"x96"

board

none

Freefoam Pvc 10 Mm Ordered In 2013

Jain Americas

Laird Plastics

Unsuitable

2024-12-21

Autry

Oddy test

The pH of water in control: 8, in test material: 9. Test 1 of 3

PVC White

board

none

Freefoam Pvc 13 Mm Ordered In 2013

Jain Americas

Laird Plastics

Unsuitable

2014-12-01

Autry

Oddy test

Test 3 of 3

PVC , White, 48"x96"

board

none

Freefoam Pvc 13 Mm Ordered In 2013

Jain Americas

Laird Plastics

Unsuitable

2024-12-21

Autry

Oddy test

The pH of water in control: 5.5-6, in test material: 8.5. Test 2 of 3

PVC, White, 48"x96"

board

none

Freefoam Pvc 13 Mm Ordered In 2013

Jain Americas

Laird Plastics

Unsuitable

2024-12-21

Autry

Oddy test

material absorbed all the water. Test 1 of 3

PVC BLUE, DARK

board

none

Expanded Closed-cell Polyvinyl Chloride ( Pvc) Material Similar To Sintra

Unknown

Laird Plastics

Suitable

2024-12-21

Autry

Oddy test

Test periodically

PVC White

board

none

6 Mm"Sintra"

Unknown

Laird Plastics

Suitable

2024-12-21

Autry

Oddy test

Test periodically. The pH of water before test: 5.5-6, after test: 7.5-8; don't use in contact with object

PVC White

board

Alucore, Platinum White

3A Composites

Temporary

2013-06-26

BM

Oddy test

PREP/Drying time: N/A, test #7889

POWDER COATED ALUMINIUM HONEYCOMB BOARD WITH PVDF LACQUER, WHITE,

board

none

Forex Classic, 5mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8019

PVC WHITE,

board

none

Forex Color, Black 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8018

PVC BLACK,

board

none

Forex Color, Blue 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8015

PVC BLUE,

board

none

Forex Color, Dark Blue 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8016

PVC BLUE, DARK,

board

none

Forex Color, Dark Yellow 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8011

PVC YELLOW DARK,

board

none

Forex Color, Green 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8014

PVC GREEN,

board

none

Forex Color, Grey 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8017

PVC GREY,

board

none

Forex Color, Orange 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8012

PVC ORANGE,

board

none

Forex Color, Red 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8013

PVC RED,

board

none

Forex Color, Yellow 3Mm

3A Composites

Suitable

2013-09-16

BM

Oddy test

PREP/Drying time: N/A, test #8010

PVC YELLOW,

board

none

Forex Print,

3A Composites

Baf Graphics

Suitable

2010-09-16

BM

Oddy test

PREP/Drying time: N/A, test #6988

POLYSTYRENE, WHITE,

White

board

none

Dibond, British Green

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6577

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, GREEN,

Green

board

none

Dibond, Butlerfinish

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6581

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER,

Silver

board

none

Dibond, Butlerfinish Copper

3A Composites

Selectaplas Limited

Suitable

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6583

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, COPPER,

Copper

board

none

Dibond, Butlerfinish Gold

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6582

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, GOLD,

Gold

board

none

Dibond, Butlerfinish Steel

3A Composites

Selectaplas Limited

Suitable

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6571

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER,

Silver

board

none

Dibond, Mayan Gold Metallic

3A Composites

Selectaplas Limited

Suitable

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6580

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, GOLD,

Gold

board

none

Dibond, Mirror

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6584

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER,

Silver

board

none

Dibond, Ral 1015

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6574

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, YELLOW,

Yellow

board

none

Dibond, Ral 1023

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6573

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, RED,

Red

board

none

Dibond, Ral 3020

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6572

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, WHITE,

White

board

none

Dibond, Ral 5002

3A Composites

Selectaplas Limited

Suitable

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6575

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, CREAM,

Cream, White

board

none

Dibond, Ral 5002

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6576

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, BLUE,

Blue

board

none

Dibond, Ral 9005

3A Composites

Selectaplas Limited

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6578

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, BLACK,

Black

board

none

Dibond, Ral 9006

3A Composites

Selectaplas Limited

Suitable

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6579

POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER, SAMPLE MELTED, MAY ACCOUNT FOR TEMPORARY RATING

Silver

board

none

Alucore, 1-type Polyester Lacquer

3A Composites

Unknown

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6587

ALUMINIUM, POLYESTER LACQUER, SILVER,

board

none

Alucore Base, Mill Finish

3A Composites

Unknown

Suitable

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6586

ALUMINIUM, SILVER,

board

none

Foam-x,

3A Composites

Unknown

Unsuitable

2010-06-08

BM

Oddy test

PREP/Drying time: N/A, test #6850

POLYSTYRENE CORE WITH COATED MULTY-LAYERED PAPER LINERS, WHITE,

White

board

none

Forex Classic,

3A Composites

Unknown

Suitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6593

PVC BLACK,

board

none

Forex Smart,

3A Composites

Unknown

Suitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6591

UV RESISTANT POLYSTYRENE SUFACE AND POLYSTYRENE CORE, WHITE,

board

none

Gatorfoam,

3A Composites

Unknown

Unsuitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6595

POLYSTYRENE CORE, UREA RESIN SURFACE, WHITE,

White

board

none

Gatorfoam,

3A Composites

Unknown

Unsuitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6602

POLYSTYRENE CORE WITH RESIN INPREGNATED LINERS, BLACK,

Black

board

none

Hylite,

3A Composites

Unknown

Temporary

2009-08-05

BM

Oddy test

PREP/Drying time: N/A, test #6585

POLYPROPYLENE CORE, ALUMINIUM SKIN, SILVER, SLIGHT YELLOWISH HUE

Silver

board

none

Kapa Colour,

3A Composites

Unknown

Temporary

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6601

POLYSTYRENE CORE WITH COLOURED PLASTIC COATED LINERS, BLACK,

Black

board

none

Kapa Fix,

3A Composites

Unknown

Unsuitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6596

POLYSTYRENE CORE WITH ALUMINIUM REINFORCED LINERS, WHITE,

White

board

none

Kapa Line,

3A Composites

Unknown

Unsuitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6599

POLYSTYRENE CORE WITH CROMA-SUBSITUTE LINERS, WHITE,

White

board

none

Kapa Mount,

3A Composites

Unknown

Unsuitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6597

POLYSTYRENE CORE WITH ALUMINIUM REINFORCED LINERS, WHITE,

White

board

none

Kapa Plast,

3A Composites

Unknown

Suitable

2009-09-25

BM

Oddy test

PREP/Drying time: N/A, test #6611

POLYSTYRENE CORE WITH PLASTIC COATED CELLUCARTLON LINERS, WHITE,

White

board

none

Kapa Premium Poly Board,

3A Composites

Unknown

Suitable

2009-07-06

BM

Oddy test

PREP/Drying time: N/A, test #6545

POLYURETHANE AND PAPER, WHITE,

White

board

none

3A Composites

Unknown

Suitable

2012-09-26

NHM

Oddy test

None

Expanded PVC Bodard

wood alternative

n/a

Bumpons,

3M

Unsuitable

2011-03-16

BM

Oddy test

PREP/Drying time: STUCK TO ITSELF, test #7206

POLYURETHANE, CLEAR,

Clear

antislip/ antivibration

none

Bumpons (small), Sj530209 (w7.9 H2.2)

3M

Unsuitable

2011-08-25

BM

Oddy test

PREP/Drying time: STUCK TO THEMSELVES, test #7286

POLYURETHANE, CLEAR,

Clear

mount/ mount making

none

Bumpon Self Adhesive Bumpers

3M

Home Depot

Unsuitable

2012-01-10

CMA

Oddy test

none

Plasticizer-free urethane, A-20 Acrylic adhesive

polymer

none

Oxidation Arrest Paper

3M

Unknown

Temporary

1996-01-24

GCI

Oddy test

None

pollutant scavenger?

n/a

Sparkfast Lightweight Filler

3M

Unknown

Temporary

2005-08-22

GCI

Oddy test

None

spackle

n/a

Sparkfast Lightweight Filler

3M

Unknown

Temporary

2005-08-22

GCI

Oddy test

None

filler, spackle

n/a

Ptfe Tubing, Tw18 1.14 X 0.31mm

Adtech

Suitable

2009-04-13

BM

Oddy test

PREP/Drying time: N/A, test #6420

PTFE, CLEAR,

Clear

polymer

sleeving/ tubing

none

Ptfe Tubing (thick), Tw Series

Adtech

Suitable

2009-03-20

BM

Oddy test

PREP/Drying time: N/A, test #6329

POLYETRAFLUOROETHYLENE, CLEAR,

Clear

polymer

sleeving/ tubing

none

Aeroflex Epdm (ethylene Propylene Diene Monomer) Closed Cell Elastometric Thermal Insulation

Aeroflex

Airefrig Australia

Suitable

2006-01-01

NAA

PAT

none

7 mm thick

closed cell insulation, foam

n/a

Polypropylene 35 Mm Negative Page

Albox Australia

Suitable

1996-01-01

NAA

PAT

none

6 strip

polypropylene, protective plastic sheet

n/a

Polypropylene Box

Albox Australia

Suitable

1996-01-01

NAA

PAT

none

box, polypropylene

n/a

Polypropylene Box

Albox Australia

Suitable

2006-01-01

NAA

PAT

none

box, polypropylene

n/a

Polypropylene Photo Album Cover

Albox Australia

Suitable

2004-01-01

NAA

PAT

none

polypropylene

album, cover

n/a

Airex Rigid Foam, R82.60

Alcan Airex Ag

Unsuitable

2009-08-25

BM

Oddy test

PREP/Drying time: N/A, test #6604

RIGID POLYMER FOAM , CREAM,

Cream, White

foam

none

Archivart Interleaving Paper

Archivart

Zetta Florence

Suitable

1996-01-01

NAA

PAT

none

paper

n/a

Archivart Library Board

Archivart

Zetta Florence

Suitable

1996-01-01

NAA

PAT

none

grey, light

Gray, Light

board, paper

n/a

Archivart Photographic Storage Paper

Archivart

Zetta Florence

Suitable

1996-01-01

NAA

PAT

none

paper

n/a

Archivart Photo-tex Tissue

Archivart

Zetta Florence

Suitable

1997-01-01

NAA

PAT

none

paper, tissue

n/a

Antique Range Thickness 2800, 64934

Arquadia

Cxd

Suitable

2014-03-12

BM

Oddy test

PREP/Drying time: N/A, test #8159

MOUNTBOARD, BROWN,

board

none

Optix Offset Milli Vanilla

Australian Paper

Suitable

2000-01-01

NAA

PAT

none

110 gsm, paper

n/a

Reflex Archival (copypaper)

Australian Paper

Suitable

2004-01-01

NAA

PAT

none

copy, paper

n/a

Saxton Chardonnay Paper 140 Gsm

Australian Paper

Spicers

Suitable

2012-01-01

NAA

PAT

none

140 gsm

paper

n/a

Archival Folder Board(white)

Australian Paper

Zetta Florence

Suitable

2006-01-01

NAA

PAT

none

320 gsm

board, folder

n/a

Cotton Linter Paper

Australian Paper

Suitable

2004-01-01

NAA

PAT

none

cotton linter

paper

n/a

Fixit

Aves Studio

Suitable

2012-02-01

CMA

Oddy test

used for custom contoured mounts, not in direct contact with artwork

Aluminum/ two-part epoxy putty

epoxy putty, filler

none

Barex Resins Barrier, 4261 0.05 Mm

Barex Resins

Suitable

2010-04-09

BM

Oddy test

PREP/Drying time: N/A, test #6793

ACRYLONITRILE METHYL ACRYLATE COPOLYMER, CLEAR,

barrier

none

Bead Along, 19 Strand

Bead Along

Suitable

2009-10-08

BM

Oddy test

PREP/Drying time: N/A, test #6619

STEEL WIRE COATED IN NYLON, ,

fastener

none

Bead Along, 49 Strand

Bead Along

Temporary

2009-10-08

BM

Oddy test

PREP/Drying time: N/A, test #6620

STEEL WIRE COATED IN NYLON, ,

fastener

none

Bead Along, 7 Strand

Bead Along

Suitable

2009-10-08

BM

Oddy test

PREP/Drying time: N/A, test #6618

STEEL WIRE COATED IN NYLON, ,

fastener

none

Sticky Wax, 09-100

Benchmark Catalog

Unsuitable

2009-02-19

BM

Oddy test

PREP/Drying time: 48 HOURS, test #6235

WAX, CLEAR,

moulding material

none

Makrolon Uv Clear Sheet, 2099

Beyer

Amari Plastics

Suitable

2013-12-30

BM

Oddy test

PREP/Drying time: N/A, test #8132

POLYCARBONATE, CLEAR, SAMPLE MELTED, MAY ACCOUNT FOR TEMPORARY RATING

board

none

Foamalux, Gsm9100, Mic1300

Brett Martin

Suitable

2010-08-27

BM

Oddy test

PREP/Drying time: N/A, test #6924

PVC WHITE,

board

none

Master Flex, 460

Bsfa

Unsuitable

2012-03-20

BM

Oddy test

PREP/Drying time: 4 WEEKS, test #7422

POLYURETHANE, GREY,

Gray

flooring

none

Mastertop 1324, 1324

Bsfa

Unsuitable

2012-03-20

BM

Oddy test

PREP/Drying time: 4 WEEKS, test #7423

POLYURETHANE WITH EPOXY PRIMER, GREY,

Gray

flooring

none

Mastertop Tc441p, Tc441p

Bsfa

Suitable

2012-03-20

BM

Oddy test

PREP/Drying time: 8 WEEKS , test #7426

POLYURETHANE, GREY, STICKY DEPOSIT ON LEAD COUPON BUT NO CORROSION VISIBLE

Gray

flooring

none

Ucrete Mfa, Mfa

Bsfa

Suitable

2012-03-20

BM

Oddy test

PREP/Drying time: 4 WEEKS, test #7425

HYBRID POLYURETHANE, GREY,

flooring

none

Ucrete Mfas, Mfas

Bsfa

Suitable

2012-03-20

BM

Oddy test

PREP/Drying time: 4 WEEKS, test #7424

HYBRID POLYURETHANE ANTISTATIC, GREY,

flooring

none

Wedi Board, 6mm Ba6

Caesar Ceramics

Suitable

2009-07-29

BM

Oddy test

PREP/Drying time: N/A, test #6551

POLYSTYRENE CORE, POLYMER MODIFIED CEMENT AND GLASS FIBER, GREY,

Gray

board

none

Barrier Paper

Canson Australia (arjo Wiggins)

Suitable

1996-01-01

NAA

PAT

none

paper

n/a

Library Board, Light Weight

Canson Australia (arjo Wiggins)

Suitable

2003-01-01

NAA

PAT

none

lightweight

board

n/a

Canson Conservation Board

Canson Australia (arjo Wiggins)

The Heirloom Boxcompany

Suitable

2003-01-01

NAA

PAT

none

board

n/a

Slide Sleeves

Champion Plastics

Suitable

1996-01-01

NAA

PAT

none

sleeve, slide

n/a

Chemodex L.Q.G. Moly Liquid Grease Aerosol,

Chemodex

Unknown

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: 1 WEEK, test #8079

BUTANE, MINERAL OIL, MOLYBDENUM DISULPHIDE, GELLED WITH CALCIUM LANOLATE, PROPELLANTS, BLACK, USED TO REPAIR FLOORS

misc

none

Peel Wallcovering Release Coat, Diluted

Clam-brummer

Clam-Brummer

Temporary

2013-09-10

BM

Oddy test

PREP/Drying time: 24 HOURS, test #7938

barrier

none

Gasket 8325

Clean Seal

Suitable

2011-07-07

CMA

Oddy test

8490, 8543, 8556, 8598, 8531; don't use in contact with object

black Silicone with 3m double-stick tape

Black

gasket

none

Gasket 8325

Clean Seal

Suitable

2012-05-15

CMA

Oddy test

other profiles of same material 8490, 8543, 8556, 8598, 8531

black Silicone gasket with 3m double-stick tape

Black

gasket, silicone

none

Archival Plus Polypropylene Storage Bag

Clear File

Suitable

1996-01-01

NAA

PAT

none

polypropylene

bag

n/a

Coated Fabric Tape, 7995c, 25mm, Ecru

Cole Fabrics

Temporary

2013-05-30

BM

Oddy test

PREP/Drying time: N/A, test #7857

POLYURETHAN COATED COTTON, CREAM,

Cream, White

misc

none

Textile Ribbon, 73969

Cole Fabrics

Temporary

2013-11-14

BM

Oddy test

PREP/Drying time: N/A, test #8056

POLYESTER TAFFETA, POLTURETHANE COATING, WHITE,

fastener

none

Acid-free Tissue Paper

Conservation By Design

Unknown

Suitable

2009-01-20

BM

Oddy test

test 6175

white paper

White

paper, tissue

n/a

Corrosion Intercept Coin Bag

Conservation By Design

Unknown

Suitable

2009-01-20

BM

Oddy test

orange/dark brown in color

polymer film with copper

Copper

bag, pollutants scavenger/filter

n/a

Polyester Pocket, 115 X 158 Mm Pyspol 0006

Conservation By Design

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: N/A, test #8081

POLYESTER, CLEAR

Clear

container

none

Premier Archival Box Board, 1300

Conservation By Design

Suitable

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7367

CARD, GREY,

Gray

board

none

Premier Fluted Box Board, Eb Flute 4.4mm

Conservation By Design

Suitable

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7368

CARD, GREY,

Gray

board

none

Timecare Heritage Museum Board, Unbuffered, 4 Ply, 1650 Microns, Dull White, Bdthmc3304

Conservation By Design

Suitable

2013-05-09

BM

Oddy test

PREP/Drying time: N/A, test #7850

PAPER, WHITE,

White

board

none

Timecare Range Museum Board , C3311, 1650 Microns

Conservation By Design

Suitable

2014-03-12

BM

Oddy test

PREP/Drying time: N/A, test #8161

PAPER, BLACK,

Black

board

none

Tycore Board, 12mm

Conservation By Design

Suitable

2014-01-16

BM

Oddy test

PREP/Drying time: N/A, test #8138

BUFFERED ARCHIVAL PAPER, WHITE,

White

board

none

Whisper Tissue Remoistenable Starch Coated Japanese Paper, Pajapl7910

Conservation By Design

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: N/A, test #8082

TOSA KOZO PAPER COATED WITH TAPIOCA STARCH ADHESIVE, WHITE, LIGHTWEIGHT SAMPLE

paper

none

Acid Free Tissue Paper

Conservation By Design

Suitable

2009-01-20

BM

Oddy test

PREP/Drying time: N/A, test #6175

TISSUE PAPER, WHITE, LIGHTWEIGHT SAMPLE

paper

none

Ecophant Super Mill Board Lydamore, Bdsmbe1171 1.1 Mm

Conservation By Design

Suitable

2010-05-28

BM

Oddy test

PREP/Drying time: N/A, test #6819

ACID-FREE BOARD, GREEN,

board

none

Ecophant Super Mill Board Lydamore, Bdsmbe1571 1.5 Mm

Conservation By Design

Suitable

2010-05-28

BM

Oddy test

PREP/Drying time: N/A, test #6820

ACID-FREE BOARD, GREEN,

board

none

Heritage Museum Board, A3311 550 Microns

Conservation By Design

Suitable

2009-06-09

BM

Oddy test

PREP/Drying time: N/A, test #6480

Black

board

none

Heritage Museum Board, D4711 2200 Microns

Conservation By Design

Suitable

2009-06-09

BM

Oddy test

PREP/Drying time: N/A, test #6479

Black

board

none

Silicone Vegetable Parchment Release Paper,

Conservation By Design

Suitable

2010-05-28

BM

Oddy test

PREP/Drying time: N/A, test #6821

SILICONE ON PAPER, WHITE, WHITE LINING

White

film

none

Corrosion Intercept Foam

Conservation By Design

Unknown

Suitable

2009-01-20

BM

Oddy test

orange/dark brown color

polymer foam with copper particles

Copper

foam, pollutant scavenger/filter

n/a

Corrosion Intercept Foam

Conservation By Design

Unknown

Suitable

2009-01-20

BM

Oddy test

orange/dark brown color

polymer foam with copper particles

Copper

foam, pollutant scavenger/filter

n/a

Tycore Board

Conservation By Design

Unknown

Suitable

2014-01-16

BM

Oddy test

none

12 mm, 2G, white buffered archival paper

board, paper reinforced

n/a

Corex Polypropylene Fluteboard (grey)

Corex Plastics

Suitable

1996-01-01

NAA

PAT

none

grey

Gray

board, fluted polypropylene

n/a

Needled Polyester,

Cowens

Temporary

2009-01-22

BM

Oddy test

PREP/Drying time: N/A, test #6140

POLYESTER, WHITE,

White

padding

none

Polyester Wadding, 202

Cowens

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7469

POLYESTER, WHITE,

White

padding

none

Polyester Wadding, 402

Cowens

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7467

POLYESTER, WHITE,

White

padding

none

Polyester Wadding, Ultrasoft

Cowens

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7468

POLYESTER, WHITE,

White

padding

none

Honeycombed Polypropylene T2 Cases,

Cp Cases

Suitable

2009-07-06

BM

Oddy test

PREP/Drying time: N/A, test #6548

POLYPROPYLENE, BLACK,

Black

container

none

Honeycombed Polypropylene T2 Cases,

Cp Cases

Suitable

2009-07-06

BM

Oddy test

PREP/Drying time: N/A, test #6549

POLYPROPYLENE, BLUE,

Blue

container

none

Honeycombed Polypropylene T2 Cases,

Cp Cases

Suitable

2009-07-06

BM

Oddy test

PREP/Drying time: N/A, test #6550

POLYPROPYLENE, RED,

Red

container

none

Wonderflex,

Dazan Fabrics

Dazian Fabrics

Suitable

2013-07-08

BM

Oddy test

PREP/Drying time: N/A, test #7902

POLYCAPROL ACETATE, POLYSTYRENE, EVA FILM POLYESTER FIBRE, CREAM,

mount/ mount making

none

Silicone Gasket

Delta Design

Unknown

Suitable

2000-09-19

GCI

Oddy test

None

gasket

n/a

Depron

Depron Foam

Unknown

Suitable

2009-01-20

BM

Oddy test

test 6171

white polystyrene foam

White

foam

n/a

Ethafoam, 900

Dow Chemical Company

Dow Chemical

Suitable

2009-02-09

BM

Oddy test

PREP/Drying time: N/A, test #6280

HDPE, WHITE,

White

foam

none

Silastic P1 Casting Silicone, P-1

Dow Corning

Suitable

2010-12-07

BM

Oddy test

PREP/Drying time: 12 HOUR CURE, test #7064

SILICONE, WHITE,

White

antislip/ antivibration

none

Silastic P1 Casting Silicone, P-1

Dow Corning

Suitable

2010-12-07

BM

Oddy test

PREP/Drying time: 12 HOUR CURE, test #7065

SILICONE, BLACK,

Black

antislip/ antivibration

none

Ethafoam 220, Polyethylene Foam, Closed Cell

Dunlop Foams

Suitable

2006-01-01

NAA

PAT

none

100 mm thick

closed cell polyethylene, foam

n/a

Eva 30

Dunlop Foams

Suitable

2006-01-01

NAA

PAT

none

15 mm thick (Code Q86454)

ethylene vinyl acetate, foam

n/a

Eva 45

Dunlop Foams

Suitable

2006-01-01

NAA

PAT

none

11 mm thick, cream

ethylene vinyl acetate, foam

n/a

3 Panels

DuPont

Unknown

Unsuitable

1991-03-12

GCI

Oddy test

None

panel

n/a

Ptfe Sheet 'relic Wrap',

DuPont

Screwfix Direct

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7473

PTFE, WHITE, LIGHTWEIGHT SAMPLE

White

mount/ mount making

none

Corian,

DuPont

Unknown

Suitable

2009-04-13

BM

Oddy test

PREP/Drying time: N/A, test #6402

ACRYLIC RESIN WITH FILLERS, WHITE,

board

none

Ptfe Thread Seal Tape, 12mm X 0.075mm

DuPont

Dupont Screw Fix Direct

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7472

PTFE, WHITE, LIGHTWEIGHT SAMPLE

White

mount/ mount making

none

Polylight,

Earlsmann

Suitable

2010-06-08

BM

Oddy test

PREP/Drying time: N/A, test #6844

ACRYLIC, CLEAR,

board

none

Fingeblobbs, Pd2010

Fingeblobbs

Temporary

2009-04-14

BM

Oddy test

PREP/Drying time: STUCK TO ITSELF, test #6401

POLYURETHANE, CLEAR,

Clear

antislip/ antivibration

none

Showcase Seal 'd' ,

Florea D.Sign

Suitable

2012-12-04

BM

Oddy test

PREP/Drying time: N/A, test #7659

SILICON RUBBER, BLACK, SAMPLE DID NOT DRY (DESIGNED NOT TO)

Black

seal

none

Showcase Seal 'd' With Flange,

Florea D.Sign

Suitable

2012-12-04

BM

Oddy test

PREP/Drying time: N/A, test #7660

SILICON RUBBER, BLACK, SAMPLE DID NOT DRY (DESIGNED NOT TO)

Black

seal

none

Flugger,

Flügger

Unknown

Suitable

2011-08-11

BM

Oddy test

PREP/Drying time: 2 WEEKS, test #7302

WHITE, GREY WITH BLUE SWIRLS

White

moulding material

none

Foam, Ft-s170/30

Foam Techniques

Unknown

Suitable

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7374

Gray

foam

none

Foam, Ft-s180/30 Uv

Foam Techniques

Unknown

Suitable

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7373

WHITE,

White

foam

none

Foam, Fts-hlb

Foam Techniques

Unknown

Unsuitable

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7384

POLY URETHANE FOAM, GREY,

foam

none

Westbond Carpet, N9733

Forbo Flooring Systems

Unknown

Temporary

2013-11-14

BM

Oddy test

PREP/Drying time: N/A, test #8057

POLYAMIDE PILE, RECYCLED VINYL BACKING, PURPLE, DARK,

flooring

none

Formica, Ocean Grey F7853 Mat

Formica

Unknown

Suitable

2013-04-18

BM

Oddy test

PREP/Drying time: N/A, test #7788

RESIN IMPREGNATED PAPER, GREY,

Gray

board

none

Fuji Xerox – 'gold'

Fuji Xerox Australia

Suitable

1999-01-01

NAA

PAT

none

copy, paper

n/a

Fuji Xerox – 'x'

Fuji Xerox Australia

Suitable

1999-01-01

NAA

PAT

none

copy, paper

n/a

8mm Double Wall Polycarbonate Panel

Gallina USA

Unknown

Suitable

2009-12-09

CMA

Oddy test

none

Polycarbonate panel

board, corrugated

none

Polycarbonate Channel

Gallina USA

Unknown

Suitable

2009-12-09

CMA

Oddy test

none

Polycarbonate

board, channeled

none

Garfilm Emcl (polyethylene Terephthalate Film)

Garware Polyester

Multapex

Suitable

2006-01-01

NAA

PAT

none

film, polyethylene terephtalate

n/a

Garfilm Emsc Pt077

Garware Polyester

Multapex

Suitable

2006-01-01

NAA

PAT

none

film, polyester

n/a

Click Netherfield Evolution Case Seal, Sea 210

GE Silicones

Ge Bayer Silicones

Suitable

2013-02-01

BM

Oddy test

PREP/Drying time: N/A, test #7704

SILICONE SEAL, CLEAR,

Clear

seal

none

Sylodyn,

Getzner

Suitable

2009-04-28

BM

Oddy test

PREP/Drying time: N/A, test #6424

POLYURETHANE FOAM, PURPLE,

Purple

foam

none

Sylodyn,

Getzner

Suitable

2009-04-28

BM

Oddy test

PREP/Drying time: N/A, test #6425

POLYURETHANE FOAM, GREEN,

Green

foam

none

Sylodyn,

Getzner

Suitable

2009-04-28

BM

Oddy test

PREP/Drying time: N/A, test #6426

POLYURETHANE FOAM, PINK,

Pink

foam

none

Sylomer ,

Getzner

Suitable

2009-04-28

BM

Oddy test

PREP/Drying time: N/A, test #6429

POLYURETHANE FOAM, BLACK,

Black

foam

none

Sylomer Hd,

Getzner

Suitable

2009-04-03

BM

Oddy test

PREP/Drying time: N/A, test #6354

POLYURETHANE FOAM, GREEN, DARK,

Dark, Green

foam

none

Sylomer Hd,

Getzner

Suitable

2009-04-03

BM

Oddy test

PREP/Drying time: N/A, test #6355

POLYURETHANE FOAM, GREEN,

Green

foam

none

Sylomer Hd,

Getzner

Suitable

2009-04-28

BM

Oddy test

PREP/Drying time: N/A, test #6423

POLYURETHANE FOAM, BLUE, LIGHT,

Blue, Light

foam

none

Geko Tape Nanoplast, 7014-00 (3098) 140711-1g1

Gottlieb Binder Gmbh

Suitable

2012-10-02

BM

Oddy test

PREP/Drying time: WASHED, test #7642

SILICON, CLEAR,

Clear

fastener

none

Gratnells Lidded Tray, No F1t

Gratnells

Suitable

2013-03-29

BM

Oddy test

PREP/Drying time: N/A, test #7748

POLYPROPYLENE, CLEAR,

Clear

container

none

Anti - Static Cleaner, Scva

Hammond Chemicals

Suitable

2009-11-30

BM

Oddy test

PREP/Drying time: SPRAYED ON, DRIED 24 HOURS, test #6690

Clear

cleaning

none

Harlequin High Shine Flooring,

Harlequin

Temporary

2010-05-28

BM

Oddy test

PREP/Drying time: BACK AND SIDES SEALED WITH AL TAPE, test #6813

LAMINATED PVS WITH POLYETHELYNE TEREPHTHALATE SURFACE, BLACK,

flooring

none

Mannequin, 6270-10-6273-10

Hindsgual

Temporary

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7376

PLASTIC AND PAINT, WHITE, LIGHTWEIGHT SAMPLE

mount/ mount making

none

Homasote, 440

Homasote

Unsuitable

2009-01-20

BM

Oddy test

PREP/Drying time: N/A, test #6166

RECYCLED NEWSPAPER, BROWN,

board

none

Intecel,

Inteplast Group

Unknown

Suitable

2012-06-29

BM

Oddy test

PREP/Drying time: N/A, test #7580

EXTRUDED PVC FOAM BOARD, WHITE,

board

none

500 Year Archival Photocopy Paper

International Paper

Jackaroo

Suitable

2006-01-01

NAA

PAT

none

watermarked,A4; 120 and 150 gsm

copy, paper

n/a

Archival Folder

International Paper

Jackaroo

Suitable

2006-01-01

NAA

PAT

none

(codes UFF701, UDW704, ULW705)

folder

n/a

Hi-yield Manila File Folder Board (white)

International Paper

Jackaroo

Suitable

2006-01-01

NAA

PAT

none

293 gsm(#180), 374 gsm (#180)

file folder white, folder

n/a

Hi-yield Manila File Folder Board(buff)

International Paper

Jackaroo

Suitable

2006-01-01

NAA

PAT

none

163gsm (#100), 202 gsm (#124), 293 gsm (#180), 374 gsm (#180)

board, file folder manila

n/a

Manila (buff) Filefolder

International Paper

Jackaroo

Suitable

2003-01-01

NAA

PAT

none

179, 244,293, 285, 325, 375 gsm

file, folder

n/a

White File Folder

International Paper

Jackaroo

Suitable

2003-01-01

NAA

PAT

none

179, 244,285, 325, 375 gsm

file, folder

n/a

Snap Rivet, Snr027-clr

Jet Press

Suitable

2010-12-07

BM

Oddy test

PREP/Drying time: N/A, test #7066

POLYCARBONATE, CLEAR,

fastener

none

Archival Cover Paper, 300 Gsm

John Purcell Paper

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: N/A, test #8086

, GREY, LIGHTWEIGHT SAMPLE

Gray

paper

none

Archive Folding Box Board, Blue Grey 1300 Micron

John Purcell Paper

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: N/A, test #8083

Gray

board

none

Canson Conservation Board, 6 Ply, 2400 Microns, Antique White, Cana2x

John Purcell Paper

Suitable

2013-05-09

BM

Oddy test

PREP/Drying time: N/A, test #7853

Cream

board

none

Canson Conservation Board, 8 Ply, 3000 Microns, White, Canw30

John Purcell Paper

Suitable

2013-05-09

BM

Oddy test

PREP/Drying time: N/A, test #7854

WHITE,

White

board

none

Heritage Conservation Board, Buffered, 3 Ply, 1380 Microns, Ivory, Heciv2

John Purcell Paper

Suitable

2013-05-09

BM

Oddy test

PREP/Drying time: N/A, test #7851

Cream

board

none

Heritage Conservation Board, Buffered, 3 Ply, 1380 Microns, White, Hecw2

John Purcell Paper

Suitable

2013-05-09

BM

Oddy test

PREP/Drying time: N/A, test #7852

WHITE,

White

board

none

Heritage Museum Board, Buffered, 2200 Microns

John Purcell Paper

Suitable

2013-05-09

BM

Oddy test

PREP/Drying time: N/A, test #7856

100% COTTON, WHITE,

board

none

Heritage Museum Board, Buffered, 6 Ply, 2200 Microns, Cream, Hemc5

John Purcell Paper

Suitable

2013-05-09

BM

Oddy test

PREP/Drying time: N/A, test #7855

100% COTTON, CREAM,

board

none

Heritage Wood-free Paper, Book White 160 Gsm

John Purcell Paper

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: N/A, test #8085

WHITE, LIGHTWEIGHT SAMPLE

White

paper

none

Meridian High Density Board, 2800 Micron

John Purcell Paper

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: N/A, test #8084

Brown, light

board

none

Superzote, Em26

Kewell Vonverters

Kewell Vonverters.

Suitable

2009-04-03

BM

Oddy test

PREP/Drying time: N/A, test #6353

FOAM, BLACK,

Black

foam

none

Kilner Jar Seal,

Kilner

Suitable

2013-05-30

BM

Oddy test

PREP/Drying time: N/A, test #7866

RUBBER , ORANGE, TO BE APPLIED ON A LAYER OF PARALOID B72

Orange

seal

none

Purple Nitrile Gloves

Kimberly-Clark

Starnes

Unsuitable

2013-05-10

CMA

Oddy test

none

nitrile

barrier, glove

Komacel,

Kömmerling

Unknown

Suitable

2012-06-29

BM

Oddy test

PREP/Drying time: N/A, test #7579

EXTRUDED PVC FOAM BOARD, WHITE,

board

none

Le Parfait Rubber Seals Kilner Jars, 85mm

Le Parfait

Unknown

Suitable

2013-04-18

BM

Oddy test

PREP/Drying time: N/A, test #7789

RUBBER?, RED,

Red

seal

none

Clear Sav Self Adhesive Film,

Avery Dennison

Leach Graphics

Temporary

2009-12-16

BM

Oddy test

PREP/Drying time: STUCK TO ITSELF, test #6760

VINYL AND PVC WITH ACRYLIC ADHESIVE, CLEAR,

film

none

Polyfilla,

Lepage Products

Unknown

Unsuitable

2011-08-11

BM

Oddy test

PREP/Drying time: 2 WEEKS, test #7307

WHITE,

White

moulding material

none

Bristle Strip, 6.7 Ec Ss

Lista Uk

Suitable

2013-03-11

BM

Oddy test

PREP/Drying time: ADHESIVE STUCK TO MELINEX, test #7732

BRISTLES, ADHESIVE AND SILICON GASKET, BROWN,

seal

none

Ram Foam, Ld33

Lista Uk/ Ramplast

Suitable

2009-12-23

BM

Oddy test

PREP/Drying time: N/A, test #6749

POLYETHELENE, WHITE,

White

foam

none

West Foam Board,

London Graphics

London Graphics Centre

Suitable

2009-07-06

BM

Oddy test

PREP/Drying time: N/A, test #6546

POLYURETHANE AND PAPER, WHITE,

White

board

none

Somerset Textured Paper, Radiant White 225 G/m2

London Graphics Centre?

Suitable

2014-01-16

BM

Oddy test

PREP/Drying time: N/A, test #8137

100% COTTON, WHITE, LIGHTWEIGHT SAMPLE

paper

none

Corrosion Intercept Foil,

Intercept Technologies

Lucent Technologies

Suitable

2009-02-12

BM

Oddy test

PREP/Drying time: N/A, test #6200

POLYETHYLENE WITH COPPER, ORANGE, DARK, SAMPLE DID NOT DRY (DESIGNED NOT TO)

Dark, Orange

pollution control

none

Perspex Colours, Opaque, 4494, 5mm

Lucite International

Unknown

Suitable

2013-09-10

BM

Oddy test

PREP/Drying time: N/A, test #8006

ACRYLIC (POLYMETHYLMETHACRYLATE), RED, DARK,

board

none

Perspex Colours, Opaque, 744, 3Mm

Lucite International

Unknown

Temporary

2013-09-10

BM

Oddy test

PREP/Drying time: N/A, test #8005

ACRYLIC (POLYMETHYLMETHACRYLATE), BLUE, DARK,

board

none

Perspex, 9t30 3Mm

Lucite International

Lucite Solutions

Suitable

2013-07-08

BM

Oddy test

PREP/Drying time: N/A, test #7901

ACRYLIC, EXTRUDED , CLEAR,

board

none

Metallic' Cast Acrylic Sheet, 4260 Antique Gold

Madreperla S.P.A.

Unknown

Suitable

2013-09-10

BM

Oddy test

PREP/Drying time: N/A, test #8004

ACRYLIC (POLYMETHYLMETHACRYLATE), GOLD,

board

none

Meadows & Passmore Mainspring Grease, 0604 012015

Meadows & Passmore

Unknown

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: 1 WEEK, test #8078

CLEAR, BEIGE WITH RED SWIRLS

Clear

misc

none

Blunder Pest Trap,

Mitie

Suitable

2013-02-25

BM

Oddy test

PREP/Drying time: N/A, test #7712

PAPER AND ADHESIVE, WHITE, LIGHTWEIGHT SAMPLE

pest control

none

Moebius Natural Grease, 8201

Moebius

Unknown

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: 1 WEEK, test #8076

MINERAL OILS, VASELINE GREASE, NEATSFOOT OIL, MOLYBDANE DISULPHIDE, BLACK,

misc

none

Moebius Natural Grease, 8301

Moebius

Unknown

Suitable

2013-12-12

BM

Oddy test

PREP/Drying time: 1 WEEK, test #8077

MINERAL OILS, VASELINE GREASE, NEATSFOOT OIL, MOLYBDANE DISULPHIDE, BLACK,

misc

none

Musion Eyliner Foil,

Musion Events

Musion Events Limited

Suitable

2010-03-01

BM

Oddy test

PREP/Drying time: N/A, test #6775

Clear

film

none

Window Film, C-171

Nakagawa Chem.

Nakagawa Chem

Unsuitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7112

Clear

film

none

Window Film, C-181

Nakagawa Chem.

Nakagawa Chem

Unsuitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7113

CLEAR, North American version of Forex Classic board

Clear

film

none

Wallpaper, Sc622

Nip Corporation

Suitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7115

CELLULOSE, GREY, LIGHTWEIGHT SAMPLE

paper

none

Wallpaper, Sc626

Nip Corporation

Suitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7114

CELLULOSE, BLACK, LIGHTWEIGHT SAMPLE

paper

none

Wallpaper, Sc665

Nip Corporation

Suitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7116

CELLULOSE, BLUE, LIGHT, LIGHTWEIGHT SAMPLE

paper

none

Nomapack Foam

Nmc

Britestar

Suitable

2012-01-01

NAA

PAT

none

grey, blue (PAD Profile), bright yellow (WS ee*264 Edge Pad)

Blue, Gray

foam

n/a

Walnut

Unknown

Frame Supplier

Unsuitable

2012-01-10

CMA

Oddy test

none

wood

none

Walnut Wood

Unknown

Frame Supplier

Unsuitable

2012-01-10

CMA

Oddy test

for comparison to coated Walnut

wood

none

Silicone Novabond 2, S29306000

Novabond

Unknown

Unsuitable

2009-01-20

BM

Oddy test

2 part silicone

black silicone sealant

Black

caulk or adhesive, sealant

n/a

Nu-alum

Nudo

Unknown

Unsuitable

2011-07-07

CMA

Oddy test

barrier to cover wood products or as alternative to wood

.13" aluminum bonded to plywood substrate

barrier, structural

none

Nu-alum (with Fabric Covering)

Nudo

Unknown

Unsuitable

2011-07-07

CMA

Oddy test

barrier to cover wood products or as alternative to wood

.13" aluminum bonded to plywood substrate

barrier, structural

none

Obomodulan Tooling Board 500 Magma

OBO-Werke

Mccausey Lumber

Suitable

2011-01-20

CMA

Oddy test

alternative to wood for risers/blocks, backboards and decks

Polyurethane, medium density/pink

Pink

board, wood alternative

none

Ofrexs Ohp Permanent Pen,

Ofrexs

Suitable

2010-04-09

BM

Oddy test

PREP/Drying time: 2 HOURS, SUBSTRATE FULLY COVERED, test #6800

RED,

Red

misc

none

Crios Bag,

Orla Solutions

Suitable

2009-07-06

BM

Oddy test

PREP/Drying time: N/A, test #6544

COPPER IMPREGNATED POLYMER, CLEAR, TO BE APPLIED ON A LAYER OF PARALOID B72

pollution control

none

Crios Foam,

Orla Solutions

Suitable

2010-02-11

BM

Oddy test

PREP/Drying time: N/A, test #6766

COPPER IMPREGNATED POLYMER, PURPLE, DARK, SAMPLE DID NOT DRY (DESIGNED NOT TO)

pollution control

none

Palight, St-10

Palram

Suitable

2014-04-04

BM

Oddy test

PREP/Drying time: N/A, test #8179

FOAMED PVC SHEET, WHITE,

White

board

none

Clear Ldpe Continuous Roll

Pinpak–grayson Packaging

Suitable

2007-01-01

NAA

PAT

none

50 mm wide x 100 micron thick

film, low density polyethylene

n/a

Plascoat Vitroguard 12

Plascoat

Suitable

2011-01-11

CMA

Oddy test

barrier coating for brass mounts

modified polyolefins

barrier/padding

none

Modostuc, Interior

Plasveroi International

Unknown

Unsuitable

2011-08-11

BM

Oddy test

PREP/Drying time: 2 WEEKS, test #7306

WHITE,

White

moulding material

none

Polyflex Plus Pu, 7350 Lakeland Blue

Polyflor

Temporary

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7383

PVC WITH POLYURETHANE COATING, BLUE,

flooring

none

Polyflor 2000 Pur, 8500 Lace Blue

Polyflor

U

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7922

POLYURETHANE, GREY, LIGHT,

Gray, Light

flooring

none

Polyflor 2000 Pur, 8650 Wild Lilac

Polyflor

U

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7923

POLYURETHANE, BLUE, LIGHT,

Blue, Light

flooring

none

Polyflor 2000 Pur, 8850 Buckwheat

Polyflor

U

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7924

POLYURETHANE, BEIGE,

Beige

flooring

none

Polyflor 2000 Pur, 8150 Shadow

Polyflor

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7920

POLYURETHANE, GREY, DARK,

Dark, Gray

flooring

none

Polyflor 2000 Pur, 8300 Oak

Polyflor

Unknown

Temporary

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7921

POLYURETHANE, BEIGE,

Beige

flooring

none

Portex Tubing, 800/100/260

Portex

Consumables.com

Suitable

2013-11-28

BM

Oddy test

PREP/Drying time: N/A, test #8073

POLYETHYLENE, CLEAR,

Black

polymer

sleeving/ tubing

none

Posa Sr-70/t, Sr-70/t

Posa Spa

Suitable

2012-09-08

BM

Oddy test

PREP/Drying time: N/A, test #7602

SILICONE RUBBER, BLACK,

Black

seal

none

Posa Sr-70/t, Sr-70t

Posa Spa

Suitable

2012-10-28

BM

Oddy test

PREP/Drying time: N/A, test #7646

SILICONE RUBBER, CLEAR,

Clear

seal

none

Cellair (closed Cell Foam)

Precision Foam Manufacturing

Metro Foam Products

Suitable

1996-01-01

NAA

PAT

none

closed cell, foam

n/a

Archival Cloth Tape,

Preservation Equipment

Temporary

2010-04-09

BM

Oddy test

PREP/Drying time: N/A, test #6804

COTTON, BEIGE,

Beige

fastener

none

Alu-kraft Paper Barrier, 70545 20

Pure Nature

Temporary

2009-02-09

BM

Oddy test

PREP/Drying time: N/A, test #6277

ALUMINIUM FOIL WITH PAPER BACKING, SILVER,

barrier

none

Pure Aluminium Barrier Foil, 70542 20

Pure Nature

Suitable

2009-02-09

BM

Oddy test

PREP/Drying time: N/A, test #6278

ALUMINIUM, SILVER,

barrier

none

Foam Core Board

Quill Stationery Manufacturers

Suitable

2006-01-01

NAA

PAT

none

5 mm Gold OW (J)

Gold

board, composite, foam core

n/a

Mohawk Digital Paper

Raleighpaper

Rolls Filingsystem

Suitable

2005-01-01

NAA

PAT

none

paper

n/a

Really Useful Box - 1.6 Litre, 1.6 Litre

Really Useful Box Uk

Really Useful Box UK

Suitable

2013-03-29

BM

Oddy test

PREP/Drying time: N/A, test #7747

POLYPROPYLENE, CLEAR,

Clear

container

none

Really Useful Box - 9 Litre, Model No.287048

Really Useful Box Uk

Really Useful Box UK

Suitable

2013-03-29

BM

Oddy test

PREP/Drying time: N/A, test #7746

POLYPROPYLENE, CLEAR,

Clear

container

none

Polyester Boning, 4224

Rigilene

Unsuitable

2009-01-22

BM

Oddy test

PREP/Drying time: N/A, test #6138

POLYESTER, BLACK,

Black

mount/ mount making

none

Polyester Boning, 4224

Rigilene

Unsuitable

2009-01-22

BM

Oddy test

PREP/Drying time: N/A, test #6139

POLYESTER, WHITE,

White

mount/ mount making

none

Foamalux Ultra Foam, Gsm:2100 Mic:3000

Robert Horne Group

Suitable

2013-06-26

BM

Oddy test

PREP/Drying time: N/A, test #7892

PVC E FOAM, BLACK,

foam

none

Skybond Composite Acm Board, Jh-9185

Robert Horne Group

Temporary

2013-06-26

BM

Oddy test

PREP/Drying time: N/A, test #7888

COATED AL SKIN WITH PLASTIC CORE, BLACK,

board

none

Flowcrete Flowfresh Sl Anti Slip, Ral 7012 Ref A8447

Rpm Flowcrete

Suitable

2012-11-02

BM

Oddy test

PREP/Drying time: EDGES SEALED WITH ALUMINIUM TAPE, test #7648

SUPER PU ANTI SLIP (SILICA) FLOORING WITH PRIMER AND SELF SMOOTHING BASE LAYER, GREY,

flooring

none

Lexan Polycarbonate Film

Sabic Innovative Plastics

Mulford Plastics

Suitable

1996-01-01

NAA

PAT

none

film, polycarbonate

n/a

Shatterproof Film, Clm-2hc-r

Sansho

Sansho.

Unsuitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7111

Clear

film

none

Polyfelt Padding, T500 Tsl

Severnside Fabrics

Temporary

2009-01-22

BM

Oddy test

PREP/Drying time: N/A, test #6141

POLYFELT, WHITE,

White

padding

none

Polyfelt Padding, T600 Tsl

Severnside Fabrics

Temporary

2009-01-22

BM

Oddy test

PREP/Drying time: N/A, test #6142

POLYFELT, WHITE, LIGHTWEIGHT SAMPLE

White

padding

none

Polyfelt Padding, T700 Tsl

Severnside Fabrics

Temporary

2009-01-22

BM

Oddy test

PREP/Drying time: N/A, test #6143

POLYFELT, WHITE, LIGHTWEIGHT SAMPLE

White

padding

none

Polyfelt Padding, T900 Tsl

Severnside Fabrics

Temporary

2009-01-22

BM

Oddy test

PREP/Drying time: N/A, test #6144

POLYFELT, WHITE,

White

padding

none

Cotton Knit Pad, C/1180/kcp

Severnside Fabrics

Temporary

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7474

COTTON, CREAM,

Cream, White

padding

none

Polyfelt, Nt/1200/txl

Severnside Fabrics

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7476

POLYESTER, WHITE, LIGHTWEIGHT SAMPLE

White

padding

none

Polyfelt, T/4000/t51

Severnside Fabrics

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7475

POLYESTER, WHITE,

White

padding

none

Polyfelt, T/500/tcl

Severnside Fabrics

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7480

POLYESTER, WHITE, LIGHTWEIGHT SAMPLE

White

padding

none

Polyfelt, T/600/tcl

Severnside Fabrics

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7479

POLYESTER, WHITE, LIGHTWEIGHT SAMPLE

White

padding

none

Polyfelt, T/700/tcl

Severnside Fabrics

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7478

POLYESTER, WHITE,

White

padding

none

Polyfelt, T/900/tcl

Severnside Fabrics

Suitable

2012-03-30

BM

Oddy test

PREP/Drying time: N/A, test #7477

POLYESTER, WHITE, LIGHTWEIGHT SAMPLE

White

padding

none

Flame Retardant Cushion Wrap,

Sfsl

Conservation Resources International

Suitable

2013-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7677

WHITE,

White

padding

none

Archival Liner Board, Blue/grey

Shoalhaven Paper Mill

Australian Paper

Suitable

2009-01-01

NAA

PAT

none

blue/grey

Blue/Gray

board

n/a

Archival Liner Board

Shoalhaven Paper Mill

Australian Paper

Suitable

2009-01-01

NAA

PAT

none

board

n/a

Dim Out 7000 Range Blind, 41

Silent Gliss

Coniston

Suitable

2011-08-16

BM

Oddy test

PREP/Drying time: N/A, test #7314

PES, FLOCKED, GREY,

environmental control

none

Midnight Range Blind, 608

Silent Gliss

Coniston

Unsuitable

2011-08-16

BM

Oddy test

PREP/Drying time: N/A, test #7313

GLASS FIBRE COATED AND FLOCKED, GREY,

environmental control

none

Super Clear Sheet 0.8mm,

Silex

Unsuitable

2010-03-26

BM

Oddy test

PREP/Drying time: N/A, test #6788

SILICONE, CLEAR,

Clear

film

none

Super Clear Sheet 0.8mm,

Silex

Suitable

2010-05-28

BM

Oddy test

PREP/Drying time: N/A, test #6824

SILICONE, WHITE,

White

film

none

Archival Corrugated (blue/grey) Board

Suitable

2012-09-21

BM

Oddy test

PREP/Drying time: N/A, test #7621

PVC WHITE,

board

none

Siroflex Trade Strength Glass Celaner, Sx Glass Cleaner

Siroflex

Unknown

Suitable

2013-02-25

BM

Oddy test

PREP/Drying time: BUFFED TO REMOVE RESIDUE, test #7708

PROPANOL AND BUTOXYETHANOL, BLUE,

Blue

cleaning

none

Sorbothane, 30 Duro 0204050-30-10

Sorbothane

Unknown

Temporary

2013-04-18

BM

Oddy test

PREP/Drying time: N/A, test #7774

POLUYURATHANE, BLACK,

antislip/ antivibration

none

Sorbothane, 50 Duro 0204062-50-10

Sorbothane

Unknown

Suitable

2013-04-18

BM

Oddy test

PREP/Drying time: N/A, test #7775

POLUYURATHANE, BLACK,

antislip/ antivibration

none

Sorbothane, 70 Duro 0204050-70-10

Sorbothane

Unknown

Temporary

2013-04-18

BM

Oddy test

PREP/Drying time: N/A, test #7776

POLUYURATHANE, BLACK,

antislip/ antivibration

none

Lumicolour Permanent 's', Art. No.: 313-9, Ean 4007817 308820

Staedtler

Suitable

2011-08-11

BM

Oddy test

PREP/Drying time: 2 HOURS, FULLY COLOURED SUBSTRATE, test #7311

BLACKTOP LAYER FOR MASTERTOP 1324

STILL SMELLED AFTER 4 WEEKS

misc

none

Lumicolour Special 'f', Art. No.: 319 F-9, Ean 4007817 319079

Staedtler

Unsuitable

2011-08-11

BM

Oddy test

PREP/Drying time: 2 HOURS, FULLY COLOURED SUBSTRATE, test #7312

Black

misc

none

Plastic Box (with Top), 6147008

Stewart

Suitable

2009-02-09

BM

Oddy test

PREP/Drying time: N/A, test #6281

POLYSTYRENE, CLEAR,

Clear

container

none

Stop G-p,

Stopgap

Suitable

2009-03-20

BM

Oddy test

PREP/Drying time: N/A, test #6328

POLYCARBONATE WITH PLASTISIZERS , CLEAR,

seal

none

Sugru, F.03

Formformform

Unknown

Temporary

2011-02-17

BM

Oddy test

PREP/Drying time: 48 HOURS, test #7137

SILICONE, RED,

Red

moulding material

none

Decorative Film, Ps-948

Sumitomo

Suitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7127

PVC CLEAR,

film

none

Depron,

Technisches Merblatt - Glutolin

Suitable

2009-01-20

BM

Oddy test

PREP/Drying time: N/A, test #6171

POLYSTYRENE, WHITE,

White

foam

none

Gel Pac Membrane Box (outer Case), Mb-15ot/100

Teltec

Suitable

2013-02-01

BM

Oddy test

PREP/Drying time: N/A, test #7702

Clear

container

none

Gelpack Membrane Box (membrane), Mb-15ot/101

Teltec

Suitable

2013-02-01

BM

Oddy test

PREP/Drying time: N/A, test #7703

Clear

container

none

Lexan, 10mm

The Plastic Shop

Temporary

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7370

POLYCARBONATE SHEET, WHITE,

board

Lexan, 5mm

The Plastic Shop

Temporary

2012-01-20

BM

Oddy test

PREP/Drying time: N/A, test #7371

POLYCARBONATE SHEET, CLEAR,

board

none

Antique Range Thickness 2800, 64858

Timecase

Cxd

Suitable

2014-03-12

BM

Oddy test

PREP/Drying time: N/A, test #8160

MOUNTBOARD, BLACK,

board

none

Film Canister

Tuscan Industries

Suitable

1997-01-01

NAA

PAT

none

(blue) fire retardant

Blue

film canister

n/a

Film Canister

Tuscan Industries

Suitable

1997-01-01

NAA

PAT

none

polypropylene (grey):MB 91603A, MB 91603B, MB 91603C, MB 91603D, MB 91603E, MB 91603F

Gray

film canister

n/a

Polypropylene Film Canister, Round

Tuscan Industries

Suitable

1996-01-01

NAA

PAT

none

polypropylene, (grey, blue)

Blue, Gray

film canister

n/a

Polypropylene Film Canister, Square

Tuscan Industries

Suitable

1996-01-01

NAA

PAT

none

polypropylene (blue)

Blue

film canister

n/a

System Boxes,

Ultraplast-hofstatter & Ebbesen A/s

Suitable

2009-02-12

BM

Oddy test

PREP/Drying time: N/A, test #6198

POLYSTYRENE, CLEAR, needs label

Clear

container

none

Perspex, 1.5mm

Unknown

Amari Plastics

Suitable

2011-08-11

BM

Oddy test

PREP/Drying time: N/A, test #7310

ACRYLIC, EXTRUDED , CLEAR,

board

none

Corrosion Intercept Coin Bag,

Unknown

Conservation By Design

Suitable

2009-01-20

BM

Oddy test

PREP/Drying time: N/A, test #6159

POLYMER FILM WITH COPPER , ORANGE, DARK, LIGHTWEIGHT SAMPLE

Dark, Orange

pollution control

none

Corrosion Intercept Foam,

Unknown

Conservation By Design

Suitable

2009-01-20

BM

Oddy test

PREP/Drying time: N/A, test #6160

POLYMER FOAM WITH COPPER PARTICLES, ORANGE, DARK, LIGHTWEIGHT SAMPLE

Copper

pollution control

none

Jac Serialass Self Adhesive Vinyl Sheet, 7000d

Unknown

Display Ways

Suitable

2014-02-12

BM

Oddy test

PREP/Drying time: STUCK TO ITSELF, test #8148

VINYL ADHESIVE, CLEAR, WHITE LINING

film

none

Macal Glass Décor, 798-01

Unknown

Display Ways

Temporary

2014-02-12

BM

Oddy test

PREP/Drying time: STUCK TO ITSELF, test #8147

VINYL WITH ADHESIVE, GREY, LIGHT, WHITE LINING

film

none

Metamark Sign Vinyl 4 Series, M4-of Frost

Unknown

Display Ways

Suitable

2014-02-12

BM

Oddy test

PREP/Drying time: STUCK TO ITSELF, test #8149

VINYL WITH ADHESIVE, CLEAR, WHITE LINING

film

none

Ritrama - Pics Supreme Series Self Adhesive Vinyl Sheet, Cast Silver

Unknown

Display Ways

Temporary

2014-02-12

BM

Oddy test

PREP/Drying time: STUCK TO ITSELF, test #8146

VINYL ADHESIVE, GREY, LIGHT, WHITE LINING

film

none

Correx Board,

Unknown

Europoint Display

Suitable

2009-12-23

BM

Oddy test

PREP/Drying time: N/A, test #6742

POLYPROPYLENE, WHITE,

White

board

none

Excel Free Foam (ff),

Unknown

Holbourne Industrial Plastics

Temporary

2013-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7678

PVC FOAM BOARD, WHITE,

board

none

Excel Integral Foam (if),

Unknown

Holbourne Industrial Plastics

Suitable

2013-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7679

PVC FOAM BOARD, WHITE,

board

none

Corrugated Board, Bc, 0314107, 6.4 Mm Light Grey /natural White

Unknown

Klug

Suitable

2013-11-28

BM

Oddy test

PREP/Drying time: N/A, test #8068

CALCIUM CARBONATE BUFFERED BOARD, GREY, LIGHT,

board

none

Corrugated Board, Quality 021, E Flute, 02110x, 1.6 Mm, 560 G/m2, Light Grey/ Natural White

Unknown

Klug

Suitable

2013-11-28

BM

Oddy test

PREP/Drying time: N/A, test #8070

CALCIUM CARBONATE BUFFERED BOARD, GREY, LIGHT,

board

none

Corrugated Board, Quality 021, E Flute, 021147, 1.7 Mm, 680 G/m2, Grey Blue/ White

Unknown

Klug

Suitable

2013-11-28

BM

Oddy test

PREP/Drying time: N/A, test #8067

100% BLEACHED CELLULOSE, GREY, DARK,

board

none

Corrugated Board, Quality 031, B Flute, 03110x, 3 Mm, 570 G/m2, Light Grey/ Natural White

Unknown

Klug

Suitable

2013-11-28

BM

Oddy test

PREP/Drying time: N/A, test #8069

CALCIUM CARBONATE BUFFERED BOARD, GREY, LIGHT,

board

none

Corrugated Board, Quality 031, B Flute, 03147107, 3.1 Mm, 680 G/m2, Grey Blue/ Natural White

Unknown

Klug

Suitable

2013-11-28

BM

Oddy test

PREP/Drying time: N/A, test #8071

CALCIUM CARBONATE BUFFERED BOARD, GREY, DARK,

board

none

Vinyl-macal Sheeting,

Unknown

Mactac/baf Graphics

Suitable

2010-06-08

BM

Oddy test

PREP/Drying time: N/A, test #6845

VINYL WITH ACRYLIC ADHESIVE, WHITE,

film

none

Vinyl-macal Sheeting,

Unknown

Mactac/baf Graphics

Suitable

2010-06-08

BM

Oddy test

PREP/Drying time: N/A, test #6846

VINYL WITH ACRYLIC ADHESIVE, GREY,

film

none

Vinyl-macal Sheeting,

Unknown

Mactac/baf Graphics

Suitable

2010-06-08

BM

Oddy test

PREP/Drying time: N/A, test #6847

VINYL WITH ACRYLIC ADHESIVE, CREAM,

film

none

Vinyl-macal Sheeting,

Unknown

Mactac/baf Graphics

Suitable

2010-06-08

BM

Oddy test

PREP/Drying time: N/A, test #6848

VINYL WITH ACRYLIC ADHESIVE, SILVER,

film

none

Vinyl-macal Sheeting,

Unknown

Mactac/baf Graphics

Unsuitable

2010-06-08

BM

Oddy test

PREP/Drying time: N/A, test #6849

VINYL WITH ACRYLIC ADHESIVE, BLACK,

film

none

Foam , F104

Unknown

Pentonville

Suitable

2011-01-18

BM

Oddy test

PREP/Drying time: N/A, test #7107

POLYURETHANE, GREY,

Gray

foam

none

Vanguard Card, Vanguard, Celestial Blue, 380mic

Unknown

Ss Graphics/elliot Baxter

Suitable

2010-10-01

BM

Oddy test

PREP/Drying time: N/A, test #6993

CELLULOSE, BLUE, LIGHT, LIGHTWEIGHT SAMPLE

paper

none

Cellite Panel, 840

Unknown

Unsuitable

2013-11-28

BM

Oddy test

PREP/Drying time: EDGES TAPED WITH AL FOIL, test #8074

HONEYCOMB PANEL WITH PHENOLIC SKIN, BEIGE,

board

none

Cellite Panel, 920

Unknown

Suitable

2013-11-28

BM

Oddy test

PREP/Drying time: EDGES TAPED WITH AL FOIL, test #8075

NOMEX HONEYCOMB PANEL WITH CARBON SKIN, BLACK,

board

none

Contract 2600 Series Blackout Blind, 2603 Light Grey

Unknown

Temporary

2013-11-14

BM

Oddy test

PREP/Drying time: N/A, test #8058

100% POLYESTER, GREY, LIGHT,

environmental control

none

Dry Mount Photo Album

Unknown

Abbey Plastics Products

Suitable

2004-01-01

NAA

PAT

black page and interleaf

none

black page and interleaf

page, photo album

n/a

Semi-rigid Polypropylene

Unknown

Abbey Plastics Products

Suitable

2003-01-01

NAA

PAT

none

polypropylene, sheet

n/a

Photo Corners

Unknown

Albox Australia

Suitable

2004-01-01

NAA

PAT

none

250, LERO 81/03

photo corners

n/a

Paperboard Inserts

Unknown

Albox Australia

Suitable

2003-01-01

NAA

PAT

none

cream, black, white

board

n/a

Paperboard Inserts

Unknown

Albox Australia

Suitable

2003-01-01

NAA

PAT

none

cream, black, white

board

n/a

Unknown

Archival Survival

Suitable

2006-01-01

NAA

PAT

none

single and double wall

board, corrugated

n/a

Archival Corrugated Board, Blue/grey, Double Wall

Unknown

Archival Survival

Suitable

2012-01-01

NAA

PAT

none

(code BRDMUB); corrugated archival

board, cellulosic

n/a

Archival Corrugated Board, Blue/grey, Single Wall

Unknown

Archival Survival

Suitable

2012-01-01

NAA

PAT

none

(code BRDMUB); corrugated archival

board, cellulosic

n/a

Archival Folder Board (white)

Unknown

Archival Survival

Suitable

2006-01-01

NAA

PAT

none

320 gsm

board, folder

n/a

Archival Folder

Unknown

Archival Survival

Suitable

2012-01-01

NAA

PAT

none

260 and 320 gsm, (code FLDMAN)

archival, folder

n/a

Buffered Seamless Envelope

Unknown

Archival Survival

Suitable

2012-01-01

NAA

PAT

none

90 gsm

buffered seamless, envelope

n/a

Buffered Seamless Envelope

Unknown

Archival Survival

Suitable

2006-01-01

NAA

PAT

none

90 gsm (code ENCSEAM 85X110)

buffered seamless, envelope

n/a

Green Grey Library Board

Unknown

Archival Survival

Suitable

2006-01-01

NAA

PAT

none

240 gsm (10 point)

board, library

n/a

Green Grey Library Board

Unknown

Archival Survival

Suitable

2006-01-01

NAA

PAT

none

490 gsm (20 point)

board, library

n/a

Library Board

Unknown

Archival Survival

Suitable

2012-01-01

NAA

PAT

none

240 and 490 gsm, (code BRDLIB)

board, library

n/a

Perpetuum Wove Paper, 120 Gsm

Unknown

Archival Survival

Suitable

2012-01-01

NAA

PAT

none

120 gsm

paper, wove

n/a

Perpetuum Wove

Unknown

Archival Survival

Suitable

2003-01-01

NAA

PAT

none

90 gsm (code PAPA4-90)

paper

n/a

Perpetuum Wove

Unknown

Archival Survival

Suitable

2006-01-01

NAA

PAT

none

90 gsm (code PAPA4-90)

paper

n/a

Ever Fast File Pin Holder

Unknown

Avery Dennison Office Products

Suitable

2004-01-01

NAA

PAT

none

Code 81996

holder

n/a

Cellaire, Polyethylene Foam Cushioning Material

Unknown

Bunzl, Sealed Air Australia

Suitable

2006-01-01

NAA

PAT

none

2 mm thick (Code RH0210), 6 mm thick (Code RH06D)

foam, polyethylene

n/a

Prolong 500 Year Archival Corrugated(blue/grey) Board

Unknown

Byrne Sign, Cleveland

Suitable

2012-09-26

CMA

Oddy test

on coupons spotty iridescent areas overall, concentrated at edges

3/4" white Expanded PVC Board

wood alternative

n/a

Archive Text

Unknown

Conservation Resources International

Suitable

1996-01-01

NAA

PAT

none

copy, paper

n/a

Prolong 500 Year Archival Document Wallet (white)

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

270gsm

buffered, envelope

n/a

Prolong 500 Year Archival Document Wallet (white)

Unknown

Conservation Resources International

Suitable

2006-01-01

NAA

PAT

none

270gsm

buffered, envelope

n/a

Prolong 500 Year Archival Folder (white)

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

270gsm

buffered, envelope

n/a

Prolong 500 Year Archival Folder (white)

Unknown

Conservation Resources International

Suitable

2006-01-01

NAA

PAT

none

270gsm

buffered, envelope

n/a

Prolong 500 Year Archival Folder Board(white)

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

white, 270 gsm

white,270 gsm

White

board, folder

n/a

Prolong 500 Year Archival Folder Board(white)

Unknown

Conservation Resources International

Suitable

2006-01-01

NAA

PAT

none

white, 270 gsm

white,270 gsm

White

board, folder

n/a

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

single and double wall

board, corrugated

n/a

Prolong 500 Year Archival Folder Board

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

270gsm

board, folder

n/a

Prolong 500 Year Archival, Four Flap Folder

Unknown

Conservation Resources International

Suitable

2006-01-01

NAA

PAT

none

270gsm; retest

15 mm expansion, folder, four flap

n/a

Prolong 500 Year Watermarked Archival Laser/copy Paper

Unknown

Conservation Resources International

Suitable

2001-01-01

NAA

PAT

none

watermarked archival

copy/laser, paper

n/a

Prolong 500 Year Watermarked Archival Laser/copy Paper

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

watermarked,archival, 80 gsm

copy/laser, paper

n/a

Prolong 500 Year Archival Envelope

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

watermarked, 80gsm, buffered, ungummed

buffered, envelope

n/a

Prolong 500 Year Archival Envelope

Unknown

Conservation Resources International

Suitable

2006-01-01

NAA

PAT

none

watermarked, 80gsm, buffered, ungummed

buffered, envelope

n/a

Negative Preservers, Print File

Unknown

Get Smart Products

Suitable

1996-01-01

NAA

PAT

none

Code 35–6HB

negative, sleeve

n/a

Magnetic Photograph Album Page

Unknown

Grant Studio

Suitable

2003-01-01

NAA

PAT

paper, plastic, and adhesive elements

none

page, photo album

n/a

Memory Scrapbook Page

Unknown

Grant Studio

Suitable

2003-01-01

NAA

PAT

paper and plastic elements

none

page, scrapbook

n/a

Photo Album Page

Unknown

Grant Studio

Suitable

2003-01-01

NAA

PAT

paper and plastic elements

white

White

page, photo album

n/a

Pocket Page Photo Album Page

Unknown

Grant Studio

Suitable

2003-01-01

NAA

PAT

paper and plastic elements

none

page, photo album

n/a

Acid Free White Paper

Unknown

Guisepak

Suitable

2009-01-01

NAA

PAT

none

400 µm

paper

n/a

Archival (grey, Blue/white) Corrugated Board

Unknown

Guisepak

Suitable

2010-01-01

NAA

PAT

none

(Code GPO31B); corrugated archival grey, blue/white

Blue/White

board, cellulosic

n/a

Archival Liner

Unknown

Guisepak

Suitable

2009-01-01

NAA

PAT

none

blue/grey

Blue/Gray

board

n/a

Archival Liner (blue/grey)

Unknown

Guisepak

Suitable

2009-01-01

NAA

PAT

none

220gsm

board

n/a

Conservation Board

Unknown

Guisepak

Suitable

2008-01-01

NAA

PAT

none

300 gsm, 1000 µm

board

n/a

E Flute Corrugated Board (grey/natural White)

Unknown

Guisepak

Suitable

2009-01-01

NAA

PAT

none

1.60mm, grey/natural white

board, corrugated

n/a

Klug Corrugated Board (ref Kcb Bf)

Unknown

Guisepak

Suitable

2009-01-01

NAA

PAT

none

1600µm, 560 gsm, Ref KCB BF

board, corrugated

n/a

Klug Karton Board

Unknown

Guisepak

Suitable

2009-01-01

NAA

PAT

none

350µm, 330 gsm- 277 µm, 240 gsm- 1600 µm, 560 gsm

paper

n/a

Renaissance Tissue

Unknown

Light Impressions

Suitable

1996-01-01

NAA

PAT

none

unbuffered

paper, tissue

n/a

Slide Guard Polypropylene Sleeve

Unknown

Light Impressions

Suitable

1996-01-01

NAA

PAT

none

sleeve, slide

n/a

Somerset Textured Paper

Unknown

London Graphics Centre?

Suitable

2014-01-16

BM

Oddy test

showcase graphics

Radiant White 225 G/M2, 100% cotton paper

White

paper

n/a

Mylar

Unknown

Maria Anttems

Suitable

2011-01-01

NAA

PAT

none

100 micron thickness, A4 size

film, polyester

n/a

Manila File Folder

Unknown

Mcdonald Printing Group

Suitable

2005-01-01

NAA

PAT

none

285 gsm

file manila, folder

n/a

Polyolefin Heat-shrink Tubing 8098k323

Unknown

Mcmaster-Carr

Suitable

2011-01-11

CMA

Oddy test

barrier/coating material for brass mounts

Standard polyolefin

barrier/padding

none

Polyolefin Heat-shrink Tubing 8098k323

Unknown

Mcmaster-Carr

Suitable

2011-01-20

CMA

Oddy test

barrier/coating material for brass mounts

Standard polyolefin

barrier/padding

none

Rising Museum Mount Board

Unknown

Neenah Paper (formerly Rising Paper

Suitable

1996-01-01

NAA

PAT

none

board, paper

n/a

Millenium Manila Board (buff)

Unknown

Rolls Filing System

Suitable

2003-01-01

NAA

PAT

none

244, 285, 326, 374 gsm

board

n/a

Millenium Manila Board (buff)

Unknown

Rolls Filing System

Suitable

2007-01-01

NAA

PAT

none

244,285, 326, 374 gsm

board

n/a

Millenium Manila Board (white)

Unknown

Rolls Filing System

Suitable

2007-01-01

NAA

PAT

none

285,326, 374 gsm

board

n/a

Archive Paper

Unknown

Rolls Filing System

Suitable

2008-01-01

NAA

PAT

none

paper

n/a

Millenium Manila Board (white)

Unknown

Rolls Filingsystem

Suitable

2003-01-01

NAA

PAT

none

285, 326, 374 gsm

board

n/a

Ultimate Archive

Unknown

Rolls Filingsystem

Suitable

2009-01-01

NAA

PAT

none

unknown

n/a

Ultimate Archive Paper

Unknown

Rolls Filingsystem

Suitable

2009-01-01

NAA

PAT

none

paper

n/a

Heritage Photo Album, Tomahawk

Unknown

Salmat (formerly Hermes Precisa Australia)

Suitable

1996-01-01

NAA

PAT

none

Creme and Black leaf paper

album, photo

n/a

Marbig Folder Sleeve And Refill Sleeve

Unknown

The Q Store/ Webshops

Suitable

1997-01-01

NAA

PAT

none

folder, plastic sleeve

n/a

Polyethylene Storage Bag

Unknown

University Products

Suitable

1997-01-01

NAA

PAT

none

polyethylene

bag, storage

n/a

Black Rabbet Tape

Unknown

University Products

Unsuitable

2013-08-22

CMA

Oddy test

none

acrylic adhesive backed volara 1/16" thickness

gasket

Fosshape Thin

Unknown

University Products

Suitable

2011-02-24

CMA

Oddy test

custom shapeable mount support

white Polyester

White

polymer

support

none

Mohawk Digital Paper

Unknown

University Products

Suitable

1996-01-01

NAA

PAT

none

paper

n/a

Fosshape Thick

Unknown

University Products

Suitable

2011-03-03

CMA

Oddy test

sets with heat

white/ Polyester

White

polymer

mount, support

none

Fosshape Thin

Unknown

University Products

Suitable

2011-02-24

CMA

Oddy test

sets with heat

white/ Polyester

White

polymer

mount, support

none

Bending Plywood Or Wigglewood

Unknown

Unsuitable

2000-03-21

GCI

Oddy test

None

plywood

n/a

Book Binding Board

Unknown

X-press Graph-X

Suitable

2000-01-01

NAA

PAT

none

double sided, smooth/textured

board, paper

n/a

Multimat

Unknown

X-press Graph-X

Suitable

2000-01-01

NAA

PAT

none

matboard

n/a

White Core Board

Unknown

X-press Graph-X

Suitable

2000-01-01

NAA

PAT

none

1 mm

board, paper

n/a

500 Yeartm

Unknown

Zetta Florence

Suitable

2003-01-01

NAA

PAT

none

watermarked; 90, 120, 150 gsm

archival barrier, paper

n/a

500 Year™ Archival Photocopy Paper, Watermarked

Unknown

Zetta Florence

Suitable

2006-01-01

NAA

PAT

none

watermarked;90, 120, 150 gsm

copy, paper

n/a

500 Year™ Corrugated Archival Board, Blue/grey

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

double wall and single wall, corrugated blue/grey single and double wall

board

n/a

500 Year™ Corrugated Archival Board, Double Wall, Blue/grey

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

(code MUB), corrugated archival double wall blue/grey

Blue/Gray

board

n/a

500 Year™ Corrugated Archival Board, Single Wall, Blue/grey

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

(code MUB), corrugated archival single wall blue/grey

Blue/Gray

board

n/a

Acid-free Library Board

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

665 x 970 mm, 280 gsm, code (ZFLIB180P)

board, library

n/a

Acid-free Library Board

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

505 x 735 mm, 280 gsm, code (ZFLIB190P)

board, library

n/a

Barrier Paper App/zfbp (off White)

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

90 & 120 gsm

barrier off white, paper

n/a

Brilliant Enclosures, 5 X 7" M415x7-a-5

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

5 x 7" M415X7-A-5

envelope

n/a

Copy Paper, 80 Gsm

Unknown

Zetta Florence

Suitable

2011-01-01

NAA

PAT

none

80 gsm

copy, paper

n/a

Mylar Film

Unknown

Zetta Florence

Suitable

2006-01-01

NAA

PAT

none

75 µm and 100 µm

film, polyester

n/a

Papenv7record, 18.3 X 18.3 Cm Envelope

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

18.3 cm square

envelope

n/a

Polyethylene Envelope

Unknown

Zetta Florence

Suitable

1996-01-01

NAA

PAT

none

envelope, polyethylene

n/a

Seamless Envelope, Off White

Unknown

Zetta Florence

Suitable

2010-01-01

NAA

PAT

none

90 gsm (code PAPSEA)

envelope, seamless

n/a

500 YeartmBuffered Envelopes

Unknown

Zetta Florence

Suitable

2003-01-01

NAA

PAT

none

seamless and standard style; 90 and 120 gsm

buffered, envelope

n/a

500 Year™ Archival Folder

Unknown

Zetta Florence

Suitable

2003-01-01

NAA

PAT

none

folder

n/a

500 Year™ Archival Folder

Unknown

Zetta Florence

Suitable

2006-01-01

NAA

PAT

none

folder

n/a

500 Year™ Folder Board

Unknown

Zetta Florence

Suitable

2003-01-01

NAA

PAT

none

white; 260 and 330gsm

White

board, folder

n/a

Green/grey Library Board

Unknown

Zetta Florence

Suitable

2003-01-01

NAA

PAT

none

240 and 490gsm

board, library

n/a

Green/grey Libraryboard

Unknown

Zetta Florence

Suitable

2006-01-01

NAA

PAT

none

240 and 490gsm

board, library

n/a

500 Yeartm Archival Corrugated (blue/grey) Board

Visy

Zetta Florence

Suitable

2002-01-01

NAA

PAT

none

single and double wall

board, corrugated

n/a

Aluminium Kitchen Foil,

Waitrose

Suitable

2009-09-25

BM

Oddy test

PREP/Drying time: N/A, test #6614

ALUMINIUM SILVER,

Silver

barrier

none

Archival Box,

Walter Newburyt

Walter Newbury

Unsuitable

2009-03-20

BM

Oddy test

PREP/Drying time: N/A, test #6318

ARCHIVAL BUCKRAM, RED,

container

none

Whatman Filter Paper , Grade 1 1001-150

Whatman

Vwr

Suitable

2013-06-26

BM

Oddy test

PREP/Drying time: N/A, test #7891

PAPER, WHITE,

White

paper

none

Fosshape, 300 (3Mm) Or 600 (6.5mm)

Wonderflex World

Preservation Equipment

Temporary

2013-11-28

BM

Oddy test

PREP/Drying time: N/A, test #8072

LOW MELT POLYESTER, WHITE,

mount/ mount making

none

Glad Zip-lock Bag

Woolworths

The Dow Chemical Company

Suitable

1997-01-01

NAA

PAT

none

bag, resealable

n/a

Echo Panel, Woven Image Echo Panel

Woven Image

Suitable

2013-03-22

BM

Oddy test

PREP/Drying time: N/A, test #7739

POLYETHYLENE TEREPHTHALATE (PET), BLACK,

Black

board

none

Book Binding Board, Double Sided (smooth/textured)

X-press Graph-x

X-press Graph-X

Suitable

2008-01-01

NAA

PAT

none

double-sided,smooth/textured

binding, board

n/a

Plastazote, Ld45

Zotefoams

Suitable

2009-02-12

BM

Oddy test

PREP/Drying time: N/A, test #6199

POLYETHYLENE, WHITE,

White

foam

none

Evazote, Ev 30 We

Zotefoams

Unknown

Suitable

2013-08-20

BM

Oddy test

PREP/Drying time: N/A, test #7917

CROSS-LINKED ETHYLENE COPOLYMER, WHITE,

foam

none

Evazote, Ev50 Be

Zotefoams

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7932

CROSS-LINKED ETHYLENE COPOLYMER, BLUE,

foam

none

Evazote, Ev50 Rgy

Zotefoams

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7931

CROSS-LINKED ETHYLENE COPOLYMER, GREY, WITH SILVER METALLIC FLECKS

foam

none

Plastazote, Hl 34 We

Zotefoams

Unknown

Suitable

2013-08-20

BM

Oddy test

PREP/Drying time: N/A, test #7918

POLYETHYLENE, WHITE,

White

foam

none

Plastazote, Hl47 Bk

Zotefoams

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7928

POLYETHYLENE, BLACK,

White

foam

none

Plastazote, High Density, Hd 115 We

Zotefoams

Unknown

Suitable

2013-08-20

BM

Oddy test

PREP/Drying time: N/A, test #7919

POLYETHYLENE, WHITE,

White

foam

none

Plastazote, High Druability, Mp15 Bk

Zotefoams

Unknown

Suitable

2013-08-08

BM

Oddy test

PREP/Drying time: N/A, test #7912

METALLOCENE POLYETHYLENE, BLACK,

Black

foam

none

Plastazote, High Durability, Flame Retardant, Mp15 Fr Pgy

Zotefoams

Unknown

Suitable

2013-08-08

BM

Oddy test

PREP/Drying time: N/A, test #7911

METALLOCENE POLYETHYLENE, FLAME RETARDANT, GREY,

Gray

foam

none

Plastazote, Low Density, Ld24 Lc Bk

Zotefoams

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7929

LOW DENSITY POLYETHYLENE, BLACK,

foam

none

Plastazote, Low Density, Ld45 Rd

Zotefoams

Unknown

Suitable

2013-09-10

BM

Oddy test

PREP/Drying time: N/A, test #7940

LOW DENSITY POLYETHYLENE, RED,

foam

none

Plastazote, Low Density, Ld45 Wt

Zotefoams

Unknown

Suitable

2013-09-10

BM

Oddy test

PREP/Drying time: N/A, test #7941

LOW DENSITY POLYETHYLENE, WHITE,

foam

none

Plastazote, Semi Rigid, Pk33 Mgy

Zotefoams

Unknown

Suitable

2013-08-08

BM

Oddy test

PREP/Drying time: N/A, test #7910

POLYETHYLENE, GREY,

Blue, Light

foam

none

Plastazote, Semi Rigid, Pk80 Sgy

Zotefoams

Unknown

Suitable

2013-08-08

BM

Oddy test

PREP/Drying time: N/A, test #7913

POLYETHYLENE, GREY, LIGHT,

Gray, Light

foam

none

Plastazote, Standard, Ld45 Gy

Zotefoams

Unknown

Suitable

2013-08-08

BM

Oddy test

PREP/Drying time: N/A, test #7909

LOW DENSITY POLYETHYLENE, GREY, WITH SILVER METALLIC FLECKS

foam

none

Plastazote, Standard Flame Retardant, Ld45 Fr

Zotefoams

Unknown

Suitable

2013-08-08

BM

Oddy test

PREP/Drying time: N/A, test #7914

POLYETHYLENE, FLAME RETARDANT, BLUE, LIGHT,

Clear

foam

none

Zotek, High Temperature, N A 30kg/m3

Zotefoams

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7927

POLYAMIDE (NYLON), BLACK,

foam

none

Zotek, High Temperature, N B50 50kg/m3

Zotefoams

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7926

POLYAMIDE (NYLON), BLACK,

foam

none

Zotek, Low Flame, Smoke Toxicity, F35 30kg/m3 1.9 Pcf

Zotefoams

Unknown

Suitable

2013-08-27

BM

Oddy test

PREP/Drying time: N/A, test #7925

KYNAR PVDF, WHITE,

foam

none

Evazote Ev50

Zotefoams

Sekisui

Suitable

2006-01-01

NAA

PAT

none

10 mm thick (white)

eva copolymer, foam

n/a

Plastazote Ld45

Zotefoams

Sekisui

Suitable

2006-01-01

NAA

PAT

none

10 mm thick

closed cell, cross-linked polythene, foam

n/a

Ethafoam® 220

Sealed Air

Suitable

2012-06-06

CH

Oddy test

Lab sample purchased 2011

Polyethylene, white

White

foam

Ethafoam® Mrc®

Sealed Air

Suitable

2012-06-06

CH

Oddy test

Sample received Feb 2012

100% recycled content polyethylene, black, 2" thick

foam

Ethafoam® Hrc®

Sealed Air

Suitable

2012-03-10

CH

Oddy test

Sample received Feb 2012

min. 65% recycled content polyethylene, black, 2" thick

Black

foam

Stratocell® Rc®

Sealed Air

Suitable

2012-03-10

CH

Oddy test

Sample received Feb 2012

min. 65% recycled content polyethylene, black, 2" thick

Black

foam

Coroplast® Archival

Coroplast

Talas

Suitable

2012-06-06

CH

Oddy test

Lab sample purchased 2011

Polypropylene, translucent

Clear

plastic board

Corogreen™

Coroplast

Coroplast. Inc.

Suitable

2012-06-06

CH

Oddy test

Sample Received Feb 2012

Polypropylene with recycled content, 4 mm, white faces with black core

plastic board

Heritage Corrugated Board

Unknown

Talas

Suitable

2012-03-10

CH

Oddy test

Lab sample. Purchased 2011

Light blue-grey face with white flutes and white face

Blue/Gray, Light

board, cellulosic

Archivart® Multiuse Board

Archivart

Archivart®

Suitable

2012-03-10

CH

Oddy test

Lab sample. Purchased 2011

Light blue-grey, single wall

Blue/Gray, Light

board, cellulosic

Superior Millboard Sample#1

Conservation By Design

Conservation By Design, Larson-Juhl

Unsuitable

2012-06-06

CH

Oddy test

Sample Received Feb 2012

Dark green pressed millboard made from pre-consumer recycled waste

Dark, Green

board, cellulosic

Superior Millboard Sample#2

Conservation By Design

Conservation By Design, Larson-Juhl

Suitable

2012-06-06

CH

Oddy test

Sample Received May 2012

Light green pressed millboard made from pre-consumer recycled waste

Green, Light

board, cellulosic

Eva Foam, Sev 035

Unknown

Keng Huat Rubber Products

Temporary

2017-02-16

HCC

Oddy test

none

Black Ethylene-Vinyl Acetate foam

Black

foam, polymer

Eva Foam

Unknown

Fagerdala Singapore Pte

Unsuitable

2017-02-16

HCC

Oddy test

none

White Ethylene-Vinyl Acetate foam

White

foam, polymer

Mesh Fabric 07-64/45

Unknown

Sefar Petex

Unsuitable

2017-08-16

HCC

Oddy test

none

Off-White Plastic mesh

Off-White

polymer mesh

Mesh Fabric 07-425/46

Unknown

Sefar Petex

Suitable

2017-08-16

HCC

Oddy test

none

Off-White Plastic mesh

Off-White

polymer mesh

Mesh Fabric 07-102/44

Unknown

Sefar Petex

Suitable

2017-08-16

HCC

Oddy test

none

Off-White Plastic mesh

Off-White

polymer mesh

Mesh Fabric 07-285/55

Unknown

Sefar Petex

Suitable

2017-08-16

HCC

Oddy test

none

Off-White Plastic mesh

Off-White

polymer mesh

Mesh Fabric 07-120/50

Unknown

Sefar Petex

Suitable

2017-08-16

HCC

Oddy test

none

Off-White Plastic mesh

Off-White

polymer mesh

Carbon Fibre Fabric

Unknown

Polymer Technologies Pte.

Suitable

2017-08-16

HCC

Oddy test

none

BLACK

Black

carbon fibre

Barrikade Ep Terrazzo

Hesselberg Bygg As/norway, Company Of Sto Se & Co Kg Aa, Germany

Sto Sea Pte. (Singapore)

Suitable

2018-03-20

HCC

Oddy test

none

Epoxy terrazzo coating system for floors

epoxy

Non-archival Roller

Sonoco

Sonoco Singapore

Unsuitable

2018-06-28

HCC

Oddy test

none

board, paper

Card Board Roller

Talas

Unsuitable

2018-06-28

HCC

Oddy test

none

board, paper

Artcare Archival Foam White Board

University Products

Suitable

2018-06-28

HCC

Oddy test

none

foam, paper board

Archival Roller

University Products

Suitable

2018-06-28

HCC

Oddy test

none

paper

Mg Interleaving Kraft Paper

Sonoco

Sonoco Singapore

Unsuitable

2018-06-28

HCC

Oddy test

none

paper

Marveal Seal Equivalent

Sonoco

Sonoco Singapore

Suitable

2018-06-28

HCC

Oddy test

none

aluminium foil

Glassine

Sonoco

Sonoco Singapore

Suitable

2018-06-28

HCC

Oddy test

none

coated paper

Stosilent Board

Sto Se & Co Kgaa

Sto Sea Pte. (Singapore)

Suitable

2018-08-23

HCC

Oddy test

none

Acoustic panel made of expanded glass granulate

glass granulate

Polyester Wadding

Unknown

Ae Model Singapore

Suitable

2019-02-14

HCC

Oddy test

none

batting & padding, fabric

Polystyrene Beads

Unknown

Spotlight Singapore

Suitable

2019-02-14

HCC

Oddy test

none

block/bulk/pellet, polymer

Prosorb Humidity Stabiliser

Prosorb

Preservation Equipment

Suitable

2019-02-14

HCC

Oddy test

only beads were tested

block/bulk/pellet, polymer

Sintra 3a

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

PVC

board, plastic/polymeric/synthetic

6 Plywood

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

board, natural

12 Plywood

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

board, natural

Ash Hardwood

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

board, natural

Blueboard

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Jute Fiber

paper-based, sheet

Delrin

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Polyacetal

block/bulk/pellet, polymer

Flame Retardant Plywood

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

block/bulk/pellet, polymer

Gatorboard

Temporary

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Polystyrene

board, composite

Komatex

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

PVC

board, plastic/polymeric/synthetic

Medex Mdf Wood

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

board, natural

Oak Hardwood (aged 50 Years)

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

board, natural

Paulownia Wood

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

board, natural

Plexi Glass

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Polymethyl methacrylate

polymer, sheet (>1mm thick)

Oak Hardwood (aged 1 Year)

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

board, natural

Fome-cor With Zeolites

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Polystrene with a Jute Fiber Face

board, composite

Volara Foam

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Polyethylene

foam, non building insulation, polymer

Pur (ester) Foam

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Polyester Urethane Resin

foam, non building insulation, polymer

Purple Nitrile Gloves

Kimberly-Clark

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

none

Acrylonitrile-butadiene Copolymer

glove, polymer

Methocel™ A4c Methylcellulose

Dow Chemical Company

Dow Chemical

Suitable

2021-03-19

MMA

Oddy test (method: 20190226_OT_1)

Water-soluble, high purity, non-ionic cellulose ether that performs as thickener, binder, and film former. Also functions as a suspending aid, stabilizer, surfactants, lubricants, protective colloids, and emulsifiers. Consists of methylcellulose, water, and sodium chloride. Received February 2020, tested in solid form. Not dissolved or prepared in any way prior to testing

adhesive, glue, liquid, polymer

Dowsil™ 795 Silicone Building Sealant White

Dow Corning

Amazon.com

Temporary

2021-03-19

MMA

Oddy test (method: 20190226_OT_1)

One-part, neutral cure, RTV silicone sealant, unaffected by sunlight, rain, snow, ozone and temperature extremes of -40°C to 149°C. 3 hr tack free time, 7-14 days of curing time, 14-21 days for full adhesion, 20-30 min. working time, 32 g/L VOC content, 1.52 relative density, contains methanol and diisopropoxydi(ethoxyacetoacetyl)titanate. Purchased January 2020, cured for 24 days

caulk or sealant, adhesive, polymer

Dowsil 791 Silicone Weatherproofing Sealant

Dow Corning

Dow Chemical

Temporary

2021-03-19

MMA

Oddy test (method: 20190226_OT_1)

One-part, neutral-cure, grey RTV silicone sealant; 20 minute working time, 40 minute tack-free time, 7-14 days to cure; 31 g/L VOC, 1.46 relative density; Contains dodecamethylcyclohexasiloxane and unsaturated fatty acids treated with calcium carbonate; Purchased February 2020; applied to mylar and spread into an even layer about 2 mm thick using a glass slide, cured for 15 days

caulk or sealant, adhesive, polymer

3M™ Sprayable Hot Melt Adhesive 6111

3M

Temporary

2021-03-19

MMA

Oddy test (method: 20190226_OT_1)

100% solids, sprayable polyolefin copolymer thermoplastic adhesive. 0.92 g/mL density, 177-196°C application temperature, 1 min open time surface foam to PVC, 6 min open time surface foam to foam. Contains hydrocarbon resin, polyolefin copolymer, and polypropylene. Sheet of Mylar placed on hot plate at 185°C, rubbed glue stick against it in circles to melt and cure; cured for 15 days

adhesive, heat activated, polymer

Titebond Iii Ultimate Wood Glue

Franklin International

Amazon.com

Unsuitable

2021-02-18

MMA

Oddy test (method: 20190226_OT_1)

One-part, waterproof wood glue, proprietary polymer-based formula. 1.11 relative density, 98.889°C boiling point. Purchased March 2020, applied to mylar and spread out thinly using a glass slide, cured for 2 days.

adhesive, glue, liquid, polymer

Vhb 4952 Acrylic Foam Tape

3M

Temporary

2020-12-02

MMA

Oddy test (method: 20190226_OT_1)

White, low surface energy, high strength permanent bond adhesive with a firm acrylic foam core; 2 cm width, 0.045 (1.1mm) thick; 24 month shelf life; lot number 19324; Purchased October 2020

White

adhesive, double-sided, polymer

Filmoplast P90

Neschen Coating

Talas

Temporary

2020-12-02

MMA

Oddy test (method: 20190226_OT_1)

Self adhesive white archival paper tape; 50 g/m^2; acid-free, buffered with calcium carbonate, age-resistant permanent acrylic adhesive, non-yellowing, solvent-free; Purchased

adhesive, polymer, single-sided

P.C. Woody Epoxy, Part A And B

Protective Coating Company

Temporary

2020-12-02

MMA

Oddy test (method: 20190226_OT_1)

Two part bulked epoxy filler; Part A contains Bisphenol A - Epichlorohydrin polymer, Kaolin, Hydrous magnesium silicate, Bis(2-ethylhexyl) terephthalate, Glycidyl Ethers of Bisphenol F Resin, Titanium Dioxide, Polyethylene fiber. Part B contains Styrenated phenol, Kaolin, Aliphatic Polyaminoamide, Polyoxypropylenediamine, Talc, N-Aminoethyl piperazine, Bis(2-ethylhexyl) terephthalate; workable for 1/2 hour, 12-24 hour full cure; Prepared in a 1:1 mixture by weight and applied to mylar with a wooden tongue depressor, cured 2 days prior to testing, removed from mylar before testing; Purchased March 2020

filler/binder mixtures (eg.: plaster, paste, spackle)

Lineco Frame Sealing Tape Gray, L387-0151

Lineco, Holyoke

Lineco

Suitable

2020-11-12

MMA

Oddy test (method: 20190226_OT_1)

Manufactured from Perma/Seal label stock with a foil layer, a non-yellowing, permanent acrylic adhesive. Acid-free, lignin-free, with aluminum barrier. Sample purchased August 2020

adhesive, polymer, single-sided

3M™ Scotchcal™ Luster Overlaminate 3645

3M

Unsuitable

2020-10-22

MMA

Oddy test (method: 20190226_OT_1)

Slip-resistant overlaminate designed for floor graphics; 7.874 mil thick; printable vinyl and pressure-sensitive acrylic adhesive; Received September 2020

adhesive, polymer, single-sided

Aquazol 500

Polymer Chemistry Innovations

Talas

Temporary

2020-10-22

MMA

Oddy test (method: 20190226_OT_1)

Poly(2-ethyl-2-oxazoline), also known as PEOX or PEtOx, is a non-toxic, non-hazardous, and biocompatible water-soluble polymer. Kinematic viscosity range of 18-24 cSt, refractive index of 1.52, glass temperature of 69°C, neutral pH. Off-white solid Purchased February 2020, tested in solid form. Not dissolved or prepared in anyway prior to testing

adhesive, glue, liquid, polymer

Klucel G

Hercules/ashland

Talas

Temporary

2020-10-22

MMA

Oddy test (method: 20190226_OT_1)

Non-ionic adhesive (hydroxypropylcellulose) soluble in water and alcohol, mixes well with hot waxes. Thermoplastic, dries clear and very flexible. Often used as a leather consolidant and as an adhesive with vellums. Insoluble at temperatures above 113°F (45 C), pH value of 5-8.5 in water solution, softening point of 212-302°F (100-150 C). Purchased February 2020, tested as a dry powder without dissolving or additional preparation

adhesive, glue, liquid, polymer

Double Coated Urethane Foam Tape, 4056

3M

Unsuitable

2020-10-16

MMA

Oddy test (method: 20190226_OT_1)

Black double sided foam tape with green and white liner; 1.6 mm thick; polyurethane foam and pressure-sensitive acrylic adhesive; liner removed before testing

Black

adhesive, double-sided, polymer

Itac Plus Vinyl Laminate

Continental Grafix

Unsuitable

2020-10-16

MMA

Oddy test (method: 20190226_OT_1)

White vinyl laminate with pressure sensitive adhesive. PVC and unknown adhesive. Coated paper backing removed for Oddy test. Received 3/2019

White

adhesive, polymer, pressure-sensitive

Crompton Heat-set Tissue

Crompton

Talas

Temporary

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

Long fibered heat activated abaca hemp tissue coated on one side with an acrylic archival heat set adhesive (Texicryl/Paraloid). 9g/m^2, pH netural, reversible with mineral spirits. Prepared by heating to 176-197F between mylar sheets, tested without mylar. Purchased January 2020

adhesive, heat activated, polymer

Filmoplast R

Neschen Coating

Talas

Temporary

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

Light, transparent, technical Japanese paper, coated with heat actiavted acrylic-acid ester copolymer. Free of lignin and hemicellulose, with a high percentage of alpha cellulose. Adhesive is colorless, ageing-resistant, free of softeners, contains magnesium carbonate, and does not yellow. 8.5 g/m^2, sealing temperature must be over 100°C. Purchased January 2020

Colorless

adhesive, heat activated, polymer

Fusion 4000 Dry Mount Adhesive

D&k

D&K Framing Products

Unsuitable

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

Ultra-clear, removable, thermal activated, 100% inert, acid-free pure adhesive film. Recommended temperature of 175°F. Sample cut from a roll produced within the past year. Activated on hot plate between two sheets of Mylar at 80°C, pressed down firmly by a beaker, peeled from Mylar. Received January 2020, cured 12 days

adhesive, heat activated, polymer

Beva 371 Film

Conservator's Products Company

Conservator's Products

Unsuitable

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

Made of pure BEVA 371 solution, sandwiched between two sheets: one of 1.5-mil silicone-coated Mylar release film and a sheet of 4-mil silicone-coated release paper. Solvent-free. Activated on hot plate between two sheets of Mylar at 65°C, pressed down firmly by a beaker, adhesive layer peeled from Mylar and the original backing. Received January 2020, cured 12 days

adhesive, heat activated, polymer

3M™ Hot Melt Adhesive 3779q

3M

Temporary

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

100% solids hot melt adhesive. 0.99 g/mL density, 177-196°C application temperature, 25 sec open time, 75 sec delivery time. Contains polyamide polymer. Sheet of Mylar placed on hot plate at 180°C, rubbed glue stick against it in circles to melt and cure. Received September 2020, cured 12 days

adhesive, heat activated, polymer

3M™ Hot Melt Adhesive 3797tc

3M

Digi-key

Temporary

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

100% solids hot melt adhesive. 0.92 g/mL density, 177-196°C application temperature, 30 sec open time, 55 sec delivery time. Contains polypropylene, hydrocarbon resin, polyethylene, ethylene-propylene copolymer, antioxidant, and polyolefin wax. Sheet of Mylar placed on hot plate at 180°C, rubbed glue stick against it in circles to melt and cure. Purchased September 2020, cured 12 days

adhesive, heat activated, polymer

3M™ Hot Melt Adhesive 3748q

3M

Arrow

Suitable

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

100% solids, no VOCs thermoplastic resin. 0.93 g/mL density, 177-196°C application temperature, 45 sec open time, 65 sec delivery time. Contains polypropylene, hydrocarbon resin, styrene-butadiene polymer, ethylene-propylene polymer, polyethylene, and non-hazardous additives. Sheet of Mylar placed on hot plate at 180°C, rubbed glue stick against it in circles to melt and cure. Purchased September 2020, cured 12 days

adhesive, heat activated, polymer

Lascaux 498 Hv

Lascaux Colours & Restauro

Talas

Temporary

2020-10-08

MMA

Oddy test (method: 20190226_OT_1)

Thermoplastic acrylic resin composed of a water-based dispersion butyl acrylate and methylmethacrylate thickened with acrylic butylester. Water thinnable, insoluble in water when dry. Permanently soluble in acetonem toluene, xylene, etc. Min film formation temp of ~5°C, glass transition temperature of ~6°C, 400% elongation at break, minimum sealing temperature of ~68-76°C, elastic hard dry film consistency. 100°C boiling point, 1.0 g/cm3 density. Purchased November 2018, opened April 2019, cured for 7 days

adhesive, glue, liquid, polymer

File:2973 GA.jpg

Wheat Starch Aytex-p

Adm Arkady

Talas

Temporary

2020-10-08

MMA

Oddy test (method: 20190226_OT_1)

Highly refined, unmodified food grade wheat starch. Used in bookbinding and paper conservation as an adhesive for paper, leather, fabric, and other porous materials. High water holding capacity, pH 5-6.5 (measured in 70% slurry). To buffer, add 10% (by weight) of calcium carbonate. Bulk density of 32 lb/ft^3 (512.6 kg/m^3) loose, 45 lb/ft^3 (720.8 kg/m^3) packed. Purchased February 2020, cured for 7 days

adhesive, glue, liquid, polymer

Lineco Frame Sealing Tape White, L387-0152

Lineco, Holyoke

Lineco

Temporary

2020-10-08

MMA

Oddy test (method: 20190226_OT_1)

Manufactured from Perma/Seal label stock with a foil layer, a non-yellowing, permanent acrylic adhesive. Acid-free, lignin-free, with aluminum barrier. Purchased August 2020

adhesive, polymer, single-sided

Ge Supreme Silicone

GE Silicones

Lowe's

Unsuitable

2020-10-08

MMA

Oddy test (method: 20190226_OT_1)

100% silicone and waterproof sealant that provides a reliable seal in weather-prone areas like windows, doors, basements, roofs, sidewalks, siding, tuckpointing and attics. Contains octamethylcyclotetrasiloxane, hexamethyldisilazane, and dibutyl tin bis acetylacetonate. Purchased August 2020, cured for 7 days

caulk or sealant, adhesive, polymer

Ge Silicone Ii Clear Caulk #ge5000

GE Silicones

Amazon.com

Unsuitable

2020-10-08

MMA

Oddy test (method: 20190226_OT_1)

Waterproof one-part silicone sealant. 28 g/L VOC, 5-10 min work life, 20-30 min tack-free time, 2-3 day cure time, temperature range of -55°F to 400°F, relative density of 1.006. Contains hydrotreated middle distillates (petroleum), hexamethyldisilazane, and dibutyl tin bis acetylacetonate. Purchased August 2020, cured for 7 days

caulk or sealant, adhesive, polymer

Xt-765, 2-part Silicone

Silicones

Unsuitable

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Thixotropic tin catalyzed RTV-2 silicone. 40 min work time, 6 month shelf life, 1.10 specific gravity. 0.99 relative density for part A, 1.10 relative density for part B. Part A contains polydimethyl siloxane, silicon dioxide, trimethoxyphenylsilane, tetrapropyl orthosilicate, dimethyltin dineodecanoate, and green pigment. Part B contains polydimethylsiloxane, silicon dioxide, titanium diooxide, and trihydroxystearin. Received March 2020, cured for 5 days

caulk or sealant, adhesive, polymer

Xp-565, 2-part Silicone

Silicones

Unsuitable

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Transparent, two-component, addition reaction, platinum catalyzed silicone rubber. Designed to remain water-clear even after extended exposure to the sun. 1.5 hr work time, 1.02 specific gravity, -60 to 600°F service temperature. 0.98 relative density for part A, 1.02 relative density for part B. Part A contains polydimethylsiloxane dimethylvinyl terminated and dimethyl, methylhydrogen polydimethylsiloxane. Part B contains platinum catalyst and polydimethylsiloxane, dimethylvinyl terminated. Received March 2020, cured for 5 days

caulk or sealant, adhesive, polymer

Xt-493, 2-part Silicone

Silicones

Unsuitable

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Thixotropic, two-component, tin catalyzed RTV silicone rubber. Designed for casting polyurethanem polyester and epoxy parts. 1.10 specific gravity, 1-1.5 hr working time, 6 month shelf life. 0.99 relative density for part A, 1.10 relative density for part B. Part A contains dibutyltin dilaurate, ethyl silicate, polymeric ethyl silicate, silicon dioxide, blue pigment, and polydimethyl siloxane. Part B contains polydimethylsiloxane, silicon dioxide, titanium dioxide, and trihydroxystearin. Received March 2020, cured for 5 days

caulk or sealant, adhesive, polymer

Gi 1000, 2-part Silicone

Silicones

Unsuitable

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Two-part tin-catalyzed RTV-2 silicone rubber designed for casting polyester parts. 1.5-2.5 hr working time, 6 month shelf life, -60 to 350°F service temperature, 1.09 specific gravity. 0.99 relative density for part A, 1.1 relative density for part B. Part A contains dibutyltin dilaurate, ethyl silicate, polymeric ethyl silicate, silicon dioxide, blue pigment, and polydimethyl siloxane. Part B contains polydimethylsiloxane, silicon dioxide, and titanium dioxide. Received March 2020, cured for 5 days

caulk or sealant, adhesive, polymer

3M™ Scotch-weld™ Epoxy Adhesive 420 Off-white

3M

Temporary

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Two-part epoxy, part A contains modified epoxy resin, 4,7,10-Trioxatridecane-1,13-Diamine, 2,4,6-tris((Dimethylamino)Methyl)Phenol, amorphous silica, and calcium salt, and part B contains epoxy resin and acrylic polymer. Sample received August 2020, cured for 5 days.

adhesive, glue, liquid, polymer

Fibre Glast 2000 Epoxy Resin + Fibre Glast 2060 Epoxy Hardener

Fibre Glast

Unsuitable

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Two-part epoxy, resin contains epoxy resin based mixture and multifunctional acrylate, and hardener contains modified amine mixture. Purchased in 2017, cured for 5 days.

adhesive, glue, liquid, polymer

West System G/flex 650 Toughened Epoxy

Gougeon Brothers

Amazon.com

Unsuitable

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Two-part Epoxy resin and Rubber modified-polyamine mixture. Part A: Propane, 2,2-bis[p-(2,3-epoxypropoxy)phenyl], polymers, Phenol-Formaldehyde Polymer Glycidyl Ether. Part B: ATBN polymer, Non-hazardous, Triethylenetetramine, Benzene-1,3-dimethanamine, Phenol, 2,4,6-tris[(dimethylamino)methyl] reaction products with triethylenetetramine, Tris-2, 4, 6(dimethylaminomethyl) phenol, Aminoethylpiperazine, Tetraethylenepentamine. Purchased March 2020, cured for 5 days

adhesive, glue, liquid, polymer

West System 105 Epoxy Resin® / 205 Fast Hardener®

Gougeon Brothers

Gougeon Brothers, Inc

Unsuitable

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

Two-part epoxy used for general coating and bonding applications at lower temperatures. 1.18 specific gravity, 1-4 days for cure. 105 contains benzyl alcohol, phenol-formaldehyde polymer glycidyl ether, and propane, 2,2-bis[p-(2,3-epoxypropoxy)phenyl]-, polymers. 205 contains hydroxybenzene, tetraethylenepentamine, triethylenetetramine, polyethylenepolyamines, reaction products of triethylenetetramine with phenol and formaldehyde, and triethylenetetramine, reaction products with propylene oxide. Received February 2020, cured for 5 days

adhesive, glue, liquid, polymer

Titebond Iii Ultimate Wood Glue

Franklin International

Amazon.com

Unsuitable

2020-09-25

MMA

Oddy test (method: 20190226_OT_1)

One-part, waterproof wood glue, proprietary polymer-based formula. Non-toxic, solvent free. 98.889°C boiling point. 24 month shelf life. 20-25 minute total assembly time; Purchased March 2020, cured for 1 day

adhesive, glue, liquid, polymer

3M™ Hi-strength 90 Ca Spray Adhesive - Low Voc <25%< /td>

3M

Itapestore

Unsuitable

2020-09-25

MMA

Oddy test (method: 20190226_OT_1)

A clear, industrial grade high strength aerosol spray adhesive. 0.863 g/mL density, <25% VOC, 1-4 min dry time, synthetic elastomer base. Contains methyl acetate, dimethyl ether, propane, 1,1-difluoroethane, hexmethyldisiloxane, cyclohexane, chlorobenzotrifluoride, and N-butyl acetate. Purchased July 2020, cured for 1 day

adhesive, glue, liquid, polymer

3M™ Foam Fast 74 Ca Spray Adhesive - Low Voc <25%< /td>

3M

Amazon.com

Unsuitable

2020-09-25

MMA

Oddy test (method: 20190226_OT_1)

A clear, industrial grade high strength lace spray adhesive. 0.853 g/mL density, <25% VOC, 30s-2 min dry time, synthetic elastomer base. Contains methyl acetate, dimethyl ether, propane, 1,1-difluoroethane, hexmethyldisiloxane, cyclohexane, chlorobenzotrifluoride, and N-butyl acetate. Purchased July 2020, cured for 1 day

adhesive, glue, liquid, polymer

3M™ Super 77™ Ca Multi-purpose Spray Adhesive - Low Voc <25%< /td>

3M

Amazon.com

Unsuitable

2020-09-25

MMA

Oddy test (method: 20190226_OT_1)

A translucent, high tack and fast drying mist spray adhesive. 0.80 g/mL density, <25% VOC, 15-30s dry time, synthetic elastomer base. Contains acetone, 1,1-difluoroethane, propane, and cyclohexane. Purchased July 2020, cured for 1 day

adhesive, glue, liquid, polymer

Rtv615, 2-part Silicone

GE Silicones

Momentive

Unsuitable

2020-09-18

MMA

Oddy test (method: 20190226_OT_1)

Silicone rubber compound, clear liquid that cures at room temperature to high strength silicone rubber with the addition of curing agents. Parts A and B mixed 10:1 by weight, specific gravity of 1.02 for part A, temperature range of -60 to 204°C, 4 hr. work time, 6-7 day full cure. Contains octamethylcyclotetrasiloxane. Received January 2020, cured for 13 days

caulk or sealant, adhesive, polymer

Liquidwood Epoxy Wood Consolidant

Abatron

Ace Hardware

Unsuitable

2020-09-18

MMA

Oddy test (method: 20190226_OT_1)

Two-part epoxy wood consolidant consisting of a resin and a hardener, mix parts A and B 1:1 by volume. Part A contains bisphenol-a-(epichlorhydrin), 2,3-epoxypropyl o-tolyl ether, butyl glycidyl ether, and γ-butyrolactone. Part B contains tetraethylene pentamine and fatty acids, tall-oil, reaction products with tetraethylenepentamine. Cured for 13 days. Purchased February 2020

adhesive, glue, liquid, polymer

Lok Lift Adhesive Netting

Optitech

Temporary

2020-09-08

MMA

Oddy test (method: 20190226_OT_1)

Coarse adhesive netting with yellow backing, adhesive for flooring installation of surfaces including wood, carpet, vinyl, etc; adhered to thin Mylar for Oddy testing. Received July 2020

adhesive, double-sided, polymer

Fusible Bonding Web For Medium Fabrics, 261

Dritz

Amazon.com

Unsuitable

2020-09-08

MMA

Oddy test (method: 20190226_OT_1)

Fusible bonding web for medium fabrics, UPC:072879280258, for use with steam iron; 18 x 36 inches; 100% polyamide; Purchased December 2019, sample material ironed between sheets of mylar before testing

adhesive, heat activated, polymer

Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; Received June 2019

adhesive, polymer, single-sided

Dowsil 3145 Silicone Adhesive Clear Mil-a-46146, 4812mktw

Dow Corning

Ellsworth Adhesive

Temporary

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Neutral cure silicone adhesive; 90mL tube; date of manufacture: March 1, 2019 - Lot No. H050J31072; Prepared 1/27/2020, extruded through the 1/2" nozzle opening in lines onto aluminum foil. After setting for four days, cut into ~1cm lengths. Pieces mixed on aluminum foil by hand (wearing nitrile gloves). Purchased December 2019

adhesive, glue, liquid, polymer

Hot Melt Adhesive 3764q

3M

Mcmaster-Carr

Unsuitable

2020-04-03

MMA

Oddy test (method: 20190226_OT_1)

Low temp hot-melt glue for 3M EC and TC guns; catalog number 7333A37; ethylene-vinyl acetate polymer, naphtha, hydrocarbon resin; solid stick 5/8" x 8"; Prepared on 7/2/2019 and 7/5/2019; Extruded with a used 3M Plygun LT with Quadrack Converter (no temperature settings). Remains of previous glue stick and first new glue stick extruded and discarded. Extruded in dots onto aluminum foil. Dots mixed in large glass lab beaker by hand (wearing nitrile gloves). Purchased May 2019

adhesive, heat activated, polymer

Scotch-weld Urethane Adhesive Dp605ns

3M

Unsuitable

2020-03-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Off-white

Two-part, 1:1 mix ratio, non-sagging, semi-flexible, thixotropic urethane adhesive. Boiling point of 178°C, density of 1.17 g/mL, glass transition temperature of 41°C. Contains diphenylmethane diisocyanate, polymethylene polyphenyl isocyanate, polypropylene glycols, and amorphous silica. Sample received February 2020, cured for 1 week prior to testing

Off-white

adhesive, glue, liquid, polymer

Scotch-weld Epoxy Adhesive Dp100

3M

Temporary

2020-03-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Yellow, amber

Two-part, 1:1 mix ratio, fast-curing rigid epoxy adhesive containing mercaptan polymer, tris(2,4,6-Dimethylaminomonomethyl)phenol, bis((Dimethylamino)methyl)phenol, and Poly(Bisphenol A-co-epichlorohydrin). Color may vary from nearly white to yellow/amber. Boiling points of parts A and B are 93°C and 260°C and densities are 1.13 g/mL and 1.17 g/mL respectively. Glass transition temperature of 33°C. Sample received February 2020, cured for 1 week prior to testing

Yellow, amber

adhesive, glue, liquid, polymer

Gorilla Heavy Duty Construction Adhesive

The Gorilla Glue Company

Amazon.com

Temporary

2020-03-27

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Waterproof construction adhesive with application temperature of 40 to 100°F and service temperature of -40 to 200°F. Consists of limestone, calcium carbonate, stearic acid, quartz, and dibutyltin bis(acetylacetonate). Sample received February 2020, cured for 1 week prior to testing

White

caulk or sealant, adhesive, polymer

Jade 711 Pva Adhesive

Unknown

Talas

Unsuitable

2020-03-25

Oddy test (method: 20190226_OT_1)

Color: White

Acid-free polyvinyl acetate adhesive similar to Jade 403, with reduced odor. For use on paper, fabric, board, canvas, leather, and film. 1.05-1.10 g/cm3 density, pH 7.1-7.3, initial boiling point of >212°F. Sample received January 2020, cured for 5 days prior to testing

White

adhesive, glue, liquid, polymer

No

Jade R Reversible Pva Bookbinding Adhesive

Unknown

Talas

Unsuitable

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Acid-free multi polymer (PVA and EVA) water reversible adhesive. For use on paper, board, leather and fabric. 1.05-1.10 g/cm3 density, pH 7.1-7.3, initial boiling point of >212°F. Sample received January 2020, cured for 5 days prior to testing

White

adhesive, glue, liquid, polymer

White Gorilla Glue

The Gorilla Glue Company

Amazon.com

Temporary

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: White

100% waterproof white polyurethane glue. Bonds to foam, wood, metal, ceramic, and stone. Contains 4,4’diphenylmethane diisocyanate, 2,4’diphenylmethane diisocyanate, and Oxirane, methyl, polymer with .alpha.hydro.omega.-hydroxypolyoxy(methyl-1,2-ethanediyl) and 1,1-methylenebisisocyanatobenzene. Sample received February 2020, cured for 5 days prior to testing

White

adhesive, glue, liquid, polymer

Titebond Ii Premium Wood Glue

Franklin International

Unsuitable

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: Yellow

Cross-linking polyvinyl acetate wood glue with strong initial tack and fast to set. 3.0 g/L VOC, relative density of 1.09, pH 3.0. Honey cream colored as liquid, translucent/yellow as dried film. Contains aluminum chloride. Sample received February 2020, cured for 5 days prior to testing

Yellow

adhesive, glue, liquid, polymer

Titebond Original Wood Glue

Franklin International

Unsuitable

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: Yellow

Aliphatic resin emulsion wood glue with strong initial tack and fast to set. 10.7 g/L VOC, relative density of 1.0771, pH 4.0. Yellow as liquid, translucent as dried film. Sample received February 2020, cured for 5 days prior to testing

Yellow

adhesive, glue, liquid, polymer

Sikaflex®-11 Fc Sealant Adhesive

Sika

Hd Supply

Unsuitable

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: White

One part polyurethane, moisture-cured elastomeric sealant/adhesive. For use on cement, ceramics, glass, metals, wood, and epoxy. Service temperature of -40°F to 170°F, 1-2 hour tack-free time, 3-5 day final cure time. Contains xylene, 4,4'-methylenediphenyl diisocyanate, ethylbenzene, and silica quartz. Sample purchased January 2020, cured for 12 days prior to testing

White

caulk or sealant, adhesive, polymer

Silglaze* Ii Silicone Sealant, Scs2800

GE Silicones

Amazon.com

Unsuitable

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

One-part, neutral, fast cure, medium modulus silicone sealant, primerless adhesion. 33 g/L VOC, density of 1.035 g/cm3, 6-12 min work life, 30 min tack free time, 24 hour cure time, 3-4 days for full cure, temperature range of -55°F to 300°F. Contains octamethylcyclotetrasiloxane, hexamethyldisilazane, and dibutyl tin bis acetylacetonate. Sample purchased January 2020, cured for 12 days prior to testing

Clear

caulk or sealant, adhesive, polymer

Dowsil™ 795 Silicone Building Sealant Gray

Dow Corning

Amazon.com

Unsuitable

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: Gray

One-part, neutral cure, RTV silicone sealant. Unaffected by sunlight, rain, snow, ozone and temperature extremes of -40°C to 149°C. 3 hr tack free time, 7-14 days of curing time, 14-21 days for full adhesion, 20-30 min. working time, 32 g/L VOC content, 1.52 relative density, contains methanol and magnesium carbonate. Sample purchased January 2020, cured for 14 days prior to testing

Gray

caulk or sealant, adhesive, polymer

Dowsil™ 795 Silicone Building Sealant Black

Dow Corning

Amazon.com

Unsuitable

2020-03-25

MMA

Oddy test (method: 20190226_OT_1)

Color: Black

One-part, neutral cure, RTV silicone sealant. Unaffected by sunlight, rain, snow, ozone and temperature extremes of -40°C to 149°C. 3 hr tack free time, 7-14 days of curing time, 14-21 days for full adhesion, 20-30 min. working time, 32 g/L VOC content, 1.52 relative density, contains methanol. Sample purchased January 2020, cured for 14 days prior to testing

Black

caulk or sealant, adhesive, polymer

Rubber And Vinyl 80 Spray Adhesive

3M

Unsuitable

2020-03-19

MMA

Oddy test (method: 20190226_OT_1)

Color: Yellow

A high performance polychloroprene based contact aerosol spray adhesive. 0.835g/mL density, 12.9% solids content by weight, <55% VOC, 3 min dry time, 3 - 30 min bonding range. Contains methyl acetate, dimethyl ether, cyclohexane, toluene, naphthol spirits, rosin, and zinc oxide. Sample received February 2020, cured for 1 day prior to testing

Yellow

adhesive, glue, liquid, polymer

Hi-strength 90 Spray Adhesive

3M

Unsuitable

2020-03-19

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

An industrial grade synthetic elastomer spray adhesive that is typically used for bonding HPL to wood. 0.69g/mL density, 13% solids content by weight, <55% VOC, 1 min dry time, 1 - 10 min bonding range. Contains dimethyl ether, isobutane, acetone, pentane, cyclohexane, and propane. Sample received February 2020, cured for 1 day prior to testing

Clear

adhesive, glue, liquid, polymer

Foam Fast 74 Spray Adhesive

3M

Unsuitable

2020-03-19

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

An extremely fast tacking industrial grade synthetic elastomer spray adhesive for bonding foam and fabric. 0.718 g/mL density, 22% solids content by weight, <55% VOC, 30s dry time, 30 sec - 15 min bonding range. Contains dimethyl ether, isobutane, acetone, pentane, methyl acetate, cyclohexane, petroleum naphtha, cyclopentane, and drometrizole (antioxidant, an aromatic conjugated amine). Sample received February 2020, cured for 1 day prior to testing

Clear

adhesive, glue, liquid, polymer

Briteline Shield, Uv Matte Overlaminate

Grimco

Unsuitable

2020-03-05

MMA

Oddy test (method: 20190226_OT_1)

Color: Green

Calendered PVC matte overlaminate; permanent acrylic adhesive; protection against UV degradation, moisture, and abrasion; 1 year shelf life; 3 mil thickness; Purchased December 2019

Green

adhesive, polymer, single-sided

3M 4952 Very High Bond (vhb) Tape

3M

Mcmaster-Carr

Temporary

Consistent with Control

Overall gray haze and white crystal growth on edges

2018-01-04

FMNH

Oddy test

White acrylic foam with rubber adhesive on Kraft paper liner, double-sided, 3/4"

White

adhesive tape, double sided, polymer

3M 465 Adhesive Tape

3M

Grainger

Suitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2018-01-16

FMNH

Oddy test

Clear, double-sided acrylic transfer tape

Clear

adhesive tape, double sided, polymer

3M Double-coated Medical Tape

3M

Suitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2018-03-30

FMNH

Oddy test

Double-sided sheet adhesive on transparent polyethylene film

adhesive tape, double sided, polymer

Glue Dots, Permanent

Glue Dots International

Office Max

Suitable

Copper: Consistent with Control

Silver: Consistent with Control

Lead: Consistent with Control

2018-03-30

FMNH

Oddy test

Double-sided adhesive. Translucent oval with a blue tinge. Comes in different oval sizes.

adhesive, polymer, pressure-sensitive

Very High Bond Acrylic-adhesive Tape

C.R. Laurence Company

Unsuitable

Hazy with red to black color change

Consistent with Control

Minor white crystal accumulation

2018-06-04

FMNH

Oddy test

Double-sided clear tape - 1/4" w.

adhesive tape, double sided, polymer

Glue Dots, Removable

Glue Dots International

Office Max

Suitable

Consistent with Control

Orange haze consistent with control

2017-10-24

FMNH

Oddy test

Double-sided. Removable, clear, comes in different diameters or ovals.

adhesive, polymer, pressure-sensitive

Mactac Adhesive - Mac Ip5000 Perma Print Rl Mounting Adhesive

Mactac

Agfa

Unsuitable

Red discoloration

Black discoloration

Consistent with Control

2017-10-24

FMNH

Oddy test

Double-sided, acrylic, pressure-sensitive film

adhesive, polymer, pressure-sensitive

Fep Teflon Tape With Silicone Adhesive

Cs Hyde

Suitable

Consistent with Control

2016-06-14

FMNH

Oddy test

Optically-clear, pressure-sensitive PTFE tape

adhesive tape, polymer, single sided

3M Atg #9082

3M

Unsuitable

fail, dark black corrosion at both tips, more than control

pass

fail, green and white with areas of orange/red. Also, overall very small platelets of shiny white/irridescent. This was not on control

2006-02-21

BKM

Oddy test

acid free adhesive transfer (double sided, no carrier)

adhesive tape, double sided, polymer

3M Aluminum Foil Tape #431

3M

Temporary

unspecified temp: pass, very slight overall darkening, same as control

pass

pass, intermediate (light green on inside edge, slight white on outside edge)

2006-02-23

BKM

Oddy test

Pass for short term exhibition, not long term

2"" wide, acrylic adhesive

adhesive tape, polymer, single sided

3M Scotch #853

3M

Unsuitable

pass

fail (orange/red at inside tip grown along side very light white along tip)

2006-02-23

BKM

Oddy test

polyester film with acrylic adhesive

adhesive tape, polymer, single sided

Nashua #330x

Nashua

Suitable

unspecified temp: pass, very slight overall darkening, same as control

pass

unspecified temp: pass

2006-04-04

BKM

Oddy test

Aluminum foil tape with pressure sensitive acrylic adhesive

adhesive tape, polymer, single sided

3M Scotch-weld Epoxy Adhesive Tube Kit 2212

3M

Suitable

2007-02-14

BKM

Oddy test

No specific results for metals or temps. Comments ""great- no tarnish pass""

B/A grey

filler/binder mixture (non-paint), paste

3M Vhb 9473 Adhesive Transfer Tape

3M

Suitable

no change

2008-12-30

BKM

Oddy test

adhesive tape, double sided, polymer

Gudy 808

Neschen Coating

Suitable

no change

2008-12-30

BKM

Oddy test

permanent water based acrylic adhesive

adhesive, polymer

Adchem 254-74 Tape

Adchem

Suitable

very slightly corroded

ok

very slightly corroded

2009-02-10

BKM

Oddy test

same result as Volara sample, but slightly more corroded than control

double faced acrylic pressure sensitive adhesive tape with release liner

adhesive tape, double sided, polymer

3M Hot Melt Glue #3792

3M

Suitable

2009-03-16

BKM

Oddy test

pass but should not be used in direct contact with object or in sealed case

adhesive, polymer

Ag:,Cu: 4/13/09: tarnished slightly,Pb: 4/13/09: appearance of brownish yellow material on surface

3M Hot Melt Glue #3797

3M

Suitable

2009-03-16

BKM

Oddy test

pass but should not be used in direct contact with object or in sealed case

adhesive, polymer

Ag:,Cu: 4/13/09: tarnished slightly,Pb: 4/13/09: appearance of brownish yellow material on surface

3M 415 Double Sided Tape ""splicing Tape""

3M

Talas

Suitable

very slight darkening, no significant corrosion

no change, same as control

2016-07-05

BKM

Oddy test

uses 3M adhesive 400 (medium firm acrylic pressure sensitive adhesive system), carrier is a polyester film, liner is tan #60 kraft paper

adhesive tape, double sided, polymer

Ag: no change,Cu: very slight darkening, no significant corrosion,Pb: no change

3M 465 Double Sided Tape

3M

Talas

Suitable

very slight darkening, no significant corrosion

no change, same as control

2016-07-05

BKM

Oddy test

uses 3M adhesive 400 (medium firm acrylic pressure sensitive adhesive system), no carrier film, liner is tan #60 kraft paper

adhesive tape, double sided, polymer

Ag: no change,Cu: very slight darkening, no significant corrosion,Pb: no change

3M Vhb / Acrylic Foam Tape 4910 F

3M

Suitable

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Acrylic foam tape

adhesive tape, double sided, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Dow Corning 3145 Rtv Mil-a-46146 Transparent / Structural Sealant And Adhesive

Dow Corning

Suitable

2017-05-26

BKM

Oddy test

same as controls

Silicone adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: red - same as control,Pb: dark gray, same as control

Dow Corning Rtv Sealant 737 Neutral Cure Sealant

Dow Corning

Unsuitable

2017-05-26

BKM

Oddy test

much more corrosion on Pb than control

Silicone adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: red - same as control,Pb: white corrosion, none on control

3M Scotch 924 Atg Tape, Clear

3M

Suitable

2017-05-26

BKM

Oddy test

same as controls

Adhesive 400 (medium firm acrylic, pressure sensitive), no carrier film

adhesive tape, polymer, single sided

Ag: no corrosion,Cu: red - same as control,Pb: dark gray, same as control

3M Bumpon

3M

Unsuitable

2017-05-26

BKM

Oddy test

different from control, a better alternative to this product was already found

Polyurethane acrylic-adhesive backed pads (Resilient rollstock-clear series, SJ5600)

polymer, sheet (>1mm thick)

Ag: no corrosion,Cu: 1 coupon purplish, other very red, both darker than control,Pb: some white corrosion, none on control

3M Scotch Blue Tape 2090

3M

Amazon.com

Suitable

2017-06-23

BKM

Oddy test

Only 1 out of 2 sample jars were able to be opened, yet both looked okay

Acrylic-adhesive backed washi paper (low-medium adhesion)

adhesive tape, polymer, single sided

Ag: no corrosion,Cu: no corrosion,Pb: No corrosion

3M Scotch Blue Tape 2080

3M

Amazon.com

Suitable

2017-06-23

BKM

Oddy test

Acrylic-adhesive backed crepe paper, (medium adhesion)

adhesive tape, polymer, single sided

Ag: no corrosion,Cu: no corrosion,Pb: no corrosion

J-lar Super Clear Tape (shurtape)

J-lar

Suitable

2018-11-27

BKM

Oddy test

clear tape

Clear

adhesive tape, polymer, single sided

Ag: same as control,Cu: darkened slightly (purple-red) same as control,Pb: very slight yellowing, similar to control

Versimold Rubber Compound

Rowe Industries

Suitable

2018-12-17

BKM

Oddy test

rubber compound

block/bulk/pellet, polymer

Ag: no corrosion,Cu: darkened slightly compared to control,Pb: no corrosion

Sugru Mouldable Glue, Original Formula, Black, Semi-cured

Formformform

Unsuitable

2019-01-25

BKM

Oddy test

semi-cured (~6 hours) Control lead FAIL

mouldable glue

block/bulk/pellet, polymer

Ag: same as control,Cu: rainbow corrosion from edges,Pb: Control lead FAIL

Sugru Mouldable Glue, Original Formula, White, Semi-cured

Formformform

Unsuitable

2019-01-25

BKM

Oddy test

semi-cured (~6 hours) Control lead FAIL

mouldable glue

block/bulk/pellet, polymer

Ag: same as control,Cu: overall yellowed compared to control,Pb: Control lead FAIL

Sugru Mouldable Glue, Original Formula, Black, Fully Cured

Formformform

Unsuitable

2019-01-31

BKM

Oddy test

fully cured - re-test with longer set/cure time

mouldable glue

block/bulk/pellet, polymer

Ag: same as control,Cu: overall yellowed compared to control,Pb: yellowish corrosion

Sugru Mouldable Glue, Original Formula, White, Fully Cured

Formformform

Unsuitable

2019-01-31

BKM

Oddy test

fully cured - re-test with longer set/cure time

mouldable glue

block/bulk/pellet, polymer

Ag: same as control,Cu: overall yellowed compared to control,Pb: yellowish corrosion

Kraftmark Pro-create Professional Sculptors Putty

Kraftmark

Suitable

corroded

2008-12-30

BKM

Oddy test

Ok to useif allowed to cure for two weeks. Better to use outside case.

2 part epoxy putty

filler/binder mixture (non-paint), paste

Kraftmark Pro-create Professional Sculptors Putty

Kraftmark

Suitable

2008-12-30

BKM

Oddy test

Pass if allowed to cure for 2+ weeks. Oddy tested 5/8/08, new Oddy test requested

2 part epoxy putty (white and grey), similar to pliacre, 60hr air time, 50/50 mix ratio

filler/binder mixture (non-paint), paste

Magic Sculpt 2 Part Epoxy Putty

Wesco Enterprises

Suitable

oxidized

2009-03-27

BKM

Oddy test

considered for use in mountmaking

cured for two weeks

filler/binder mixture (non-paint), paste

Cef 2910 Contrast Enhancement Film

3M

Unsuitable

2019-08-21

MMA

Oddy test (method: 20190226_OT_1)

Colorless; Comment: Lead coupons in the control jars had significant blue tarnish

Pressure sensitive acrylic adhesive film, no liner; adhesion to glass 16.6N/cm; received July 2019

Colorless

adhesive, polymer, pressure-sensitive

Avery Black A6080, Adhesive Vinyl

Avery

Unknown

Temporary

2019-08-16

MMA

Oddy test (method: 20190226_OT_1)

Grey, Dark

Calendered opaque vinyl label (PVC) with permanent solvent adhesive; purchased in 2018

Dark, Grey

adhesive, polymer, single-sided

530 Utility-grade Flatback Packaging Tape

Intertape Polymer Group

Amazon.com

Unsuitable

2019-08-16

MMA

Oddy test (method: 20190226_OT_1)

Brown

Intertape™ brand Flatback Tape (pressure-sensitive paper tape, kraft paper tape) is designed for superior performance in a variety of packaging, splicing and tabbing applications. 2 in x 60 yds; Adhesion: 60 oz per inch; Adhesive: natural / synthetic rubber; Thickness: 7.2 mils (carrier, adhesive)

Brown

adhesive, polymer, single-sided

Black Artist Tape 5326-1

Proart

Amazon.com

Unsuitable

2019-08-16

MMA

Oddy test (method: 20190226_OT_1)

Black

Black artist tape, 1 in x 60 yds; Non-glare paper tape

Black

adhesive, polymer, single-sided

Acryloid B-72, Sy7-05

Unknown

Conservation Resources International

Temporary

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

Colorless, transparent

B-72; tested as pellets; Chemical Components: an ethyl methacrylate co-polymer; unknown purchase date.

Colorless, transparent

block/bulk/pellet, polymer

Paper Tape With Gumming 067-60/0; Temporary Talas Part Number #tad607001 - Sold As Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2019-07-17

MMA

Oddy test (method: 20190226_OT_1)

White

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; purchased August 2018

White

adhesive, polymer, single-sided

Frame Sealing Tape, Tad055001

Unknown

Talas

Suitable

2019-07-05

MMA

Oddy test (method: 20190226_OT)

Blue-Grey

Frame sealing tape, used as a means of sealing backing boards to frames; blue-grey pressure-sensitive tape composed of a layer of acid-free label stock, foil barrier, adhered with a non-yellowing, permanent acrylic adhesive.

Blue/grey

adhesive, polymer, single-sided

88250 Transfer Tape

Tesa

Temporary

2018-12-19

MMA

Oddy test (method: 20180821_OT)

Colorless

Pressure-sensitive adhesive transfer tape; thickness: 127 um / 4.00 mils; colorless; no carrier just adhesive; liner is white with blue logo; temp. resistance from -40 deg F; adhesion to steel is 10 N/cm; Chemical Components: water-based acrylic adhesive; liner is polycoated paper

Colorless

adhesive, polymer, pressure-sensitive

Elastosil Rt480+ Catalyst T40

Wacker Silicones

Unknown

Unsuitable

2018-05-31

MMA

Oddy test (method: 20171116_OT)

Natural (kind of beige)

Arrived cured in a metal channel. Wacker Primer G790 was used to prime the channel prior to adding sealant. Received April 2018

Natural (kind of beige)

caulk or sealant, adhesive, polymer

Paper Tape With Potato Starch, #067-25/0

Klug Conservation

Temporary

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #20

Strip of paper tape with potato starch gumming - White - Cut to weight

White

adhesive tape, polymer, single sided

Copper: very slight red tarnish - Silver: light purple tarnish - Lead: Darkening

Vhb Tape 5925 Double-sided

3M

Temporary

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #23

Double coated pressure-sensitive closed-cell acrylic foam tape with modified acrylic adhesive and a PE film liner - White - Strip was cut to weight with liner removed. Tape was tested on a mylar sheet to prevent its sticking to inside of jar.

adhesive tape, double sided, polymer

Copper: Very Slight Red Tarnish - Silver: ok - Lead: darkening, light white haze, yellow/green compacted, violet tarnish

Titebond Ii Premium Wood Glue

Franklin International

Unsuitable

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #24

Industrial use cross-linking PVA wood glue, poured onto glass panel and allowed to dry. - Orange - Sample was scraped from panel using a razor blade.

adhesive, glue, liquid, polymer

Copper: Spots of heavy green corrosion, heavy haze overall - Silver: yellow tarnish, black tarnish - Lead: complete corrosion, turned to powder

Dowsil 791 Weatherproofing Sealant

Dow Corning

Temporary

OK

darkening and thin compact corrosion (B),darkening with spots of compact corrosion (A)

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #6

neutral-cure, one-part sealant; applied to Mylar and allowed to cure - Grey - Peeled/scraped from mylar

adhesive caulk, polymer

Dowsil 791 Weatherproofing Sealant

Dow Corning

Temporary

OK

darkening

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #7

neutral-cure, one-part sealant; applied to Mylar and allowed to cure - Black - Peeled/scraped from mylar

adhesive caulk, polymer

933 Structural Glazing Sealant

Dow Corning

Unsuitable

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #8

two-component, neutral curing silicone; applied to Mylar and allowed to cure - Black - Peeled/scraped from mylar

adhesive caulk, polymer

Copper: Heavy haze (black),purple tarnish - Silver: ok - Lead: darkening with grey compact corrosion

Sea-210, Ge5070 Rtv Silicone Rubber Compound

GE Silicones

Temporary

OK

thin orange compact corrosion and darkening

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #9

Two-part silicone rubber adhesive; Applied to Mylar and allowed to cure - Grey - Peeled/scraped from mylar

adhesive caulk, polymer

Paper Tape With Gumming 067-60/0; Temporary Talas Part Number #tad607001 - Sold As Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2019-05-29

MMA

Oddy test (method: 20190226_OT)

white

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; purchased August 2018

White

adhesive, polymer, single-sided

Synthetic Felt

Unknown

Mcmaster-Carr

Temporary

2019-05-29

MMA

Oddy test (method: 20190226_OT), SPME GCMS

white

1" Thick; 1/8"wide; density, lbs./sq. yd. 1.88. Material, Polyester. Hardness, Durometer 35A, Hardness Rating, Firm. Pressure to Compress 10%, psi 21. Temperature range, °F -40° to 300°. Adhesive type, rubber. Adhesive Temperature Range, °F 0° to 180°. Lengths, ft 10, 25, 50.

White

adhesive, polymer, single-sided

Shurtape Fp-227 High Adhesion Flatback Paper Tap.

Shurtape

Unsuitable

2019-05-29

MMA

Oddy test (method: 20190226_OT), SPME GCMS

white

Backing: Colored flatback paper. Adhesive: Rubber-based adhesive. Liner: NA. Size: 2 in. x 60 yds. Adhesion to Stainless Steel: 57 oz/in width (6.24 N/10 mm). Elongation: 2.50%. Service Temperature Range: 40 F to 150 F (4 C to 66 C). Tensile: 30 lbs/in width (52.5 N/10 mm). Thickness: 5.8 mils (0.15 mm). Purchased in Spring 2019.

White

adhesive, polymer, single-sided

3M 9576, 021200-84266 Acrylic Double-sided Tape

3M

R. S. Hughes

Unsuitable

2019-05-23

MMA

Oddy test (method: 20190226_OT)

colorless tape, brown liner

Acrylic double-sided tape; adhesion strength 21.28 N/cm.; colorless; liner is densified kraft paper; thickness 4 mil; width 1 in; Chemical Components: carrier polypropylene; acrylic adhesive; purchased November 2018.

brown liner, colorless tape

adhesive, double-sided, polymer

Fillet Tape Double Sided - 6mm X 50m, Ukpfs605

Unknown

UK Picture Framing Supplies

Unsuitable

2019-05-23

MMA

Oddy test (method: 20190226_OT)

COLORLESS

Acid free double-sided acrylic tape; width 6mm; Chemical Components: acrylic adhesive; polyester carrier; purchased november 2018; repeat of Oddy 2360 and 2444.

Colorless

adhesive, double-sided, polymer

Filmoplast Sh Gummed 'linen' Tape

Neschen Coating

Gaylord Archival

Unsuitable

2019-03-26

MMA

Oddy test (method: 20190226_OT), SPME GCMS

white

Neschen filmoplast SH Gummed 'Linen'Tape 50 yds.; Catalog Number: AFGLT50; Purchased: December 2018

White

adhesive, polymer, single-sided

Jade 403 Pva Adhesive

Unknown

Talas

Unsuitable

2019-03-14

MMA

Oddy test (method: 20190214_OT_a)

colorless, clear

PVA adhesive; dries transparent and colorless; Adhesive is water soluble when wet, and permanent when dry. pH neutral, acid free; modified polyvinyl acetate resin emulsion; SKU: TAD007001; Purchased: January 2019

Clear

adhesive, glue, liquid, polymer

Pc-7 Multi-purpose Super Strength Epoxy 2 Oz.

Protective Coating Company

Ace Hardware

Unsuitable

2019-03-14

MMA

Oddy test (method: 20190214_OT_b)

black

2-Part epoxy; black; mix 1:1; 1 hr work time; mixed 3 days prior to testing; Use as adhesive, sealant, or filler; Purchased Jan 2019.

Black

adhesive, glue, liquid, polymer

Magic Smooth

Wesco Enterprises

Artplace

Unsuitable

2019-03-14

MMA

Oddy test (method: 20190214_OT_a), SPME GCMS

yellow

2-Part epoxy; doesn't dissolve foams; mixed 3 days prior to testing; Purchased: January 2019

yellow

adhesive, glue, liquid, polymer

J-b Weld Twin Tube

J-b Weld

J-B Weld

Unsuitable

2019-03-14

MMA

Oddy test (method: 20190214_OT_b), SPME GCMS

black

2-Part epoxy; black; mixed 1:1; "set time 4-6 hrs; cure time 15-24 hrs" but mixed 3 days prior to testing; strength 3960 PSI; Purchased: January 2019

Black

adhesive, glue, liquid, polymer

Foam Fast 74 Spray Adhesive

3M

Grainger

Unsuitable

2019-03-14

MMA

Oddy test (method: 20190214_OT_b)

orange

Spray adhesive; aerosol can; "dries in 15 minutes" but sprayed out 2 days prior to testing; can was shaken for 2 minutes and adhesive was sprayed 3-5 inches from the surface; for bonding foam and fabric; Model/Catalog Number: Item # 3MA18; Month/Year Purchased: January 2019

Orange

adhesive, glue, liquid, polymer

Araldite Av 1253 + Hardener Hv 1253

Huntsman International

Conservation Resources International

Unsuitable

2019-02-27

MMA

Oddy test (method: 20180821_OT)

tan, blonde wood

2-Part bulked epoxy; tan color; cure start on 1/9/19; Model/Catalog Number: AV1253, HV 1253; Purchased: August 2017; Chemical Components: Araldite: BISPHENOL A EPOXY RESIN, butyl 2,3-epoxypropyl ether. Hardener: Amides, from Me epoxyhydroxyoctadecanoate, tetraethylenepentamine and vegetable-oil fatty acids, Formaldehyde, oligomeric reaction products with phenol, titanium dioxide, 4,4'isopropylidenediphenol, Silicon, amorphous, 3,6,9-triazaundecamethylenediamine, 2,2'-iminodi(ethylamine), N(2-aminoethyl)piperazine-1,4-diethylamine, N,N,N'tris(2-aminoethyl)ethylenediamine, N(2-aminoethyl)N'[2-(1-piperazinyl)ethyl]ethylenediamine, Amines, polyethylenepoly-, trientine

blonde wood, tan

adhesive, glue, liquid, polymer

Renpaste Sv 427-2 / Ren Hv 427-1 Epoxy

Huntsman International

Restauro-online

Unsuitable

2019-02-27

MMA

Oddy test (method: 20180821_OT)

brown

2-Part bulked epoxy; brown; cure start on 1/9/19; Model/Catalog Number: 00051367; Purchased: September 2018; Chemical Components: Part 1: tetraethylenepentamine, 4,4'-isopropylidenediphenol. Part 2: 2,2'-[(1-methylethylidene)bis(4,1-phenyleneoxymethylene)]bisoxirane

Brown

adhesive, glue, liquid, polymer

Epoxy - Epocast 1645 Fr A/b

Huntsman International

Krayden Corporate

Unsuitable

2019-02-27

MMA

Oddy test (method: 20180821_OT)

red, mauve

Ultra-Low Density Epoxy Void and Edge Filler; cure start on 1/9/19; Catalog Number: HT3573108; Purchased: March 2018

Red, mauve

adhesive, glue, liquid, polymer

Paper Tape With Gumming 067-60/0; Temporary Talas Part Number #tad607001 - Sold As Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2019-02-13

MMA

Oddy test (method: 20180821_OT)

white

Sample material: single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; purchased August 2018

White

adhesive, polymer, single-sided

Sealant - Farbpaste El Fl Black 9005 + Wacker Elastosil Rt 480 + Wacker Catalyst T 40

Wacker Silicones

Unknown

Unsuitable

2018-07-31

MMA

Oddy test (method: 20171116_OT), SPME GCMS

4-Part curable sealant; arrived cured in aluminum U-channel. Wacker Primer G 790 was used to prepare the channels for the sealant; Delivered April 2018.

caulk or sealant, adhesive, polymer

Carpet Adhesive: Commercialon Premium Modular Tile And Lvt Adhesive

Unknown

J & J Flooring

Unsuitable

2018-08-02

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Acrylic-latex pressure sensitive carpet adhesive for PVC backed tiles. Instructions indicate that no more should be spread than can be covered in 2 hours.; Chemical Components: Acrylic-latex pressure sensitive adhesive; blue; Month/Year Purchased: 6/2018

adhesive, polymer, pressure-sensitive

Scotch® Long Lasting Storage Packaging Tape

3M

Amazon.com

Temporary

2018-09-13

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

Pressure-sensitive transparent colorless adhesive; catalogue #3650-6; Strong, secure, solvent-free acrylic adhesive; Chemical Components: Adhesive Type Acrylic; Purchased: April, 2017

adhesive, polymer, pressure-sensitive

Framer’s Tape Ii Clear

Specialty Tapes

Dick Blick

Temporary

2018-09-13

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

When this tape was put over laserjet printed paper, the black printer ink bled a bit.

Archival-grade self-adhesive tape; transparent, colorless; catalogue # 23028-1002; Month/Year Purchased: April, 2017

adhesive, polymer, pressure-sensitive

Scotch® Scrapbooking Tape

3M

Uline

Unsuitable

2018-09-13

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

Scotch tape; dimensions: 3/4 in x 400 in; catalogue # S-16634; Purchased: April, 2017

adhesive, polymer, pressure-sensitive

Uline Painter’s Masking Tape

Uline

Unsuitable

2018-09-13

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

Blue masking tape; catalogue #S-13752; Purchased: April, 2017

Blue

adhesive, polymer, pressure-sensitive

Polyester Repair Material + Quality Hardener “cream Hardener"

Mccausey Lumber

Unsuitable

2017-12-28

MMA

Oddy test (method: 20171116_OT), SPME GCMS

100:2 by volume; Plastic filler & fillet material 302; cream hardener; off-gassed 24 hours prior to testing

adhesive, glue, liquid, polymer

Nusil Cv-2680-12

Nusil

Unknown

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

2-part film adhesive; colorless; CV = controlled volatility; for bonding or sealing silicone elastomers and some metals or plastics; incompatible with sulfur-cured organic rubbers, latex, chlorinated rubbers, some RTV silicones, and unreacted residues of some curing agents; Chemical Components: silicone, glass, oxide, “chemicals” (according to SDS); Purchased: 06/2018

adhesive, glue, liquid, polymer

Preservation Double Sided Tape 889

3M

Unknown

Temporary

2018-10-25

MMA

Oddy test (method: 20180821_OT), SPME GCMS

permanent double-sided adhesive tape; colorless; 3/4" wide x 1296" long; acrylic adhesive; polyester backing; pH 7-8; transparent; purchased september 2018

adhesive, double-sided, polymer

4200 Silicone Tape (red)

Tesa

Unsuitable

2018-12-19

MMA

Oddy test (method: 20180821_OT), SPME GCMS

red double-sided silicone adhesive tape; peel adhesion 5 N/cm; PET backing; Thickness excluding liner – 3.5mil; Chemical Components: silicone adhesive; PET liner; (info not on website yet); purchased November 2018

Red

adhesive, double-sided, polymer

Food-grade High-temperature Silicone Rubber Sheet, 5827t21

Unknown

Mcmaster-Carr

Temporary

2018-12-19

MMA

Oddy test (method: 20180821_OT), SPME GCMS

colorless silicone rubber sheet; 1/32" thickness; purchased 11/2018

Colorless

adhesive, double-sided, polymer

3M 9731

3M

Unknown

Temporary

2019-01-11

MMA

Oddy test (method: 20181031_OT), SPME GCMS

colorless double-sided tape; silicone adhesive on one side of polyester film carrier and acrylic adhesive on the other side; purchased fall 2018

Colorless

adhesive, double-sided, polymer

Tesa® 51575

Tesa

Temporary

2018-09-11

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

Double-sided tape with a non-woven backing and glassine liner; coated with a water-borne acrylic adhesive, translucent, 90 um thick, 12 mm wide; Chemical Components: acrylic adhesive, glassine liner; Purchased 8/2018; Adhesion to steel: 3.2 N/cm

adhesive, double-sided, polymer

Tesa® 4965

Tesa

Temporary

2018-09-11

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

Transparent double-sided tape with high shear and temperature resistance with red liner; 0.2mm thick; Batch 01B0001-01; Chemical Components: PET backing with tackified acrylic adhesive; Purchased: 7/2018; Adhesion to steel: 8.4 N/cm (initial); 76.12 (after 14 days)

adhesive, double-sided, polymer

Tesa® 4985

Tesa

Temporary

2018-09-11

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

Transparent transfer tape with no backing and light 'brown' glassine liner; 0.05 mm thick; Batch 703221; Chemical Components: tackified acrylic adhesive with no backing material/substrate; Purchased: 7/2018; Adhesion to steel: 11 N/cm (initial); 71.6 (after 14 days)

adhesive, double-sided, polymer

Tesa® 4959

Tesa

Temporary

2018-09-11

MMA

Oddy test (method: 20180706_C_OT), SPME GCMS

Translucent double-sided mounting and splicing tape with non-woven backing material and light 'brown' glassine liner; 0.1 mm thick; Batch 60614H1.; Chemical Components: 'non-woven' backing and tackified acrylic adhesive; Purchased: 7/2018; Adhesion to steel: 8.5 N/cm (initial); 54.83 (after 14 days)

adhesive, double-sided, polymer

Gudy® 870, No. 614826464

Neschen Coating

Talas

Temporary

2018-09-27

MMA

Oddy test (method: 20180821_OT), SPME GCMS

pressure sensitive adhesive; colorless, transparent; purchased 8/2018; 12 x 33' roll; Chemical Components: adhesive: waterbased polyacrylate dispersion; backing: double-side siliconised, white glassine paper; pH value: ~7; weight: 40 g/m^2; transverse strength: 500 g: > 5000 min, 1000 g: > 600 - 1500 min; adhesive strength: 10 min: >3,7 N/25mm, 24 hr: >5,2 N/25mm; temperature stability: -40 degrees F - 194 degrees F; purchase 8/2018

Colorless

adhesive, polymer, pressure-sensitive

Instabond C Adhesive

Unknown

Quality Media And Laminating Solutions (qmls)

Unsuitable

2018-09-27

MMA

Oddy test (method: 20180821_OT), SPME GCMS

double-sided adhesive; Catalog Number: L#415170, R#7H22554807, PN#0470137, A#1-303058, I#1384C; Purchased 8/2018; PO#OCT-5-140; Details: thicknesses: liner & exposed adhesive = 1.1 mils; release liner = 5.1 mils nominal processing range: 50-120 degrees F; service temperature range: -30 - 200 degrees F; Peel adhesion: PSTC #103; backed w/ 1 mil polyester; exposed side = 40 oz./inch width; liner side = 40 oz./inch width; Statis shear: PSTC #107 modified; 500 gm/sq inch @ room temp.; exposed & liner side = 7+ days resistance: one applied to substrate, product is generally resistant to water, mild acids and alkalis and many solvents; outdoor durability: 2 years; shelf life: 1 year at 73 degrees F; Chemical Components: adhesive: acrylic solvent, pH neutral; carrier: 1 mil clear polyester

adhesive, double-sided, polymer

Paper Tape With Gumming 067-60/0; Temporary Talas Part Number #tad607001 - Sold As Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; purchased August 2018

adhesive, polymer, single-sided

3M 431 Aluminum Foil Tape

3M

Grainger

Temporary

2018-10-09

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Aluminum foil tape; roll; tape width: 1"; length: 5 yd.; thickness: 3.10 mm; acrylic adhesive; tape tensile strength: 19 lb./in/; tape adhesive strength: 41 oz./in.; min tape performance temp: -65 degrees F; max tape performance temp: 300 degrees F; color: silver; purchased august 2018

adhesive, polymer, single-sided

Crystal Clear Non-perf Splicing Tape

Crystal Clear

Cutfilm.Com

Unsuitable

2016-06-22

MMA

Oddy test (method: 20160512_OT)

non-perf splicing tape; April 2016

adhesive, polymer, single-sided

J-lar

Shurtape

Unsuitable

2016-06-22

MMA

Oddy test (method: 20160512_OT), SPME GCMS

solvent-based acrylic packing tape; single-sided; Purchased April 2016

adhesive, polymer, single-sided

Super 77 Multipurpose Spray Adhesive

3M

Unknown

Temporary

2017-12-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

adhesive, glue, liquid, polymer

Dp-1183 2-part Urethane Adhesive-slo;

Bcc Products

Mccausey Lumber

Suitable

2017-12-28

MMA

Oddy test (method: 20171116_OT), SPME GCMS

2-part polyurethane adhesive; part A resin and Part B pink hardener mixed in a 1:1 ratio and cured 24 hours

adhesive, glue, liquid, polymer

R-2141 Adhesive Caulk

Nusil

Suitable

2017-09-20

MMA

Oddy test (method: 20170913_OT), SPME GCMS

2-part adhesive caulk; Silicone-base; Purchased 2017

caulk or sealant, adhesive, polymer

Neoprene Epdm Foam Tape, 4311n

Jacobs And Thompson

Jacobs & Thompson

Temporary

2018-07-24

MMA

Oddy test (method: 20180525_OT), SPME GCMS

Neoprene EPDM foam tape, black, closed cell foam with acrylic adhesive on one side; Chemical Components: EPDM foam, acrylic adhesive; www.foamparts.com; Purchased: 5/2017;

Black

gasket, polymer

Scotch-weld Epoxy Adhesive Dp 420 Off White

3M

Amazon.com

Temporary

2017-11-27

MMA

Oddy test (method: 20171030_OT), SPME GCMS

2 PART adhesive, MIXED W/ 3M NOZZLE; purchased 10/17; cured for 3 days prior to testing

adhesive, glue, liquid, polymer

Scotch-weld Urethane Adhesive Dp605ns Off White

3M

Amazon.com

Temporary

2017-11-27

MMA

Oddy test (method: 20171030_OT), SPME GCMS

Urethane adhesive; cured for 5 days prior to testing; purchased 10/2017

caulk or sealant, adhesive, polymer

Gorilla White Gorilla Glue

Gorilla Glue Company

Temporary

2017-11-21

MMA

Oddy test (method: 20171024_OT)

Waterproof adhesive; non-foaming; low odor; cured for 1 week prior to testing;

adhesive, glue, liquid, polymer

3M 96042

3M

Temporary

2017-09-13

MMA

Oddy test (method: 20161215_OT), SPME GCMS

Double-sided silicone adhesive transfer tape with mylar core; purchased june 2017

adhesive, double-sided, polymer

Gorilla Heavy Duty Construction Adhesive

Gorilla Glue Company

Temporary

2017-08-09

MMA

Oddy test (method: 20161215_OT), SPME GCMS

White construction adhesive; cured for 1 week before testing; purchased June 2017

White

adhesive, glue, liquid, polymer

Pl Premium Polyurethane Construction Adhesive; "pl3x"

Unknown

Loctite

Suitable

2017-12-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

polyurethane construction adhesive; this sample was cured 19 days before testing; purchased october 2017

caulk or sealant, adhesive, polymer

Vhb 4910 Double Sided Adhesive - With White Liner

3M

Unsuitable

2018-02-26

MMA

Oddy test (method: 20171116_OT), SPME GCMS

"general purpose acrylic" adhesive with foam core; purchased Januray 2018

adhesive, double-sided, polymer

3145 Rtv Mil-a-46146 Clear Adhesive Sealant

Dow Corning

Temporary

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

cured 2 months; clear silicone adhesive

gasket, polymer

Scotch Atg Gold Adhesive Transfer Tape 908, Model #b0000v4pg2c

3M

Amazon.com

Temporary

2018-02-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Details: labeled as "acid neutral" 3M Scotch 908 ATG Gold Tape, 'gold' refers to yellow and black-plaid removable backing. 1/4 inch x 36 yards; purchased januray 2018

adhesive, double-sided, polymer

Paraloid B72 Restoration Adhesive

Ardex Henry 622 Flooring Adhesive (petroleum Solvents, Urea, Koh, Plus Unnamed Polymers), White-ish Paste, Translucent Yellowish Film

Ardex

Unsuitable

2016-05-09

AWMM

Oddy test

Adhesives, consolidants

anti-slip), anti-wear, coating, floor (eg. stain

not tested on fully dried films given the full offgassing period. Should be re-tested on dried films given 4 weeks of offgassing.

Resene Aquaclear

Suitable

1996-04-01

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

coating, paint & primer

Resene Polythane

Suitable

1996-04-01

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

coating, paint & primer

Wattyl Estapol Speed Clear

Suitable

1996-04-01

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

coating, paint & primer

Ameron Coatings Ac-10 Etch Primer Stain, Black

Temporary

Slight discolouration of the copper coupon

1999-02-24

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

coating, paint & primer

Ameron Coatings Ac-10 Etch Primer Stain

Suitable

1999-02-24

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

coating, paint & primer

Cabot’s Crystal Clear Water-based Polyurethane

Akzo Nobel, Dulux

Temporary

Slight corrosion on one side of Pb coupon

2003-01-12

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

coating, paint & primer

Slight corrosion on one side of Pb coupon. Suitable for temporary use only with selected collections.

Fireproc640-wd Base Fireproofing Product And Fireproc640-wd Topcoat

Temporary

1997-05-12

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

-abbrasion, -tarnish), coating, protective (eg. anti-uv

Caprithane

Croda Lusteroid Paints

Temporary

Slight corrosion on and dulling of Pb coupon

1998-05-07

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

-abbrasion, -tarnish), coating, protective (eg. anti-uv

Slight corrosion on and dulling of Pb coupon – suitable for permanent use with selected collections,otherwise suitable only for temporary use.

Cotene 4610 Polyethylene Fluidised Bed Powder

Suitable

1999-03-19

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

cotene 4610 polyethylene fluidised bed powder

Fiwa, Black

Beele Engineering Bv

Suitable

2014-03-06

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

fire barrier, other

Quakehold Gel, Clear

Ready America

Suitable

2017-02-17

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

other, siicone gel

Bostik Super Contact Multi Purpose Brushable Adhesive

Bostik Nz

Bostik NZ

Suitable

2002-02-18

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive, glues, liquid, polymer

Plastipad Water Based Pva Adhesive

Holdfast

Unsuitable

2003-01-12

AWMM

Oddy test

Adhesives, consolidants

adhesive, glues, liquid, polymer

Evasol Adhesive, Clear

Temporary

visibly differently than control, but not really extreme

2015-07-22

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

adhesive, glues, liquid, polymer

Pb and Cu reacted visibly differently than control, but not really extreme. Probably ok if not in direct contact with object in a well ventilated area, for temporary use.

Aquence Bg P195 (vinyl Acetate Butyl Acrylate, Methyl Acrylate, Water, Plus Other Ingredients), White Liquid, Translucent Film

Glue Guru. Henkel New Zealand

Glue Guru. Henkel New Zealand Limited

Unsuitable

2016-05-09

AWMM

Oddy test

Adhesives, consolidants

adhesive, glues, liquid, polymer

not tested on fully dried films given the full offgassing period. Should be re-tested on dried films given 4 weeks of offgassing.

Aquence Bg P195 (vinyl Acetate Butyl Acrylate, Methyl Acrylate, Water, Plus Other Ingredients), Dried Film, Transparent

Glue Guru. Henkel New Zealand

Glue Guru. Henkel New Zealand Limited

Temporary

2016-08-18

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

adhesive, glues, liquid, polymer

Ardex Henry 622 Flooring Adhesive (petroleum Solvents, Urea, Koh, Plus Unnamed Polymers), Dried Film, Transparent

Ardex

Temporary

2016-08-18

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

adhesive, glues, liquid, polymer

Acrifix, Ir0192

Evonik Industries

Unsuitable

2017-02-17

AWMM

Oddy test

Adhesives, consolidants

adhesive, glues, liquid, polymer

3M Scotch-weld Hot Melt Adhesive 3762-lm-q, 3762-lm-pg, 3762-lm-tc, 3762-lm-b, 3762-lm-ae (3762-lm-q, Cloudy, Colourless, Slightly Yellow)

Ec Attwoods

Suitable

2014-05-07

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive, heat activated, polymer

3M Scotch-weld Hot Melt Adhesive 3792-lm-q, 3792-lm-pg, 3792-lm-tc, 3792-lm-b, 3792-lm-ae (3792-lm-q, Cloudy, Colourless)

Ec Attwoods

Suitable

2014-05-07

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive, heat activated, polymer

Low Melt Glue, 3M Scotchweld, 3792 Lmq, Clear

3M New Zealand

Suitable

Same as control

2015-07-22

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive, heat activated, polymer

Pretty much the same as the control.

3M Silicone/acrylic Double Coated Film Tape 9731

Suitable

1998-07-20

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants

adhesive tape, double sided, polymer

3M Tape Double Sided 415

3M

Suitable

2003-02-18

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive tape, double sided, polymer

3M Tape, Double Coated Vinyl Foam Tape, Adhesive 430, 4432, Black

3M New Zealand

Unsuitable

2008-02-28

AWMM

Oddy test

Tapes (adhesive plus backing material)

adhesive tape, double sided, polymer

Sellotape 1205 Double Sided Vinyl Tape, Colourless

The Sellotape Company

Unsuitable

2014-05-07

AWMM

Oddy test

Tapes (adhesive plus backing material)

adhesive tape, double sided, polymer

Double sided tape used between two barrier materials does not have a large surface area exposed to offgassing, so it can still be used in appropriate circumstances.

3M Double Sidedcoated Vinyl Foam Tape, Tape 4432

Unsuitable

2014-05-07

AWMM

Oddy test

Tapes (adhesive plus backing material)

adhesive tape, double sided, polymer

Sellotape 3950

Unsuitable

2003-09-16

AWMM

Oddy test

Tapes (adhesive plus backing material)

adhesive tape, polymer, single sided

Sellotape 3824

Unsuitable

Moderate corrosion on all coupons.

2003-09-16

AWMM

Oddy test

Tapes (adhesive plus backing material)

adhesive tape, polymer, single sided

Moderate corrosion on all coupons.

Sellotape 3829

Unsuitable

2003-09-16

AWMM

Oddy test

Tapes (adhesive plus backing material)

adhesive tape, polymer, single sided

Gaska Tape V1515, Black

Gaska

Temporary

2007-11-29

AWMM

Oddy test

Outside vitrine or case

Tapes (adhesive plus backing material)

adhesive tape, polymer, single sided

Dual Adhesive Tape, Clear

Frank Europe

Temporary

2007-11-29

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive tape, polymer, single sided

3M Vhb Tape, 4910 Tape, Clear

3M New Zealand

Suitable

2008-02-28

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive tape, polymer, single sided

Vhb Tape, 3M, Ga14, Ga14a, Ga14b, Clear

Glasscorp

Suitable

Same as control

2015-07-22

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

adhesive tape, polymer, single sided

Pretty much the same as the control.

Netherfield Sealant For Glass Panels/showcases, Extruded Silicone, Seal M/s -004

Netherfield

Temporary

Small specks of corrosion products on lower edge of lead coupon with uneven patina

2008-02-28

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants

gasket, polymer

Small specks of corrosion products on lower edge of lead coupon with uneven patina. Suitable for permanent use to apply to leading edges of doors and opposing edges.

S40 (previous Sh4clarl) Window Film, 3M

Unsuitable

loss of polish/corrosion of copper coupon

slight tarnishing of silver

Severe corrosion of lead coupon

2008-02-28

AWMM

Oddy test

Adhesives, consolidants

membrane (<1mm thick), polymer

Severe corrosion of lead coupon, loss of polish/corrosion of copper coupon, slight tarnishing of silver. Needs to be retested to establish if adhesive causes corrosion and if plastic film is permeable or would block chemical evaporating from adhesive.

Filmoplast P90

Neschen Coating

Unknown

Suitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

acrylic adhesive on white paper carrier

tape

none

Filmoplast P90 With Liquitex Soft Body Mars Black

Liquitex And Neschen

Unknown

Unsuitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

black acrylic dispersion paint on acrylic adhesive white paper carrier tape

Black

tape with paint

none

3M Double-sided Tape

3M

Unknown

Suitable

2013-01-01

Hodgkins

Oddy test, silver nanofilm

none

tape

none

305 Tape

3M USA

3M Australia

Suitable

1997-01-01

NAA

PAT

none

tape

n/a

3M 415 Double-sided Tape

3M USA

3M Australia

Suitable

1997-01-01

NAA

PAT

none

double-sided, tape

n/a

3M Double Sided Adhesive Tape

3M

Suitable

2009-12-23

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #6748

ACRYLIC, CLEAR, 465

Clear

adhesive, tape

none

3M Double Sided Adhesive Tape

3M

Temporary

2009-12-23

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #6747

ARCYLIC, CLEAR, 468 MP

Clear

adhesive, tape

none

3M Scotch Photo Splits

3M

Unsuitable

2010-04-09

BM

Oddy test

sample prep: N/A, test #6791

ACRYLIC ON PAPER, WHITE, 009

White

adhesive, film

none

3M Super 77

3M

Suitable

2012-09-21

BM

Oddy test

sample prep: 48 HOURS, test #7620

SOLVENT BASED ADHESIVE SPRAY WITH HEXONE AND PETROLIUM, CLEAR, SUPER 77

Clear

adhesive

none

2500 Pc Tape

3M

Unknown

Suitable

2006-09-17

GCI

Oddy test

none

tape

n/a

Adhesive

3M

Unknown

Unsuitable

1999-10-25

GCI

Oddy test

none

adhesive

n/a

Adhesive 9453

3M

Unknown

Unsuitable

1991-10-01

GCI

Oddy test

none

adhesive

n/a

Adhesive 9458

3M

Unknown

Unsuitable

1991-10-01

GCI

Oddy test

none

adhesive

n/a

Adhesive 9459

3M

Unknown

Temporary

1991-10-01

GCI

Oddy test

none

adhesive

n/a

Adhesive Transfer Tape 465

3M

Unknown

Suitable

2012-02-01

CMA

Oddy test

none

acrylic Pressure-sensitive tape

pressure-sensitive, tape

none

Aluminium Foil Tape

3M

Suitable

2013-09-10

BM

Oddy test

sample prep: N/A, test #7946

ALUMINIUM FOIL, ACRYLIC ADHESIVE, SILVER, 431

Silver

adhesive, tape

none

Correction And Coverup Tape #652

3M

Unknown

Unsuitable

1994-09-13

GCI

Oddy test

none

tape

n/a

Dp-100 Epoxy Adhesive

3M

Unknown

Suitable

1993-11-10

GCI

Oddy test

none

adhesive

n/a

Fast Bombed 30-nf Neutral Adhesive

3M

Unknown

Suitable

1996-10-28

GCI

Oddy test

none

adhesive

n/a

Fastbond Construction Mastic (9323)

3M

Unknown

Unsuitable

2000-09-18

GCI

Oddy test

none

adhesive

n/a

High Strength Adhesive

3M

Unknown

Suitable

1990-05-07

GCI

Oddy test

none

adhesive

n/a

Industrial Mastic (4289-nf)

3M

Unknown

Unsuitable

2000-09-18

GCI

Oddy test

none

adhesive

n/a

Jet Melt Hot Glue (3762-pg)

3M

Unknown

Unsuitable

2001-02-19

GCI

Oddy test

none

adhesive, hot melt

n/a

Jet Melt Hot Glue (3792-g)

3M

Unknown

Suitable

2001-02-19

GCI

Oddy test

none

adhesive, hot melt

n/a

Jet-melt Adhesive (3764)

3M

Unknown

Unsuitable

1996-03-03

GCI

Oddy test

none

adhesive, hot melt

n/a

Laminating Acrylic Adhesives (465)

3M

Unknown

Suitable

1990-09-23

GCI

Oddy test

none

adhesive

n/a

Laminating Acrylic Adhesives (467)

3M

Unknown

Unsuitable

1989-03-09

GCI

Oddy test

none

adhesive

n/a

Laminating Acrylic Adhesives (9471)

3M

Unknown

Unsuitable

1989-03-09

GCI

Oddy test

none

adhesive

n/a

Laminating Strips

3M

Unknown

Unsuitable

2005-03-22

GCI

Oddy test

none

adhesive

n/a

Low Temp Hot Melt Adhesive #3762 Lm

3M

Unknown

Unsuitable

1993-10-28

GCI

Oddy test

none

adhesive, hot melt

n/a

Scotch Roll-on Adhesive

3M

Unknown

Suitable

2000-09-26

GCI

Oddy test

none

double sided, tape

n/a

Scotch Tape #4416

3M

Unknown

Unsuitable

2001-01-15

GCI

Oddy test

none

tape

n/a

Scotch Vhb Foam Tape

3M

Unknown

Suitable

2007-05-09

GCI

Oddy test

none

tape

n/a

Scotch Weld Urethane Adhesive

3M

Unknown

Unsuitable

2000-03-27

GCI

Oddy test

none

adhesive

n/a

Super 74 Foam Fast Adhesive

3M

Unknown

Suitable

1992-01-20

GCI

Oddy test

none

adhesive

n/a

Super 77-n Spray Adhesive

3M

Unknown

Suitable

1992-01-20

GCI

Oddy test

none

adhesive, spray

n/a

Tape With Adhesive: Red

3M

Unknown

Temporary

2007-03-26

GCI

Oddy test

none

tape

n/a

Urethane Adhesive Dp-605ns, Off-white

3M

Unknown

Suitable

1994-02-17

GCI

Oddy test

none

adhesive

n/a

Vhb Acylic Foam Tape 4910 Clear

3M

Unknown

Suitable

2007-03-12

GCI

Oddy test

none

tape

n/a

Aluminium Foil Tape

Aga

Suitable

2012-11-02

BM

Oddy test

sample prep: STUCK TO ITSELF, test #7649

ALUMINIUM TAPE WITH ADHESIVE, SILVER, G256

Silver

adhesive, tape

none

No More Nails Double Sided Tape

Amazon.com

Unibond

Unsuitable

2013-09-10

BM

Oddy test

sample prep: N/A, test #7968

CLEAR, 781746

Clear

adhesive, tape

none

Buffermount Acid-free Removable Dry Mount Tissue

Bienfang Framing Products

Unknown

Suitable

2009-05-15

CMA

Oddy test

none

Nylon fiber matrix

adhesive, backed paper

none

Fusion 4000 Dry Mount Adhesive

Bienfang Framing Products

D&K Framing Products

Suitable

2012-01-01

NAA

PAT

none

adhesive, mounting

n/a

Evacon-r Conservation Adhesive

Conservation By Design

Unknown

Unsuitable

2012-09-08

BM

Oddy test

sample prep: 48 HOURS, test #7609

ETHYLENE VINYL ACRYLATE (EVA), WHITE,

White

adhesive

none

Rhoplex N-580

Dow Chemical Company

Conservation Resources International

Unsuitable

2013-09-22

CMA

Oddy test

for use in lieu of sticky wax

dried adhesive dots/ aqueous dispersion of polybutyl acrylate

Clear

adhesive, pressure sensitive

Zetta Florence Double-sided Tape'

DuPont

Zetta Florence

Suitable

1997-01-01

NAA

PAT

none

unknown

double-sided, tape

n/a

Tyvek (spun Bonded Polyolefin) Tape

DuPont

Zetta Florence

Suitable

1997-01-01

NAA

PAT

(adhesive and carrier tested separately)

tape, tyvek

n/a

Stera Double Sided Tissue Tape

Duraco

Kenwell Converters

Temporary

2009-08-05

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #6588

ACRYLIC, CLEAR, 2331

Clear

adhesive, tape

none

Supalux Barcode Label

The Elna Press

Suitable

1997-01-01

NAA

PAT

adhesive and carrier tested separately

polypropylene base and SP240 adhesive

barcode, label

n/a

Elna Press #7815 Barcode Label

The Elna Press

Zetta Florence

Suitable

1997-01-01

NAA

PAT

none

polyester base with #310 Hi Precision acrylic adhesive (adhesive and carrier tested separately)

label, polyester and acrylic

n/a

Mammoth Tape Powerful Grip Doublesided Tape

Everbuild

Everbuild (m)

Temporary

2011-08-16

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7315

Clear

adhesive, tape

none

Acid Free Self Adhesive Linen Hanging Tape

Framers Equipment.Com

Temporary

2012-01-20

BM

Oddy test

sample prep: STUCK TO ITSELF, test #7375

COTTON TAPE WITH WATER BASED ACRYLIC ADHESIVE, WHITE, SLT1

White

adhesive, tape

none

Gripit Adhesive

Henkel AG

Henkel Adhesives

Suitable

2002-01-01

NAA

PAT

none

Code 3113

adhesive

n/a

Sellotape, Double Sided

Henkel AG

London Graphic Centre

Unsuitable

2013-09-10

BM

Oddy test

sample prep: N/A, test #7960

ACRYLIC ADHESIVE?, CLEAR, 50mm

Clear

adhesive, tape

none

Le Page Pl Premium Construction Adhesive

Henkel AG

Unknown

Suitable

2013-04-18

BM

Oddy test

sample prep: 48 HOURS, test #7787

POLYURETHANE, BEIGE,

Beige

adhesive

none

Araldite Rapid

Huntsman International

Unknown

Temporary

2013-05-03

BM

Oddy test

sample prep: 48 HOURS, test #7824

2 PART EPOXY , CLEAR,

Clear

adhesive

none

Acid Free Paper Tape

Klug Conservation

Suitable

2013-01-09

BM

Oddy test

sample prep: STUCK TO ITSELF, test #7676

PAPER TAPE WITH POTATO STARCH ADHESIVE, WHITE,

White

adhesive, tape

none

Lamacoll Double Sided Adhesive Film

Lahmann

Suitable

2010-06-08

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #6842

ACRYLIC, CLEAR, 115H5G02

Clear

adhesive, film

none

Normount Foam Adhesive Tape

Norton Performance Plastics

Leach Graphics

Suitable

2009-12-16

BM

Oddy test

sample prep: STUCK TO ITSELF, test #6761

POLYURETHANE FOAM WITH ACRYLIC ADHESIVE, BLACK, V2800

Black

adhesive, tape

none

Teppichband Gewebe (carpet Tape With Cloth Backing)

Leylands Sdm (s)

Leyland Sdm

Unsuitable

2011-08-16

BM

Oddy test

sample prep: STUCK TO ITSELF, test #7317

WHITE, ART. NO. 502107000

White

adhesive, tape

none

Duplocoll Double Sided Adhesive Film

Lohmann Technologies

Temporary

2013-12-12

BM

Oddy test

sample prep: N/A, test #8080

ACRYLIC, CLEAR, VP 20391

Clear

adhesive, film

none

Filmoplast P90

Neschen Coating

Hughes Mouldings

Suitable

1997-01-01

NAA

PAT

adhesive and carrier tested separately

none

repair, tape

n/a

Gudy Transfer Adhesive

Neschen Coating

Unknown

Suitable

2010-06-08

BM

Oddy test

sample prep: 48 HOURS, test #6852

POLYACRYLATE AND SILICONISED GLASSINE PAPER, CLEAR, 870

Clear

adhesive, film

none

Toffee Tape

Pal Adhesive Products

Suitable

2013-05-30

BM

Oddy test

sample prep: N/A, test #7859

SYNTHETIC RUBBER RESIN, CLEAR,

Clear

adhesive, tape

none

Rohm And Haas

Conservation By Design

Suitable

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #7970

SOLVENT BASED ACRYLIC ADHESIVE, CLEAR,

Clear

adhesive

none

Cellulose Nitrate

Rohm And Haas

Hmg Paints

Suitable

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #7980

CELLULOSE NITRATE, CLEAR,

Clear

adhesive

none

Magic Tape

3M

Temporary

2013-09-10

BM

Oddy test

sample prep: N/A, test #7951

WATER BASED ADHESIVE, CLEAR, 810

Clear

adhesive, tape

none

Scotch Tape

3M

Scotch Tape Mer Services

Temporary

2012-07-22

BM

Oddy test

sample prep: STUCK TO ITSELF, test #7586

PAPER AND ACRYLIC ADHESIVE, BROWN, 926 TRANSFER TAPE

Brown

adhesive, tape

none

Double Sided Fabric Tape

Sealant And Tools Direct

Temporary

2013-04-19

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7796

CLEAR, 4934

Clear

adhesive, tape

none

Double Sided Pe Mounted Tape

Sealant And Tools Direct

Temporary

2013-04-19

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7800

PE FOAM WITH ADHESIVE, CLEAR, 4952

Clear

adhesive, tape

none

Tesa Double-coated Tape With High Shear And Temperature Resistance

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7530

PET BACKING, ACRYLIC ADHESIVE, CLEAR, 4965

Clear

adhesive, tape

none

Tesa Double-sided Fabric Tape

Tesa

Sealant And Tools Direct

Unsuitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7526

FABRIC BACKING, SYNTHETIC RUBBER ADHESIVE, CLEAR, 4934

Clear

adhesive, tape

none

Tesa Double-sided Filmic High Adhesion Tape

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7529

PVC FILM BACKING, ACRYLIC ADHESIVE, WHITE, 4970

White

adhesive, tape

none

Tesa Double-sided Non-woven Tape

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7534

ACRYLIC ADHESIVE, CLEAR, 4959

Clear

adhesive, tape

none

Tesa Double-sided Non-woven Tape

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7527

WATER-BASED ACRYLIC ADHESIVE, CLEAR, 51575

Clear

adhesive, tape

none

Tesa Double-sided Pe Foam Mounting Tape

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7531

PE FOAM, ACRYLIC ADHESIVE, WHITE, 4952

White

adhesive, tape

none

Tesa Double-sided Pe Foam Mounting Tape

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7532

PE FOAM, ACRYLIC ADHESIVE, WHITE, 4957

White

adhesive, tape

none

Tesa Double-sided Pe Foam Mounting Tape

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7535

PE FOAM, ACRYLIC ADHESIVE, BLACK, 62936

Black

adhesive, tape

none

Tesa Double-sided Tape With Fabric Backing

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7533

CLOTH, NATURAL RUBBER ADHESIVE, WHITE, 4964

White

adhesive, tape

none

Tesa Tacky Transfer Tape, Double Sided

Tesa

Sealant And Tools Direct

Suitable

2012-06-06

BM

Oddy test

sample prep: BETWEEN MELINEX SHEETS, test #7528

MODIFIED ACRYLIC ADHESIVE, CLEAR, 4985

Clear

adhesive, tape

none

Splicing Tape

Unknown

Christy's Editorial Film And Video Supply

Suitable

1997-01-01

NAA

PAT

adhesive and carrier tested separately

25 mm

splicing, tape

n/a

Evasol

Unknown

Conservation Resources International

Suitable

2003-01-01

NAA

PAT

none

EVA, buffered, acid-free and reversible

adhesive

n/a

Fuji Archival Laminating Film

Unknown

Direct National Business Machines And Supplies

Suitable

2006-01-01

NAA

PAT

none

film, laminating

n/a

Cine Care' Film Splicing Tape

Unknown

John Barry

Suitable

1997-01-01

NAA

PAT

adhesive and carrier tested separately

16 mm

splicing, tape

n/a

Klucel G

Unknown

Preservation Equipment

Suitable

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #7997

CELLULOSE ETHER, CLEAR,

Clear

adhesive

none

Lascaux Adhesive

Unknown

Preservation Equipment

Suitable

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #7989

ACRYLIC EMULSION, CLEAR, D360

Clear

adhesive

none

Lineco Neutral Ph Adhesive

Unknown

Preservation Equipment

Temporary

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #7974

POLYVINYL ACRYLATE (PVA), CLEAR, 901-1128

Clear

adhesive

none

Low Melt Adhesive

Unknown

Preservation Equipment

Temporary

2012-08-14

BM

Oddy test

sample prep: MELTED AND COOLED, test #7600

WHITE, PEL 419-1044 BATCH 1117422

White

adhesive

none

Tyvek Adhesive Tape

Unknown

Preservation Equipment

Unsuitable

2013-09-16

BM

Oddy test

sample prep: STUCK TO ITSELF, test #8021

POLYETHYLENE, ACRYLIC ADHESIVE, WHITE, 57MM, 804-2250

White

adhesive, tape

none

Nichiban Double Sided Tape

Unknown

Regal Craft Cards

Suitable

2012-01-01

NAA

PAT

none

6mm

double-sided, tape

n/a

Optically Clear Double Sided Mounting Film

Unknown

Starleaton Digital Solutions

Suitable

2012-01-01

NAA

PAT

none

film, mounting

n/a

Carboxy Methyl Cellulose

Unknown

Suitable

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #8001

CARBOXY METHYL CELLULOSE, CLEAR,

Clear

adhesive

none

Clam 58

Unknown

Suitable

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #7993

VINYL ACRYLIC, CLEAR,

Clear

adhesive

none

Mowilith 50 (50% In Ims)

Unknown

Suitable

2013-09-10

BM

Oddy test

sample prep: 48 HOURS, test #7984

PVA , CLEAR,

Clear

adhesive

none

Glazing Sealant Tape

Work Site

Unknown

Unsuitable

2000-03-21

GCI

Oddy test

none

tape

n/a

World Brand 300 Adhesive

World Brand

Unknown

Suitable

2013-02-25

BM

Oddy test

sample prep: 48 HOURS, test #7705

POLYCHLOROPRENE RUBBER, YELLOW, 300

POLYCHLOROPRENE RUBBER

Yellow

adhesive

none

Economy Hot Glue

Temporary

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

Ethylene Vinyl Acetate Polymer

adhesive

Economy Hot Glue

Temporary

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

Isobutylene/Butane Copolymer

adhesive

3M Double Sided Tape

3M

Preservation Equipment

Unsuitable

2019-02-14

HCC

Oddy test

none

adhesive tape, double sided, polymer

Kap Bond Acid-free Repair Glue

Unknown

Promatech (Singapore)

Unsuitable

2019-02-14

HCC

Oddy test

none

adhesive sealant, polymer

Silicone Release Tape

Talas

Suitable

2021-02-22

NYUL

Oddy test

Color: Green

Tape designed to adhere to silicone-coated surfaces. Catalog number SKU: TPB018001.

Green

adhesive tape, polymer, single sided

Plasti-dip Black Multi-purpose Rubber Coating

Plasti Dip International

Auto Zone

Unsuitable

2020-12-02

MMA

Oddy test (method: 20190226_OT_1)

Matte black synthetic rubber coating applied by spraying, brushing, or dipping; Resists moisture, acids, abrasion, corrosion, slipping; 30 minutes dry between coats, 4 hours per coat to full dry; 4 coats sprayed onto mylar, allowed to cure for 2 days prior to testing, removed from mylar before testing; Purchased in 2020

Black

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Monokote Mk-6 Hy Cementitious Fireproofing

Gcp Applied Technologies

Temporary

2020-11-04

MMA

Oddy test (method: 20190226_OT_1)

Single component, spray applied, mill-mixed fire resistive plaster; Contains calcium carbonate, quartz (SiO2), and calcium sulfate; Sample prepared by manufacturer, received September 2020

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Monokote Z-146 High Density Proofing

Gcp Applied Technologies

Temporary

2020-11-04

MMA

Oddy test (method: 20190226_OT_1)

Portland cement-based, factory-mixed high density fireproofing; applied with water and spray applied directly to structural steel; provides up to 4 hours of fire resistance; 40 pcf dry density; contains portland cement, quarts (SiO2), and hexavalent chromium; sample prepared by manufacturer, received September 2020

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Bonaseal Waterborne Organic Solvent Sealer (now Known As Classicseal)

Bona

Amazon.com

Unsuitable

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

Wood floor sealer specially formulated for use with Bona Naturalem Bona Traffic, and Bona Mega Finishes. Non-yellowing, odorless, 2-3 hr dry time, maximum cure: 1 week. pH 7.8, 1.04 specific gravity. Contains water, acrylic resin, (2-methoxymethylethoxy)propanol (also known as dipropylene glycol monomethyl ether), and defoamers. Purchased August 2020, cured for 20 days

anti-slip), coating, floor (eg.: anti-wear

Bonatraffic Hd (+ Hardener) Waterborne Floor Finish

Bona

Amazon.com

Temporary

2020-10-21

MMA

Oddy test (method: 20190226_OT_1)

Clear, colorless, nonflammable finishing for hardwood floor. Dries in about 2-3 hours, full cure in 3 days. pH 7.9, 1.04 specific gravity, 0°C melting point, 100°C boiling point. Contains water, polymeric resins, and amorphous silica. Hardner has 1.09 relative density, contains propylene carbonate, hydrofilic aliphatic polyisocyanate, and Hexane, 1,6-diisocyanato-, homopolymer. Purchased August 2020, cured for 20 days

Clear

anti-slip), coating, floor (eg.: anti-wear

Dc315, Intumescent Paint

International Fireproof Technology

Unsuitable

2020-10-08

MMA

Oddy test (method: 20190226_OT_1)

Intumescent fireproofing paint, contains ammonium polyphosphate, melamine, pentaerythritol, PVAC resin, and titanium dioxide. Received January 2020, cured for 7 days

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Sancure™ 878, Polyurethane Sealant

Lubrizol

Temporary

2020-09-29

MMA

Oddy test (method: 20190226_OT_1)

High gloss polyurethane sealant for hardness, abrasion resistance and flexibility; co-solvent free. Adhesion to wood, plastic, metal, and textiles. Received February 2020, cured for 5 days

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

394 Perimeprime, Anti-corrosion Primer

Tnemec

Unsuitable

2020-09-18

MMA

Oddy test (method: 20190226_OT_1)

Anti-corrosion primer for use under fireproofing systems. Specially formulated, one-component, moisture-cured, micaceous iron oxide and zinc filled primer that offers superior bonding to marginally prepared rusty steel and tightly adhered old coatings. Triple barrier mechanism of zinc, mio and urethane resin built into the dry film. 100°C boiling point, 2.56 specific gravity. Contains micaceous iron oxide, zinc (total dust), diphenylmethane diisocyanate polymer, p-chlorobenzotrifluoride, aromatic hydrocarbon mixture, 1,2,4-trimethylbenzene, C.I. pigment brown 24, tert-butyl acetate, diphenylmethane diisocyanate reactive monomer, talc (respirable dust), polymeric MDI, p-toluenesulfonyl isocyanate, 1,3,5-trimethylbenzene, diphenylmethane-2,2-diisocyanate monomer, and cumene (skin). Received August 2020, cured onto steel panels by manufacturer

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

27wb Typoxy

Tnemec

Temporary

2020-09-18

MMA

Oddy test (method: 20190226_OT_1)

A unique, low odor, low VOC, water-based epoxy coating fordurability and corrosion resistance on steel and concrete structures. 72°C boiling point, 1.59 specific gravity. Contains titanium oxide (total dust), epoxyamine adduct resin, amorphous calcium aluminosilicate, silicon dioxide/aluminum oxides, crystalline silica (quartz), amorphous silica, proprietary pigment, and boron oxide. Received August 2020, cured onto steel panels by manufacturer

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Cafco Blaze Shield Ii

Isolatek International

Unsuitable

2020-09-04

MMA

Oddy test (method: 20190226_OT_1)

A high strength commercial density, Portland cement based Spray-Applied Fire Resistive Material (SFRM). R-value of 2.94 R/inch, 0.240 g/mL density. Contains slag wool, Portland cement, quartz (SiO2), and petroleum distillates, hydrotreated middle. Received July 2020

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Southwest Type 7hd Fireproofing

Carboline

Temporary

2020-03-04

MMA

Oddy test (method: 20190226_OT_1)

Color: Grey

A cementitious spray-applied fire-resistive materials intended for the fire protection of structural columns, beams, joists, decks, walls, roofs, girders, floors and pre-cast concrete units. 40 lb./ft³ (640 kg/m³) average density. ~1-inch thick sample received January 2020. Sprayed onto wooden board during preparation according to manufacturer, but came without the board.

Gray

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Pyrocrete 40 Fireproofing

Carboline

Temporary

2020-03-04

MMA

Oddy test (method: 20190226_OT_1)

Color: Tan

Portland cement based, cementitious fireproofing. Provides both hydrocarbon and cellulosic fire protection for structural steel. Can also be used to upgrade the fire resistance of existing concrete. 40 lb./ft³ (640 kg/m³) density. ~1-inch thick sample received January 2020. Sprayed onto wooden board during preparation according to manufacturer, but came without the board

Tan

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Krylon Color Master, Gloss Crystal Clear Spray Paint, 3403

Rust-Oleum

Walmart

Suitable

Consistent with Control

2019-01-11

FMNH

Oddy test

Gloss crystal clear spray. Acetone, n-butyl acetate, propane, butane, ethyl 3-ethoxypropionate, xylene (mixed isomers), ethylbenzene

Clear

coating, paint & primer

Krylon Color Master, Flat Crystal Clear Spray Paint, 3430

Rust-Oleum

Walmart

Suitable

Consistent with Control

2019-01-11

FMNH

Oddy test

Flat crystal clear spray. Acetone, n-butyl acetate, propane, butane, xylene (mixed isomers), ethyl 3-ethoxypropionate, amorphous silica, ethylbenzene

Clear

coating, paint & primer

Krylon Industrial Tough Coat Primer, Light-gray Spray Paint, A00341007

Sherwin Williams

Global Industrial

Suitable

Consistent with Control

2019-01-11

FMNH

Oddy test

Light-gray primer. Acetone, Propane, Butane, Xylene, Isobutyl Acetate, Toluene, 2-Propanol, Titanium Dioxide, Ethybenzene, Dibutly phthalate.

Gray, Light

coating, paint & primer

Rust-oleum 2x Ultra Cover, Clear Gloss Spray Paint, 327864

Rust-Oleum

Walmart

Suitable

Consistent with Control

2019-01-11

FMNH

Oddy test

Clear gloss spray. Acetone, n-butyl acetate, propane, n-butane, 1-methoxy-2-propyl acetate, ethyl 3-ethoxypropionate, xylenes, ethylbenzene

Clear

coating, paint & primer

Rust-oleum 2x Ultra Cover, Matte Clear Spray Paint, 327862

Rust-Oleum

Walmart

Suitable

Consistent with Control

2019-01-11

FMNH

Oddy test

Clear matte spray. Acetone, n-butyl acetate, propane, n-butane, dimethyl carbonate, propylene glycol monobutyl ether, naphta, ethylbenzene

Clear

coating, paint & primer

Rust-oleum Hard Hat High Performance Enamel Primer Spray Paint, Flat Grey Primer, V2182838 Bar Code 20066 00129

Rust-Oleum

Temporary

Consistent with Control

Minimal white crystal growth and gray/orange oxidative layer

2019-08-07

FMNH

Oddy test

Flat grey primer. Propane, n-butyl acetate, acetone, dimethyl carbonate, hydrous magnesium silicate, n-butane, titanium dioxide, hydrotreated light distillate, solvent naphtha, 1,2,4-trimethylbenzene, zinc phosphate, zinc oxide, methyl ethyl ketoxime, ethylbenzene

Gray

coating, paint & primer

Krylon Colormaster Paint+primer, Indoor/outdoor Spray Paint, Flat White, 3432

Krylon Products Group

Walmart

Unsuitable

Consistent with Control

White crystal growth overall

2018-03-30

FMNH

Oddy test

Flat white primer. Acetone, propane, n-butyl acetate, butane, aliphatic hydrocarbon solvent, ethyl 3-ethoxpropionate, xylene

White

coating, paint & primer

Krylon Colormaster Primer Indoor/outdoor Spray Paint, Flat White, 3455

Krylon Products Group

Walmart

Unsuitable

Consistent with Control

White crystal growth overall

2018-03-30

FMNH

Oddy test

Flat white primer. Acetone, propane, ethylbenzene, dimethyl carbonate, butane, 2-methyl-1-propanol, aliphatic hydrocarbon solvent

White

coating, paint & primer

Krylon Plastic Primer Indoor/outdoor Spray Paint, White, 51321

Krylon Products Group

Walmart

Unsuitable

Consistent with Control

White crystal growth overall

2019-08-07

FMNH

Oddy test

Flat white primer

White

coating, paint & primer

Rust-oleum Painters Touch 2x Ultra Cover Primer Spray Paint, Flat White, 249058

Rust-Oleum

Menards

Unsuitable

Consistent with Control

White crystal growth overall

2018-03-30

FMNH

Oddy test

Flat white spray paint. Acetone, petroleum distillates, and xylene

White

coating, paint & primer

Krylon Industrial Acryli-quik Primer Spray Paint, Black, 1316, #38em22

Sherwin Williams

Grainger

Unsuitable

Consistent with Control

Heavy white crystals

2017-05-08

FMNH

Oddy test

Black acrylic lacquer. Acetone, toluene, propane, butane, light aliphatic hydrocarbon solven, 2-methyl-1-propanol

Black

coating, paint & primer

Krylon Industrial Acryli-quik Primer Spray Paint, Reddish Brown, 1317, #38em46

Sherwin Williams

Grainger

Unsuitable

Consistent with Control

Few white crystals

2019-08-07

FMNH

Oddy test

Brown acrylic lacquer. Acetone, toluene, propane, butane, light aliphatic hydrocarbon solven, 2-methyl-1-propanol

Brown

coating, paint & primer

Krylon Industrial Acryli-quik Primer Spray Paint, Flat Platinum Grey, 1314, #38em33

Sherwin Williams

Grainger

Unsuitable

Consistent with Control

Few white crystals

2019-08-07

FMNH

Oddy test

Flat grey acrylic lacquer. Acetone, propane, ethylbenzene, dimethyl carbonate, butane, talc, 2-methyl-1-propanol, titanium dioxide, light aliphatic hydrocarbon solvent

Gray

coating, paint & primer

Krylon Industrial Acryli-quik Primer Spray Paint, Gray, 1318, #38em47

Sherwin Williams

Grainger

Suitable

Consistent with Control

2019-08-07

FMNH

Oddy test

Gray acrylic lacquer. Acetone, toluene, propane, butane, light aliphatic hydrocarbon solvent, 2-methyl-1-propanol, titanium dioxide

Gray

coating, paint & primer

Krylon Industrial Acryli-quik Spray Paint, Flat White, 1502, # 38em26

Sherwin Williams

Grainger

Unsuitable

Consistent with Control

Yellow and white crystals

2019-08-07

FMNH

Oddy test

Flat white acrylic lacquer. Acetone, propane, methyl ethyl ketone, xylene, butane, titanium dioxide, ethylbenzene, toluene, methyl isobutyl ketone

White

coating, paint & primer

Krylon Industrial Iron Guard Latex Enamel Spray Paint, Flat White, 7910, #3cpv3

Sherwin Williams

Grainger

Suitable

Consistent with Control

2019-08-07

FMNH

Oddy test

Flat white latex. Titanium dioxide, 2-propanol, 2-butoxyethanol

White

coating, paint & primer

Krylon Industrial Iron Guard Spray Paint, Flat Black, 7911, #3cpv4

Sherwin Williams

Grainger

Suitable

Consistent with Control

2019-08-07

FMNH

Oddy test

Flat black latex enamel. 2-propanol, 2-(2-butoxyethoxy)-ethanol, carbon black

Black

coating, paint & primer

Krylon Industrial Iron Guard Spray Paint, Satin Gray, 7914, #3cpv7

Sherwin Williams

Grainger

Unsuitable

Consistent with Control

Heavy white crystals

2019-08-07

FMNH

Oddy test

Satin gray latex enamel. Titanium dioxide, 2-butoxyethanol, 2-propanol, carbon black

Gray

coating, paint & primer

Krylon Rust Protector Enamel Spray Paint, Flat Brown, 69036

Sherwin Williams

Mcmaster-Carr

Unsuitable

Consistent with Control

Heavy white crystals

2019-08-07

FMNH

Oddy test

Flat brown spray. Acetone, propane, n-butyl acetate, butane, talc, light aliphatic hydrocarbon solvent, xylene, ethyl 3 ethoxypropionate, iron oxide, ethylbenzene, unsaturated fatty acids, carbon black

Brown

coating, paint & primer

Krylon Rust Protector Rust Preventative Primer Spray Paint, Gloss Gray, 69038, # 38ep15

Sherwin Williams

Grainger

Unsuitable

Consistent with Control

Few white crystals

2019-08-07

FMNH

Oddy test

Gloss gray spray. Acetone, propane, ethylbenzene, dimethyl carbonate, butane, talc, 2-methyl-1-propanol, titanium dioxide, light aliphatic hydrocarbon solvent

Gray

coating, paint & primer

Krylon Supermaxx All-in-one Spray Paint And Primer, Flat Black, 8970, #38en09

Sherwin Williams

Grainger

Unsuitable

Consistent with Control

Heavy white crystals

2019-08-07

FMNH

Oddy test

Flat black spray. Acetone, propane, n-butyl acetate, butane, talc, aliphatic hydrocarbon solvent, ehyl 3-Eehoxypropionate, xylene, carbon black, ethylbenzene, unsaturated fatty acids

Black

coating, paint & primer

Plasti-kote Premium Enamel, Flat Black, T-2

The Valspar Corporation

Mcmaster-Carr

Suitable

Consistent with Control

2017-05-08

FMNH

Oddy test

Flat black enamel. Acetone, methyl isobutyl ketone, butyl acetate, ethyl 3-ethoxypropinate

Black

coating, paint & primer

Plasti-kote Premium Primer, Gray, T-18

The Valspar Corporation

Mcmaster-Carr

Unsuitable

Consistent with Control

White crystals

2017-05-08

FMNH

Oddy test

Gray primer. Acetone, propane, isobutyl acetate, titanium dioxide, petroleum distillates

Gray

coating, paint & primer

Rust-oleum High Performance Enamel Primer Spray Paint, Flat Grey, V2182838

Rust-Oleum

Suitable

Consistent with Control

2018-01-16

FMNH

Oddy test

Flat grey enamel spray. Propane, n-butyl acetate, acetone, dimethyl carbonate, hydrous magnesium silicate, titanium dioxide, n-Butane, hydrotreated light distillate, solvent naphtha, 1,2,4-trimethylbenzene, zinc phosphate, methyl ethyl ketoxime, ethylbenzene

Gray

coating, paint & primer

Rust-oleum High Performance Enamel Spray Paint, Flat Black, V2178838

Rust-Oleum

Unsuitable

Consistent with Control

Heavy white crystals

2018-01-16

FMNH

Oddy test

Flat black enamel spray. Acetone, propane, hydrous magnesium silicate, n-butyl acetate, n-butane, solvent naphtha, light aromatic hydrotreated, Llght distillate, dimethyl carbonate, 1,2,4-trimethylbenzene, carbon black, ethylbenzene

Black

coating, paint & primer

Rust-oleum Industrial Choice Multi-purpose Spray Paint, Flat White, 1690830, #6kp29

Rust-Oleum

Grainger

Unsuitable

Consistent with Control

White crystals

2018-01-16

FMNH

Oddy test

Flat white enamel spray. Acetone, propane, n-butane, titanium dioxide, hydrotreated light distillate, xylenes, hydrous magnesium silicate, naphtha, petroleum, hydrotreated light kaolin, ethylbenzene, methyl ethyl ketoxime

White

coating, paint & primer

Rust-oleum Industrial Choice Multi-purpose Primer, Gray, 1680830, #6kp23

Rust-Oleum

Grainger

Unsuitable

Consistent with Control

White crystals

2017-05-08

FMNH

Oddy test

Gray primer. Acetone, propane, titanium dioxide, n-butane, naphtha, light hydrotreated distillate, hydrous magnesium silicate, n-butyl acetate, xylenes, zinc phosphate, ethylbenzene, carbon black, octane, zinc oxide

Gray

coating, paint & primer

Duralaq Waterborne Finish, 1 Wb.104

Benjamin Moore

Suitable

Consistent with Control

2016-09-13

FMNH

Oddy test

Waterborne paint. Propylene glycol, propylene glycol monoethyl ether, 2-butoxyethanol, solvent naptha

coating, paint & primer

Gennex Waterborne Colorant, Black, 229s1

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Colorant. Carbon black, wollanstonite

coating, paint & primer

Gennex Waterborne Colorant, Bright Blue, 229b1

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

2016-10-25

FMNH

Oddy test

Colorant. Proprietary pigment, wollanstonite, alcohols

coating, paint & primer

Gennex Waterborne Colorant, Gray, 229s2

Benjamin Moore

Jc Licht

Unsuitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Colorant. Kaolin, carbon black

coating, paint & primer

Gennex Waterborne Colorant, Magenta, 229m1

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Colorant. Kaolin

coating, paint & primer

Gennex Waterborne Colorant, Orange, 229o1

Benjamin Moore

Jc Licht

Unsuitable

Consistent with Control

White crystals

2016-12-21

FMNH

Oddy test

Colorant. Zinc oxide

coating, paint & primer

Gennex Waterborne Colorant, Organic Red, 229r2

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

2016-10-25

FMNH

Oddy test

Colorant. Wollanstonite

coating, paint & primer

Gennex Waterborne Colorant, Organic Yellow, 229y1

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Colorant

coating, paint & primer

Gennex Waterborne Colorant, Organic Yellow, 229y2

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

White crystals

2016-12-21

FMNH

Oddy test

Colorant

coating, paint & primer

Gennex Waterborne Colorant, Oxide Red, 229r3

Benjamin Moore

Jc Licht

Unsuitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Colorant. Iron oxide

coating, paint & primer

Gennex Waterborne Colorant, Oxide Yellow, 229y3

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

2016-10-25

FMNH

Oddy test

Colorant

coating, paint & primer

Gennex Waterborne Colorant, Red Toner, 229r1

Benjamin Moore

Jc Licht

Unsuitable

Consistent with Control

Yellow crystals

2016-10-25

FMNH

Oddy test

Colorant. Kaolin

coating, paint & primer

Gennex Waterborne Colorant, Thalo Green, 229g1

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

White crystals

2016-12-21

FMNH

Oddy test

Colorant. Proprietary pigment, kaolin

coating, paint & primer

Gennex Waterborne Colorant, White 229w1

Benjamin Moore

Jc Licht

Suitable

Consistent with Control

2016-12-21

FMNH

Oddy test

Colorant. Titanium dioxide, amorphous silica, aluminum hydroxide

coating, paint & primer

Ben Waterborne Interior Flat Finish Base 1, W6251x, Tinted To #2060-30 (seaport Blue)

Benjamin Moore

Thybony Paint

Suitable

Consistent with Control

2015-10-14

FMNH

Oddy test

Water-thinned paint. Titanium dioxide, kaolin, amorphous silica

coating, paint & primer

Ben Flat Premium Interior Paint & Primer, W625-1x, Tinted To Sico Paint #6198-21 (very Pale Grey)

Benjamin Moore

Thybony Paint

Suitable

Consistent with Control

2015-10-14

FMNH

Oddy test

Water-thinned paint. Titanium dioxide, kaolin, amorphous silica

coating, paint & primer

Natura Flat Waterborne Interior Paint And Primer, Premium Performance, 512-1x, Tinted To Sico Paint #6198-21 (very Pale Grey)

Benjamin Moore

Thybony Paint

Suitable

Consistent with Control

2015-09-30

FMNH

Oddy test

Acrylic waterborne paint. Titanium dioxide, nepheline syenite, calcined kaolin, amorphous silica, diatomaceous earth

coating, paint & primer

Natura Interior Waterborne Paint, Flat, 512, Tinted To #2060-30 (seaport Blue)

Benjamin Moore

Thybony Paint

Suitable

Consistent with Control

2015-10-14

FMNH

Oddy test

Acrylic waterborne paint. Titanium dioxide, nepheline syenite, calcined kaolin, amorphous silica

coating, paint & primer

Natura Waterborne Interior Paint, Eggshell Finish, 5131x Tinted To #2060-30 (seaport Blue)

Benjamin Moore

Thybony Paint

Suitable

Consistent with Control

2015-10-14

FMNH

Oddy test

Acrylic waterborne paint. Titanium dioxide, nepheline syenite, calcined kaolin, amorphous silica

coating, paint & primer

Oece 414-9001 / White Back Paint For Glass

Oece [organizzazione Economica Commercio Emiliano (emilia Commerce Economic Organization)]

Suitable

very minor darkening

good - no corrosion

No corrosion

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

White back paint for glass - case material for Goppion cases

White

coating, paint & primer

Ag: good - no corrosion,Cu: very minor darkening,Pb: No corrosion

Europolveri Ral 9005 / Powdercoat (textured) On Steel

Europolveri

Suitable

very minor darkening

no corrosion

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Powdercoated steel

Steel

coating, paint & primer

Ag: no corrosion,Cu: very minor darkening,Pb: No corrosion

Dow Corning 3145 Rtv Mil-a-46146 Transparent / Structural Sealant And Adhesive

Dow Corning

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Sealant and Adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: very minor darkening,Pb: No corrosion

Dow Corning 7091 Black / Structural Adhesive / Sealant

Dow Corning

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Sealant and Adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Dow Corning 3145 Rtv Mil-a-46146 Transparent / Structural Sealant And Adhesive

Dow Corning

Suitable

2017-05-26

BKM

Oddy test

same as controls

Silicone adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: red - same as control,Pb: dark gray, same as control

Dow Corning Rtv Sealant 737 Neutral Cure Sealant

Dow Corning

Unsuitable

2017-05-26

BKM

Oddy test

much more corrosion on Pb than control

Silicone adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: red - same as control,Pb: white corrosion, none on control

Dow Corning Rtv Sealant 737 Neutral Cure Sealant, 100% Silicone Rubber

Dow Corning

Unsuitable

2018-10-05

BKM

Oddy test

extended Oddy test - 52 days

sealing casework (SmallCorp cases on the 2nd floor)

adhesive caulk, polymer

Ag: no corrosion,Cu: multicolored corrosion,Pb: significantly darker than controls

Dow Corning Rtv Sealant 737 Neutral Cure Sealant, 100% Silicone Rubber

Dow Corning

Suitable

2018-12-17

BKM

Oddy test

sealing casework (SmallCorp cases on the 2nd floor)

adhesive caulk, polymer

Ag: no corrosion,Cu: darkened slightly compared to control,Pb: no corrosion

Oece 414-9001 / White Back Paint For Glass + Dow Corning 7091 Black / Structural Adhesive / Sealant

Oece [organizzazione Economica Commercio Emiliano (emilia Commerce Economic Organization)] and Dow Corning

Suitable

slightly red, but okay

no corrosion

No corrosion

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

2 Materials: Glass tested in combination w/ Adhesive

coating, paint & primer

Ag: no corrosion,Cu: slightly red, but okay,Pb: No corrosion

Cafco® 300

Isolatek International

Suitable

2020-01-08

MMA

Oddy test (method: 20190226_OT_1)

Color: Beige

Wet-mix gypsum based spray-applied fire resistive material; Sprayed and prepared onto wooden board by manufacturer to a thickness of less than 1 inch, tested without wood, test sample taken from area farthest from the board; Mix time of 2 minutes, mixed material must be used within 30 minutes, set-in time of 4-7 hours; A minimum substrate temperature: 40°F; Acquired November 2019

Beige

anti-abraision, anti-tarnish), coating, protective (eg.: anti-uv

Nazdar 4700 Series Water-based Screen Ink (4724) (formerly Aquasafe 2700 Series)

Nazdar Ink Technologies

Unsuitable

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #34

Permanent acrylic ink - Brown - Brushed on Mylar; air dried for 4 weeks; cut to weight; tested on Mylar

Brown

coating, paint or primer

Copper: heavy haze - Silver: OK - Lead: light white compacted corrosion

Speedball Acrylic Screen Printing Ink

Speed Ball

Temporary

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #35

Permanent acrylic ink - Black - Brushed on Mylar; air dried for 4 weeks; cut to weight; tested on Mylar

Black

coating, paint or primer

Copper: slight red tarnish - Silver: white film - Lead: darkening, light white compacted corrosion

Dowsil 7091 Adhesive/sealant

Dow Corning

Temporary

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #36

One component neutral curing silicone (alkoxy cure system - condensation cure); Formed-In-Place Gasket (FIPG) material; contains silicone, methanol - Black - Cured on Mylar for 1 week; removed from Mylar and cut to weight

caulk, sealant

Copper: very slight red tarnish - Silver: - Lead: Darkening, Thin Yellow/green compacted corrosion

Dowsil 3145 Rtv Mil-a-46146 Adhesive Sealant Clear

Dow Corning

Temporary

OK

darkening

2019-03-25

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #37

One-part polydimethylsiloxane adhesive (silicone elastomer); contains methyltrimethoxysilane, methanol, octamethyl cyclotetrasiloxane (D4), dimethyldimethoxysilane (DMDEOS) - Clear - Cured on Mylar; removed from Mylar and cut to weight

caulk, sealant

Nazdar 9700 Series Sv Screen Ink (9724)

Nazdar Ink Technologies

Color Edge

Unsuitable

OK

Thick Yellow/green compacted corrosion, Fluffy white crystals

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #55

High gloss, solvent-based screen ink; contains 2-butoxyethanol - Black - Brushed on Mylar; air dried for 10 days; cut to weight and tested on Mylar.

coating, paint or primer

Nazdar 9700 Series Sv Screen Ink

Nazdar Ink Technologies

Coloredge

Unsuitable

OK

Thick Yellow/green compacted corrosion, Fluffy white crystals

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #56

High gloss, solvent-based screen ink; contains 2-butoxyethanol - Brown - Brushed on Mylar; air dried for 10 days; cut to weight and tested on Mylar.

coating, paint or primer

Transfer/ Rubdown Ink

Coloredge

Unsuitable

Red tarnish, Diffuse heavy haze

White film likely manufacturer defect

Thin Yellow/green compacted corrosion, Fluffy white crystals

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #57

Dry ink between two non-stick protective sheets - Black - Ink transfered onto Mylar support; only one jar tested

coating, paint or primer

Copper: Red tarnish, Diffuse heavy haze - Silver: White film likely manufacturer defect - Lead: Thin Yellow/green compacted corrosion, Fluffy white crystals

Transfer/ Rubdown Ink

Coloredge

Unsuitable

Rainbow tarnish, Light haze

White film likely manufacturer defect

Thin Yellow/green compacted corrosion, Fluffy white crystals

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #58

Dry ink between two non-stick protective sheets - Brown - Ink transfered onto Mylar support; only one jar tested

coating, paint or primer

Copper: Rainbow tarnish, Light haze - Silver: White film likely manufacturer defect - Lead: Thin Yellow/green compacted corrosion, Fluffy white crystals

Kodak Ektacolor Ra Chemicals On Kodak Professional Endura Premium Paper

Kodak Alaris

Coloredge

Temporary

OK

Very slight darkening, Light yellow tinge overall

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #74

Ektacolor RA Chemicals for Process RA-4 (photographic processing); on Professional Endura Premium Paper (resin-coated multi-layers paper) - White - Cut to weight

coating, paint or primer

Epson Ultrachrome Hdx Ink-jet Inks On Epson Archival Matte Paper

Epson

Coloredge

Temporary

OK

Coupon B Slight darkening, Coupon A light blue tarnish

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #75

UltraChrome HDX Inks for ink-jet process printing; contains water, glycerol, triethanol amine (TEOA); on Archival Matte Pape white paper - Black (T8041), dark blue, and dark brown inks - Cut to weight

coating, ink, paint or primer

Natura Waterborne Interior Paint Semi-gloss Finish Base 4 (5144x) (2053-20)

Benjamin Moore

Beacon Paint

Temporary

OK

Light purple tarnish

Darkening

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #95

100% acrylic latex, zero VOC - Dark teal - Spread on Mylar; air dried for 5 weeks including one week at 45C; cut to weight; tested on Mylar

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Darkening

Natura Waterborne Interior Paint Semi-gloss Finish (1651)

Benjamin Moore

Beacon Paint

Temporary

OK

Light purple tarnish

Slight darkening, Light white compacted corrosion

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #96

100% acrylic latex, zero VOC - Dark teal - Spread on Mylar; air dried for 5 weeks including one week at 45C; cut to weight; tested on Mylar

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Slight darkening, Light white compacted corrosion

Natura Waterborne Interior Paint Semi-gloss Finish (2057-30)

Benjamin Moore

Beacon Paint

Temporary

Very slight red tarnish

Light purple tarnish

Darkening

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #97

100% acrylic latex, zero VOC - Naples blue - Spread on Mylar; air dried for 5 weeks including one week at 45C; cut to weight; tested on Mylar

coating, paint or primer

Copper: Very slight red tarnish - Silver: Light purple tarnish - Lead: Darkening

Natura Waterborne Interior Paint Semi-gloss Finish (2130-20)

Benjamin Moore

Beacon Paint

Temporary

OK

Light purple tarnish

Thin Yellow/green compacted corrosion

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #98

100% acrylic latex, zero VOC - Pine cone brown - Spread on Mylar; air dried for 5 weeks including one week at 45C; cut to weight; tested on Mylar

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Thin Yellow/green compacted corrosion

Aquasafe 2700 Series #2775 (now 4700 Series)

Nazdar Ink Technologies

Temporary

2019-07-10

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #164

Gloss water base screen ink; contains titanium dioxide, dipropylene glycol monmethyl ether, 2-(dimethylamino)ethanol, nonylphenol, additives - Super Opaque White - Spread on Mylar; air dried for 2 weeks; cut to weight and tested on Mylar.

coating, paint or primer

Copper: Very slight red tarnish - Silver: OK - Lead: Very thin Yellow/green compacted corrosion, Slight darkening

Aura Waterborne Interior Eggshell Finish Base 1 (5241x)

Benjamin Moore

Temporary

OK

Light purple tarnish

Very light white compacted corrosion, Darkening, Thin Yellow/green compacted corrosion

2019-07-10

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #165

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - White - Spread on Mylar; air dried for 3 weeks; cut to weight and tested on Mylar.

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Very light white compacted corrosion, Darkening, Thin Yellow/green compacted corrosion

Aura Waterborne Interior Eggshell Finish (2057-10)

Benjamin Moore

Temporary

slight red tarnish

Very light purple/pink tarnish

Violet/pink tarnish, Light white compacted corrosion

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #178

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - River blue - Spread on Mylar; air dried for 3 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Slight red tarnish - Silver: Very light purple/pink tarnish - Lead: Violet/pink tarnish, Light white compacted corrosion

Ink Jet Ink T8041 On Lexjet Premium Archival Matte Paper

Epson

Coloredge

Temporary

OK

Very slight darkening

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #179

Ink jet inks on LexJet Premium Archival Matte Paper - Blacks, blues - Cut to weight

coating, ink, paint or primer

Canon Lucia Inkjet Inks (1033b To 1042b And Clear Cartridge 2442b) On Somerset Enhanced Velvet 225 Paper

Canon (ink), Moab (paper)

Duggal

Temporary

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #180

Inkjet inks on Somerset Enhanced Velvet 225 paper - All colors including black - Cut to weight

coating, ink, paint or primer

Copper: OK - Silver: Light purple tarnish (coupon B) - Lead: Blue tarnish, Violet tarnish

Lucia Inkjet Inks (1033b-1042b, 2442b) On Entrada Rag Bright 300

Canon (ink), Moab (paper)

Duggal

Temporary

OK

OK, slight darkening of edges

Very slight darkening

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #181

Inkjet inks on Entrada Rag Bright 300 paper - All colors (including black) - Cut to weight

coating, ink, paint or primer

Ral Series Powder Coating (teal)

Nic Industries

Temporary

OK

Thin Yellow/green compacted corrosion on coupon B

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #198

Powder coating; polyester resin - Teal - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

Blue/Green

coating, paint or primer

Aura Waterborne Interior Eggshell Finish (2062-10 )

Benjamin Moore

Temporary

OK

Very light purple tarnish only near the band, White film likely manufacturer defect

Light white compacted corrosion heavier at base and edges

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #200

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Dark blue - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: OK - Silver: Very light purple tarnish only near the band, White film likely manufacturer defect - Lead: Light white compacted corrosion heavier at base and edges

Aura Waterborne Interior Eggshell Finish (2057-20)

Benjamin Moore

Temporary

OK

Light purple tarnish

Light white compacted corrosion

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #201

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Teal - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Light white compacted corrosion

Aura Waterborne Interior Eggshell Finish (1673)

Benjamin Moore

Temporary

OK

light purple tarnish on band only

Darkening, Light white compacted corrosion, Light fluffy white crystals

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #202

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Blue/ grey - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: OK - Silver: light purple tarnish on band only - Lead: Darkening, Light white compacted corrosion, Light fluffy white crystals

Aura Waterborne Interior Eggshell Finish (1652)

Benjamin Moore

Temporary

OK

Light purple tarnish

Darkening, Very light white compacted corrosion

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #203

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Dark teal - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Darkening, Very light white compacted corrosion

Aura Waterborne Interior Eggshell Finish (2134-20)

Benjamin Moore

Temporary

OK

Light purple tarnish

Darkening, Very light white compacted corrosion

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #204

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Medium brown - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Darkening, Very light white compacted corrosion

Aura Waterborne Interior Eggshell Finish (2134-30)

Benjamin Moore

Temporary

OK

Light purple tarnish

Slight darkening, Thin Yellow/green compacted corrosion, Light white compacted corrosion

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #205

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Grey/brown - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: OK - Silver: Light purple tarnish - Lead: Slight darkening, Thin Yellow/green compacted corrosion, Light white compacted corrosion

Map-lvs: Polyester Primer Surfacer (6001sp)

Matthews Paint

Unsuitable

OK

Thin yellow/ green compacted corrosion on A coupon, Light white compacted corrosion

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #206

Matthews Acrylic Polyurethane Ultra Low VOC, chemically crossed linked; contains styrene, acrylate monomer - White - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Map-lvs: Low Voc Satin Paint (map-lvs-1) With Spray Reducer (map-lvrs02) With Hardener (map Lvx270)

Matthews Paint

Unsuitable

OK

Darkening, Light white compacted corrosion

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #207

Matthews Acrylic Polyurethane Ultra Low VOC (mixture ratio: 3 paint:1 hardener:1 reducer); reducer contains trifluorotoluene, acetylacetone; hardener contains hexamethylene diisocyanate (HDI), trifluorotoluene; paint contains trifluorotoluene, pyrrolo, heptane-2-one, 2-ethylhexyl acetate, pentane-2-4-dione, 2-butoxyethanol, 2-methoxy-1-methylethyl acetate (PGMEA), UV-328. - Teal - Brushed on Mylar (not air-brushed); air dried for 4 weeks; cut to weight; tested on Mylar.

coating, paint or primer

Map-lvs: Flat Clear Coat (map-lvc238)

Matthews Paint

Unsuitable

OK

Thin orange compacted corrosion on coupon A, Thin Yellow/green compacted corrosion on coupon A, Fluffy white crystals on base of coupon B

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #208

Matthews Acrylic Polyurethane Ultra Low VOC; contains trifluorotoluene - Clear - Brushed on Mylar; air dried for 4 weeks (blanched upon drying in fumehood); cut to weight; tested on Mylar

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Map-lvs: Primer, Paint, Top Coat Layers

Matthews Paint

Temporary

OK

Very slight darkening

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #209

Matthews Acrylic Polyurethane Ultra Low VOC (MAP-LVS) layering (primer, paint, top coat); chemically cross linked coating; less than 50g/L VOC - Teal - Layers brushed on Mylar 24hrs apart; top layer blanched; cut to weight and tested on Mylar

coating, paint or primer

Aura Waterborne Interior Eggshell Finish (hc 159)

Benjamin Moore

Temporary

Very slight red tarnish

OK, very slight purple near holder on coupon B

Rainbow tarnish

2019-10-15

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #238

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Blue/grey - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Very slight red tarnish - Silver: OK, very slight purple near holder on coupon B - Lead: Rainbow tarnish

Aura Waterborne Interior Eggshell Finish (1672)

Benjamin Moore

Temporary

Very slight red tarnish

Very light purple tarnish

Rainbow tarnish

2019-10-15

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #239

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Light blue grey - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Very slight red tarnish - Silver: Very light purple tarnish - Lead: Rainbow tarnish

Aura Waterborne Interior Eggshell Finish (1671)

Benjamin Moore

Temporary

OK

Very light purple tarnish

Rainbow tarnish, Blue tarnish

2019-10-15

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #240

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Light blue - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: OK - Silver: Very light purple tarnish - Lead: Rainbow tarnish, Blue tarnish

Colore Powder Coating P.2 Series (ral 230 50 15)

Colore Srl

Goppion

Temporary

OK

Darkening, Very thin yellow/green compacted corrosion on coupon B

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #246

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Spruce blue - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 230 40 20)

Colore Srl

Goppion

Temporary

OK

Very slight darkening, Very light blue tarnish, Thin yellow/green compacted corrosion

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #247

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Loon turquoise - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 230 20 20)

Colore Srl

Goppion

Temporary

OK

Very slight darkening, Thin Yellow/green compacted corrosion

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #248

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Prussian blue - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 220 20 20)

Colore Srl

Goppion

Temporary

OK

Very slight blue tarnish

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #249

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Natural Indigo - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 230 30 15)

Colore Srl

Goppion

Temporary

OK

Very slight blue tarnish on coupon A, Very slight thin yellow/green compacted corrosion on coupon B

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #250

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Berry blue green - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 240 40 15)

Colore Srl

Goppion

Temporary

OK

Slight darkening on coupon B, Very slight thin yellow/green compacted corrosion

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #251

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Celeste blue - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 250 30 15)

Colore Srl

Goppion

Temporary

Very slight red tarnish

OK

violet tarnish on coupon A, very slight thin yellow/green compacted corrosion on coupon B

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #252

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Black forest - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Copper: Very slight red tarnish - Silver: OK - Lead: violet tarnish on coupon A, very slight thin yellow/green compacted corrosion on coupon B

Colore Powder Coating P.2 Series (ral 250 20 20)

Colore Srl

Goppion

Temporary

OK

darkening and very slight thin yellow/green compacted corrosion on coupon B, very slight darkening on coupon A

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #253

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Cosmos blue - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 220 40 20)

Colore Srl

Goppion

Temporary

OK

Very thin Yellow/green compacted corrosion, very slight darkening

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #254

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Mordant blue - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 220 50 15)

Colore Srl

Goppion

Temporary

OK

darkening, light blue tarnish, slight thin yellow/green compacted corrosion

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #255

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Holbein blue grey - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Colore Powder Coating P.2 Series (ral 220 30 20)

Colore Srl

Goppion

Temporary

OK

very slight film

2019-12-02

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #256

Epoxy/polyester hybrid powder coating (heavy metals and TGIC free) - Watercolor Blue - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Accolade Z4680 (z4600 Series - Flat)

Pratt And Lambert Paints

Temporary

Very slight red tarnish

Very light purple tarnish on edges and along holder

Darkening, thin yellow/green compacted corrosion

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #257

100% acrylic waterborne paint - Bright White - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Very slight red tarnish - Silver: Very light purple tarnish on edges and along holder - Lead: Darkening, thin yellow/green compacted corrosion

Super Spec Hp Alkyd Metal Primer P06 (p0601 White)

Benjamin Moore

Unsuitable

OK

Fluffy white crystals, Light white compacted corrosion

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #258

Modified alkyd with corrosion inhibitors; primer for ferrous substrates - White - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Ultra Spec Scuff X Interior Matte Finish (white 4801)

Benjamin Moore

Temporary

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #259

One-component latex paint (proprietary acrylic copolymer); contains propanoic acid and anionic surfactant - White - Spread on Mylar; air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Very slight red tarnish - Silver: Light purple tarnish on edges and along holder - Lead: Slight darkening, Thin orange compacted corrosion, light white compacted corrosion

Super Spec Hp Alkyd Primer And Ultra Spec Scuff-x Paint

Benjamin Moore

Unsuitable

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #260

Modified alkyd and one-component latex paint - White - Primer spread on Mylar and air dried for 24 hours; paint applied and air dried for 4 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Very slight red tarnish - Silver: Very ight purple tarnish on coupon A at holder fold - Lead: Fluffy white crystals

Interpon D1036 Textura Powder Coating (ral 8022)

Akzo Nobel

Goppion

Temporary

OK

Coupon A: Very slight darkening, darkening on coupon B, very thin yellow/green compacted corrosion

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #261

Polyester powder coating; lead and TGIC free - Black - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Glass Paint Polimat Pt-ma02/s (ral 8019) And Cpt-50 Hardener

Materia Srl

Temporary

2019-12-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #264

Solvent-based acrylic polyurethane glass paint - Brown - Sample B was prepared in lab on Mylar (paint and harderner, ratio 2:1) (mixture was lumpy; air dried for4 weeks; cut to weight and tested on Mylar); Sample A was prepared by supplier (sprayed and cured on glass in Italy) (sample scrapped and tested)

Brown

coating, paint or primer

Copper: OK - Silver: Yellow tarnish on coupon A on lower half, very light blue/blue-green tarnish on coupon B lower edge - Lead: Slight darkening, Fluffy white crystals only on lower half of coupon A

Interpon D1036 Textura Powder Coating (ral 9004)

Akzo Nobel

Goppion

Temporary

OK

Very slight darkening

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #266

Polyester powder coating; lead and TGIC free - Black - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Interpon D1036 Textura Powder Coating (ral 9005)

Akzo Nobel

Goppion

Temporary

OK

Very slight darkening

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #267

Polyester powder coating; lead and TGIC free - Black - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Interpon D1036 Textura Powder Coating (ral 9011)

Akzo Nobel

Goppion

Temporary

OK

Very slight darkening

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #268

Polyester powder coating; lead and TGIC free - Black - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Interpon D1036 Textura Powder Coating (ral 9017)

Akzo Nobel

Goppion

Temporary

OK

Very slight darkening

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #269

Polyester powder coating; lead and TGIC free - Black - Sample prepared on aluminum foil by supplier; cut to weight; tested with foil

coating, paint or primer

Nazdar 59000 Series Enamel Screen Ink (59122)

Nazdar Ink Technologies

Unsuitable

2020-01-03

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #270

Glossy solvent-based enamel ink - Flat white - Spread on Mylar; air dried for 3 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Slight red tarnish - Silver: White film likely manufacturer defect - Lead: Fluffy white crystals

Interpon 200 Powder Coating (pz801i Pu Tra Bonzo "cerchi Scuri")

Akzo Nobel

Goppion

Suitable

OK

Very slight darkening

2020-02-19

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #282

Polyurethane-based powder coating - Dark bronze color - Sample prepared by supplier on aluminum panel; scrapped and tested

Copper, Dark

coating, paint or primer

Aura Waterborne Interior Eggshell Finish (2057-20)

Benjamin Moore

Temporary

slight red tarnish

Light purple tarnish on edges

Light white compacted corrosion

2020-03-13

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #287

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Galapagos Turquoise - Spread on Mylar; air dried for 3 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Slight red tarnish - Silver: Light purple tarnish on edges - Lead: Light white compacted corrosion

Aura Waterborne Interior Eggshell Finish (3098)

Benjamin Moore

Temporary

slight red tarnish

Light purple tarnish on the edges

Light white compacted corrosion

2020-03-13

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #288

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Medium teal - Spread on Mylar; air dried for 3 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Slight red tarnish - Silver: Light purple tarnish on the edges - Lead: Light white compacted corrosion

Aura Waterborne Interior Eggshell Finish (csp-690)

Benjamin Moore

Beacon Paint

Temporary

red tarnish

Very light purple tarnish on the edges

Light white compacted corrosion

2020-03-13

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #289

100% acrylic latex paint; contains hexanedioic acid (adipic acid), sodium C14-C16 olefin sulfonate (anionic surfactant) - Hidden Saphire - Spread on Mylar; air dried for 3 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Red tarnish - Silver: Very light purple tarnish on the edges - Lead: Light white compacted corrosion

Liquitex Professional Spray Paint (titanium White)

Colart

Unsuitable

2020-03-13

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #292

Water-based technology, no lead, CFCs or aromatic hydrocarbons; contains triethylamine, dimethyl ether, denatured alcohol - Titanium white - Spread on Mylar; air dried for 8 weeks; cut to weight and tested on Mylar

coating, paint or primer

Copper: Slight red tarnish - Silver: OK - Lead: Fluffy white crystals

Enviro-pox Series 287, Epoxy Floor Coating

Tnemec Company

Tnemec Company Inc.

Suitable

2019-10-11

MMA

Oddy test (method: 20190226_OT_1)

Black

Waterborne 2 part epoxy-amine adduct; low odor, rapid cure, wear-resistant coating for floors, walls and other substrates; the epoxy was mixed according to the manufacturer's directions and spread in a thin coat onto a BoPET mylar-like sheet using a paint roller 7 days before testing; sample produced September 2019

Black

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Oece Paint For Case Glass, 414-9901

Oece [organizzazione Economica Commercio Emiliano (emilia Commerce Economic Organization)]

Unknown

Temporary

2018-08-01

MMA

Oddy test (method: 20180704_OT)

Black

Acrylic/polyurethane blended paint with 1 additive. Spec'd. as 3% by weight '840-03' (additive) and 4% by weight Reticulator 840-02. Dilutable with 0-10% water. Dry for stacking 24-48 hours at 25C (60% RH), 90 min 50C. 150-180 g/m^2; prodced June 2018

Black

coating, paint or primer

Co-ne65/g

Materia

Unknown

Unsuitable

2018-08-01

MMA

Oddy test (method: 20180704_OT)

Black

Black acrylic/polyurethane blended paint with adhesion promotor and activator. Spec'd. as (PA-3 + RT-4) 3% and 4% respectively. dilutable at 5-10% with water. Contains opacifiers and organic and inorganic pigments, water and glycol ethers. Produced June 2018

Black

coating, paint or primer

Resicoat Powder Coat R4-es/hgf17r

Akzo Nobel

Unknown

Temporary

2018-05-31

MMA

Oddy test (method: 20171116_OT)

Brown

Resin baked onto aluminum; samples were cut to fit into Oddy jar; weight of the aluminum far surpasses 2 grams but was subtracted so that 2 grams of coating was tested; R3-ES - Resicoat electrostatic spray application on preheated surfaces; epoxypowder coating; produced April 2018

Brown

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

Paintcote Resin, Ral 7012 Bpg

Decorative Resins International

Unsuitable

slight red tarnish (streaks)

ok

fluffy white crystals

2019-02-08

AMNH

Oddy test (method: 20190130_OT)

AMNH Test #13

Acrylic resin system; Applied to Mylar and allowed to cure - Grey - Peeled/scraped from mylar

coating, paint & primer

Copper: slight red tarnish (streaks) - Silver: ok - Lead: fluffy white crystals

Pow 85361-1 Cerchi Chiari

Akzo Nobel

Goppion

Temporary

2019-02-13

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Brown, chiari dark

Powder Coating; scraped off of aluminum plate; bronze color; purchased 10/2018; jar A contains: MT100A 20 minutes at 180C on aluminum sheet; jar B contains:MT100A 40 minutes at 180C on aluminum sheet

Brown, Dark

coating, paint or primer

Elast-o-coat (medium Grey) Resin And Hardener

Dur-a-flex

Temporary

2019-02-13

MMA

Oddy test (method: 20180821_OT)

Medium grey

Epoxy flooring; purchased 12/2019; cured for 7 days onto Mylar about 3 mm thick; Details: elast-o-coat resin and Hardener mixed on-site by Scientific Research by volume: 2 resin to 1 hardener. mixed thoroughly for 1 minute. Cure time is 8 hours at 70 degrees F. coat to 10 mil thickness.; Chemical Components: Resin: diglycidyl ether bisphenol A epoxy resin (CAS 25068-38-6) + alkyl phenol blocked polyisocyanate, aliphatic glycidyl ether diluent (oxirane, mono((C12-14-alkyloxy)methyl) derivs.) (CAS 68609-97-2), epoxy resin, titanium dioxide, carbon black, phenol, nonyl-branced. Hardener: benzyl alcohol, salicyclic acid, aminomethyl-3,5,5-trimethylcyclohexylamine, aminoethylethanolamine, 1,3-cyclohexanedimethanamine, aminopropylamorpholine, tris(2,4,6, dimethylaminomethyl) phenol, glyceryl poly(oxypropylene)tramine

Gray, medium

anti-slip), coating, floor (eg.: anti-wear

Oece 8019 Paint

Oece [organizzazione Economica Commercio Emiliano (emilia Commerce Economic Organization)]

Goppion (who Sourced From Aurelio Giannobi Industria Specchi)

Temporary

2018-09-27

MMA

Oddy test (method: 20180821_OT), SPME GCMS

Brown

Details: Painted onto A4 sized glass and scraped off. Equal mixture of paint that went through one heat treatment and paint that went through two heat treatments. One heat treatment equals 40 minutes at 35 degrees Celsius followed by 40 minutes at 70-75 degrees Celsius. The paint formulation is 3 parts 840-03 plus 4 parts 840-02 (activator).

Brown

coating, paint or primer

737 Rtv

Dow Corning

Unsuitable

2016-07-21

MMA

Oddy test (method: 20170623_OT), SPME GCMS

silicone buildings sealant; Cured for 24 hrs. (per manufacturer) before putting in Oddy test; purchased November 2015

caulk or sealant, adhesive, polymer

799 White

Dow Corning

Unsuitable

2016-07-21

MMA

Oddy test (method: 20170623_OT), SPME GCMS

white silicone buildings sealant; Cured for 14 days (per manufacturer) before putting in Oddy test; purchaed November 2015

White

caulk or sealant, adhesive, polymer

Regal Select Flate Anchor Gray 2126-30 Paint (base 547 3x)

Benjamin Moore

Temporary

2017-09-11

MMA

Oddy test (method: 20161215_OT), SPME GCMS

Wall paint; Benjamin Moore Regal Select Flat Anchor Gray 2126-30 paint (base 547 3X); 3 week dry; painted on aluminum foil with brush; Oddy tested on aluminum foil

coating, paint or primer

Regal Select Flat Anchor Gray 2126-30 (base 547 3x)

Benjamin Moore

Temporary

2017-09-25

MMA

Oddy test (method: 20161215_OT), SPME GCMS

Paint; 1 week dry; painted on aluminum foil with brush; Oddy tested on aluminum foil

coating, paint or primer

Permalac Matte

Peacock Laboratories

Temporary

2018-03-14

MMA

Oddy test (method: 20171116_OT)

Clearcoat laquer; 10554.02 - two coats applied; Chemical Components: toluene and acrylate polymers. Month/Year Purchased: 2/2018

anti-abrasion, anti-tarnish), coating, protective (eg.: anti-uv

9-1374 Clear Silicone Sealant

Dow Corning

Temporary

2016-11-28

MMA

Oddy test (method: 20161007_OT), SPME GCMS

cured according to manufacturer's instructions - 7 day room temperature cure

caulk or sealant, adhesive, polymer

739 Silicone Sealant

Dow Corning

Suitable

2016-11-28

MMA

Oddy test (method: 20161007_OT), SPME GCMS

cured according to manufacture instructions 3 days at room temperature

caulk or sealant, adhesive, polymer

791 Gray Silicone Building Sealant

Dow Corning

Unknown

Temporary

2016-09-22

MMA

Oddy test (method: 20160822_OT), SPME GCMS

silicone sealant; Cured 22 days

caulk or sealant, adhesive, polymer

795 White Silicone Building Sealant

Dow Corning

Unknown

Suitable

2016-09-22

MMA

Oddy test (method: 20160822_OT), SPME GCMS

silicone sealant; Cured 22 days

caulk or sealant, adhesive, polymer

795 Gray Silicone Building Sealant

Dow Corning

Unknown

Suitable

2016-07-21

MMA

Oddy test (method: 20170623_OT), SPME GCMS

silicone building sealant

caulk or sealant, adhesive, polymer

7091 Black One Part Silicone Sealant With Excellent Adhesion To Plastics

Dow Corning

Unknown

Suitable

2017-12-21

MMA

Oddy test (method: 20171116_OT), SPME GCMS

Cure start: 11/14/17 (6 day cure); product expiration date: 12/6/2017

caulk or sealant, adhesive, polymer

Super 77 Multipurpose Spray Adhesive

3M

Unknown

Temporary

2017-12-14

MMA

Oddy test (method: 20171116_OT), SPME GCMS

adhesive, glue, liquid, polymer

Opacicoat-300 Silicone Water Based Elastomer

Industrial Control Development, Inc

Temporary

2018-03-06

MMA

Oddy test (method: 20180206_OT), SPME GCMS

OpaciCoat 300 with "white pure" colorant; Cured for > 7 days

coating, paint or primer

Egosilicon 460 White

Ego Dichstoffwerke Gnbh & Co. Betriebs Kg

Suitable

2018-02-13

MMA

Oddy test (method: 20171116_OT), SPME GCMS

cured at least 24 hours; model #366; silicone sealant;

caulk or sealant, adhesive, polymer

Egosilicon 460 Black

Ego Dichstoffwerke Gnbh & Co. Betriebs Kg

Suitable

2018-02-13

MMA

Oddy test (method: 20171116_OT), SPME GCMS

cured at least 24 hours; model #366; silicone sealant

caulk or sealant, adhesive, polymer

Resene Lumbersider Acrylic

Resene Paints

Suitable

1996-04-01

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Resene Lustacryl Semi Gloss Water Based Enamel Paint

Resene Paints

Suitable

1997-01-01

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Resene Supergloss Interior/exterior Enamel, White

Resene Paints

Temporary

1997-02-06

AWMM

Oddy test

Paints, varnishes,stains

coating, paint & primer

Alto Country Colours Cabinet Interior Acrylic

Alto

Suitable

1997-04-03

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Levene Goldline Low Sheen Acrylic Interior/exterior Paint

Levene

Temporary

1997-04-03

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

coating, paint & primer

Suitable for use in temporary exhibition spaces only, ie up to 6 mths. Not suitable for storage spaces.

Resene Zylone Sheen Washable Wallpaint Vinyl Interior Interior/exterior

Resene Paints

Temporary

1997-04-03

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

coating, paint & primer

Suitable for use in temporary exhibition spaces only, ie up to 6 mths. Not suitable for storage spaces.

Resene Zylone Sheen Low Sheen Acrylic Interior/exterior

Resene Paints

Temporary

1997-04-03

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

coating, paint & primer

Suitable for use in temporary exhibition spaces only, i.e. up to 6 mths. Not suitable for storage spaces.

Resene Lumbersider Acrylic

Resene Paints

Suitable

1997-05-12

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Resene Supergloss Interior/exterior Enamel (oil Based, White)

Resene Paints

Unsuitable

1997-05-12

AWMM

Oddy test

Paints, varnishes,stains

coating, paint & primer

Resene Zylone 20 Vinyl Flat Wallpaint Interior

Resene Paints

Suitable

1997-05-12

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Suitable for use in temporary exhibition spaces only, i.e. up to 6 mths. Not suitable for storage spaces.

Resene Pva Semigloss Acrylic Decorator Series Paint

Resene Paints

Suitable

1997-05-12

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Resene Enamacryl Gloss Water Based Enamel Paint

Resene Paints

Suitable

1997-05-12

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Resene Alkyd Satin Oil Based Enamel Paint, Decorator Series

Resene Paints

Unsuitable

1997-05-12

AWMM

Oddy test

Paints, varnishes,stains

coating, paint & primer

Dulux Breatheasy Low Sheen Interior Paint

Akzo Nobel, Dulux

Suitable

1999-02-24

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Dulux Interior Low Sheen Acrylic Wash And Wear

Akzo Nobel, Dulux

Temporary

Slight discolouration on the silver coupon

1999-02-24

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

coating, paint & primer

Slight discolouration on the silver coupon. Suitable for use with selected displays only, or for temporary use.

Plasti-kote Premium Water Based Enamel Spray Paint , Black Semi-gloss

Unsuitable

1999-08-15

AWMM

Oddy test

Paints, varnishes,stains

coating, paint & primer

Paintplus Colour Systems Quikprep , White

Suitable

2001-08-30

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Paintplus Colour Systems Scenic Flat White

Suitable

2001-08-30

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Paintplus Colour Systems Acrynamel , White

Temporary

slight overall corrosion on lead coupon.

2001-08-31

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Suitable for temporary use – slight overall corrosion on lead coupon.

Paintplus Colour Systems , Scenic Flat White

Suitable

2001-09-01

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Plastikote Spray Primer

Unsuitable

2003-01-12

AWMM

Oddy test

Paints, varnishes,stains

coating, paint & primer

Mirotec Wb-8060 Clear Water Based Topcoat

Calavera Specialist Construction And Installation

Suitable

Very slightly more reacted than controls, borderline acceptable.

2014-05-07

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Dulux Kulorthene 500es, 9239133s, Black

Akzo Nobel, Dulux

Dulux Powder And Industrial Coatings

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Ao 470 Mirotone Polyurethane Coating, Topcoat, 1k

Industria Chimica Adriatica S.P.A.

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Ao 470 Mirotone Polyurethane Coating, Topcoat, 2k

Industria Chimica Adriatica S.P.A.

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Fa452b Mirotone Polyurethane Coating, Undercoat, 1k

Industria Chimica Adriatica S.P.A.

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Fa452b Mirotone Polyurethane Coating, Undercoat, 2k

Industria Chimica Adriatica S.P.A.

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Aob510g25 Mirotone Polyurethane Coating, Topcoat, 1k

Industria Chimica Adriatica S.P.A.

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Aob510g25 Mirotone Polyurethane Coating, Topcoat, 2k

Industria Chimica Adriatica S.P.A.

Suitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Speedlac Black, Ppg262

PPG Industries, New Zealand

PPG Industries (New Zealand)

Unsuitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Ppg849 G30

PPG Industries, New Zealand

PPG Industries (New Zealand)

Unsuitable

2017-05-18

AWMM

Oddy test

In vitrine or case

Paints, varnishes,stains

coating, paint & primer

Densi-proof

Protect Crete Nz

Protect Crete (NZ)

Temporary

2009-01-12

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

-abbrasion, -tarnish), coating, protective (eg. anti-uv

Lustre-shield

Protect Crete Nz

Protect Crete (NZ)

Suitable

2009-01-12

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

-abbrasion, -tarnish), coating, protective (eg. anti-uv

Pinnacle (wet), Cloudy, Colourless

Johnsondiversey

Temporary

2013-10-16

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

-abbrasion, -tarnish), coating, protective (eg. anti-uv

Pinnacle (redone, Dried)

Johnsondiversey

Temporary

2013-10-16

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

-abbrasion, -tarnish), coating, protective (eg. anti-uv

Sika Remover 208

Hydestor

Suitable

2013-03-13

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

other, stripper

Sika Remover 208

Hydestor

Suitable

2013-03-13

AWMM

Oddy test

Outside vitrine or case

Paints, varnishes,stains

other, stripper

Sikaflex At Façade,wet Sealant

Hydestor

Suitable

2013-03-13

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

coating, paint & primer

Sikaflex At Façade, Wet Sealant

Hydestor

Suitable

2013-03-13

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

coating, paint & primer

Sikaflex At Façade, Dry Sealant

Hydestor

Suitable

2013-03-13

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

coating, paint & primer

Sikaflex At Façade, Dry Sealant

Hydestor

Suitable

2013-03-13

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

coating, paint & primer

Mirotec Wb-8022 Clear Water Based Sealer

Calavera Specialist Construction And Installation

Suitable

Very slightly more reacted than controls, borderline acceptable.

2014-05-07

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants, sealants

coating, paint & primer

3M Barrier Cp25wb+ Sealant, Red

3M

Suitable

2014-03-06

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

fire barrier, other

Silastic 1080 Silicone Rtv Adhesive Sealant

Dow Corning

Suitable

1998-07-20

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

3145 Rtv Mil-a-46146 Adhesive Sealant

Dow Corning

Suitable

1998-07-20

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

Selleys All Clear Universal Copolymer Sealant

Sellys

Unsuitable

1999-02-24

AWMM

Oddy test

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

Selleys Roof And Gutter Silicone Sealer , Clear

Sellys

Suitable

1999-02-24

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

Dow Corning 580 Glass, Metal And Masony Silicone Sealant, Translucent 580

Dow Corning

Temporary

2007-11-29

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

795 Silicone Building Sealant, Neutral One Part Silicone, Black

Dow Corning

Unsuitable

2008-02-28

AWMM

Oddy test

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

Suitable for permanent use for large showcases as joint sealant /support for glass and panel materials. Not suitable in small showcases under 1m3 displaying metal objects or when in direct contact with artifacts)

580 Glass, Metal & Masonry Silicone Sealant, Dow Corning, 580, Translucent

Glasscorp Auckland

Temporary

2008-03-04

AWMM

Oddy test

In vitrine or case

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

380 Glazing And Partition Sealant, Dow Corning, Transparent, Neutral Cure

Glasscorp Auckland

Unsuitable

2008-03-04

AWMM

Oddy test

Adhesives, consolidants, sealants

caulk or sealant, adhesive, polymer

Suitable for permanent use as joint sealant for glass and panel materials. Not suitable for mounts or when in direct with artefacts in particular lead and copper objects.

Selleys Brick And Concrete Silicone Sealer , Opaque

Sellys

Suitable

1999-05-24

AWMM

Oddy test

Outside vitrine or case

Adhesives, consolidants, sealants

-abbrasion, -tarnish), coating, protective (eg. anti-uv

Regal Classic Interior 100% Acrylic Paint Semi-gloss Finish Medium Base N3332b

Benjamin Moore

Temporary

2016-06-08

CAM

Oddy test

for use as interior paint; test run at 60 ˚C for 4 weeks

100% Acrylic Paint Semi-Gloss Finish Medium Base N3332B

paint/coating

Description: Ag - no change, Cu - Darkened, Pb - light grey in middle

Regal Select Eggshell Finish Base 4 S494x

Benjamin Moore

Suitable

2016-06-08

CAM

Oddy test

for use as interior paint; test run at 60 ˚C for 4 weeks

Eggshell Finish Base 4 S494X

White

paint/coating

Description: Ag - no change, Cu - Slight darkening, Pb - slight grey in middle

Dow Guard

Dow Chemical Company

Dow Chemical

Temporary

2006-01-19

CAM

Oddy test

for use in exhibit cases; test run at 60 ˚C for 8 weeks

paint/coating

Description: Ag - Slight to moderate darkening, Cu - Severe multicolotred tarnishing, Pb - Dark grey

Crystal Clear

Krylon Products Group

Unsuitable

2015-07-28

CAM

Oddy test

for use as coating; test run at 65 ˚C for 4 weeks

Acrylic Coating 1303

paint/coating

Description: Ag - no change, Cu - dark brown specks and dark purple appearance, Pb - hazy bluish corrosion

Crystal Clear

Krylon Products Group

Retest

2016-05-25

CAM

Oddy test

for use as coating; test run at 60 ˚C for 4 weeks

Acrylic Coating 1304

paint/coating

Description: Ag - no change, Cu - Tarnish, Pb - Grey spots

Crystal Clear

Krylon Products Group

Temporary

2016-07-01

CAM

Oddy test

for use as coating; test run at 60 ˚C for 4 weeks

Acrylic Coating 1305

paint/coating

Description: Ag - no change, Cu - Uneven darkening, Pb - Tarnish

Purebond + Sancure+ Pure Performance

Suitable

2007-01-31

CAM

Oddy test

for use in exhibit cases; test run at 60 ˚C for 4 weeks

substrate with paint/coating

Description: Ag - good, Cu - very slight oragne tone, Pb - moderate white haze

Sancure 878

Noveon

Suitable

shiny- OK

corrosion associated with H2O

slight darker

2006-09-29

CAM

Oddy test

for use in exhibit cases; test run at 60 ˚C for 3 weeks

Aliphatic Waterborne Urethane Polymer

coating

Description: Ag - corrosion associated with H2O, Cu - shiny- OK, Pb - slightly darker

Sancure 878

Noveon

Suitable

corrosion associated w H2O

shiny-ok

heavier corrosion near H2O

2006-09-29

CAM

Oddy test

for use in exhibit cases; test run at 60 ˚C for 4 weeks

Aliphatic Waterborne Urethane Polymer

coating

Description: Ag - shiny-ok, Cu - corrosion associated w H2O, Pb - heavier corrosion near H2O

Sancure 878

Noveon

Suitable

good

slight darkening

2007-01-31

CAM

Oddy test

for use as coating; test run at 60 ˚C for 4 weeks

Aliphatic Waterborne Urethane Polymer

coating

Description: Ag - good, Cu - good, Pb - slight darkening

Porter Flat Wall Paint

Porter

Suitable

2007-01-31

CAM

Oddy test

for use as interior paint; test run at 60 ˚C for 4 weeks

paint/coating

Description: Ag - good, Cu - slight tarnishing, Pb - slight darkening

Pure Performance Acrylic Latex Cam 17

Pittsburgh Paints

Porter

Retest

2006-09-29

CAM

Oddy test

for use in exhibit cases; test run at 60 ˚C for 3 weeks

Acrylic latex CAM 17

paint/coating

Description: Ag - slightly dull at edges, Cu - slight darkening, Pb - dark overall

Pure Performance Acrylic Latex Cam 17

PPG Industries

Porter

Retest

2006-09-29

CAM

Oddy test

for use in exhibit cases; test run at 60 ˚C for 3 weeks

Acrylic latex CAM 17

paint/coating

Description: Ag - shiny-ok, Cu - slight darkening, Pb - dark overall

Pure Performance Acrylic Latex Cam 17

Pittsburgh Paints

Porter

Suitable

2007-01-31

CAM

Oddy test

for use in exhibit cases; test run at 60 ˚C for 4 weeks

Acrylic latex CAM 18

paint/coating

Description: Ag - good, Cu - very slight, Pb - very slight

Pure Performance Acrylic Latex Eggshell 9-340 Ultra Deep Base

PPG Industries

Porter

Suitable

2016-06-08

CAM

Oddy test

for use in walls and cases; test run at 60 ˚C for 4 weeks

Acrylic Latex Eggshell 9-340 Ultra Deep Base

paint/coating

Description: Ag - no change, Cu - no change, Pb - slight grey in middle

Super Premim Silken Touch Interior Eggshell Latex Ultra Deep Base Pp999-40

PPG Industries

Porter

Temporary

2016-06-08

CAM

Oddy test

for use in walls and cases; test run at 60 ˚C for 4 weeks

Interior Eggshell Latex Ultra Deep Base pp999-40

paint/coating

Description: Ag - no change, Cu - no change, Pb - corrosion

Emerald Interior Acrylic Latex Ultra Deep Base Matte

Sherwin Williams

Suitable

2016-06-08

CAM

Oddy test

for use in walls and cases; test run at 60 ˚C for 4 weeks

Interior Acrylic Latex Ultra Deep Base Matte

paint/coating

Description: Ag - no change, Cu - no change, Pb - slight grey patches in middle

To Limn 4711 White

To Limn

Unsuitable

2009-05-18

CAM

Oddy test

for use in walls and cases; test run at 60 ˚C for 4 weeks

4710 white

White

paint/coating

Description: Ag - no change, Cu - darken overall, slight purple irridescence, Pb - very light gray overall with a band of white

To Limn 4711 White

To Limn

Temporary

2009-05-18

CAM

Oddy test

for use in walls and cases; test run at 60 ˚C for 4 weeks

4711 white

White

paint/coating

Description: Ag - no change, Cu - darken overall, Pb - hazy gray overall. Band of white corossion.

Ben Latex Interior, W625-4x

Benjamin Moore

Jill's Paint

Unsuitable

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 4

coating, paint

none

Ben Latex Interior, W625-3x

Benjamin Moore

Jill's Paint

Unsuitable

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 3

coating, paint

none

Ben Latex Interior, W625-2x

Benjamin Moore

Jill's Paint

Temporary

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 2

coating, paint

none

Ben Latex Interior, W625-1x

Benjamin Moore

Jill's Paint

Unsuitable

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 1

coating, paint

none

Regal Select Latext Interior, W547-4x

Benjamin Moore

Jill's Paint

Unsuitable

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 4

coating, paint

none

Regal Select Latext Interior, W547-3x

Benjamin Moore

Jill's Paint

Unsuitable

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 3

coating, paint

none

Regal Select Latext Interior, W547-2x

Benjamin Moore

Jill's Paint

Unsuitable

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 2

coating, paint

none

Regal Select Latext Interior, W547-1x

Benjamin Moore

Jill's Paint

Unsuitable

2024-12-21

Autry

Oddy test

Pigment-less base painted onto plastic sheeting and peeled up, Drying time: 4 weeks

Flat Base 1

coating, paint

none

Safe Coat Semi Gloss, 80290

Afm Safecoat

Temporary

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6520

ACRYLIC EMULSION, WHITE

coating, paint

none

Safe Seal Mdf Sealer, 3104

Afm Safecoat

Temporary

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6540

ACRYLIC PIGMENTED POLYMER EMULSION, CLEAR

coating, primer

none

Dulux Lifemaster Eggshell, 30bb 10/112 Signautre Blue

Akzo Nobel Canada

Dulux Paint Store Toronto

Suitable

2013-03-02

BM

Oddy test

Drying time: 4 WEEKS, test #7820

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Lifemaster Eggshell, 45yy 83/062 Stone White

Akzo Nobel Canada

Dulux Paint Store Toronto

Suitable

2013-03-02

BM

Oddy test

Drying time: 4 WEEKS, test #7821

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Interpon Powder Coat Paint, 3002

Akzo Nobel

Suitable

2010-04-15

BM

Oddy test

Drying time: BAKED, test #6808

POWDER COAT PAINT, RED

Red

coating, powder

none

Interpon Powder Coat Paint, 9005

Akzo Nobel

Suitable

2010-04-15

BM

Oddy test

Drying time: BAKED, test #6809

POWDER COAT PAINT, BLUE

Blue

coating, powder

none

Eco Spec Wb Interior Latex Eggshell Finish Base 1, Oc-17 White Dove

Benjamin Moore

Paint Colours Unlimited Toronto

Suitable

2013-03-02

BM

Oddy test

Drying time: 4 WEEKS, test #7823

ACRYLIC EMULSION, WHITE

coating, paint

none

Natura Interior Waterborne Eggshell, Af-645 Chambourd

Benjamin Moore

Paint Colours Unlimited Toronto

Suitable

2013-03-02

BM

Oddy test

Drying time: 4 WEEKS, test #7822

ACRYLIC EMULSION, PURPLE, DARK

coating, paint

none

Qualicoat Paint, Ral 7024 Matt

Bso Metallverederlung

Suitable

2013-06-26

BM

Oddy test

Drying time: N/A, test #7890

POWDER COATING PAINT, GREY, DARK

Dark, Gray

coating, powder

none

Crown Trade Ct Colour Collection Matt, 21-31t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7517

VINYL EMULSION, PURPLE

Purple

coating, paint

none

Crown Trade Ct Colour Collection Matt, 23-30t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7523

VINYL EMULSION, PURPLE

Purple

coating, paint

none

Crown Trade Ct Colour Collection Matt, 23-31t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7522

VINYL EMULSION, GREY

Gray

coating, paint

none

Crown Trade Ct Colour Collection Matt, 24-30t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7519

VINYL EMULSION, BLUE

Blue

coating, paint

none

Crown Trade Ct Colour Collection Matt, 38-32t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7524

VINYL EMULSION, GREEN

Green

coating, paint

none

Crown Trade Ct Colour Collection Matt, 42-31t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7518

VINYL EMULSION, GREEN

Green

coating, paint

none

Crown Trade Ct Colour Collection Matt, 42-32t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7516

VINYL EMULSION, GREEN

Green

coating, paint

none

Crown Trade Ct Colour Collection Matt, 48-32t

Crown Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7520

VINYL EMULSION, BROWN

Brown

coating, paint

none

Sanderson Spectrum Paint, 42-30 T, Old Leaf

Crown Paints

C Brewer & Sons

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7228

ACRYLIC EMULSION, GREEN

coating, paint

none

Crown Trade Ct Colour Collection Matt, Blue, Dark

Crown Paints

Leyland Sdm

Temporary

2013-07-08

BM

Oddy test

Drying time: L9072W, test #7896

SHOWCASE, VINYL EMULSION

crown paints ltd (m)

none

Crown Trade Ct Colour Collection Matt, Grey, Dark

Crown Paints

Leyland Sdm

Temporary

2013-07-08

BM

Oddy test

Drying time: B4070C, test #7895

SHOWCASE, VINYL EMULSION

crown paints ltd (m)

none

Crown Trade Ct Colour Collection Matt, Purple, Dark

Crown Paints

Leyland Sdm

Unsuitable

2013-07-08

BM

Oddy test

Drying time: W1081M, test #7893

SHOWCASE, VINYL EMULSION

crown paints ltd (m)

none

Crown Trade Ct Colour Collection Matt, Purple, Dark

Crown Paints

Leyland Sdm

Temporary

2013-07-08

BM

Oddy test

Drying time: U7062E, test #7894

SHOWCASE, VINYL EMULSION

crown paints ltd (m)

none

Crown Trade Ct Colour Collection Matt, Purple, Dark

Crown Paints

Leyland Sdm

Unsuitable

2013-07-08

BM

Oddy test

Drying time: W5061H, test #7897

SHOWCASE, VINYL EMULSION

crown paints ltd (m)

none

Dacrylate Gloss Varnish, 103-1

Dacrylate Paints

Suitable

2013-04-19

BM

Oddy test

Drying time: 4 WEEKS, test #7767

ACRYLIC EMULSION, CLEAR

coating, varnish

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 0036 Mars Black

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6370

ACRYLIC PAINT, BLACK

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 009 Titanium White

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6369

ACRYLIC PAINT, WHITE

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 111 Coeruleum

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6372

ACRYLIC PAINT, BLUE

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 123 Ultramarine

Daler-rowney

Unsuitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6371

ACRYLIC PAINT, BLUE

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 221 Burnt Sienna

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6366

ACRYLIC PAINT, BROWN, DARK

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 223 Burnt Umber

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6365

ACRYLIC PAINT, BROWN, DARK

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 247 Raw Umber

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6363

ACRYLIC PAINT, BROWN

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 501 Cadmium Red

Daler-rowney

Temporary

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6367

ACRYLIC PAINT, RED

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 525 Crimson Alizarin

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6368

ACRYLIC PAINT, RED

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 612 Cadmium Yellow

Daler-rowney

Temporary

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6362

ACRYLIC PAINT, YELLOW

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 651 Lemon Yellow

Daler-rowney

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6361

ACRYLIC PAINT, YELLOW, LIGHT

coating, paint

none

Daler-rowney Cryla Artists' Heavy Body Acrylic Colour, 663 Yellow Ochre

Daler-rowney

Temporary

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6364

ACRYLIC PAINT, YELLOW, DARK

coating, paint

none

Skywhite Paint

Delta Design

Unknown

Suitable

2000-09-19

GCI

Oddy test

tested for gallery walls

white paint

White

paint, water based

n/a

Transparent Noncorrosive Silicone Adhesive Sealant, As 7096n

Dow Corning

Suitable

2009-09-16

BM

Oddy test

Drying time: 24 HRS, test #6605

SILICONE ADHESIVE, CLEAR

Clear

sealant

none

Dow Corning Adhsive Selant, 799

Dow Corning

Conservation By Design

Suitable

2013-01-18

BM

Oddy test

Drying time: 48HRS, test #7680

NEUTRAL 1 PART SILICONE SEALANT, WHITE

sealant

none

Dow Corning , 993 2k

Dow Corning

Temporary

2013-03-22

BM

Oddy test

Drying time: 48 HOURS, test #7738

SILICON, BLACK

Black

sealant

none

Ascodur Sf Hv Polyurethane Soft Feel Coat, Ral7024

Dr. A, Schoch Ag/ Leo Lachenner Malergesschaft

Temporary

2010-07-19

BM

Oddy test

Drying time: 4 WEEKS, test #6903

POLYURETHANE, BLACK

Black

coating, paint

none

Claypaint, 3-1211

Earth Born

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6523

CLAY PAINT, WHITE

coating, paint

none

Pro Aqua Eggshell, 2-3792

Earth Born

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6530

WATER BASED EMULSION, WHITE

White

coating, paint

none

Atmosphere Purifying Wall Paint,

Ecos

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6522

EMULSION, WHITE

White

coating, paint

none

Mdf Passivating Primer,

Ecos

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6533

EMULSION, WHITE

White

coating, primer

none

Farrow & Ball Estate Emulsion, 1 Lime White

Farrow & Ball

C Brewer & Sons

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7489

VINYL EMULSION, CREAM

Cream, White

coating, paint

none

Farrow & Ball Estate Emulsion, 2003 Pointing

Farrow & Ball

C Brewer & Sons

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7488

VINYL EMULSION, WHITE

White

coating, paint

none

Farrow & Ball Estate Emulsion, 2005 All White

Farrow & Ball

C Brewer & Sons

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7491

VINYL EMULSION, WHITE

White

coating, paint

none

Farrow & Ball Estate Emulsion, 2009 Clunch

Farrow & Ball

C Brewer & Sons

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7490

VINYL EMULSION, CREAM

Cream, White

coating, paint

none

Farrow & Ball Estate Emulsion, 2010 James White

Farrow & Ball

C Brewer & Sons

Temporary

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7492

VINYL EMULSION, CREAM

Cream, White

coating, paint

none

Farrow & Ball Estate Emulsion, 43 Eating Room Red

Farrow & Ball

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7521

VINYL EMULSION, RED

Red

coating, paint

none

Golden Heavy Body Acrylics, Series 1/ Pw6 Titanium White

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6375

ACRYLIC PAINT, WHITE

coating, paint & primer

none

Golden Heavy Body Acrylics, Series 1/1020-2/pbr7 Burnt Sienna

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6374

ACRYLIC PAINT, BROWN, DARK

coating, paint & primer

none

Golden Heavy Body Acrylics, Series 1/1030-2/pbr7 Burnt Umber

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6381

ACRYLIC PAINT, BROWN

coating, paint

none

Golden Heavy Body Acrylics, Series 1/1340-2/py43 Raw Sienna

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6373

ACRYLIC PAINT, BROWN, LIGHT

coating, paint

none

Golden Heavy Body Acrylics, Series 1/1350-2/pbr7 Raw Umber

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6382

ACRYLIC PAINT, BROWN

coating, paint

none

Golden Heavy Body Acrylics, Series 1/1407-2/py43 Yellow Ochre

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6380

ACRYLIC PAINT, YELLOW, DARK

coating, paint

none

Golden Heavy Body Acrylics, Series 1/pbk11 Mars Black

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6376

ACRYLIC PAINT, BLACK

coating, paint

none

Golden Heavy Body Acrylics, Series 1/pr112 Napthol Red Light

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6379

ACRYLIC PAINT, RED

coating, paint

none

Golden Heavy Body Acrylics, Series 2/pb29 Ultramarine

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6383

ACRYLIC PAINT, BLUE

coating, paint

none

Golden Heavy Body Acrylics, Series 3/py73 Hansa Yellow Medium

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6377

ACRYLIC PAINT, YELLOW

coating, paint

none

Golden Heavy Body Acrylics, Series 4/1554-2 Py83/py53/py3 Cadmium Yellow Medium

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6378

ACRYLIC PAINT, YELLOW

coating, paint

none

Golden Heavy Body Acrylics, Series 4/p43/pg7 Permanent Green Light

Golden Artist Colors

London Graphics Centre

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6384

ACRYLIC PAINT, GREEN, LIGHT

coating, paint

none

Halfords Enamel Matt Spray Paint, Articelcode: 155666

Halfords

Temporary

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6983

SOLVENT BASED AEROSOL, WHITE

White

coating, paint

none

Halfords Enamel Matt Spray Paint, Articelcode: 155724

Halfords

Temporary

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6985

SOLVENT BASED AEROSOL, BLACK

Black

coating, paint

none

Halfords Enamel Matt Spray Paint, Articelcode: 451583

Halfords

Temporary

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6984

SOLVENT BASED AEROSOL, BLACK

Black

coating, paint

none

Halfords Enamel Spray Paint, Articelcode: 156581

Halfords

Suitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6987

SOLVENT BASED AEROSOL, GREY

Gray

coating, paint

none

Halfords Primer Spray Paint, Articelcode: 451542

Halfords

Temporary

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6986

SOLVENT BASED AEROSOL, GREY

Gray

coating, paint

none

Halfords Primer Spray Paint, Articelcode: 473124

Halfords

Suitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6982

SOLVENT BASED AEROSOL, WHITE

White

coating, paint

none

Hammerite Direct To Rust Metal Paint,

Hammerite

Unsuitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6537

SOLVENT BASED, WHITE

White

coating, paint

none

Terostat, 9220

Henkel AG

Henkel Teroson

Suitable

2012-10-26

BM

Oddy test

Drying time: 48 HOURS, test #7644

MS POLYMER, BLACK

sealant

none

Morelli Spray Paint, Ral 7030 Stone Grey

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6837

Gray

coating, paint

none

Morelli Spray Paint, Ral 7037 Dusty Grey

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6838

Gray

coating, paint

none

Morelli Spray Paint, Ral 9001

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6834

Cream

coating, paint

none

Morelli Spray Paint, Ral 9003 Signal White

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6836

WHITE

White

coating, paint

none

Morelli Spray Paint, Ral 9004 Matt Black

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6840

Black

coating, paint

none

Morelli Spray Paint, Ral 9004 Signal Black Gloss

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6841

Black

coating, paint

none

Morelli Spray Paint, Ral 9010 Pure White

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6835

WHITE

White

coating, paint

none

Morelli Spray Paint, Ral7022 Umber Grey

Hmg Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6839

Gray

coating, paint

none

Nauteco Mdf Sealer, F2014

Hmg Paints

Temporary

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6524

WHITE

White

coating, primer

none

Humbrol Acrylic Spray Paint, White Matt 34

Hornby Hobbies Kent

Temporary

2012-06-06

BM

Oddy test

Drying time: BAKED 60C/24 HRS, test #7545

ACRYLIC, WHITE

coating, paint

none

Dulux Enviro 2 Premium Low Sheen Acrylic, Pw2.B5

Ici Paints

Suitable

2009-02-13

BM

Oddy test

Drying time: 4 WEEKS, test #6349

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Enviro 2 Premium Low Sheen Acrylic, Pw2.D4

Ici Paints

Suitable

2009-02-13

BM

Oddy test

Drying time: 4 WEEKS, test #6348

WATER BASED ACRYLIC COPOLYMER, CREAM

Cream, White

coating, paint

none

Dulux Professional 1-step Primer, Sealer And Undercoat,

Ici Paints

Suitable

2009-02-13

BM

Oddy test

Drying time: 4 WEEKS, test #6351

ACRYLIC, CREAM

coating, primer

none

Dulux Trade Diamond Eggshell Emulsion, 5502b Battleship

Ici Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6831

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Diamond Eggshell Emulsion, Ooe53

Ici Paints

Unsuitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6832

WATER BASED ACRYLIC COPOLYMER, BLACK

Black

coating, paint

none

Dulux Trade Diamond Eggshell Emulsion, Pure Brilliant White

Ici Paints

Suitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6829

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Diamond Quick Drying Eggshell, Light W26

Ici Paints

Temporary

2009-02-12

BM

Oddy test

Drying time: 4 WEEKS, test #6192

ACRYLIC COPOLYMER, WATER-BASED, BEIGE

coating, paint

none

Dulux Trade Flat Matt Emulsion, 00yy09087

Ici Paints

Suitable

2009-11-23

BM

Oddy test

Drying time: 4 WEEKS, test #6654

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Flat Matt Emulsion, 10yy 08093

Ici Paints

Suitable

2009-11-23

BM

Oddy test

Drying time: 4 WEEKS, test #6658

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Flat Matt Emulsion, 48yr 06091

Ici Paints

Suitable

2009-11-23

BM

Oddy test

Drying time: 4 WEEKS, test #6657

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Flat Matt Emulsion, 50yr 09162

Ici Paints

Suitable

2009-11-23

BM

Oddy test

Drying time: 4 WEEKS, test #6659

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Flat Matt Emulsion, 70yr 07093

Ici Paints

Suitable

2009-11-23

BM

Oddy test

Drying time: 4 WEEKS, test #6656

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Flat Matt Emulsion, 80yr 09163

Ici Paints

Temporary

2009-11-23

BM

Oddy test

Drying time: 4 WEEKS, test #6655

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 00nn16000, Ice Storm 2

Ici Paints

Suitable

2011-03-10

BM

Oddy test

Drying time: 4 WEEKS, test #7200

WATER BASED ACRYLIC COPOLYMER, GREY, DARK

Dark, Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 10bg21141

Ici Paints

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7497

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 10yy83071

Ici Paints

Suitable

2011-11-09

BM

Oddy test

Drying time: 4 WEEKS, test #7329

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30bg23124

Ici Paints

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7496

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30gg29196

Ici Paints

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7493

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30gg33275

Ici Paints

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7494

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30yr07157, Bitter Chocolate

Ici Paints

Suitable

2011-03-10

BM

Oddy test

Drying time: 4 WEEKS, test #7201

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 40yy67087 Bleached Linen

Ici Paints

Suitable

2012-03-20

BM

Oddy test

Drying time: 4 WEEKS, test #7404

WATER BASED ACRYLIC COPOLYMER, CREAM

Cream, White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 40yy75084

Ici Paints

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7499

WATER BASED ACRYLIC COPOLYMER, CREAM

Cream, White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 4yy74056

Ici Paints

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7498

WATER BASED ACRYLIC COPOLYMER, CREAM

Cream, White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 502yr50r

Ici Paints

Suitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6830

WATER BASED ACRYLIC COPOLYMER, CREAM

Cream, White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 50gg43213

Ici Paints

Unsuitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7495

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 50rr26361

Ici Paints

Unsuitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7025

WATER BASED ACRYLIC COPOLYMER, PINK, DARK

Dark, Pink

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 5502b Battleship

Ici Paints

Suitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6827

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Ooe53

Ici Paints

Temporary

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6828

WATER BASED ACRYLIC COPOLYMER, BLACK

Black

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Pure Brilliant White

Ici Paints

Suitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6826

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Ro2y50r

Ici Paints

Suitable

2010-06-07

BM

Oddy test

Drying time: 4 WEEKS, test #6825

WATER BASED ACRYLIC COPOLYMER, CREAM

Cream, White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, S1502y50r

Ici Paints

Suitable

2012-10-02

BM

Oddy test

Drying time: 4 WEEKS, test #7630

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, S15o2r

Ici Paints

Suitable

2012-10-02

BM

Oddy test

Drying time: 4 WEEKS, test #7628

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, S200250r

Ici Paints

Suitable

2012-10-02

BM

Oddy test

Drying time: 4 WEEKS, test #7629

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 00nn13000, Night Jewels

Ici Paints

Temporary

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6958

WATER BASED ACRYLIC COPOLYMER, GREY, DARK

Dark, Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 09yr11475

Ici Paints

Suitable

2011-03-09

BM

Oddy test

Drying time: BAKED 12H/60°C + AIR DRIED 12 H, test #7196

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 10bb09155

Ici Paints

Temporary

2010-09-20

BM

Oddy test

Drying time: 4 WEEKS, test #6970

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 10rb08125, Amethyst Falls 1 Rv 3

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7223

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 10yr07125, Cocoa Blush 2 Rn2

Ici Paints

Temporary

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7212

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 10yr09250

Ici Paints

Temporary

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7218

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 11yr07229, Volcanic Splash

Ici Paints

Suitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6946

WATER BASED ACRYLIC COPOLYMER, RED, DARK

Dark, Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 12yr07279

Ici Paints

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7239

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 13yr07157, Hot Paprika

Ici Paints

Suitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6944

WATER BASED ACRYLIC COPOLYMER, RED, DARK

Dark, Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 14yr10434, Volcanic Splash 2 Ro 2

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7219

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30rr12281

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7029

WATER BASED ACRYLIC COPOLYMER, RED, DARK

Dark, Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30rr13328

Ici Paints

Temporary

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7051

WATER BASED ACRYLIC COPOLYMER, PINK, DARK

Dark, Pink

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30yr11219

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7220

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30yy08082

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7225

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 31yr10591

Ici Paints

Temporary

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7237

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 33bg14023, Ral 7012

Ici Paints

Unsuitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6956

WATER BASED ACRYLIC COPOLYMER, GREY, DARK

Dark, Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 40yy08107

Ici Paints

Suitable

2011-03-10

BM

Oddy test

Drying time: 4 WEEKS, test #7202

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 40yy08107

Ici Paints

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7231

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 47bb09031, Ral 7024

Ici Paints

Suitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6954

WATER BASED ACRYLIC COPOLYMER, GREY, DARK

Dark, Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 5030r90b, High Tide

Ici Paints

Suitable

2010-09-20

BM

Oddy test

Drying time: 4 WEEKS, test #6964

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50bb08171, Sapphire Springs

Ici Paints

Temporary

2010-09-20

BM

Oddy test

Drying time: 4 WEEKS, test #6966

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50bb10112

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7221

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50bg14036

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7227

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50rb12174

Ici Paints

Temporary

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7027

WATER BASED ACRYLIC COPOLYMER, PURPLE, DARK

Dark, Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50rr15400

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7037

WATER BASED ACRYLIC COPOLYMER, PINK, DARK

Dark, Pink

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50yr09244, Mexican Mosaic 1 Rg01

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7217

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50yy47053

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7211

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70bb07103

Ici Paints

Suitable

2011-03-10

BM

Oddy test

Drying time: 4 WEEKS, test #7199

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70rb10157

Ici Paints

Suitable

2010-12-22

BM

Oddy test

Drying time: 4 WEEKS, test #7095

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70rb11196, Himalayan Musk

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7049

WATER BASED ACRYLIC COPOLYMER, PURPLE, DARK

Dark, Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70rb18117, Mellow Heather 1

Ici Paints

Suitable

2010-12-22

BM

Oddy test

Drying time: 4 WEEKS, test #7093

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70rr10140

Ici Paints

Temporary

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7216

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70yy06088

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7224

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 72rr07173

Ici Paints

Temporary

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7214

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 78rr06137

Ici Paints

Temporary

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7213

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 82bg08029, Ral 7016

Ici Paints

Suitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6952

WATER BASED ACRYLIC COPOLYMER, GREY, DARK

Dark, Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 83bb07202, Plush Velvet 1 Rv2

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7222

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 90bb09186

Ici Paints

Unsuitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6948

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 90bg10067

Ici Paints

Temporary

2010-09-20

BM

Oddy test

Drying time: 4 WEEKS, test #6968

WATER BASED ACRYLIC COPOLYMER, GREY, DARK

Dark, Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 90yy07093, Tarragon Glory 1 Rg 1

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7226

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 93gy10014, Ral 7043

Ici Paints

Unsuitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6960

WATER BASED ACRYLIC COPOLYMER, GREY, DARK

Dark, Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 98rr06206

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7215

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 98rr10318

Ici Paints

Temporary

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7238

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, Blush Rambler 1, 50rr13343

Ici Paints

Suitable

2010-12-22

BM

Oddy test

Drying time: 4 WEEKS, test #7085

WATER BASED ACRYLIC COPOLYMER, PINK

Pink

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, Fire Cracker 2

Ici Paints

Suitable

2009-04-13

BM

Oddy test

Drying time: 4 WEEKS, test #6407

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, Hot Paprika 4

Ici Paints

Suitable

2009-04-13

BM

Oddy test

Drying time: 4 WEEKS, test #6403

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, Ruby Fountain 2

Ici Paints

Suitable

2009-04-13

BM

Oddy test

Drying time: 4 WEEKS, test #6405

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, Volcanic Splash 3

Ici Paints

Suitable

2009-04-13

BM

Oddy test

Drying time: 4 WEEKS, test #6404

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 00yy47036

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7039

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 0500n, Jabot

Ici Paints

Unsuitable

2011-07-25

BM

Oddy test

Drying time: 4 WEEKS, test #7283

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30bb10019

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7209

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30bb72003

Ici Paints

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7236

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30bg72017, Clouded Pearl 1 Fn 8

Ici Paints

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7233

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30yy53125

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7041

WATER BASED ACRYLIC COPOLYMER, BEIGE

Brown, Light

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30yy56060

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7210

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30yy68024

Ici Paints

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7235

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30yy78018

Ici Paints

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7232

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 40yy41054

Ici Paints

Suitable

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7207

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 40yy51084

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7043

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 50bg72006

Ici Paints

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7234

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 50rr43228

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7033

WATER BASED ACRYLIC COPOLYMER, PINK

Pink

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 50yy57082

Ici Paints

Temporary

2011-03-16

BM

Oddy test

Drying time: 4 WEEKS, test #7208

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 70yy46053, Grey Tope

Ici Paints

Suitable

2011-03-10

BM

Oddy test

Drying time: 4 WEEKS, test #7198

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 80yr50085

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7031

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, So300n

Ici Paints

Unsuitable

2011-07-25

BM

Oddy test

Drying time: 4 WEEKS, test #7280

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 10bb18106

Ici Paints

Suitable

2010-09-20

BM

Oddy test

Drying time: 4 WEEKS, test #6972

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 30yy51098, Chalky Downs

Ici Paints

Suitable

2010-12-22

BM

Oddy test

Drying time: 4 WEEKS, test #7089

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 34gy23002, Ral 7037

Ici Paints

Suitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6950

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 4030r90b, Personality

Ici Paints

Temporary

2010-09-20

BM

Oddy test

Drying time: 4 WEEKS, test #6962

WATER BASED ACRYLIC COPOLYMER, BLUE, LIGHT

Blue, Light

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 40yy65061

Ici Paints

Suitable

2010-12-22

BM

Oddy test

Drying time: 4 WEEKS, test #7087

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 5005r50b

Ici Paints

Unsuitable

2011-07-25

BM

Oddy test

Drying time: 4 WEEKS, test #7282

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 50rb18149

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7047

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 50rb27126

Ici Paints

Suitable

2011-01-04

BM

Oddy test

Drying time: 4 WEEKS, test #7035

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 50rr23282, Blush Rambler 2

Ici Paints

Temporary

2010-12-22

BM

Oddy test

Drying time: 4 WEEKS, test #7083

WATER BASED ACRYLIC COPOLYMER, PINK

Pink

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 70rb31090, Mellow Heather 2

Ici Paints

Suitable

2010-12-22

BM

Oddy test

Drying time: 4 WEEKS, test #7091

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 90bg38185, Luna Landscape

Ici Paints

Temporary

2010-09-20

BM

Oddy test

Drying time: 4 WEEKS, test #6974

WATER BASED ACRYLIC COPOLYMER, BLUE, LIGHT

Blue, Light

coating, paint

none

Dulux Weather Shield Exterior Gloss, Pure Brilliant White

Ici Paints

Unsuitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6534

POLYMER WITH PROPYLENE GLYCOL, WHITE

White

coating, paint

none

Dulux Weather Shield Exterior Satin, Pure Brilliant White

Ici Paints

Temporary

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6535

POLYMER WITH PROPYLENE GLYCOL, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 00nn13000

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7505

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 00nn25000

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7500

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 00nn31000

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7510

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 00nn53000

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7508

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 00nn72000

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7513

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 04yr11537

Ici Paints

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7698

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 07yr10489

Ici Paints

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7699

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 10bb08200

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7507

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 10bb11123

Ici Paints

C Brewer & Sons

Suitable

2012-12-28

BM

Oddy test

Drying time: 4 WEEKS, test #7673

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 11rr07229

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7511

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30bb08188

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7506

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30bg64072

Ici Paints

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7694

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30rr08044

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7512

WATER BASED ACRYLIC COPOLYMER, PURPLE

Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30rr17034

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7515

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30yr22059

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7501

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30yy10038

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7502

WATER BASED ACRYLIC COPOLYMER, BROWN

Brown

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30yy14070

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7504

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30yy20029

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7509

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 30yy33047

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7503

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 50bg10175

Ici Paints

C Brewer & Sons

Suitable

2012-12-28

BM

Oddy test

Drying time: 4 WEEKS, test #7674

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 50gb08021

Ici Paints

C Brewer & Sons

Suitable

2012-12-28

BM

Oddy test

Drying time: 4 WEEKS, test #7670

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 70bg 56061

Ici Paints

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7696

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 70bg 68056

Ici Paints

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7695

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 70bg07086

Ici Paints

C Brewer & Sons

Suitable

2012-12-28

BM

Oddy test

Drying time: 4 WEEKS, test #7672

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 70bg72086

Ici Paints

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7697

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 70yy27064

Ici Paints

C Brewer & Sons

Suitable

2012-04-20

BM

Oddy test

Drying time: 4 WEEKS, test #7514

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, 90bg08075

Ici Paints

C Brewer & Sons

Suitable

2012-12-28

BM

Oddy test

Drying time: 4 WEEKS, test #7671

WATER BASED ACRYLIC COPOLYMER, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 19yr14629

Ici Paints

C Brewer & Sons

Temporary

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8094

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 19yy51758 Earth Glaze 4

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8093

WATER BASED ACRYLIC COPOLYMER, YELLOW

Yellow

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 2070y10r Sunbed

Ici Paints

C Brewer & Sons

Unsuitable

2014-04-04

BM

Oddy test

Drying time: 4 WEEKS, test #8165

WATER BASED ACRYLIC COPOLYMER, YELLOW

Yellow

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 20yy23246 Labrador Sands 1

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8049

WATER BASED ACRYLIC COPOLYMER, BROWN, LIGHT

Brown, Light

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 20yy27225

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8052

WATER BASED ACRYLIC COPOLYMER, BEIGE

Brown, Light

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 20yy34700 Sundrenched Saffron

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8046

WATER BASED ACRYLIC COPOLYMER, YELLOW

Yellow

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 20yy54342 Golden Umber 3

Ici Paints

C Brewer & Sons

Temporary

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8103

WATER BASED ACRYLIC COPOLYMER, YELLOW, LIGHT

Light, Yellow

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30bb08263 Atomic Surf 1

Ici Paints

C Brewer & Sons

Suitable

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8047

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30yr11393

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8053

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30yr13471

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8050

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 30yr14365

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8043

WATER BASED ACRYLIC COPOLYMER, ORANGE

Orange

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 4040980y

Ici Paints

C Brewer & Sons

Unsuitable

2014-04-04

BM

Oddy test

Drying time: 4 WEEKS, test #8170

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 43bb09340

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8044

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50bb08257

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8051

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50bb11216 Morning Jewel 1

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8045

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 50bb11321 Sapphire Spring 2

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8048

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70gy14187 Tuscan Glade 1

Ici Paints

C Brewer & Sons

Unsuitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8090

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 70yy12167

Ici Paints

C Brewer & Sons

Temporary

2013-11-14

BM

Oddy test

Drying time: 4 WEEKS, test #8042

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 7500n

Ici Paints

C Brewer & Sons

Temporary

2014-04-04

BM

Oddy test

Drying time: 4 WEEKS, test #8166

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, 90gy16151 Highland Falls 1

Ici Paints

C Brewer & Sons

Temporary

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8091

WATER BASED ACRYLIC COPOLYMER, GREEN

Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, S3060y90r

Ici Paints

C Brewer & Sons

Temporary

2014-04-04

BM

Oddy test

Drying time: 4 WEEKS, test #8169

WATER BASED ACRYLIC COPOLYMER, RED

Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 0500n Jabot

Ici Paints

C Brewer & Sons

Suitable

2014-04-04

BM

Oddy test

Drying time: 4 WEEKS, test #8167

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 10bg39244

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8100

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 10gg53030 Hebridean Mists 4

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8099

WATER BASED ACRYLIC COPOLYMER, GREY, LIGHT

Gray, Light

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30bb45049

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8098

WATER BASED ACRYLIC COPOLYMER, GREY, LIGHT

Gray, Light

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Light Base, 30yy65171

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8101

WATER BASED ACRYLIC COPOLYMER, CREAM

Cream, White

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 10bg22275 Blue Diamond 3

Ici Paints

C Brewer & Sons

Temporary

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8107

WATER BASED ACRYLIC COPOLYMER, TURQUOISE, DARK

Blue, Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 16bg24357 Blue Diamond 4

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8108

WATER BASED ACRYLIC COPOLYMER, TURQUOISE

Blue, Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 30bb31043

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8097

WATER BASED ACRYLIC COPOLYMER, GREY

Gray

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 5020b309 Tarn

Ici Paints

C Brewer & Sons

Suitable

2014-04-04

BM

Oddy test

Drying time: 4 WEEKS, test #8168

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 50bg20230

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8096

WATER BASED ACRYLIC COPOLYMER, BLUE

Blue

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 88gg32346 Crystal Surprise 1

Ici Paints

C Brewer & Sons

Temporary

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8105

WATER BASED ACRYLIC COPOLYMER, TURQUOISE

Blue, Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Medium Base, 90gg28133 Sea Urchin 2

Ici Paints

C Brewer & Sons

Suitable

2014-01-16

BM

Oddy test

Drying time: 4 WEEKS, test #8106

WATER BASED ACRYLIC COPOLYMER, TURQUOISE

Blue, Green

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Hot Paprika 1 R03

Ici Paints

Leyland Sdm

Suitable

2013-07-08

BM

Oddy test

Drying time: 5 WEEKS 4 DAYS, test #7898

VINYL EMULSION, RED, DARK

Dark, Red

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, Himalayan Musk 70rb11196

Ici Paints

Leyland Sdm

Temporary

2013-09-10

BM

Oddy test

Drying time: 4 WEEKS, test #7933

WATER BASED ACRYLIC COPOLYMER, PURPLE, DARK

Dark, Purple

coating, paint

none

Dulux Trade Vinyl Matt Emulsion, Extra Deep Base, Venetian Crystal 10bb07150

Ici Paints

Leyland Sdm

Temporary

2013-09-10

BM

Oddy test

Drying time: 4 WEEKS, test #7934

WATER BASED ACRYLIC COPOLYMER, TURQUOISE, DARK

Blue, Green

coating, paint

none

Intercoat Primer, 20846

Intercoat

Goodford Pty

Suitable

2013-12-30

BM

Oddy test

Drying time: 4 WEEKS, test #8128

ACRYLIC EMULSION, WHITE

coating, primer

none

Intercoat Satin Enamel, 12830

Intercoat

Goodford Pty

Temporary

2013-12-30

BM

Oddy test

Drying time: 4 WEEKS, test #8127

ACRYLIC EMULSION, WHITE

coating, paint

none

Intercoat Satin Enamel, 12993

Intercoat

Goodford Pty

Suitable

2013-12-30

BM

Oddy test

Drying time: 4 WEEKS, test #8129

ACRYLIC EMULSION, BLACK

coating, paint

none

International 3 In 1 Primer, Sealer, Undercoat,

International

Unsuitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6526

PETROLIUM BASED, WHITE

coating, primer

none

International Exterior Wood Primer,

International

Unsuitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6527

PETROLIUM BASED, WHITE

coating, primer

none

International Quick Dry Floor Paint, Pebblestone

International

Unsuitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6536

PETROLIUM BASED, CREAM

coating, paint

none

Gardex Paint, B Light Green

Jotun

Unknown

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7816

SOLVENT BASED ALKYD ENAMEL + ACTIVE FUNGICIDE, GREEN, LIGHT

Green, Light

coating, paint

none

Gardex Paint, Black

Jotun

Unknown

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7817

SOLVENT BASED ALKYD ENAMEL + ACTIVE FUNGICIDE, BLACK

Black

coating, paint

none

Gardex Paint, P298c Dark Beige

Jotun

Unknown

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7814

SOLVENT BASED ALKYD ENAMEL + ACTIVE FUNGICIDE, BEIGE

Beige

coating, paint

none

Gardex Paint, P730c Dark Blue

Jotun

Unknown

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7813

SOLVENT BASED ALKYD ENAMEL + ACTIVE FUNGICIDE, BLUE, DARK

Blue, Dark

coating, paint

none

Gardex Paint, P7463c Dark Green

Jotun

Unknown

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7812

SOLVENT BASED ALKYD ENAMEL + ACTIVE FUNGICIDE, GREEN, DARK

Dark, Green

coating, paint

none

Gardex Paint, P7506c Light Beige

Jotun

Unknown

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7811

SOLVENT BASED ALKYD ENAMEL + ACTIVE FUNGICIDE, BEIGE

Beige

coating, paint

none

Gardex Paint, P7737c Light Blue

Jotun

Unknown

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7815

SOLVENT BASED ALKYD ENAMEL + ACTIVE FUNGICIDE, BLUE, LIGHT

Blue, Light

coating, paint

none

Color Xpress, Ultra Deep Base, 10031 Space

Kalon Decorative Products

Leyland Sdm

Temporary

2013-07-08

BM

Oddy test

Drying time: 5 WEEKS 4 DAYS, test #7899

VINYL EMULSION, BLUE, DARK

Blue, Dark

coating, paint

none

Dulux Enviro2 Professional Interior Low Sheen , Audd 1274

Ki Paints

Dulux Australia

Suitable

2013-04-18

BM

Oddy test

Drying time: 4 WEEKS, test #7766

ACRYLIC EMULSION, WHITE

coating, paint

none

Ruegener Chalk Paint, 70514 20

Kreidewerk Puger

Pure Nature

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6518

CHALK, METHYLCELLULOSE, WHITE

coating, paint

none

Casein Marble Flour Paint, 70729 20

Kreidezeit, Pure Nature

Pure Nature

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6528

CASEIN, WHITE

White

coating, paint

none

Vega Wall Paint, 70717 20

Kreidezeit

Pure Nature

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6519

Marble flour, chalk, vegetable casein, kaoline, talcum, kieselguhr, lime hydrate, borax, soda, methyl cellulose, WHITE

coating, paint

none

Ms2a Reduced Ketone Resin, Ms2a Resin

Linden Chemicals

Temporary

2009-08-05

BM

Oddy test

Drying time: 4 WEEKS, test #6589

Reduced Cyclic Ketone Polymer, CLEAR

Clear

coating, varnish

none

Ms2a Reduced Ketone Resin With Tinuvin 292 (light Stabilizer), Ms2a Resin + Tinuvin 292

Linden Chemicals

Temporary

2009-08-05

BM

Oddy test

Drying time: 4 WEEKS, test #6590

Reduced Cyclic Ketone Polymer and light stablizer, CLEAR

Clear

coating, varnish

none

Liquitex Professional, Series 1 244 Ivory Black

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6393

ACRYLIC PAINT, BLACK

coating, paint

none

Liquitex Professional, Series 1 432 Titanium White

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6395

ACRYLIC PAINT, WHITE

coating, paint

none

Liquitex Professional, Series 1 530 Bronze Yellow

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6394

ACRYLIC PAINT, YELLOW, DARK

coating, paint

none

Liquitex Professional, Series 1a 316 Phthalocyanine Blue

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6385

ACRYLIC PAINT, BLUE

coating, paint

none

Liquitex Professional, Series 1a 317 Phthalocyanine Green

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6386

ACRYLIC PAINT, GREEN

coating, paint

none

Liquitex Professional, Series 1a 570 Brilliant Blue

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6387

ACRYLIC PAINT, BLUE

coating, paint

none

Liquitex Professional, Series 1a 830 Cadmium Yellow Medium

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6389

ACRYLIC PAINT, YELLOW

coating, paint

none

Liquitex Professional, Series 2 450 Emerald Green

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6391

ACRYLIC PAINT, GREEN, DARK

coating, paint

none

Liquitex Professional, Series 2 510 Cadmium Red Light

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6392

ACRYLIC PAINT, RED

coating, paint

none

Liquitex Professional, Series 3 114 Quinacridone Magenta

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6390

ACRYLIC PAINT, PURPLE, DARK

coating, paint

none

Liquitex Professional, Series1 186 Dioxazine Purple

Liquitex

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6388

ACRYLIC PAINT, PURPLE

coating, paint

none

Little Greene English Heritage Absolute Emulsion, Bronze Red 15

Little Greene

Suitable

2013-07-08

BM

Oddy test

Drying time: 5 WEEKS 4 DAYS, test #7900

VINYL EMULSION, RED

Red

coating, paint

none

Pylox Spray Paint, 705

Nippon Paint

Unsuitable

2013-04-25

BM

Oddy test

Drying time: 4 WEEKS, test #7818

ACRYLIC MODIFIED ALKYD NITRO-CELLULOSE, GOLD

coating, paint

none

Silicone Novabond 2, S29306000

Novabond

Unsuitable

2009-01-20

BM

Oddy test

Drying time: 48 HOURS, test #6156

SILICONE, BLACK

Black

sealant

none

Super Eco Emuslion, 1-11881

Nutshell

Unsuitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6531

PAINT, WHITE

White

coating, paint

none

Powder Coating, Ral 7021, Matt 30% Gloss

Omnikote

Suitable

2013-10-30

BM

Oddy test

Drying time: BAKED, test #8037

POLYESTER, GREY, DARK

Dark, Gray

coating, powder

none

Powder Coating, Ral 8500n, Matt 30% Gloss

Omnikote

Suitable

2013-10-30

BM

Oddy test

Drying time: BAKED, test #8038

POLYESTER, BLACK

Black

coating, powder

none

Powder Coating, Ral 9004 Fine Texture

Omnikote

Suitable

2013-10-30

BM

Oddy test

Drying time: BAKED, test #8041

POLYESTER, BLACK

Black

coating, powder

none

Powder Coating, Ral 9005, Matt 30% Gloss

Omnikote

Suitable

2013-10-30

BM

Oddy test

Drying time: BAKED, test #8040

POLYESTER, BLACK

Black

coating, powder

none

Powder Coating, Ral 9011, Matt 30% Gloss

Omnikote

Suitable

2013-10-30

BM

Oddy test

Drying time: BAKED, test #8039

POLYESTER, BLACK

Black

coating, powder

none

Pactan , 7042 1k

Pactan

Unknown

Suitable

2013-03-22

BM

Oddy test

Drying time: 48 HOURS, test #7737

SILICON, WHITE

White

sealant

none

Pactan , 8051 2k

Pactan

Unknown

Suitable

2013-03-22

BM

Oddy test

Drying time: 48 HOURS, test #7736

SILICON, WHITE

White

sealant

none

Johnstone's Trade Covaplus Vinyl Matt Emulsion, 1710-1298bntb27

PPG Industries

C Brewer & Sons

Suitable

2013-01-19

BM

Oddy test

Drying time: 4 WEEKS, test #7685

VINYL EMULSION, BLUE

Blue

coating, paint

none

Johnstone's Trade Covaplus Vinyl Matt Emulsion, 3147-y94r

PPG Industries

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7700

VINYL EMULSION, RED

Red

coating, paint

none

Johnstone's Trade Covaplus Vinyl Matt Emulsion, Newtons Apple

PPG Industries

C Brewer & Sons

Suitable

2013-02-11

BM

Oddy test

Drying time: 4 WEEKS, test #7701

VINYL EMULSION, RED

Red

coating, paint

none

Leyland Trade Acrylic Eggshell, Pastel Base, Pastel Base

PPG Industries

Unknown

Suitable

2009-02-12

BM

Oddy test

Drying time: 4 WEEKS, test #6193

ACRYLIC, BEIGE

coating, paint

none

Leyland Trade Vinyl Matt Emulsion, Fire Cracker

PPG Industries

Unknown

Suitable

2009-04-13

BM

Oddy test

Drying time: 4 WEEKS, test #6406

ACRYLIC, RED

coating, paint

none

Leyland Trade Vinyl Matt Emulsion, Ral 7043

PPG Industries

Unknown

Suitable

2009-02-13

BM

Oddy test

Drying time: 4 WEEKS, test #6352

ACRYLIC, GREY, DARK

coating, paint

none

Glue Bound Wall Paint, 703301 20

Pure Nature

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6529

CHALK, MAPLE POWDER , TALCUM, METHYLCELLULOSE CAOLINE, WHITE

coating, paint

none

Sanderson Spectrum Paint, 42-27 T Ripe Olive Tr

Sanderson

Simpsons Paints London

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7230

ACRYLIC EMULSION, GREEN

coating, paint

none

Sanderson Spectrum Paint, 42-28 T, Bark Moss Tr

Sanderson

Simpsons Paints London

Suitable

2011-03-22

BM

Oddy test

Drying time: 4 WEEKS, test #7229

ACRYLIC EMULSION, GREEN

coating, paint

none

Acoustical Sealant

Sheetrock

Unknown

Temporary

2000-03-21

GCI

Oddy test

apply as a paint

sealant for walls

sealant

n/a

E27 100% Acrylic Emulsion, E27

Technical Paints Services

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6532

ACRYLIC PAINT, WHITE

coating, paint

none

Msp27 Multisurface Primer, Msp27

Technical Paints Services

Suitable

2009-04-03

BM

Oddy test

Drying time: 4 WEEKS, test #6359

PAINT, WHITE

White

coating, primer

none

Glue-all Multi-purpose Glue

Elmer's

Unknown

Unsuitable

2019-12-20

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Non-toxic, quick drying liquid adhesive. Curing instructions: allow to dry overnight. Applied to BoPET and spread to about 1 mm thick with a glass microscope slide and left to cure for 2 days before testing

White

adhesive, glue, liquid, polymer

Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2019-12-12

MMA

Oddy test (method: 20190226_OT_1)

Color: Natural

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; Received June 2019

Natural

adhesive, polymer, single-sided

Heatnbond Ultrahold

Therm-o-web

Blick Art Materials

Unsuitable

2019-12-12

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

Double-sided iron on adhesive for bonding fabrics; permanent heat activated; sample material ironed between 2 sheets of BoPET before testing, removed from BoPET before testing; Purchased April 2019

Clear

adhesive, heat activated, polymer

Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2019-11-27

MMA

Oddy test (method: 20190226_OT_1)

Color: Natural

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; Received June 2019

Natural

adhesive, polymer, single-sided

Scotch Atg Gold Adhesive Transfer Tape 908, Model #b0000v4pg2c

3M

Amazon.com

Temporary

2019-11-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

Labeled as "acid neutral" 3M Scotch 908 ATG Gold Tape, where the gold refers to a yellow and black-plaid removable backing. 1/4 inch x 36 yards; Adhesion to Steel: 6.6 N/cm; Purchased 2019

Clear

adhesive, double-sided, polymer

Hot Melt Adhesive Scotch Weld (3792 Lm)

3M

Temporary

OK

slight darkening

2019-06-20

AMNH

Oddy test (method: 20190130_OT)

AMNH test #99

Ethylene-Vinyl Acetate Polymer - Translucent white - Cut to weight

White

adhesive, heat activated

Ultimate Optical Mount Removable (4-0167)

Ritrama Inc.

Coloredge

Unsuitable

OK

B showed very slight red tarnish - Lead: Thick orange compacted corrosion, Fluffy white crystals

2019-05-14

AMNH

Oddy test (method: 20190130_OT)

AMNH test #60

Called also "Optimount"; Mounting film; two acrylic adhesive layers between two polyester liners - Clear - Cut to weight and tested on Mylar

Clear

adhesive, pressure sensitive

Colortrans Ct2200

Mactac

Temporary

OK

OK, (sample shows droplets from condensation)

slight darkening

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH test #172

Permanent/removable mounting film; 2 mil clear polyester film coated acrylic pressure sensitive adhesive - Clear - Liner removed and cut to weight

Clear

adhesive, pressure sensitive

Colortrans Ct2500

Mactac

Temporary

Very slight red tarnish

OK

Darkening, Violet tarnish

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH test #173

Permanent self-wetting removable mounting film; 2 mil polyester film coated acrylic pressure sentitive adhesive and clear silicone pressure sensitive adhesive - Clear - Liner removed and cut to weight

Clear

adhesive, pressure sensitive

Copper: Very slight red tarnish - Silver: OK - Lead: Darkening, Violet tarnish

Permatrans Puv2100

Mactac

Unsuitable

Slight red tarnish

OK

Thick orange compacted corrosion, Light white compacted corrosion

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH test #174

Thin optically clear polyester film coated on both sides with acrylic pressure sensitive adhesive - Clear - Liner removed and cut to weight

Clear

adhesive, pressure sensitive

Copper: Slight red tarnish - Silver: OK - Lead: Thick orange compacted corrosion, Light white compacted corrosion

Imagin Bfree Clear (jt5999mbf)

Mactac

Unsuitable

Slight red tarnish

OK

Violet tarnish (pinkish tone), Thick orange compacted corrosion, Light white compacted corrosion

2019-07-29

AMNH

Oddy test (method: 20190130_OT)

AMNH test #177

3.1 mil gloss clear polymeric PVC film; coated on one side with a clear acrylic pressure sensitive adhesive - Transparent - Liner removed and cut to weight

Clear

adhesive, pressure sensitive

Copper: Slight red tarnish - Silver: OK - Lead: Violet tarnish (pinkish tone), Thick orange compacted corrosion, Light white compacted corrosion

3M Vhb Tape 4910

3M

Temporary

OK

Darkening, Thin Yellow/green compacted corrosion

2019-08-23

AMNH

Oddy test (method: 20190130_OT)

AMNH test #199

Double-sided tape; acrylic foam - Clear - Sample was aired up for 2.5 weeks and tested on Mylar

adhesive, double sided, tape

3M Repositionable Tape 9415pc

3M

Temporary

OK

A: Very slight darkening, B: Light white compacted corrosion

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #219

Double coated tape; acrylic adhesive - Transparent - Liner removed; cut to weight and tested on Mylar

adhesive, double sided, tape

3M Repositionable Tape 9425

3M

Temporary

Red tarnish on sample A, sample B is OK

Blue/blue-green tarnish

Slight darkening

2019-09-26

AMNH

Oddy test (method: 20190130_OT)

AMNH test #220

Double coated tape; acrylic adhesive - Transparent - Liner removed; cut to weight and tested on Mylar

adhesive, double sided, tape

Copper: Red tarnish on sample A, sample B is OK - Silver: Blue/blue-green tarnish - Lead: Slight darkening

3M Double Coated Tape 415

3M

Temporary

OK

Very slight darkening, Thin Yellow/green compacted corrosion

2019-10-15

AMNH

Oddy test (method: 20190130_OT)

AMNH test #237

Acrylate copolymer adhesive; PET carrier - Transparent - Liner removed; cut to weight and tested on Mylar

adhesive, double sided, tape

88250 Transfer Tape

Tesa

Unsuitable

2019-10-24

MMA

Oddy test (method: 20190226_OT_1)

Colorless

Water-based acrylic adhesive; 127 µm thick; no carrier, just adhesive; liner is white with blue logo; temperature resistance from -40 deg F; adhesion to steel: 64.51 N/cm; purchased November 2018

Colorless

adhesive, polymer, pressure-sensitive

Photo Tex Ex, Adhesive Printable Fabric

Lex Jet

Unsuitable

2019-10-24

MMA

Oddy test (method: 20190226_OT_1)

White

Extra strength, high tack adhesive backed printable fabric for labels, matte finish, use with solvent, latex, UV curable or eco-solvent ink; purchased August 2019

White

adhesive, polymer, single-sided

Heritage Gummed Paper Tape #tad101002

Klug Conservation

Talas

Temporary

2019-10-23

MMA

Oddy test (method: 20190226_OT_1)

White

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; purchased June 2019

White

adhesive, polymer, single-sided

Metascape Frost M4a-of, Adhesive Vinyl

Metamark

Rdh Supply

Unsuitable

2019-10-23

MMA

Oddy test (method: 20190226_OT_1)

Colorless

Printable clear matte calendered PVC vinyl label with clear solvent acrylic adhesive and kraft paper lining with PE coating; frost etch 85% light transmission; 1 year shelf life, durable 3 years in vertical exposure; hazardous decomposition: carbon monoxide, carbon dioxide, hydrogen chloride, plasticizers, smoke; purchased August 2019

Colorless

adhesive, polymer, single-sided

Metascape Crystal M7a-cr, Adhesive Vinyl

Metamark

Rdh Supply

Unsuitable

2019-10-23

MMA

Oddy test (method: 20190226_OT_1)

Colorless

Printable clear matte calendered PVC with clear solvent acrylic adhesive and kraft paper lining with PE coating; crystal etch 57% light transmission; 1 year shelf life, 7 year durability in vertical exposure; hazardous decomposition: carbon monoxide, carbon dioxide, hydrogen chloride, plasticizers, smoke; purchased August 2019

Colorless

adhesive, polymer, single-sided

415 Double Coated Tape

3M

Fastenal

Temporary

2019-10-17

MMA

Oddy test (method: 20190226_OT_1)

Colorless

Double sided polyester tape with 3M™ Acrylic Adhesive 400 mounted on a 60. lb densified kraft paper liner; 4.0 mil thick; 3/4 inch wide. Lot # 18169 Sub 2# 007. In the lot # the first 2 digits refer to the year of production, and the next three represent the Julian date, so date of manufacture is June 18, 2018. The tape has a 2 year shelf life from the date of manufacture when stored at 72 degrees F and 50% relative humidity; adhesion to steel: 17.65N/cm; purchased September 2019

Colorless

adhesive, double-sided, polymer

Tape For Silicone Parchment Release Paper

Unknown

Masterpak

Temporary

2019-10-17

MMA

Oddy test (method: 20190226_OT_1)

Green

Green tape designed to provide firm adhesion to silicone parchment release paper; catalog number: 1-913; 3.4 mil thick; purchased July 2019

Green

adhesive, polymer, single-sided

Singer Heavy Duty Iron-on Fusing Web

Shanghai Tianyang Hot Melt Adhesives Co.,

Dyno Llc

Unsuitable

2019-10-17

MMA

Oddy test (method: 20190226_OT_1)

White

Iron-on fusing web; catalog number SKU: D00222; copolyamide hot melt adhesive; used in constructing storage boxes; ironed between BoPET mylar-like film according to package instructions before testing; purchased 2019

White

adhesive, heat activated, polymer

Macmark 8300, 832900p Adhesive Vinyl

Mactac

Unsuitable

2019-10-11

MMA

Oddy test (method: 20190226_OT_1)

Gloss White

Vinyl label, calendered soft vinyl (PVC) film coated with permanent acrylic adhesive on white kraft paper liner with silicone coating; 70 µm thick, durable up to 5 years, 2 year shelf life; for printed or cut labels; purchaced September 2019

White, gloss

adhesive, polymer, single-sided

Heritage Gummed Paper Tape, #tad101002

Klug Conservation

Talas

Temporary

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

White

Single-sided paper tape with gumming; 2.5 cm width roll; components: potato starch, paper; purchased June 2019

White

adhesive, polymer, single-sided

Hot Melt Adhesive 3764q

3M

Mcmaster-Carr

Unsuitable

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

White

Low temp hot-melt glue for 3M EC and TC guns;catalog number 7333A37; ethylene-vinyl acetate polymer, naphtha, hydrocarbon resin; solid stick 5/8" x 8"; Prepared on 7/2/2019 and 7/5/2019; Extruded with a used 3M Plygun LT with Quadrack Converter. Remains of previous glue stick and first new glue stick extruded and discarded. Extruded in dots onto aluminum foil. Dots mixed in large glass lab beaker by hand wearing nitrile gloves. Purchased May 2019

White

adhesive, heat activated, polymer

Hot Melt Adhesive 3762q

3M

Mcmaster-Carr

Unsuitable

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

Beige

Low temp hot-melt glue for 3M EC and TC Guns; catalog number 7333A35; Ethylene-Vinyl Acetate polymer, hydrocarbon resin; solid stick 5/8" x 8"; Prepared on 6/28/2019; Extruded with a used 3M Polygun LT with Quadrack Converter. Remains of previous glue stick and first new glue stick extruded and discarded. Extruded in dots onto aluminum foil. Dots mixed in large glass lab beaker by hand wearing nitrile gloves. Purchased May 2019

Beige

adhesive, heat activated, polymer

Dowsil 3145 Silicone Adhesive Clear Mil-a-46146, 4812mktw

Dow Corning

Ellsworth Adhesive

Temporary

2019-09-24

MMA

Oddy test (method: 20190226_OT_1)

Clear

Neutral cure silicone adhesive; 90mL tube; date of manufacture: March 1, 2019 - Lot No. H050J31072; Prepared on 6/24/2019, extruded through the 1/2" nozzle opening in lines onto aluminum foil. After setting, cut into ~1cm lengths. Pieces mixed on aluminum foil by hand (wearing nitrile gloves). Purchased May 2019

Clear

adhesive, glue, liquid, polymer

White A6002, Adhesive Vinyl

Avery

Avery Dennison Office Products

Unsuitable

2019-09-06

MMA

Oddy test (method: 20190226_OT_1)

Color: White; Comment: Lead coupons in the control jars had significant blue tarnish

Calendered opaque vinyl label with permanent solvent adhesive; white; purchased in 2018

White

adhesive, polymer, single-sided

Vector Prov-5 Warm Red Unp, Adhesive Vinyl

Beacon Graphics

Temporary

2019-09-06

MMA

Oddy test (method: 20190226_OT_1)

Color: Red, warm; Comment: Lead coupons in the control jars had significant blue tarnish

Vinyl label, soft PVC film, polyacrylate; 3 mil thick; warm red; item code: PV5391250; purchased 2018

Red

adhesive, polymer, single-sided

Oracal 651-091 Gold, Adhesive Vinyl

Orafol

Temporary

2019-09-06

MMA

Oddy test (method: 20190226_OT_1)

Color: Gold; Comment: Lead coupons in the control jars had significant blue tarnish

Vinyl label, special PVC film, solvent polyacrylate, permanent, 2 year shelf life, durable up to 6 years; adhesion to steel: 46.32 N/cm; 2.5 mil thick; gold; purchased 2018

Gold

adhesive, polymer, single-sided

Fastbond 30-nf Neutral Adhesive

3M

Pilots Hq

Temporary

2019-09-06

Oddy test (method: 20190226_OT_1)

Color: Tan, wood; Comment: Lead coupons in the control jars had significant blue tarnish

Liquid adhesive; water-dispersed, sprayable contact adhesive for high immediate bond strength and long bonding range; bonds most foamed plastics, plastic laminate, wood, plywood, and canvas to themselves and each other; poured onto BoPET film 2 days prior to testing and allowed to spread with gravity, average thickness of 1mm; Catalog Number: 021200-21180; purchased January 2019

Tan, wood

adhesive, glue, liquid, polymer

No

Gorilla Glue Clear

The Gorilla Glue Company

Gorilla Glue

Unsuitable

2019-09-06

MMA

Oddy test (method: 20190226_OT_1)

Color: Colorless, transparent; Comment: Lead coupons in the control jars had significant blue tarnish

Multi-purpose clear liquid adhesive; dries clear and colorless; 3.75 oz bottle; full cure in 24 hours but laid out 2 days prior to testing on BoPET film. 5 six-inch long lines of glue were layed in rows about half an inch apart and smoothed together with a spatula to form an even layer of adhesive, average thickness of 0.5 mm. Purchased January 2019

Colorless, transparent

adhesive, glue, liquid, polymer

Oca 8146-6 Optically Clear Adhesive

3M

Unsuitable

2019-08-21

MMA

Oddy test (method: 20190226_OT_1)

Colorless; Lead coupons in the control jars had significant blue tarnish

Acrylic adhesive, no liner; great for bonding PMMA, glass, PET and other high surface energy and some lower surface energy substrates; adhesion to glass 6.6N/cm; received July 2019

Colorless

adhesive, polymer, pressure-sensitive

Magic Sculpt White

Wesco Enterprises

Suitable

oxidized

2009-03-27

BKM

Oddy test

considered for use in mountmaking

2 part epoxy putty cured 2 weeks

filler/binder mixture (non-paint), paste

Pro-create Terrain Putty (2 Part)

Kraftmark

Suitable

oxidized

2009-03-27

BKM

Oddy test

considered for use in mountmaking

2 part epoxy putty cured 2 weeks

filler/binder mixture (non-paint), paste

Promante Mc Bond 2k Transparent / Structural Adhesive

Promanté

Suitable

2016-09-21

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Structural adhesive

adhesive caulk, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

Dulux Trade Vinyl Matt Emulsion, Light Base, 1005r50b, Fashion Finish

Ici Paints

Unsuitable

2011-07-25

BM

Oddy test

Drying time: 4 WEEKS, test #7281

WATER BASED ACRYLIC COPOLYMER, WHITE

White

coating, paint

none

Msp27 Multisurface Primer, Msp27

Technical Paints Services

Temporary

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6525

WHITE

White

coating, primer

none

Rust-oleum Painters Touch, Matt Spray Paint, Ae0040028e8

Tor Coatings

Unsuitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6979

SOLVENT BASED AEROSOL, GREY, LIGHT

Gray, Light

coating, paint

none

Rust-oleum Painters Touch, Matt Spray Paint, Ae0050005e8

Tor Coatings

Unsuitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6980

SOLVENT BASED AEROSOL, BLACK

Black

coating, paint

none

Rust-oleum Painters Touch, Matt Spray Paint, Ae0050008e8

Tor Coatings

Unsuitable

2010-09-16

BM

Oddy test

Drying time: 4 WEEKS, test #6981

SOLVENT BASED AEROSOL, WHITE

White

coating, paint

none

Polywhey Furniture Clear Satin Fnptsg

Vermont Natural Coatings

Unsuitable

2012-05-15

CMA

Oddy test

2 coats applied to Medex and allowed to dry 24 hours between coatings

clear, satin/ whey based coating

Clear

barrier, coating

none

Polywhey Furniture Gloss Fnptgl

Vermont Natural Coatings

Unsuitable

2012-05-15

CMA

Oddy test

2 coats applied to Medex and allowed to dry 24 hours between coatings

clear, glossy/ whey based coating

Clear

barrier, coating

none

Wood Varnish Pro Aqua, 70762 20

Volvox

Suitable

2009-06-29

BM

Oddy test

Drying time: 4 WEEKS, test #6539

WATER BASED EMULSION, CLEAR

Clear

coating, varnish

none

Uni-ball Signo Dx

Unknown

Suitable

2017-08-16

HCC

Oddy test

Accessioning pen

BLACK

Black

gel ink

Epocite 1004 T

Polymer Technologies Pte., Singapore

Unknown

Suitable

2017-08-16

HCC

Oddy test

Material gets yellow easily. For mounts with carbon fibre only.

CLEAR

Clear

epoxy

Stocolor Sil In

Sto Se & Co Kgaa

Sto Sea Pte. (Singapore)

Suitable

2018-08-23

HCC

Oddy test

none

Interior silicate paint used in public areas, colour white

silicate paint

Ultra Paint, Cured

Benjamin Moore

Temporary

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

Eggshell

White

elvace 1875

Window Gel

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

Orange

cellulose propionate

Liquid Nails Heavy Duty Construction Adhesive, Ln-903

PPG Industries

Unknown

Unsuitable

2019-12-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Grey

Low-solvent, high-strength construction adhesive for plywood, particle board, foamboard, etc; open time: 20 minutes at room temperature; applied to BoPET and spread to about 1 mm thick with a glass microscope slide and cured for 2 days before testing

Gray

adhesive, glue, liquid, polymer

H2o Water-based Contact Adhesive, Wa-h2o

Wilsonart

Unknown

Temporary

2019-12-20

MMA

Oddy test (method: 20190226_OT_1)

Color: White

Liquid adhesive; 20-30 minute dry time, open time about 60 minutes; non-flammable, low VOC and VHAP content; chemical components: benzene, tetrapropylene derivatives, sulfonated sodium salts; applied to BoPET allowed to spread with gravity to about .5 mm thick, and cured for 2 days before testing

White

adhesive, glue, liquid, polymer

Carpenter's Wood Glue

Elmer's

Unknown

Unsuitable

2019-12-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Yellow

Liquid adhesive made for furniture repair, best for woods, particle board, and porous materials; 20-30 minute clamp time, 24 hours to full bond. Applied to BoPET and spread to about 1 mm thick with a glass microscope slide and allowed to cure for 2 days before testing

Yellow

adhesive, glue, liquid, polymer

3M Atg #9082

3M

Unsuitable

fail, dark black corrosion at both tips, more than control

pass

fail, green and white with areas of orange/red. Also, overall very small platelets of shiny white/irridescent. This was not on control

2006-02-21

BKM

Oddy test

acid free adhesive transfer (double sided, no carrier)

adhesive tape, double sided, polymer

3M Vhb 9473 Adhesive Transfer Tape

3M

Suitable

no change

2008-12-30

BKM

Oddy test

adhesive tape, double sided, polymer

Adchem 254-74 Tape

Adchem

Suitable

very slightly corroded

ok

very slightly corroded

2009-02-10

BKM

Oddy test

same result as Volara sample, but slightly more corroded than control

double faced acrylic pressure sensitive adhesive tape with release liner

adhesive tape, double sided, polymer

3M 415 Double Sided Tape ""splicing Tape""

3M

Talas

Suitable

very slight darkening, no significant corrosion

no change, same as control

2016-07-05

BKM

Oddy test

uses 3M adhesive 400 (medium firm acrylic pressure sensitive adhesive system), carrier is a polyester film, liner is tan #60 kraft paper

adhesive tape, double sided, polymer

Ag: no change,Cu: very slight darkening, no significant corrosion,Pb: no change

3M 465 Double Sided Tape

3M

Talas

Suitable

very slight darkening, no significant corrosion

no change, same as control

2016-07-05

BKM

Oddy test

uses 3M adhesive 400 (medium firm acrylic pressure sensitive adhesive system), no carrier film, liner is tan #60 kraft paper

adhesive tape, double sided, polymer

Ag: no change,Cu: very slight darkening, no significant corrosion,Pb: no change

3M Vhb / Acrylic Foam Tape 4910 F

3M

Suitable

2016-08-04

BKM

Oddy test

Cu corrosion appeared the same as on both controls

Acrylic foam tape

adhesive tape, double sided, polymer

Ag: no corrosion,Cu: minor darkening,Pb: No corrosion

3M Aluminum Foil Tape #431

3M

Temporary

unspecified temp: pass, very slight overall iridescence at tip of coupon

pass

pass, intermediate (light green on inside edge, slight white on outside edge)

2006-02-23

BKM

Oddy test

Pass for short term exhibition, not long term

2"" wide, acrylic adhesive

adhesive tape, polymer, single sided

Agateen

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

CLEAR

Clear

cellulose nitrate, polymer

Aura Paint, Cured

Benjamin Moore

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

Eggshell

White

polystyrene acrylate ester

Clean Seal Adhesive Teardrop Gasket

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

Black

polydimethylsiloxane

Fuhr Sealant

Suitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

Clear/White

Clear, White

polymer, sealant

Rtv162 Silicone Caulk

Unsuitable

2016-07-01

IMA

Evolved Gas Analysis, Microchemical Tests, Oddy test

White

polymer, silicone polydimethylsiloxane

3M Scotch #853

3M

Unsuitable

pass

fail (orange/red at inside tip grown along side very light white along tip)

2006-02-23

BKM

Oddy test

polyester film with acrylic adhesive

adhesive tape, polymer, single sided

Nashua #330x

Nashua

Suitable

unspecified temp: pass, very slight overall darkening, same as control

pass

unspecified temp: pass

2006-04-04

BKM

Oddy test

Aluminum foil tape with pressure sensitive acrylic adhesive

adhesive tape, polymer, single sided

3/8"" Linen Tape

Talas

Suitable

same as control

2019-09-18

BKM

Oddy test

70% linen 30% cotton; unbleached and unsized

adhesive tape, polymer, single sided

3M Super 77 Multipurpose Spray Adhesive

3M

Amazon.com

Temporary

2020-02-14

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

A high tack, high coverage and fast drying synthetic elastomer adhesive; Translucent, density of 6 lb/gal, 51% VOC, 15 sec - 1 min dry time; Store at 60-80°F; Contains acetone, non-volatile components, propane, cyclohexane, petroleum distillates, and hexane; Purchased January 2020, cured for 7 days before testing

Clear

adhesive, glue, liquid, polymer

File:2794 GA.jpg

Pc-11 Marine All Purpose High Strength Epoxy 2 Oz

Protective Coating Company

Ace Hardware

Temporary

2020-02-14

MMA

Oddy test (method: 20190226_OT_1)

Color: White

2-Part epoxy; off-white but can be tinted with universal pigment; multipurpose epoxy designed for use as an adhesive, sealer or filler; high strength; 40 min work time; 24 hr cure time; 2.5g of each part mixed until uniform and spread on BoPET film with an average thickness of 1.5 mm. Catalog Number: Item no. 1002773; purchased January 2019, cured for 17 days before testing

White

adhesive, glue, liquid, polymer

Repositionable Spray Adhesive 75ca

3M

Mcmaster-Carr

Temporary

2020-01-02

MMA

Oddy test (method: 20190226_OT_1)

Color: White/yellow

Low VOC pressure sensitive aerosol spray adhesive; chemical components: Acetone, 1,1-difluoroethane, propane, cycloexane, isobutane, dimethyl glutaraldehyde; sprayed onto BoPET one layer at a time waiting at least 10 seconds between each layer and left to cure an additional 24 hours before testing

White/yellow

adhesive, polymer, pressure-sensitive

Sikasil Neutral Cure Sg-500 Two Part Structural Silicone Adhesive

Sikasil

Unsuitable

2020-01-02

MMA

Oddy test (method: 20190226_OT_1)

Color: Black/grey

Two-part, high modulus, neutral-curing structural silicone adhesive; Sikasil® SG-500 is manufactured in accordance with ISO 9001/14001 quality assurance system and the responsible care program; Cures in 270 minutes (~4.5 hours); Prepared using a special extrusion gun and extruded onto BoPET 24 hours before testing

Black/grey

adhesive, glue, liquid, polymer

Marmoleum Piano

Forbo Flooring Systems

Forbo Flooring Uk

Unsuitable

2018-12-11

NYUL

Oddy test

Color is grey dusk

Linseed oil, inorganic fillers, rosin, jute, wood flour

grey dusk

flooring, other

Marmoleum Piano

Forbo Flooring Systems

Forbo Flooring Uk

Unsuitable

2018-12-11

NYUL

Oddy test

Color is mellow yellow

Linseed oil, inorganic fillers, rosin, jute, wood flour

Yellow, mellow

flooring, other

Gerflor Mipolam Symbioz

Gerflor The Flooring Group

Gerflor Usa

Unsuitable

2018-12-11

NYUL

Oddy test

Color is black diamond

PVC, Plasticizer

black diamond

flooring, other

Gerflor Mipolam Symbioz

Gerflor The Flooring Group

Gerflor Usa

Unsuitable

2018-12-11

NYUL

Oddy test

Color is sunshine

PVC, Plasticizer

sunshine

flooring, other

Pe #2.2 New England Foam

Unknown

New England Foam

Suitable

2019-01-30

NYUL

Oddy test

none

Polyethylene

foam, non building insulation, polymer

Epe #1.3 Arplank

Arplank

New England Foam

Suitable

2019-01-30

NYUL

Oddy test

none

Expanded polyethylene

foam, non building insulation, polymer

Epe #1.9 Arplank

Arplank

New England Foam

Suitable

2019-01-30

NYUL

Oddy test

none

Expanded polyethylene

foam, non building insulation, polymer

Xple #4 Microcell

Microcell

New England Foam

Temporary

2019-01-30

NYUL

Oddy test

Color is black

Crosslinked polyethylene

Black

foam, non building insulation, polymer

Xple #2 Microcell

Microcell

New England Foam

Temporary

2019-01-30

NYUL

Oddy test

Color is blue

Crosslinked polyethylene

Blue

foam, non building insulation, polymer

Pe #4 New England Foams

Unknown

New England Foam

Suitable

2019-01-30

NYUL

Oddy test

Color is white

Polyethylene

white

foam, non building insulation, polymer

Neoprene Uchannel

Trim Lok Incorporated

Mcmaster-Carr

Suitable

2019-01-30

NYUL

Oddy test

Color is black, 8507K15 (Line Item #4)

Neoprene rubber

Black

u-channel

Neoprene Uchannel

Trim Lok Incorporated

Mcmaster-Carr

Unsuitable

2019-01-30

NYUL

Oddy test

Color is black, 8507K52 (Line Item #2)

Neoprene rubber

Black

u-channel

Neoprene Foam With Pressure Sensitive Adhesive (1/2" T X 1/2" W X 10ft)

Unknown

Mcmaster-Carr

Unsuitable

2019-04-02

NYUL

Oddy test

Color is black

N/A

Black

gasketing

Premium Neoprene Sponge With Pressure Sensitive Adhesive (1/8" X 3/4" X 10 Ft)

Unknown

Mcmaster-Carr

Unsuitable

2019-04-02

NYUL

Oddy test

Color is black

N/A

Black

gasketing

4311-n With Sn Psa One Side (0.125"th X 12" X 12")

Unknown

Jacobs & Thompson

Temporary

2019-04-02

NYUL

Oddy test

Color is black

SN PSA is rubber adhesive

Black

gasketing

0.125" Thick Clear Silicone Rubber Sheeting

Unknown

Acme Rubber

Suitable

2019-04-02

NYUL

Oddy test

Color is clear

Silicone

Clear

gasketing

Neoprene U-channel

Unknown

Acme Rubber

Suitable

2019-04-08

NYUL

Oddy test

Color is black, product number 8507K43

Neoprene rubber

Black

u-channel

Stopox Bb T 200

Sto Se & Co Kgaa

Sto Sea Pte. (Singapore)

Suitable

2018-08-23

HCC

Oddy test

none

Coating system for floors used in public areas, colour amber

epoxy terrazzo coating system for floors

Aqua Woodguard

Nippon Paint

Unknown

Suitable

2019-02-14

HCC

Oddy test

none

Exterior wood varnish

coating, paint & primer

Art Resin

Art Resin Ventures

Unsuitable

2019-12-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

Low VOC no BPA, 2-part epoxy resin and hardener; chemical components: DGEBA-Epoxy Resin (CAS25068-38-6), modified amine adduct; hard cure in 24 hours, full cure 72 hours; Cured in a prepared silicone rubber mold (Zhermack Elite Double 8 cured for 48 hours) that was cleaned with ethanol and left to dry for 2 hours before casting the epoxy. Prepared on 11/18/2019 using a 1:1 mix ratio, stirred with a glass rod for 3 minutes and poured into the silicone rubber mold. The epoxy was cured for 4 days

Clear

adhesive, glue, liquid, polymer

Hxtal Nyl-1 2-part Epoxy

Hxtal

Talas

Unsuitable

2019-12-20

MMA

Oddy test (method: 20190226_OT_1)

Color: Clear

2-Part epoxy resin; chemical componentes: diglycidyl ether, 1-chloro2,3-epoxy propane, poly(oxy)*methyl-1,2-ethanendiyl), alpha-hydro-omega-(2-aminomethylathoxy)-ether 2-ethyl-2-(hydroxymethyl)-1,3-propanendiol (3:1), 1,3-diaza-2,4-cyclopentadiene, glyoxaline; after 7 days at 75⁰F Hxtal has set to 90% of its ultimate bond strength; Cured in a prepared silicone rubber mold (Zhermack Elite Double 8 cured for 48 hours), prepared on 11/14/2019 using 3:1 mix ratio, stirred for 3 minutes using a glass stir rod. The mixed epoxy was poured into the silicone rubber mold and cured for 8 days

Clear

adhesive, glue, liquid, polymer

COPY OVER THIS ONE

2024-12-21

No

COPY OVER THIS ONE

2024-12-21

No

COPY OVER THIS ONE

2024-12-21

No

Manex dress form – foam support

Manex

Talas

Suitable

silght reddening (Temporary)

similar to the controls. (Pass/Permanent)

2022-05-05

CPack

Oddy Test

“Vendôme” model, style #BVF4-1, yellow foam support

Yellow

Polymer - foam - non building insulation

No Corrosion

Manex fiberglass mannequin, painted white

Manex

Temporary

similar to the controls. (Pass/Permanent)

slight yellowing (Temporary)

haze from slight crystal formation over the entire coupon (Temporary)

2022-05-05

CPack

Oddy Test

“Elle” model with Benjamin Moore paint; segment of arm taken from the wrist tested

White

Polymer

Copper: similar to the controls. (Pass/Permanent); Silver: slight yellowing (Temporary); Lead: haze from slight crystal formation over the entire coupon (Temporary)

Manex fiberglass mannequin, painted brown

Manex

Unsuitable

slight reddening (Temporary)

slight yellowing (Temporary)

white fluffy crystal formation (Fail)

2022-05-05

CPack

Oddy Test

“Elle” model with Benjamin Moore paint; segment of arm taken from the wrist tested

Brown

Polymer

Copper: slight reddening (Temporary); Silver: slight yellowing (Temporary); Lead: white fluffy crystal formation (Fail)

Manex fiberglass mannequin, painted white

Manex

Unsuitable

silght reddening (Temporary)

slight yellowing and darnkening (Temporary)

haze from slight crystal formation over the entire coupon with small spots of heavier crystal formation (Temporary)

2022-05-05

CPack

Oddy Test

White nylon coupon holder yellowed during test

“Elle” model with Benjamin Moore paint; shavings from outer paint and fiberglass layers

White

Polymer

Copper: silght reddening (Temporary); Silver: slight yellowing and darnkening (Temporary); Lead: haze from slight crystal formation over the entire coupon with small spots of heavier crystal formation (Temporary)

Manex fiberglass mannequin, painted brown

Manex

Temporary

silght reddening (Temporary)

similar to the controls. (Pass/Permanent)

haze from slight crystal formation over the entire coupon (Temporary)

2022-05-05

CPack

Oddy Test

“Elle” model with Benjamin Moore paint; shavings from outer paint and fiberglass layers

Brown

Polymer

Copper: silght reddening (Temporary); Silver: similar to the controls. (Pass/Permanent); Lead: haze from slight crystal formation over the entire coupon (Temporary)

Manex dress form - jersey cover

Manex

Temporary

silght reddening (Temporary)

similar to the controls. (Pass/Permanent)

2022-05-05

CPack

Oddy Test

“Vendôme” model, style #BVF4-1, beige jersey cover

Beige

fabric

Copper: silght reddening (Temporary); Silver: similar to the controls. (Pass/Permanent); Lead: similar to the controls. (Pass/Permanent)

Manex dress form – foam support

Manex

Suitable

2022-05-05

CPack

Oddy Test

“Vendôme” model, style #BVF4-1, yellow foam support

Yellow

Polymer - foam - non building insulation

No

No corrosion

polyester batting

Testfabrics

Suitable

2022-05-05

CPack

Oddy Test

1 ½” thick Polyester Batting without any resin

polymer

No corrosion

3D printed mannequin

CNL

LACMA

Unsuitable

Extreme corrosion on all coupons

demonstrates a very sticky film

2022-09-09

CP/GN

Oddy Test

Gray polymer base (polylactic acid?) with gray paint

Grey

polymer

Extreme corrosion on all coupons; Lead: demonstrates a very sticky film

Zing fiberglass mannequin - matte white

Zing Display

Unsuitable

similar to the controls. (Pass/Permanent)

white fluffy crystal formation on entire coupon (Fail)

2022-09-09

Oddy Test

matte white female - resin and paint layer

matte white

polymer

Copper: similar to the controls. (Pass/Permanent); Silver: similar to the controls. (Pass/Permanent); Lead: white fluffy crystal formation on entire coupon (Fail)

Dorfman Fabric Covers

Dorfman

Suitable

2022-12-08

SG/GN

Oddy Test

80% nylon/20% spandex - steel color

Steel

Fabric

No Corrosion

Dorfman Fabric Covers

Dorfman

Suitable

2022-12-09

SG/GN

Oddy Test

80% nylon/20% spandex - steel color

Copper

Fabric

No Corrosion

Dorfman Fabric Covers

Dorfman

Suitable

2022-12-10

SG/GN

Oddy Test

80% nylon/20% spandex - steel color

Black

Fabric

No Corrosion

Ethafoam

Unsuitable

similar to the controls. (Pass/Permanent)

corrosion at contact with nylon

white fluffy crystal formation (Fail)

2022-12-08

SG/GN

Oddy Test

Polyethylene open cell foam

Foam

Copper: similar to the controls. (Pass/Permanent); Silver: corrosion at contact with nylon; Lead: white fluffy crystal formation (Fail)

Shoelace

TZ Lace

Amazon

Temporary

similar to the controls. (Pass/Permanent)

haze from slight crystal formation (Temporary)

2023-09-07

SG

Oddy Test

Shoelace made of cotton and wax

Fabric

Copper: slight yellowing (Temporary); Silver: similar to the controls. (Pass/Permanent); Lead: haze from slight crystal formation (Temporary)

Dittoform

Unsuitable

severe darkening (Fail)

similar to the controls. (Pass/Permanent)

white fluffy crystal formation (Fail)

2023-09-07

SG

Oddy Test

LDPE foam

Foam

Copper: severe darkening (Fail); Silver: similar to the controls. (Pass/Permanent); Lead: white fluffy crystal formation (Fail)

Mannequin

CNL Mannequins

Unsuitable

light corrosion (Temporary)

similar to the controls. (Pass/Permanent)

haze from slight crystal formation, yellowing, distinct smell coming from container (Fail)

2023-09-07

SG

Oddy Test

ABS Polymer

polymer

Copper: light corrosion (Temporary); Silver: similar to the controls. (Pass/Permanent); Lead: haze from slight crystal formation, yellowing, distinct smell coming from container (Fail)

Manex Fabric Covers

Manex

Temporary

silght reddening (Temporary)

similar to the controls. (Pass/Permanent)

2023-12-14

CP/WJ

Oddy Test

Dark grey

Fabric

Copper: silght reddening (Temporary); Silver: similar to the controls. (Pass/Permanent); Lead: similar to the controls. (Pass/Permanent)

Manex Fabric Covers

Manex

Suitable

2023-12-14

CP/WJ

Oddy Test

Light grey

Fabric

No Corrosion

Veltex Display Loop fabric

Velcro

Levitt Industrial textile

Temporary

silght reddening (Temporary)

similar to the controls. (Pass/Permanent)

2023-12-15

CP/WJ

Oddy Test

Nylon/Polyster - White color

White

Fabric

Copper: silght reddening (Temporary); Silver: similar to the controls. (Pass/Permanent); Lead: similar to the controls. (Pass/Permanent)

Fiberglass mannequin

Unsuitable

similar to the controls. (Pass/Permanent)

white fluffy crystal formation (Fail)

2023-12-15

CP/WJ

Oddy Test

Pink

Polymer

Copper: similar to the controls. (Pass/Permanent); Silver: similar to the controls. (Pass/Permanent); Lead: white fluffy crystal formation (Fail)

Fiberglass mannequin

Zing Display

Temporary

similar to the controls. (Pass/Permanent)

haze from slight crystal formation over the entire coupon (Temporary)

2023-12-16

CP/WJ

Oddy Test

matte white female - resin and paint layer

Matte white

Polymer

Copper: similar to the controls. (Pass/Permanent); Silver: similar to the controls. (Pass/Permanent); Lead: haze from slight crystal formation over the entire coupon (Temporary)

Dorfman Fabric Covers

Dorfman

Temporary

Similar to control (Pass/Permanent)

Silght haze crystal formation over the entire coupon, yellow tarnish (Temporary)

2024-01-24

WJ

Oddy Test

Retested

80% nylon/20% spandex - chocolate color

Chocolate

Fabric - exhibition/woven

Cu: Similar to control (Pass/Permanent); Ag: Similar to control (Pass/Permanent); Pb: Silght haze crystal formation over the entire coupon, yellow tarnish (Temporary)

Dorfman Fabric Covers

Dorfman

Temporary

Similar to control (A) (Pass/Permanent), Spot reddening (B) (Temporary)

Similar to control (Pass/Permanent)

Silght yellow tarnish, darkening (A), Slight darkening (B) (Temporary)

2024-01-24

WJ

Oddy Test

Retested

80% nylon/20% spandex - Sable color

Sable

Fabric - exhibition/woven

No

Cu: Similar to control (A) (Pass/Permanent), Spot reddening (B) (Temporary); Ag: Similar to control (Pass/Permanent); Pb: Silght yellow tarnish, darkening (A), Slight darkening (B) (Temporary)

Wilsonart 950 Contact Adhesive

Wilsonart

Temporary

Reddening (Temporary)

Silght yellowing, development of white film (Temporary)

Darkening (Temporary)

2024-01-24

WJ

Oddy Test

950 Adhesive

Red

Adhesive

Cu: Reddening (Temporary); Ag: Silght yellowing, development of white film (Temporary); Pb: Darkening (Temporary)

Dorfman Fabric Covers

Dorfman

Suitable

2024-01-24

WJ

Oddy Test

Retested

80% nylon/20% spandex - natural color

Natural

Fabric - exhibition/woven

No corrosion

Unisono 4000 233

Creation Baumann

Temporary

A: Very slight red tarnish; B: Very slight red tarnish; Overall: Suitable

A: Similar to control; B: Similar to control; Overall: Suitable

A: Thick orange compacted corrosion; B: Thick orange compacted corrosion; Overall: Temporary

2024-04-18

Oddy Test

Test ID: 504; Control ID: C57; Sample was soaked in DI water overnight, then washed in a washing machine using Orvis WA Paste, air dried, and cut to weight. A: P lid B: T1 lid

Fabric - exhibition/woven

100% Cotton.

Green

plant-based (non-wood)

fabric (display cloth)

Display

Undecided

Dorfman Fabric Covers

Dorfman

Suitable

2024-01-24

WJ

Oddy Test

Retested

80% nylon/20% spandex - silver color

Silver

Fabric - exhibition/woven

No Corrosion

Superfine Eggshell White; 96-20-1732N

Mohawk

Suitable

A: Similar to control; B: Similar to control; Overall: Suitable

A: Very slight darkening; B: Similar to control; Overall: Suitable

2024-04-18

Oddy Test

Test ID: 506; Control ID: C57; Sample was cut to weight. A: P lid B: T1 lid

Board - cellulosic (eg.: paper, cardboard)

Off-white or cream, White

plant-based (non-wood)

sheet (stiff; cardstock)

Display

Undecided

Dorfman Fabric Covers

Dorfman

Suitable

2024-01-24

WJ

Oddy Test

Retested

80% nylon/20% spandex - Khaki color

Khaki

Fabric - exhibition/woven

No Corrosion

Wilsonart 7951K-335-18 Plastic Laminate

Wilsonart

Suitable

2024-01-24

WJ

Oddy Test

Asian Sun 7951

Laminate

No Corrosion

Wilsonart Water-based Conact Adhesive

Wilsonart

Suitable

2024-01-24

WJ

Oddy Test

Water-based

Adhesive

No Corrosion

TEST NAME

Unknown

Preservation Equipment

none

Temporary

2024-12-21

BM

Oddy test

WHITE, PEL 419-1044 BATCH 1117422

sample prep: MELTED AND COOLED, test #7600

White

adhesive

COPY OVER THIS ONE

2024-12-21

No

Sintra

My least favorite

Talas

Unsuitable

A: slight tarnish; B: slight tarnish; Overall: Suitable

A: light purpling; B: light purpling; Overall: Temporary

A: heavy haze; B: heavy haze; Overall: Unsuitable

2012-12-03

Oddy

Test ID: 1; Control ID: 2; Reused lid (T4) in replicate B.

board, 1/8 thick, cut to weight PVC White Board - plastic/polymeric/synthetic Display No

No

Sintra

My favorite manufacturer

Talas

Unsuitable

A: slight tarnish; B: slight tarnish; Overall: Suitable

A: light purpling; B: light purpling; Overall: Temporary

A: heavy haze; B: heavy haze; Overall: Unsuitable

2012-12-03